Submitted by Angela Maria de Oliveira (amolivei@uepg.br) on 2018-05-16T18:51:27Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Elias Pereira.pdf: 10035465 bytes, checksum: 5e61eca3b140495c2587e4ab317ff822 (MD5) / Made available in DSpace on 2018-05-16T18:51:27Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Elias Pereira.pdf: 10035465 bytes, checksum: 5e61eca3b140495c2587e4ab317ff822 (MD5) Previous issue date: 2018-02-23 / A degradação da argamassa ocasionada pelo ataque por sulfatos e reação álcali-agregado, ocorre pela presença de contaminantes nos agregados que reagem com os produtos da hidratação do cimento, sendo formados produtos expansivos, provocando efeitos deletérios ao material. Este trabalho tem por objetivo a análise isolada e combinada da reação álcali-agregado pela presença de quartzo deformado nos agregados e do ataque interno por sulfato devido à presença de pirita, também nos agregados, em argamassas de cimento Portland, em diferentes idades e meios de cura, assim como a investigação das mudanças microestruturais, com foco na absorção e na mudança de estrutura porosa do material. O programa experimental foi divido em quatro etapas: (i) caracterização dos agregados; (ii) ensaios acelerados e envelhecimento natural em prismas de argamassa; (iii) investigação do comportamento, em ambiente natural, de corpos de prova de concretos com pirita; (iv) análise da absorção e porosidade. As análises petrográficas, variações dimensionais de barras de argamassa, resistências à compressão e resistência à tração por compressão diametral, foram bons indicativos para a ocorrência da RAA e ISA de forma isolada e combinada, onde as curas parcialmente e totalmente imersa em água mantida a 40 °C intensificaram as reações pela incidência de umidade e oxigenação constantes. As porosidades, absorções de água por imersão e por capilaridade dos corpos de prova se mostraram indicativos da intensidade das reações álcali-agregado e ataque por sulfatos, sendo que para agregados contendo sulfetos as variações puderam ser atribuídas a fissuração produzida pela formação de cristais expansivos de sulfatos, e para os agregados reativos as variações puderam ser atribuídas a presença de intercrescimento mirmequíticos e extinção ondulante dos silicatos, culminando na formação de géis expansíveis. Em ambas as manifestações patológicas, a demasiada formação de fases expansivas promoveu a fissuração da matriz e aumento da proporção de macroporos nas idades finais. As análises de diâmetro de poros por intrusão de mercúrio demonstram que a RAA ocorre primeiramente nos poros próximos a 50 nm, devido ao seu caráter de borda de reação, e a ISA promove o refinamento e colmatação dos poros de toda a gama de diâmetros pela formação de sais de sulfatos, além de ambos os processos gerarem tensões internas e fissuração da matriz. Para os agregados com efeito combinado, estes processos ocorrem concomitantemente, tendo influência sobre as capacidades de absorção de água por imersão e capilaridade, além das resistências mecânicas e variações dimensionais. / The degradation of the mortar caused by the attack by sulfates and alkali-aggregate reaction occurs by the presence of contaminants in the aggregates that react with the products of the cement hydration, being formed expansive products, causing deleterious effects to the material. This work aims at the isolated and combined analysis of the alkali-aggregate reaction by the presence of deformed quartz in the aggregate and the internal attack by sulphate due to the presence of pyrite, also in the aggregate, in Portland cement mortars, at different ages and mortar cure means, as well as the investigation of the microstructural changes, focusing on the absorption and the change in the porous structure of the material. The experimental program was divided into four stages: (i) characterization of the aggregates; (ii) accelerated tests and natural aging on mortar prisms; (iii) investigation of the behavior, in the natural environment, of concrete specimens with pyrite; (iv) absorption and porosity analysis. The petrographic analyzes, dimensional variations of mortar bars, compressive strengths and tensile strength by diametrical compression were good indicative for the occurrence of RAA and ISA in an isolated and combined manner, where the cures were partially and totally immersed in water maintained at 40 ° C intensified the reactions by the incidence of constant moisture and oxygenation. The porosities, water absorptions by immersion and by capillarity of the test specimens were indicative of the intensity of the alkali-aggregate and sulfate attack reactions, and being that for aggregates containing sulfides the variations could be attributed to the cracking produced by the formation of expansive crystals of sulfates, and for the reactive aggregates the variations could be attributed to the presence of myrhythmic intergrowth and undulating extinction of the silicates, culminating in the formation of expandable gels. In both pathological manifestations, the excessive formation of expansive phases promoted matrix cracking and increased proportion of macropores in the final ages. The analysis of pore diameter by mercury intrusion shows that the RAA occurs first in pores close to 50 nm, due to its character of reaction border, and ISA promotes the refinement and filling of the pores of the whole range of diameters by the formation of sulfate salts, in addition to both processes generating internal stresses and cracking of the matrix. For aggregates with combined effect, these processes occur concomitantly, having influence on the water absorption capacities by immersion and capillarity, besides the mechanical resistances and dimensional variations.

Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2018-07-09T16:18:43Z No. of bitstreams: 1 Paôla Valentini_.pdf: 16360357 bytes, checksum: 11cfed092ec8572550d478091c843fbc (MD5) / Made available in DSpace on 2018-07-09T16:18:43Z (GMT). No. of bitstreams: 1 Paôla Valentini_.pdf: 16360357 bytes, checksum: 11cfed092ec8572550d478091c843fbc (MD5) Previous issue date: 2018-03-23 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Diversos fatores influenciam a durabilidade de argamassas de revestimento, sendo alguns deles: a absorção de água, porosidade e rugosidade da superfície do substrato; a execução, com o preparo ou não do substrato, a forma de aplicação e as condições de cura da argamassa; as condições climáticas, decorrentes da ação do vento, umidade e temperatura; e a própria argamassa com seus componentes. Partindo deste contexto, esta pesquisa tem como objetivo avaliar fatores relacionados ao substrato e à argamassa que influenciam na resistência de aderência à tração de sistemas de revestimento. O programa experimental buscou avaliar a influência da absorção de água total, da absorção por capilaridade e da rugosidade de três substratos cerâmicos e também da adição de fíler na argamassa, na resistência de aderência à tração de sistemas de revestimento. Os substratos cerâmicos foram queimados nas temperaturas de 800°C, 900°C e 1000°C, sendo que, das 144 peças cerâmicas do estudo, metade receberam aplicação de hidrofugante. Sobre as peças cerâmicas foram aplicadas argamassas confeccionadas com areia natural de rio e cimento Portland CP II-Z-32, no traço 1:3, em massa, com e sem adição de 5% de pó de quartzo. A partir dos resultados encontrados observou-se que a maior resistência de aderência à tração foi obtida nos blocos cerâmicos com temperatura de queima de 800°C, que apresentam simultaneamente maior rugosidade e maior absorção capilar de água. Verificou-se também que a adição de fíler à argamassa aumentou a resistência de aderência quando aplicada sobre os blocos de maior rugosidade, não sendo observado o mesmo comportamento nos blocos de baixa rugosidade. De um modo geral, o uso de hidrofugante sobre as peças cerâmicas diminuiu os resultados de resistência de aderência além de alterar a forma de ruptura dos revestimentos. / The durability of coating mortars applied on substrates are influenced by the water absorption, porosity and roughness of the substrate surface; the preparation of the coating´s substrate, the method used to apply and the cure conditions of the mortar; beyond the climatic conditions, through the wind, humidity and temperature; and the mortar itself with its components. Based on this context, this research aims to evaluate factors related to the coating´s substrate and the rendering mortar that influence the adhesion strength of mortar coating systems. The experimental program aimed to evaluate the influence of total water absorption, capillary absorption and roughness of three ceramic substrates, as well as the use of filler in the mortar, in the adhesion strength of mortar coating systems. The ceramic substrates were burned at 800°C, 900°C and 1000°C, and of the 144 ceramic pieces of the study, 72 were painted with water repellent. The coating mortars were made with natural river sand and Portland cement CP II-Z-32, in the proportion 1: 3 (by mass), with and without adding 5% of quartz filler. It was observed that the highest tensile strength was obtained with the substrates of ceramic blocks burned at 800°C, which simultaneously present the higher roughness and higher water absorption. The use of filler in the mortar composition increased the adhesion strength when applied on the blocks of greater roughness. In general, the use of water repellent on the ceramic substracts decrease the adhesion strength of mortar coating systems and modify the kind of rupture of the coatings.

Submitted by Mariana Dornelles Vargas (marianadv) on 2015-05-29T17:53:11Z No. of bitstreams: 1 analise_influencia.pdf: 4201896 bytes, checksum: 5bde8b1b65dd35cc811456f73f745be3 (MD5) / Made available in DSpace on 2015-05-29T17:53:11Z (GMT). No. of bitstreams: 1 analise_influencia.pdf: 4201896 bytes, checksum: 5bde8b1b65dd35cc811456f73f745be3 (MD5) Previous issue date: 2011-04-29 / FINEP - Financiadora de Estudos e Projetos / UNISINOS - Universidade do Vale do Rio dos Sinos / A construção civil é um setor industrial que provoca elevado impacto ambiental, devido ao grande consumo de matéria-prima. Em função da crescente restrição da extração de areias dos rios e a escassez de areias naturais, com conseqüente elevação de seu custo, a utilização de areia proveniente da britagem de rochas na construção civil tem se tornado cada vez mais comum nos grandes centros urbanos. A utilização deste tipo de areia, fazendo-se uso de procedimentos e equipamentos adequados, pode ser uma alternativa viável para substituição da areia proveniente dos depósitos aluvionares de rios na produção de argamassas de revestimento de alvenarias. Este estudo apresenta e discute as características tecnológicas de três tipos de agregados miúdos com diferentes formas de grãos: uma areia de leito de rio (areia aluvionar) e duas areias de britagem de rocha basáltica, produzidas através de diferentes britadores, e avalia o comportamento de argamassas produzidas com estas areias. As diferenças entre os processos de obtenção resultam em diferenças na distribuição granulométrica, forma e textura superficial dos grãos, alterando o comportamento de argamassas fabricadas com estes agregados. As propriedades de uma argamassa de cimento, cal e areia dosada para a areia de rio foram comparadas com argamassas com o mesmo traço, substituindo-se a areia de rio pelos outros agregados miúdos, e o mesmo procedimento foi realizado para diferentes teores de adição de fíler à argamassa. Utilizou-se cimento CP II Z? 32 e cal CH-I, sendo produzidas vinte misturas de argamassas, oito com areia de britagem passante pelo britador VSI, quatro com areia de britagem passante pelo britador de mandíbulas e oito com areia de rio, no traço de volume em cimento, cal e areia, 1:1:6, com índice de consistência fixado em 260mm + 5mm na mesa de consistência. As propriedades determinadas no estado fresco são o índice de consistência, a reologia (squezze flow e penetração de cone), o teor de ar incorporado, a retenção de água e a densidade de massa. Foram determinadas a densidade de massa, a resistência à compressão e à tração na flexão, a absorção de água por capilaridade, o coeficiente de capilaridade, a absorção de água total, o índice de vazios, a massa específica real, a retração linear e o módulo de elasticidade dinâmico no estado endurecido. Para os ensaios em revestimentos foram utilizados substratos com dois diferentes teores de absorção de água, sendo determinada a resistência de aderência do revestimento e o grau de fissuração. Observou-se diferenças expressivas no comportamento das argamassas confeccionadas com os diferentes agregados, como: perda de trabalhabilidade; perda de densidade de massa; redução da resistência à compressão e da resistência à tração na flexão; diminuição do módulo de elasticidade dinâmico; aumento da absorção de água por imersão; aumento do índice de vazios; e aumento da massa específica. Em função das diferenças morfológicas e das diferenças no teor de fíler na mistura. / The construction industry causes high environmental impact due to large consumption of raw materials. Due to the restriction of sand extraction and the reduction of natural sand, with a consequent increase in cost, the use of crushed fine aggregates in construction has become increasingly common in large urban centers. The use of crushed fine aggregates made with appropriate procedures and equipments can be an alternative to replace the sand extracted of rivers for the production of rendering mortars. This paper discusses the technical characteristics of three different aggregates with distinct morphologies: the natural sand (alluvial sand) and two basalt crushed fine aggregates, produced by different crushers, and evaluate the behavior of mortars produced from these sands. Differences in particle size, shape and surface texture of the grains changes the behavior of mortars made with this aggregates. The properties of a reference mortar made with river sand was compared with others, replacing the river sand aggregate by crushed aggregates, and the same procedure was performed for different levels of addition of fillers in the mortar. Brazilian CP II Z-32 cement and CH-I lime were used for production of twenty mortars: eight with VSI crushed aggregates, four with jaw crushed sand mortars and eight with natural sand. The 1: 1: 6 (cement, lime and sand by volume) proportion was adopted, with consistency index of 260mm±5mm on the consistency table. Properties measured in the fresh state were consistency index, workability (by squezze-flow and cone penetration), air content, water retention and density. On the hardened state, density, compressive strength, flexural strength, capillarity water absorption, water absorption, shrinkage and modulus of elasticity were determined. Rendering mortar were applied over two substrates with different water absorption, determining bond strength and cracking. There were observed significant differences in the behavior of mortars made with different aggregates, as loss of workability and of density, reduction of compressive and flexural strength, decreasing of modulus of elasticity, increasing of absorption and density.

Fundação de Amparo a Pesquisa do Estado de Minas Gerais / In this work, methylcellulose (MC) was produced from sugarcane bagasse cellulose by heterogeneous route in alkaline medium, according to two methodologies: i) reaction with DMS, successive exchange of reagents and a step of mercerization and ii) reaction with iodomethane in two steps of mercerization. The synthesized methylcelluloses and a commercial methylcellulose sample, used as standard, have been evaluated as admixtures for adhesive mortars in civil construction by 2 methods, being added as a suspension in water (method 1) and in the powder form, dispersed in the mortar during its preparation (method 2). One of the main points of innovation of this study was to apply the polymers as a powder during mortar preparation, so that it approaches the commercial adhesive mortars, which consist of mixtures pre-dosed powder. In this study, methylcellulose produced using DMS (MCD), iodomethane (MCI) and commercial methylcellulose (MCC) were characterized according to their degree of substitution (DS) by chemical route, by Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA) and viscosity measurements. The modifications observed in the FTIR spectra showed the efficiency of methylation processes using DMS and iodomethane. The samples showed differences in water solubility, MCI was more soluble, and related to the crystallinity, the MCD presented more crystalline pattern and MCI more amorphous. The MCD was more thermally stable. The adhesion of mortars prepared by method 1 was close to the values obtained for reference mortar, particularly only to the MCD sample that increased by about 28% compared to reference. For the mortars produced by method 2, the direct addition of polymers effectively changed the properties of mortars, especially in relation to the adhesion, that increased by approximately 23% to mortar containing MCI, about 70% for MCD and 20% for MCC. It is observed that MCD samples perform best in all tests, this may be related to the higher DS for this sample, which favors the gel formation and the water retention, making the mortar more viscous and \"sticky\", altering the interactions between mortar and substrate and increasing the adhesion. / Neste trabalho, a metilcelulose (MC) foi produzida a partir da celulose extraída do bagaço de cana-de-açúcar pela rota heterogênea em meio alcalino. Foram empregadas duas metodologias de síntese: i) reação com sulfato de dimetila (DMS), troca sucessiva de reagentes e uma etapa de mercerização e ii) reação com iodometano e duas etapas de mercerização. As amostras de MC produzidas e uma amostra de MC comercial, utilizada como padrão, foram avaliadas como aditivos para argamassas colantes na construção civil por 2 métodos, sendo adicionadas às argamassas como uma suspensão em água (método 1) e na forma de pó, disperso diretamente na argamassa durante sua preparação (método 2). Um dos principais pontos de inovação deste trabalho foi a aplicação dos polímeros na forma de pó durante a preparação das argamassas, forma essa que se aproxima das argamassas colantes comerciais que consistem em misturas pré-dosadas em pó. Neste estudo, as amostras de metilcelulose produzidas usando DMS (MCD), iodometano (MCI) e a amostra de metilcelulose comercial (MCC) foram caracterizadas quanto ao seu Grau de Substituição (GS) por via química, pelas técnicas de Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Difratometria de Raios-X (DRX), Calorimetria Exploratória Diferencial (DSC), Análise Termogravimétrica (TGA), Microscopia Eletrônica de Varredura (MEV) e por medidas de viscosidade. As modificações observadas nos espectros de FTIR mostraram a eficiência dos processos de metilação usando DMS e iodometano. As amostras apresentaram diferenças quanto à solubilidade em água, sendo a amostra MCI mais solúvel, e quanto à cristalinidade, a MCD apresentou um padrão mais cristalino e a MCI mais amorfo. A amostra MCD apresentou a maior estabilidade térmica. A adesão das argamassas preparadas pelo método 1, foi próxima dos valores da argamassa de referência, com destaque apenas para a MCD que apresentou aumento de cerca de 28%. Para as argamassas produzidas pelo método 2, a adição direta dos polímeros modificou efetivamente as propriedades das argamassas, principalmente em relação à aderência, que aumentou cerca de 23% para a argamassa com MCI, 70% para MCD e 20% para MCC. A amostra MCD apresentou o melhor desempenho em todos os ensaios, fato que pode estar relacionado ao seu maior GS, que favorece a formação de gel e a retenção de água pela argamassa, tornando-a mais viscosa e pegajosa , alterando as interações da argamassa com o substrato e consequentemente, aumentando a aderência. / Doutor em Química

The analysis of adhesion mechanisms between mortar lining and porous substrates has been the target of innumerous researchers due to its importance in ensuring system performance. Based on the theoretical reference of the topic, this work of experimental nature aimed to analyze the influence of the superficial topography of ceramic blocks in bonding slurry mortars and their relationship with the set of characteristics of fine aggregates that make up slurry mortars. Initially, the substrates and component materials of the mortars were characterized according to the Brazilian Association of Technical Standards; afterwards, characterization tests of fresh and hardened mortars were carried out. In the testing phase, the blocks received the slurry mortars. The experimental variables studied were: three types of ceramic blocks (ceramic sealing block with smooth surfaces, ceramic sealing block with horizontal grooved surfaces, and ceramic sealing block with vertical grooved surfaces); and two types of slurry mortars (one was prepared with coarse sand and the other with medium sand). Thus, six interfaces were evaluated through aspects of bonding strength and permeability and absorption by the pipe method. In order to observe the extent of adhesion and involvement of the grains of sand through the paste of the slurry mortars, interface analyses were conducted through observation by magnifying glass and petrographic microscope. The characteristics of the sands that influence the performance of fresh and hardened slurry mortars were analyzed, with emphasis on the textural parameters of the sands, which were evaluated with the aid of petrographic analysis. Results showed that there is direct correlation between the extent of adhesion provided by the grooves of the blocks, and bond tensile strength, made possible by the fluid nature of the slurry mortar. Therefore, this indicates the strong influence of the type of ceramic block on results of bond strength. On the other hand, the study of the characteristics of the sands, represented mainly by the granulometric composition, density, unitary mass, void content, degrees of roundness and sphericity, and mineralogy, proved to be useful in order to understand the role of the fine aggregates in the performance of the slurry mortar. Additionally, we observed that the tensile bonding strength was higher for the slurry mortars with coarse sand than with medium sand, when comparing the same type of block, although the tests have pointed to non-significant differences. This fact can be explained by the small difference between some of the characteristics of the sand used; however, the coarse sand studied seems to provide greater integration of the grains involved by the mortar paste, which was indicated by the degree of roundness. Moreover, it was also possible to observe direct relations in achieving results when comparing the permeability and absorption by the pipe method with the initial rate of absorption test (IRA) and extended IRA test. The final observation is that the basic treatment using slurry mortar can provide several benefits: increased roughness of the base, increased tensile bonding strength, adjustment of the suction capacity. This way, it was possible to homogenize the absorption of water by the substrate, thus avoiding different screeding times and performance for the lining layer. Thus, the treatment of the base with the use of slurry mortar can increase the performance and durability of the mortar lining. / A análise dos mecanismos de aderência entre argamassas de revestimento e substratos porosos tem sido alvo de muitos pesquisadores, devido à importância que tem para garantir o desempenho do sistema. Com base no referencial teórico sobre o tema, este trabalho de natureza experimental teve como objetivo principal analisar a influência da topografia superficial de blocos cerâmicos na aderência de argamassas de chapisco e a sua relação, ainda, com o conjunto de características dos agregados miúdos que compõem as argamassas de chapisco. Inicialmente, os substratos e os materiais componentes das argamassas foram caracterizados através do grupo de normas da Associação Brasileira de Normas Técnicas; na sequência, foram realizados ensaios de caracterização das argamassas nos estados fresco e endurecido. Na fase de testes, os blocos receberam as argamassas de chapisco. As variáveis experimentais estudadas foram: três tipos de blocos cerâmicos (bloco cerâmico de vedação com faces lisas, bloco cerâmico de vedação com faces ranhuradas horizontais, e bloco cerâmico de vedação com faces ranhuradas verticais); e dois tipos de argamassas de chapisco (uma elaborada com areia grossa e outra com areia média). Dessa forma, surgiram seis interfaces que foram avaliadas através de aspectos relacionados à resistência de aderência à tração e à permeabilidade e absorção pelo método do cachimbo. Na intenção de observar a extensão de aderência e o envolvimento dos grãos de areia pela pasta das argamassas de chapisco, foram feitas análises da interface através da observação por lupa estereoscópica e microscópio petrográfico. Foram pesquisadas as características das areias que influem no desempenho das argamassas de chapisco em seu estado fresco e endurecido, com ênfase nos parâmetros texturais das areias, avaliados com auxílio da análise petrográfica. Os resultados mostraram que há correlação direta entre a extensão de aderência, proporcionada pelas ranhuras dos blocos cerâmicos e a resistência de aderência à tração, possibilitada pela natureza fluida da argamassa de chapisco, indicando, assim, a forte influência do tipo de bloco cerâmico nos resultados de aderência à tração. De outro lado, o estudo das características das areias, representadas, principalmente, pela composição granulométrica, massa específica, massa unitária, índice de vazios, graus de arredondamento e esfericidade e mineralogia revelou-se útil no sentido de compreender o papel dos agregados miúdos perante o desempenho das argamassas de chapisco. Notou-se que a resistência de aderência à tração foi maior para as argamassas de chapisco com areia grossa do que com areia média, quando se compara um mesmo tipo de bloco, embora os testes tenham apontado diferenças não significativas. Esse fato pode ser explicado pela pouca diferença entre algumas das características das areias utilizadas; porém, a areia grossa estudada parece proporcionar um maior entrosamento dos grãos envolvidos pela pasta da argamassa, indicado pelo grau de arredondamento. Foram observadas, ainda, relações diretas na obtenção de resultados quando se compara a permeabilidade e absorção pelo método do cachimbo com o ensaio do índice de absorção inicial de água (AAI) e AAI estendido. A constatação final é de que o tratamento de base através do emprego de chapisco pode proporcionar vários benefícios: aumento da rugosidade da base, aumento da resistência de aderência à tração e regulagem da capacidade de sucção. Possibilitando, com isso, homogeneizar a absorção de água por parte do substrato, evitando diferentes tempos de sarrafeamento e desempeno para a camada de revestimento. Assim, o tratamento da base com uso do chapisco pode aumentar o desempenho e a durabilidade dos revestimentos de argamassa.