In this diploma thesis the preparation of ceramic catalytic materials was studied. They were studied by means of catalytic activity on powder samples and in a form of membrane as well. At first were multicomponent perovskite materials with the help of “glycine-nitride synthesis” synthesized. Two types of perovskite systems were prepared. First system was on the basis of nickelates LaNiO3 and the second one on the basis of cobaltites SmCoO3. Both of them were doped with aluminium and calcium. Ceramic powders were catalytic tested during reformed reaction. A part of powders was pressed with hydraulic biaxial press. Then the membranes were calcinated, sintered and polished. The membranes were tested to specify the catalytic activity. At first they were in hydrogen atmosphere reduced and afterwards came through the partial oxidation. The appearance of coke fibers on the surface was discussed.

L'utilisation de membranes pour la séparation/purification de mélanges de gaz permet d'envisager la mise en œuvre de procédés continus et faiblement énergivores. Les performances des membranes étant directement reliées à la méthode utilisée pour leur synthèse/modification, une nouvelle génération de membranes est attendue à partir de la méthode originale de dépôt « dynamique » développée et mise au point dans ce travail, en milieu CO2 supercritique (CO2SC). Les propriétés des fluides supercritiques, intermédiaires entre celles d'un liquide et d'un gaz (densité et diffusivité élevées, viscosité faible), laissent en effet présager la formation de microstructures originales. Les précurseurs sont solubilisés dans le CO2 sous pression puis transportés jusqu'au support membranaire. Cette méthode a été explorée pour : i) la synthèse directe de membranes à base de silice sur des supports macroporeux et ii) la modification de membranes zéolithiques MFI par des alcoxydes (MDES, TEOS) ou par des oligomères fluorés. Dans le premier cas, l'étude des paramètres de dépôt montre que la maîtrise des phénomènes chimiques de la transition sol-gel (contrôlés principalement par la température) dicte la microstructure du matériau final, au travers du degré de condensation/réticulation des clusters déposés. La modification des membranes zéolithiques MFI par un alcoxyde permet de doubler la permsélectivité He/SF6 initiale, sans forte baisse de perméance (Π(He)~10-6 mol.Pa-1.s-1.m-2). Dans ce cas, la force, la nature et la disponibilité des sites acides de la charpente MFI sont des critères clés pour la fixation de l'alcoxyde. Les membranes MFI modifiées par un oligomère fluoré sont imperméables au SF6 et la permsélectivé He/N2 peut atteindre une valeur de 136 à 25°C (Π(He)~10-8 mol.Pa-1.s-1.m-2). Cette nouvelle méthode dynamique de dépôt/modification développée dans ce travail apparaît comme une approche très versatile qui permet de contrôler la structure du matériau déposé en ajustant les paramètres du procédé. / Using membranes for the separation/purification of gas mixtures makes possible the implementation of continuous processes with low energy consumption. Membrane performance being directly related to their synthesis/modification method, a new membrane generation is expected from the original "dynamic" deposition method which has been designed and developed in this work, in supercritical CO2 (scCO2) media. Indeed, the properties of supercritical fluids are intermediate between those of liquids and gases (high density and diffusivity, low viscosity), original membrane microstructures are expected to be derived from this process. The selected precursors are solubilized in compressed CO2 and then transported to the membrane support. This method has been explored for both: i) the synthesis of silica-based membranes on macroporous supports and ii) the modification of MFI zeolite membranes by either alkoxides (MDES, TEOS) or fluorinated oligomers. In the first case, an investigation of the deposition parameters demonstates that the sol-gel chemistry (controlled mainly by temperature) masters the final material microstructure, through the degree of condensation/crosslinking of the deposited clusters. Modification of MFI zeolite membranes with alkoxides can double their initial He/SF6 permselectivity without lowering too much their permeance (Π(He)~10-6 mol.Pa-1.s-1.m-2). In this case, the alkoxide fixation is monitored by the strength, nature and availability of acid sites in the MFI network. MFI membranes modified with fluorinated oligomers are SF6-tight and their He/N2 permselectivity can reach 136 at 25°C (Π(He)~10-8 mol.Pa-1.s-1.m-2). This new dynamic deposition/modification method developed in this work appears as a versatile approach in which the final material structure can be controlled by adjusting the process parameters.