Submitted by Claudia Rocha (claudia.rocha@udesc.br) on 2017-12-11T13:34:57Z No. of bitstreams: 1 PGEF16MA070.pdf: 2448624 bytes, checksum: 4869319201ca98d0673aaafa7f95a8ce (MD5) / Made available in DSpace on 2017-12-11T13:34:57Z (GMT). No. of bitstreams: 1 PGEF16MA070.pdf: 2448624 bytes, checksum: 4869319201ca98d0673aaafa7f95a8ce (MD5) Previous issue date: 2016-02-26 / UNIEDU / This study aimed to evaluate the potential of Eucalyptus badjensis wood for the production of particleboard, as well as mixing it with the wood of Pinus spp. and further compare the effect of using different amounts of urea-formaldehyde adhesive (UF) on the properties of the produced panels. Thus particles were made using panels of E. badjensis and Pinus spp., As well as the mixture of two species in homogeneous composition and multilayer panels panels in proportions 25%/50%/25% using the levels of 8%, 10% and 12% of the urea formaldehyde adhesive. Were realized the analyzes of compression ratio, thickness swelling and water absorption in 2 and 24 hours of immersion in water, not return rate in thickness, modulus of elasticity (MOE) and modulus of rupture (MOR) , Traction perpendicular to the surface (Internalbond) and screw pullout , aiming to enhance discussion of the results were also conducted chemical analyzes of wood , particle geometry and basic wood density. With this study it was concluded that the Eucalyptus badjensis has the potential for making particleboards, as average values presented statistically better or equal to Pinus spp. all properties examined in the same manner was observed that the increase in adhesive, content causes an improvement in the properties of the panels / O presente estudo teve como objetivo avaliar o potencial da madeira de Eucalyptus badjensis para a produção de painéis de madeira aglomerada, bem como de sua mistura com a madeira de Pinus spp. e ainda comparar o efeito da utilizando diferentes teores do adesivo ureia-formaldeído (UF) nas propriedades dos painéis produzidos. Desse modo foram confeccionados painéis utilizando partículas de E. badjensis e de Pinus spp., bem como com a mistura das duas espécies em painéis de composição homogênea e painéis multicamada nas proporções 25%/50%/25 % utilizando os teores de 8%, 10% e 12% do adesivo ureia-formaldeído. Foram realizadas as análises de densidade aparente, razão de compactação, absorção de água e inchamento em espessura em 2 e 24h de imersão em água, taxa de não retorno em espessura (TNRE), modulo de elasticidade (MOE), modulo de ruptura (MOR), tração perpendicular à superfície (ligação interna) e arrancamento de parafuso com o objetivo de aprimorar a discussão dos resultados também foram realizadas análises químicas da madeira, da geometria de partículas e da densidade básica da madeira. Com o presente trabalho foi possível concluir que a madeira de Eucalyptus badjensis apresenta potencial para a confecção de painéis do tipo aglomerado, uma vez que apresentou valores médios melhores ou iguais ao Pinus spp. em todas as propriedades analisadas, do mesmo modo foi observado que o aumento nos teores de adesivo ocasiona uma melhora nas propriedades dos painéis

Made available in DSpace on 2016-12-12T20:12:32Z (GMT). No. of bitstreams: 1 PGEF15MA048.pdf: 2278704 bytes, checksum: 43e91b8b4735fdda209db49d5aab5db3 (MD5) Previous issue date: 2015-07-30 / The aim of this study was to evaluate the bonding quality of two adhesives (PVA and EPI) in top and side joints of Cupressus lusitanica in production of EGP panels. Anatomical, chemical and physical characterization was performed to determine the influence on the formation and performance of bonded joints. For evaluation of end-grain joints in static bending tests and tension parallel were assessed two adhesives (PVA and EPI), grammage (180 and 200 g/cm²) and two types of end-grain joints (butt-joint and finger-joint). In addition to the strength and stiffness analysis was applied the technique of scanning electron microscopy technique (SEM) to verify the influence of moisture contend in glued bonds of parallel tensile specimens. The side bonding was performed with two adhesive (PVA and EPI) and two grammage (180 and 200 g/m²) by shear test in the central glue line. As result, the specie has low porosity and fine texture; chemical properties was similar to conifers usually used to wood panels production; wood showed low density (0.41g/cm³) with high dimensional stability; for glued end-grain joints, the treatment composed of finger-joint, adhesive EPI with grammage 180 g/m² (T7), showed greater resistance to parallel traction and bending test; SEM analysis allowed the visualization and verification of PVA adhesive degradation by moisture, and demonstrated that EPI adhesive has no structural change in same condition; for side bonding of Cupressus lusitanica timber is indicated using EPI adhesive with grammage 180 g/m² (T3) due to high strength and wood failure percentage / O objetivo do presente estudo foi avaliar a qualidade de colagem de dois adesivos (PVA e EPI) em junções de topo e laterais da madeira de Cupressus lusitanica na produção de painéis EGP. Foi realizada a caracterização anatômica, química e física da madeira da espécie a fim de determinar a influência na formação e desempenho das juntas coladas. Para a avaliação das junções de topo coladas foram avaliados por meio dos ensaio de flexão estática e tração paralela, dois adesivos (PVA e EPI), duas gramaturas (180 e 200 g/m²) e dois tipos de junções de topo (plana e finger-joint). Além da análise de resistência e rigidez, foi aplicada a técnica de microscopia eletrônica de varredura (MEV) para verificar a influência do teor de umidade na qualidade de colagem dos corpos de prova de tração paralela. A colagem lateral foi realizada com dois adesivos (PVA e EPI) e duas gramaturas (180 e 200 g/m²) pelo ensaio de cisalhamento na linha de cola central. Como resultado, a espécie apresenta porosidade reduzida e textura fina; as propriedades químicas foram semelhantes às de coníferas normalmente utilizadas para produção de painéis de madeira; a madeira apresentou baixa massa específica (0,41 g/cm³) com alta estabilidade dimensional; para as juntas de topo coladas, o tratamento composto por junções do tipo finger-joint, adesivo EPI com gramatura de 180 g/m² (T7), apresentou maior resistência para o ensaio de tração paralela e flexão estática; a análise por MEV permitiu a visualização e comprovação da degradação do adesivo PVA por ação da umidade, e demonstrou que o adesivo EPI não apresenta alteração estrutural na mesma condição; e para a colagem lateral da madeira de Cupressus lusitanica é indicado a utilização de adesivo EPI com gramatura de 180 g/m² (T3), devido à elevada resistência e percentual de falha na madeira