As it becomes more important to replace fossil fuels with alternative fuels, biofuels like ethanol are becoming more commercially used. The increased use of ethanol brings good influences such as lower impact on the environment. However, the use of ethanol can also bring negative effects regarding corrosion of metals. In the automotive industry aluminium has been seen affected by a novel very aggressive corrosion phenomenon, alcoholate corrosion. This master thesis investigation has investigated the effect of a few parameters of importance for alcoholate corrosion; water, temperature, time and pressure. The aluminium alloys AA6063 and A380 have been investigated and the capacity of five different surface treatments of AA6063 has been tested to observe if they inhibit the effect of alcoholate corrosion.   Throughout the experiments the water dependence of alcoholate corrosion has showed to be of large importance for the corrosion process. An increase in water content will postpone the start of alcoholate corrosion or prevent corrosion to occur.  A correlation between temperature and time has been observed. Higher temperatures results in a shorter time period of exposure before alcoholate corrosion occurs, and vice versa. The effect of different pressures was investigated and showed no effect on alcoholate corrosion when using pressurisation with the inert nitrogen gas.   All surface treatments revealed a capacity to protect the aluminium alloy against alcoholate corrosion to different extent. The electroless nickel plating seemed to prevent alcoholate corrosion while the Keronite coating seemed more sensitive to this form of corrosion.

Im Fokus dieser Arbeit standen zwei Ziele. Zum einem war es Forschungsgegenstand, dass Konzept der Zwillingspolymerisation auf germaniumhaltige, molekulare Vorstufen wie zum Beispiel Germylene, spirozyklische Germaniumverbindungen und molekulare Germanate zu erweitern und somit organisch-anorganische Komposite beziehungsweise Hybridmaterialien darzustellen. Dazu wurden neuartige Germaniumalkoxide auf der Basis von Benzylalkoholaten, Salicylalkoholaten sowie Benzylthiolaten synthetisiert, charakterisiert und auf ihre Fähigkeit Komposite beziehungsweise Hybridmaterialien über den Prozess der Zwillingspolymerisation zu erhalten studiert. Ein zweites Ziel dieser Arbeit war es, Beziehungen zwischen der Struktur und der Reaktivität dieser molekularen Vorstufen sowie deren Einfluss auf die Eigenschaften der erhaltenen Polymerisationsprodukte zu identifizieren und systematisch zu untersuchen. Hierfür wurden zum einen verschiedene Substituenten, welche unterschiedliche elektronische sowie sterische Eigenschaften aufweisen, an den aromatischen Einheiten der molekularen Vorstufen eingeführt. Die Effekte der Substituenten auf den Prozess der Zwillingspolymerisation und auf die Eigenschaften der Komposite beziehungsweise Hybridmaterialien wurden für die Verbindungsklasse der Germanium(II)salicylalkoholate, der molekularen Germanate sowie der spiro-zyklischen Siliziumsalicylalkoholate untersucht. Spirozyklische Siliziumsalicylalkoholate, wie zum Beispiel 4H,4’H-2,2‘-Spirobi[benzo[d][1,3,2]dioxasilin], wurden im Rahmen dieser Arbeit mit einbezogen, da sie aufgrund ihres nahezu idealen Zwillingspolymerisationsprozesses geeignete Modelverbindungen für Reaktivitätsstudien darstellen. Zudem wurde der Einfluss der Substituenten auf die Charakteristika der aus den Kompositen beziehungsweise Hybridmaterialien erhaltenen Folgeprodukte (poröse Kohlenstoffmaterialien und oxydische Materialien) studiert. Des Weiteren wurde eine Serie von spirozyklischen Germaniumthiolaten, welche isostrukturell zu 4H,4’H-2,2‘-Spirobi[benzo[d][1,3,2]dioxasilin] sind, synthetisiert, um systematisch den Einfluss der Chalkogenide, Sauerstoff und Schwefel, in benzylständiger sowie phenylständiger Position auf deren Reaktionsvermögen im Polymerisationsprozess zu untersuchen. Die experimentellen Ergebnisse zu den Struktur-Reaktivitätsbeziehungsstudien wurden, soweit es jeweils durchführbar war, mittels quantenchemische Rechnungen validiert und die daraus gezogenen Schlüsse in die Diskussion zur Interpretation der experimentellen Ergebnisse mit einbezogen.

Im Fokus dieser Arbeit standen zwei Ziele. Zum einem war es Forschungsgegenstand, dass Konzept der Zwillingspolymerisation auf germaniumhaltige, molekulare Vorstufen wie zum Beispiel Germylene, spirozyklische Germaniumverbindungen und molekulare Germanate zu erweitern und somit organisch-anorganische Komposite beziehungsweise Hybridmaterialien darzustellen. Dazu wurden neuartige Germaniumalkoxide auf der Basis von Benzylalkoholaten, Salicylalkoholaten sowie Benzylthiolaten synthetisiert, charakterisiert und auf ihre Fähigkeit Komposite beziehungsweise Hybridmaterialien über den Prozess der Zwillingspolymerisation zu erhalten studiert. Ein zweites Ziel dieser Arbeit war es, Beziehungen zwischen der Struktur und der Reaktivität dieser molekularen Vorstufen sowie deren Einfluss auf die Eigenschaften der erhaltenen Polymerisationsprodukte zu identifizieren und systematisch zu untersuchen. Hierfür wurden zum einen verschiedene Substituenten, welche unterschiedliche elektronische sowie sterische Eigenschaften aufweisen, an den aromatischen Einheiten der molekularen Vorstufen eingeführt. Die Effekte der Substituenten auf den Prozess der Zwillingspolymerisation und auf die Eigenschaften der Komposite beziehungsweise Hybridmaterialien wurden für die Verbindungsklasse der Germanium(II)salicylalkoholate, der molekularen Germanate sowie der spiro-zyklischen Siliziumsalicylalkoholate untersucht. Spirozyklische Siliziumsalicylalkoholate, wie zum Beispiel 4H,4’H-2,2‘-Spirobi[benzo[d][1,3,2]dioxasilin], wurden im Rahmen dieser Arbeit mit einbezogen, da sie aufgrund ihres nahezu idealen Zwillingspolymerisationsprozesses geeignete Modelverbindungen für Reaktivitätsstudien darstellen. Zudem wurde der Einfluss der Substituenten auf die Charakteristika der aus den Kompositen beziehungsweise Hybridmaterialien erhaltenen Folgeprodukte (poröse Kohlenstoffmaterialien und oxydische Materialien) studiert. Des Weiteren wurde eine Serie von spirozyklischen Germaniumthiolaten, welche isostrukturell zu 4H,4’H-2,2‘-Spirobi[benzo[d][1,3,2]dioxasilin] sind, synthetisiert, um systematisch den Einfluss der Chalkogenide, Sauerstoff und Schwefel, in benzylständiger sowie phenylständiger Position auf deren Reaktionsvermögen im Polymerisationsprozess zu untersuchen. Die experimentellen Ergebnisse zu den Struktur-Reaktivitätsbeziehungsstudien wurden, soweit es jeweils durchführbar war, mittels quantenchemische Rechnungen validiert und die daraus gezogenen Schlüsse in die Diskussion zur Interpretation der experimentellen Ergebnisse mit einbezogen.:Contents List of Abbreviations S. 11 1 Introduction S.14 2 Germanium alkoxides and germanium thiolates S. 18 2.1 Preamble S. 18 2.2 Germanium alkoxides S. 18 2.2.1 Germanium(II) alkoxides S. 20 2.2.2 Germanium(IV) alkoxides S. 23 2.2.3 Alkoxidogermanates S. 29 2.3 Germanium thiolates S. 31 2.3.1 Germanium(II) thiolates S. 33 2.3.2 Germanium(IV) thiolates S. 34 2.3.3 Thiolatogermanates and cationic germanium thiolato transition metal complexes S. 36 2.4 Germanium alkoxido thiolates S. 38 2.5 Concluding remarks S. 40 3 Individual Contributions S. 43 4 Microporous Carbon and Mesoporous Silica by Use of Twin Polymerization: An integrated Experimental and Theoretical Approach on Precursor Reactivity S. 46 4.1 Abstract S. 46 4.2 Introduction S.46 4.3 Results and Discussion S. 48 4.3.1 Synthesis and Characterization S. 48 4.3.2 Thermally induced twin polymerization of monosubstituted Precursors (para position) S.49 4.3.2.1 Studies on reactivity according to thermally induced twin polymerization S. 50 4.3.2.2 Characterization of the hybrid materials as obtained by thermally induced twin polymerization S. 51 4.3.2.3 Thermally induced twin polymerization of di-substituted precursors (ortho and para position) S. 52 4.3.2.4 Conclusions drawn for the thermally induced twin polymerization S. 54 4.3.3 Proton-assisted twin polymerization S. 54 4.3.3.1 Studies on the reactivity according to proton-assisted twin polymerization S.55 4.3.3.2 Characterization of the hybrid materials as obtained by proton-assisted twin polymerization S.56 4.3.3.3 Computational studies on proton-assisted twin polymerization S. 58 4.3.3.4 Conclusions drawn for the process of proton-assisted twin polymerization S. 60 4.3.4 Characterization of the porous materials S.61 4.4 Conclusions S.64 4.5 Experimental Section S. 65 4.5.1 General S.65 4.5.2 General procedure for the synthesis of phenolic resin-silica hybrid materials by thermally induced twin polymerization in melt - exemplified for compound 1 S. 66 4.5.3 General procedure for the synthesis of phenolic resin-silica hybrid materials by proton-assisted twin polymerization in solution - exemplified for compound 1 S. 66 4.5.4 General procedure for the synthesis of microporous carbon - exemplified for hybrid material HM-1T S. 66 4.5.5 General procedure for the synthesis of mesoporous silica - exemplified for hybrid material HM-1T S. 67 4.5.6 Single-Crystal X-ray Diffraction Analyses S. 67 4.5.7 Computational Details S. 67 4.6 Acknowledgments S. 68 4.7 Keywords S.68 4.8 Supporting Information Chapter 4 S. 69 5 Synthesis of germanium dioxide nanoparticles in benzyl alcohols – a comparison S. 82 5.1 Abstract S. 82 5.2 Introduction S. 82 5.3 Results and Discussion S.83 5.4 Conclusions S. 87 5.5 Experimental Section S. 87 5.5.1 General S. 87 5.5.2 Syntheses S. 88 5.5.3 Synthesis of GeO2 in ortho-methoxy benzyl alcohol – sample A S. 88 5.5.4 Synthesis of GeO2 in benzyl alcohol under inert conditions – sample B S. 89 5.5.5 Synthesis of GeO2 in benzyl alcohol under ambient conditions – sample C S. 89 5.6 Acknowledgments S. 89 5.7 Keywords S.89 5.8 Supporting Information Chapter 5 S. 90 6 From a Germylene to an “Inorganic Adamantane”: [{Ge₄(μ-O)₂(μ-OH)₄}{W(CO)₅}₄]∙4THF S. 93 6.1 Abstract S.93 6.2 Introduction S. 93 6.3 Results and Discussion S. 94 6.4 Conclusions S. 98 6.5 Experimental Section S. 99 6.5.1 General S.99 6.5.2 Synthesis of germanium(II) (2-methoxyphenyl)methoxide (9) S. 99 6.5.3 Synthesis of [{Ge4(μ-O)2(μ-OH)4}{W(CO)5}4]·4THF (10·4THF) S. 100 6.5.4 Single-Crystal X-ray Diffraction Analyses S. 100 6.5.4.1 Crystal Data for (9)2 S. 101 6.5.4.2 Crystal Data for 10·4THF S. 101 6.5.5 Computational Details S. 101 6.6 Acknowledgments S. 101 6.7 Keywords S.101 6.8 Supporting Information Chapter 6 S. 102 7 Synthesis, characterization and Twin Polymerization of a novel dioxagermine S. 110 7.1 Abstract S. 110 7.2 Introduction S.110 7.3 Results and Discussion S. 111 7.3.1 Single-crystal X-ray diffraction analysis S. 111 7.3.2 IR spectroscopy S. 112 7.3.3 Mass spectrum S. 114 7.3.4 DSC/TGA analysis S. 116 7.3.5 Polymerization S. 117 7.4 Conclusions S. 118 7.5 Materials and Methods S.118 7.5.1 General S. 118 7.5.2 Synthesis of 5-bromo-2-hydroxybenzyl alcohol S. 119 7.5.3 Synthesis of di-tert-butyl-di-ethoxy germane S.119 7.5.4 Synthesis of 6-bromo-2,2-di-tert-butyl-4H-1,3,2-benzo[d]dioxagermine (11) S. 120 7.5.5 Polymerization of compound 11 S. 120 7.5.6 X-ray diffraction analysis of compound 11 S.120 7.5.6.1 Crystal data for compound 11 S.120 7.5.7 Computational Details S.121 7.6 Acknowledgments S.121 7.7 Keywords S. 121 7.8 Supporting Information Chapter 7 S. 122 8 Intramolecular C-O Insertion of a Germanium(II) Salicyl Alcoholate: A Combined Experimental and Theoretical Study S. 125 8.1 Abstract S.125 8.2 Introduction S. 125 8.3 Results and Discussion S.126 8.3.1 Syntheses and Characterization S. 126 8.3.2 1H NMR Spectroscopic Studies S.132 8.3.3 DFT-D Calculations S.134 8.4 Conclusions S. 137 8.5 Experimental Section S. 138 8.5.1 General S. 138 8.5.2 Synthesis of germanium(II) 2-tert-butyl-4-methyl-6-(oxidomethyl)phenolate (12) S. 139 8.5.3 Synthesis of 2,4,6,8-tetrakis(3-tert-butyl-5-methyl-2-oxidophenyl)methanide-1,3,5,7,2,4,6,8-tetraoxidogermocane (13) S. 139 8.5.3.1 Method a) S.139 8.5.3.2 Method b) S. 140 8.5.4 Synthesis of 7,8'-di-tert-butyl-5,6'-dimethyl-3H,4'H-spiro[benzo[d][1,2]oxager-mole-2,2'-benzo[d][1,3,2]dioxagermine] (14) S. 140 8.5.4.1 Method a) S. 140 8.5.4.2 Method b) S. 141 8.5.4.3 Method c) S. 141 8.5.5 Synthesis of the [4-(dimethylamino)pyridine][germanium(II)-2-tert-butyl-4-meth-yl-6-(oxidomethyl)phenolate] (15) S. 141 8.5.6 1H NMR spectroscopic study i) S. 142 8.5.7 1H NMR spectroscopic study ii) S. 142 8.5.7.1 Method a) S. 142 8.5.7.2 Method b) S. 142 8.5.8 1H NMR spectroscopic study iii) S. 142 8.5.8.1 Method a) S. 142 8.5.8.2 Method b) S. 142 8.5.9 1H NMR spectroscopic study iv) S. 143 8.5.10 1H NMR spectroscopic study of the mixture of complex 15 and 3-tert-butyl-2-hydroxy-5-methylbenzyl alcohol in CDCl3 S. 143 8.5.11 1H NMR spectroscopic study of complex 15 in CDCl3 at elevated temperature S. 143 8.5.12 Reaction of complex 15 at elevated temperature S. 143 8.5.13 Single-crystal X-ray diffraction analyses S. 143 8.5.14 Computational Details S.144 8.6 Acknowledgments S. 145 8.7 Keywords S.145 8.8 Supporting Information Chapter 8 S. 146 9 Porous Ge@C materials via twin polymerization of germanium(II) salicyl alcoholates for Li-ion batteries S. 159 9.1 Abstract S. 159 9.2 Introduction S. 159 9.3 Results and Discussion S. 160 9.3.1 Synthesis and Characterization of germylenes S. 160 9.3.2 Twin polymerization S. 164 9.3.2.1 Studies on the reactivity S. 164 9.3.2.2 Characterization of the hybrid materials obtained by thermally induced twin polymerization S. 166 9.3.3 Synthesis and characterization of porous materials S. 168 9.3.4 Electrochemical measurements S. 170 9.4 Conclusions S. 172 9.5 Experimental Section S.172 9.5.1 General S.172 9.5.2 Synthesis of germanium(II) 2-(oxidomethyl)phenolate (16) S. 174 9.5.3 Synthesis of germanium(II) 4-methyl-2-(oxidomethyl)phenolate (17) S. 174 9.5.4 Synthesis of germanium(II) 4-bromo-2-(oxidomethyl)phenolate (18) S. 175 9.5.5 General procedure for the synthesis of phenolic resin-germanium oxide hybrid materials by thermally induced twin polymerization in melt - exemplified for compound 16 S. 175 9.5.6 General procedure for the synthesis of porous Ge@C materials - exemplified for hybrid material HM-16 S.175 9.5.7 General procedure for the synthesis of germanium oxide - exemplified for hybrid material HM-16 S.176 9.5.8 Single-crystal X-ray diffraction analyses S. 176 9.5.9 Computational Details S. 177 9.5.10 Electrode fabrication, cell assembly and electrochemical measurements S. 178 9.6 Acknowledgments S.178 9.7 Keywords S. 178 9.8 Supporting Information Chapter 9 S.179 10 From molecular germanates to microporous Ge@C via twin polymerization S.199 10.1 Abstract S.199 10.2 Introduction 199 10.3 Results and Discussion S. 201 10.3.1 Syntheses and Characterization S. 201 10.3.2 Twin polymerization of germanate 19 S. 204 10.3.3 Synthesis and characterization of the porous materials S. 205 10.3.4 Electrochemical measurements S.206 10.4 Conclusions S. 207 10.5 Experimental Section S. 208 10.5.1 General S. 208 10.5.2 Synthesis of bis(dimethylammonium) tris[2-(oxidomethyl)phenolate(2-)]germa-nate (19) S. 209 10.5.3 Synthesis of bis(dimethylammonium) tris[4-methyl-2-(oxidomethyl)pheno-late(2-)]germanate (20) S. 210 10.5.4 Synthesis of bis(dimethylammonium) tris[4-bromo-2-(oxidomethyl)pheno-late(2-)]germanate (21) S.210 10.5.5 Synthesis of dimethylammonium bis[2-tert-butyl-4-methyl-6-(oxidomethyl)phe-nolate(2-)][2-tert-butyl-4-methyl-6-(hydroxymethyl)phenolate(1-)]germanate (22) S. 211 10.5.6 Synthesis of phenolic resin-germanium dioxide hybrid materials by thermally induced twin polymerization in melt - HM-19 S. 211 10.5.7 Synthesis of porous Ge@C material C-19 starting from HM-19 S. 212 10.5.8 Synthesis of germanium dioxide material Ox-19 - starting from HM-19 S.212 10.5.9 Single-crystal X-ray diffraction analyses S. 212 10.5.10 Electrode fabrication, cell assembly and electrochemical measurements S.213 10.6 Acknowledgments S. 214 10.7 Keywords S. 214 10.8 Supporting Information Chapter 10 S.215 11 Chiral Spirocyclic Germanium Thiolates – An Evaluation of Their Suitability for Twin Polymerization based on A Combined Experimental and Theoretical Study S.226 11.1 Abstract S.226 11.2 Introduction S. 226 11.3 Results and Discussion S.227 11.3.1 Syntheses and Characterization S. 227 11.3.2 Studies on twin polymerization S.229 11.3.3 Computational studies on proton-assisted twin polymerization S. 232 11.4 Conclusions S. 235 11.5 Acknowledgments S. 236 11.6 Keywords S.236 11.7 Supporting Information Chapter 11 S.237 12 Concluding remarks S. 257 12.1 Discussion S.257 12.1.1 Twin polymerization of germanium-containing precursors S. 257 12.1.2 Reactivity studies of precursors towards their twin polymerization S.260 12.2 Summary and Outlook S. 264 Selbständigkeitserklärung S.266 Curriculum Vitae S.267 Publications S. 268 List of Publications in Peer-Reviewed Journals S. 268 List of Conference Contributions S.269 Research proposals, additional conference and summer school participations S. 270 Acknowledgments S. 271 References S. 272