Indiana University-Purdue University Indianapolis (IUPUI) / While most sealants available are resin-based, glass ionomer-based cements can be used as sealants, with the advantage of being more tolerant to moisture during placement and of releasing fluoride. The objective of this study was to evaluate the influence of different fissure conditioning techniques on penetration and microleakage of glass ionomer (GI) and resin-modified glass ionomer cements (RMGI) used as sealants. Clinically sound extracted human molars were distributed into nine experimental groups (n = 15 each). Group 1 (control) was sealed with resin-based sealant (Delton) following clinically accepted techniques. Groups 2 through 6 were sealed with RMGI (Vitremer) after having the fissure conditioned with either polyacrylic acid (RMGI-control), 35-percent H3PO4, low viscosity 35-percent H3PO4 with a surfactant, self-etch conditioner, or 35-percent H3PO4 followed by self-etch conditioner. Groups 7 through 9 were sealed with GI sealant (Fuji Triage) after having the fissures conditioned with either polyacrylic acid (GI-control), 35- percent H3PO4 or low viscosity 35-percent H3PO4 with a surfactant. After aging through thermocycling (2500 cycles), specimens were incubated in methylene blue for four hours and sectioned at multiple locations. Digital images were obtained using a digital stereomicroscope, and microleakage was determined by scoring the dye penetration along the enamel-sealant interface. The penetration of the material was determined by calculating the percentage of the total length of the fissure penetrated by the material. Results: The use of self etch-conditioner significantly increased RMGI penetration, while surface conditioning with 35-percent phosphoric acid with surfactant significantly decreased microleakage of GI. The resin-based sealant placed after 35-percent phosphoric acid surface conditioning showed the best penetration and the least level of microleakage. In conclusion, results from this study suggest that the placement of glass ionomer-based sealants can be enhanced by modifying current conditioning methods.

Este estudo procurou verificar o efeito de dois selantes no tratamento de lesões cariosas não cavitadas em dentina, no que diz respeito à progressão da cárie na superfície oclusal de molares permanentes, em adolescentes com idades entre 11 e 15 anos. A amostra do estudo constituiu-se de 28 dentes: 14 selados com selante resinoso (Fluroshield®, Denstply), no grupo Gres, e 14 selados com selante ionomérico (RIVA Protect®, SDI), no grupo Gciv. A avaliação dos desfechos se deu por meio da análise dos exames radiográficos inicial e após 12 meses de acompanhamento; através de dois métodos: avaliação radiográfica qualitativa e quantitativa. A análise qualitativa foi realizada por um único examinador devidamente calibrado (Kappa = 0,837) com o uso de negatoscópio em sala escura e lupa de aumento 10x, e considerou como sucesso do tratamento a regressão ou paralisação da lesão; e insucesso, a evolução da lesão cariosa. A análise quantitativa se deu por meio da comparação entre os coeficientes de densidade radiográfica obtidos através do software DIGORA®, observando aumento (sucesso) ou diminuição (insucesso) dos coeficientes de densidade. Após a avaliação qualitativa, observou-se sucesso do tratamento em 64,3% dos casos (n=9) do grupo Gciv e 85,7% (n=12) do grupo Gres, sem diferença estatística entre os grupos (p=0,39). A avaliação quantitativa mostrou que no Gres foi observado um aumento significante dos coeficientes de densidade (p=0,003) e no Gciv se observou uma estabilidade dos coeficientes após 12 meses (p=0,49). Desta forma, pode-se concluir que, nas condições deste estudo, o uso de selantes de sulcos e fóssulas mostrou-se eficaz no tratamento de lesões cariosas. / This study examined the effect of two sealants in the treatment of non-cavitated occlusal carious lesions, regarding to the progression or arresting of the lesions in permanent molars in adolescents 11 to 15 years age. The sample consisted of 28 teeth: 14 sealed with resin-based sealant (Fluroshield®, Denstply), Gres group, and 14 sealed with glass ionomer sealant (RIVA Protect®, SDI), Gciv group. Caries progression was monitored by radiographic examination, using two methods: qualitative and quantitative trough radiographic evaluation. Qualitative analysis was performed by a single calibrated examiner (Kappa = 0.837) using light box in a darkened room and 10x magnifying glass, and considered as success treatment the regression or interruption of the injury caries, and failure treatment, the evolution of the lesion carious. Quantitative analysis occurred by comparing the radiographic density coefficient obtained through software DIGORA®, observing increased (success) or decreased (failure) of the coefficients. After the qualitative evaluation, it was observed success of treatment in 64.3% (n = 9) of Gciv group and 85.7% (n = 12) on Gres group, with no statistical difference between the them (p=0,39). The quantitative analysis showed in Gres group a significant increase in the density coefficient (p = 0.003) and in the Gciv group the stability of coefficients after 12 months (p = 0.49). It can be concluded that under the conditions of this study, the use of sealants proved to be effective in the treatment of occlusal carious lesions.

published_or_final_version / Dentistry / Doctoral / Doctor of Philosophy

Thesis (M.S.)--West Virginia University, 1999. / Title from document title page. Document formatted into pages; contains vii, 69 p. : ill. Vita. Includes abstract. Includes bibliographical references (p. 56-60).

As evidências mostram uma redução ou eliminação significativa na quantidade de bactérias viáveis sob selantes e restaurações e consequente diminuição na progressão da cárie quando as bactérias se encontram separadas do meio bucal. O objetivo deste ensaio clínico controlado randomizado foi avaliar a eficácia de duas estratégias de tratamentos: 1) selamento de lesões de cárie oclusal e 2) tratamento restaurador convencional com remoção total da dentina cariada em dentes permanentes. A amostra foi constituída de 52 dentes com lesões de cárie na superfície oclusal (pré-molares e/ou molares) de 47 pacientes com idade entre 8 a 43 anos. Todas as lesões de cárie apresentaram necessidade de tratamento restaurador de acordo com os seguintes critérios: presença de cavidade e impossibilidade de controle do biofilme. A profundidade máxima das lesões foi até a metade externa de dentina avaliada através de radiografias interproximais. Os dentes foram divididos aleatoriamente em um grupo teste - tratamento selante, ou grupo controle - tratamento restaurador convencional. Dados iniciais referentes à experiência de cárie (CPOD) e índice de sangramento gengival (ISG) foram avaliados. Radiografias interproximais foram realizadas após 12 meses para avaliar a integridade das restaurações e a zona radiolúcida (ZR) sob os selantes/restaurações. Os desfechos analisados foram o desempenho clínico dos tratamentos selante e restauração e a prevalência de regressão, inativação e progressão da cárie com exames radiográficos. A presença de dentina terciária também foi observada. Os dados foram avaliados por meio do teste exato de Fisher. Um total de 26 selantes e 26 restaurações foram realizadas. Não houve diferença entre os grupos quanto às características iniciais - idade, sexo, CPOD e ISG. Após um ano, foram avaliados 49 dentes, apresentando taxas de sucesso de 95,8% e 100% nos grupos selante e restauração convencional, respectivamente (p>0,05). Houve uma falha em um dos tratamentos (perda total no grupo selante) observada durante o estudo. A avaliação radiográfica (progressão, inativação, regressão e presença de dentina terciária) não demonstrou diferença entre os grupos. Nenhum dos dentes apresentou progressão de cárie; a regressão foi observada em apenas um caso (grupo do selante) e a presença de dentina terciária foi encontrada em 12,5% da amostra (5 selantes e 1 restauração). Selantes podem ser utilizados como tratamento terapêutico para lesões de cárie incipientes em dentes permanentes, uma vez que impedem a progressão das lesões de cárie, preservando a estrutura do dente, quando comparado ao tratamento restaurador convencional. / There is a significant decrease in the number of viable microorganisms under sealants and restorations and a consequent decrease in caries progression when bacteria are separated from the oral environment. The aim of this randomized controlled clinical trial was to evaluate the efficacy of two treatments strategies: 1) sealing of carious lesions and 2) operative restorative treatment of occlusal carious lesions in permanent teeth. The sample consisted of 52 carious posterior teeth (premolars and molars) from 47 patients aged 8 - 43 years. In all lesions restorative treatment was necessary according to the following current strategies: presence of cavity and impossibility to perform biofilm control. The maximum depth of lesions was halfway through the dentine assessed by bitewing radiograph. The teeth were randomly assigned to test group – sealant treatment or control group - conventional restorative treatment. Baseline caries experience (DMFT) and gingival bleeding index (GBI) was assessed. Bitewing radiographs were performed after 12 months to evaluate the integrity of the restorations and the radiolucent zone (ZR) beneath the sealants/restorations. Outcomes were defined as clinical performance of sealant and restoration and the prevalence of regression, inactivation and progression of carious lesion by radiographic examinations. Presence of tertiary dentine was also evaluated. The data were submitted to Fisher`s exact test. A total of 26 sealants and 26 restorations were performed. There were no differences between the two groups regarding baseline characteristics – age, gender, DMFT and GBI. After one year, 49 evaluations had been performed, showing 95.8% and 100% of success rates in test and control group respectively (p>0.05). There was one therapeutic failure (total loss in the sealant group) observed during the study. No difference in the radiographic evaluation (progression, inactivation, regression and tertiary dentin deposition) was observed between the groups (p>0.05). No teeth showed caries progression; regression was observed in only one case (sealant group) and tertiary dentin was founded in 12.5% of the sample (5 sealants and 1 restoration). Sealants can be used as a therapeutic treatment for incipient carious lesions in permanent teeth, since they prevent the progression of carious lesions, while preserving tooth structure when compared to conventional restorative treatment.

As evidências mostram uma redução ou eliminação significativa na quantidade de bactérias viáveis sob selantes e restaurações e consequente diminuição na progressão da cárie quando as bactérias se encontram separadas do meio bucal. O objetivo deste ensaio clínico controlado randomizado foi avaliar a eficácia de duas estratégias de tratamentos: 1) selamento de lesões de cárie oclusal e 2) tratamento restaurador convencional com remoção total da dentina cariada em dentes permanentes. A amostra foi constituída de 52 dentes com lesões de cárie na superfície oclusal (pré-molares e/ou molares) de 47 pacientes com idade entre 8 a 43 anos. Todas as lesões de cárie apresentaram necessidade de tratamento restaurador de acordo com os seguintes critérios: presença de cavidade e impossibilidade de controle do biofilme. A profundidade máxima das lesões foi até a metade externa de dentina avaliada através de radiografias interproximais. Os dentes foram divididos aleatoriamente em um grupo teste - tratamento selante, ou grupo controle - tratamento restaurador convencional. Dados iniciais referentes à experiência de cárie (CPOD) e índice de sangramento gengival (ISG) foram avaliados. Radiografias interproximais foram realizadas após 12 meses para avaliar a integridade das restaurações e a zona radiolúcida (ZR) sob os selantes/restaurações. Os desfechos analisados foram o desempenho clínico dos tratamentos selante e restauração e a prevalência de regressão, inativação e progressão da cárie com exames radiográficos. A presença de dentina terciária também foi observada. Os dados foram avaliados por meio do teste exato de Fisher. Um total de 26 selantes e 26 restaurações foram realizadas. Não houve diferença entre os grupos quanto às características iniciais - idade, sexo, CPOD e ISG. Após um ano, foram avaliados 49 dentes, apresentando taxas de sucesso de 95,8% e 100% nos grupos selante e restauração convencional, respectivamente (p>0,05). Houve uma falha em um dos tratamentos (perda total no grupo selante) observada durante o estudo. A avaliação radiográfica (progressão, inativação, regressão e presença de dentina terciária) não demonstrou diferença entre os grupos. Nenhum dos dentes apresentou progressão de cárie; a regressão foi observada em apenas um caso (grupo do selante) e a presença de dentina terciária foi encontrada em 12,5% da amostra (5 selantes e 1 restauração). Selantes podem ser utilizados como tratamento terapêutico para lesões de cárie incipientes em dentes permanentes, uma vez que impedem a progressão das lesões de cárie, preservando a estrutura do dente, quando comparado ao tratamento restaurador convencional. / There is a significant decrease in the number of viable microorganisms under sealants and restorations and a consequent decrease in caries progression when bacteria are separated from the oral environment. The aim of this randomized controlled clinical trial was to evaluate the efficacy of two treatments strategies: 1) sealing of carious lesions and 2) operative restorative treatment of occlusal carious lesions in permanent teeth. The sample consisted of 52 carious posterior teeth (premolars and molars) from 47 patients aged 8 - 43 years. In all lesions restorative treatment was necessary according to the following current strategies: presence of cavity and impossibility to perform biofilm control. The maximum depth of lesions was halfway through the dentine assessed by bitewing radiograph. The teeth were randomly assigned to test group – sealant treatment or control group - conventional restorative treatment. Baseline caries experience (DMFT) and gingival bleeding index (GBI) was assessed. Bitewing radiographs were performed after 12 months to evaluate the integrity of the restorations and the radiolucent zone (ZR) beneath the sealants/restorations. Outcomes were defined as clinical performance of sealant and restoration and the prevalence of regression, inactivation and progression of carious lesion by radiographic examinations. Presence of tertiary dentine was also evaluated. The data were submitted to Fisher`s exact test. A total of 26 sealants and 26 restorations were performed. There were no differences between the two groups regarding baseline characteristics – age, gender, DMFT and GBI. After one year, 49 evaluations had been performed, showing 95.8% and 100% of success rates in test and control group respectively (p>0.05). There was one therapeutic failure (total loss in the sealant group) observed during the study. No difference in the radiographic evaluation (progression, inactivation, regression and tertiary dentin deposition) was observed between the groups (p>0.05). No teeth showed caries progression; regression was observed in only one case (sealant group) and tertiary dentin was founded in 12.5% of the sample (5 sealants and 1 restoration). Sealants can be used as a therapeutic treatment for incipient carious lesions in permanent teeth, since they prevent the progression of carious lesions, while preserving tooth structure when compared to conventional restorative treatment.

Made available in DSpace on 2014-06-11T19:27:46Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-02-26Bitstream added on 2014-06-13T19:35:55Z : No. of bitstreams: 1 oliveira_dc_me_araca.pdf: 770246 bytes, checksum: afb5979626e6e6f01c61959aab800ef5 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A aplicação de selantes de fossas e fissuras e aplicação tópica de flúor são amplamente utilizados em procedimentos preventivos de cárie dentária, a eficácia desses materiais na prevenção de cárie dentária tem sido provada por revisões de literatura. O objetivo desse estudo foi comparar o efeito preventivo do selante de fossas e fissuras à base de ionômero de vidro (SIV) com o verniz fluoretado (VF) em molares permanentes de crianças com e sem experiência de cárie. Participaram do presente estudo 80 crianças, de ambos os gêneros, na faixa etária de 6 a 8 anos de idade, com os quatro primeiros molares permanentes recém irrompidos. Foram divididas em 2 grupos, sendo o grupo 1 formado por 53 crianças sem experiência de cárie e o grupo 2 formado por 27 crianças com experiência de cárie dentária. Em cada criança de um lado da cavidade bucal, os dois primeiros molares permanentes foram selados com um selante de ionômero de vidro (Fuji Triage), e nos outros dois primeiros molares permanentes do lado oposto, foi aplicado um verniz fluoretado (Duraflur). Para avaliar a eficácia dos materiais na prevenção da cárie dentária foi utilizado o método clínico visual, e a retenção do selante foi realizada aplicando-se os critérios de presença, parcial presença e ausência, estabelecidos por Simonsen. Os pacientes foram avaliados clinicamente após 6, 12 e 18 meses. Dos 320 primeiros molares que iniciaram o estudo, foram avaliados 319, 304, 299 aos 6, 12 e 18 respectivamente. Quanto ao efeito preventivo, mantiveram-se hígidos 307 (96%), 279 (92%) e 271 (91%) dentes, respectivamente nos períodos de análise. A lesão cariosa ocorreu em 12 (4%), 25 (8%) e 28 (9%) dentes respectivamente, sendo que em todos os períodos analisados, sua ocorrência prevaleceu no grupo de crianças com experiência de cárie dentária, sendo este... / Application of pit and fissure sealants and topical fluoride are widely used procedures in the prevention of decay, and their effectiveness in caries prevention has been proved by systematic reviews. The purpose of this clinical study was to compare the effectiveness of a glass ionomer sealant (GIS) with a fluoride varnish (FV) in the prevention of dental decay on first permanent molars of children with and without caries experience. The trial targeted eighty children aged 6 to 8 years, with all four newly erupted permanent first molars present. They were divided into 2 groups, with group 1 consisted of 53 children without caries experience and group 2 consists of 27 children with dental caries experience. In every child on one side of the oral cavity, the two first permanent molars were sealed with a glass ionomer sealant (Fuji Triage), and the other two first permanent molars on the opposite side, we applied a fluoride varnish (Duraflur). To assess the effectiveness of the materials in the prevention of tooth decay the clinical visual method was used, and retention of the sealant was performed by applying the criteria of complete presence, partial presence and absence, established by Simonsen’s. Patients were clinically evaluated after 6, 12 and 18 months. Of the 320 first molars that started the study 319, 304, 299 were evaluated to 6, 12 and 18 months respectively. Considering the preventive effect, 307 (96%), 279 (92%) and 271 (91%) teeth remained healthy respectively in the periods of analysis. The carious lesion occurred in 12 (4%), 25 (8%) and 28 (9%) respectively, and in all periods analyzed, their occurrence has prevailed in the group with caries experience, and this result was statistically significant. The materials used showed similar result in the periods of analysis, with no statistically significant... (Complete abstract, click electronic address below)

As evidências mostram uma redução ou eliminação significativa na quantidade de bactérias viáveis sob selantes e restaurações e consequente diminuição na progressão da cárie quando as bactérias se encontram separadas do meio bucal. O objetivo deste ensaio clínico controlado randomizado foi avaliar a eficácia de duas estratégias de tratamentos: 1) selamento de lesões de cárie oclusal e 2) tratamento restaurador convencional com remoção total da dentina cariada em dentes permanentes. A amostra foi constituída de 52 dentes com lesões de cárie na superfície oclusal (pré-molares e/ou molares) de 47 pacientes com idade entre 8 a 43 anos. Todas as lesões de cárie apresentaram necessidade de tratamento restaurador de acordo com os seguintes critérios: presença de cavidade e impossibilidade de controle do biofilme. A profundidade máxima das lesões foi até a metade externa de dentina avaliada através de radiografias interproximais. Os dentes foram divididos aleatoriamente em um grupo teste - tratamento selante, ou grupo controle - tratamento restaurador convencional. Dados iniciais referentes à experiência de cárie (CPOD) e índice de sangramento gengival (ISG) foram avaliados. Radiografias interproximais foram realizadas após 12 meses para avaliar a integridade das restaurações e a zona radiolúcida (ZR) sob os selantes/restaurações. Os desfechos analisados foram o desempenho clínico dos tratamentos selante e restauração e a prevalência de regressão, inativação e progressão da cárie com exames radiográficos. A presença de dentina terciária também foi observada. Os dados foram avaliados por meio do teste exato de Fisher. Um total de 26 selantes e 26 restaurações foram realizadas. Não houve diferença entre os grupos quanto às características iniciais - idade, sexo, CPOD e ISG. Após um ano, foram avaliados 49 dentes, apresentando taxas de sucesso de 95,8% e 100% nos grupos selante e restauração convencional, respectivamente (p>0,05). Houve uma falha em um dos tratamentos (perda total no grupo selante) observada durante o estudo. A avaliação radiográfica (progressão, inativação, regressão e presença de dentina terciária) não demonstrou diferença entre os grupos. Nenhum dos dentes apresentou progressão de cárie; a regressão foi observada em apenas um caso (grupo do selante) e a presença de dentina terciária foi encontrada em 12,5% da amostra (5 selantes e 1 restauração). Selantes podem ser utilizados como tratamento terapêutico para lesões de cárie incipientes em dentes permanentes, uma vez que impedem a progressão das lesões de cárie, preservando a estrutura do dente, quando comparado ao tratamento restaurador convencional. / There is a significant decrease in the number of viable microorganisms under sealants and restorations and a consequent decrease in caries progression when bacteria are separated from the oral environment. The aim of this randomized controlled clinical trial was to evaluate the efficacy of two treatments strategies: 1) sealing of carious lesions and 2) operative restorative treatment of occlusal carious lesions in permanent teeth. The sample consisted of 52 carious posterior teeth (premolars and molars) from 47 patients aged 8 - 43 years. In all lesions restorative treatment was necessary according to the following current strategies: presence of cavity and impossibility to perform biofilm control. The maximum depth of lesions was halfway through the dentine assessed by bitewing radiograph. The teeth were randomly assigned to test group – sealant treatment or control group - conventional restorative treatment. Baseline caries experience (DMFT) and gingival bleeding index (GBI) was assessed. Bitewing radiographs were performed after 12 months to evaluate the integrity of the restorations and the radiolucent zone (ZR) beneath the sealants/restorations. Outcomes were defined as clinical performance of sealant and restoration and the prevalence of regression, inactivation and progression of carious lesion by radiographic examinations. Presence of tertiary dentine was also evaluated. The data were submitted to Fisher`s exact test. A total of 26 sealants and 26 restorations were performed. There were no differences between the two groups regarding baseline characteristics – age, gender, DMFT and GBI. After one year, 49 evaluations had been performed, showing 95.8% and 100% of success rates in test and control group respectively (p>0.05). There was one therapeutic failure (total loss in the sealant group) observed during the study. No difference in the radiographic evaluation (progression, inactivation, regression and tertiary dentin deposition) was observed between the groups (p>0.05). No teeth showed caries progression; regression was observed in only one case (sealant group) and tertiary dentin was founded in 12.5% of the sample (5 sealants and 1 restoration). Sealants can be used as a therapeutic treatment for incipient carious lesions in permanent teeth, since they prevent the progression of carious lesions, while preserving tooth structure when compared to conventional restorative treatment.

Este estudo procurou verificar o efeito de dois selantes no tratamento de lesões cariosas não cavitadas em dentina, no que diz respeito à progressão da cárie na superfície oclusal de molares permanentes, em adolescentes com idades entre 11 e 15 anos. A amostra do estudo constituiu-se de 28 dentes: 14 selados com selante resinoso (Fluroshield®, Denstply), no grupo Gres, e 14 selados com selante ionomérico (RIVA Protect®, SDI), no grupo Gciv. A avaliação dos desfechos se deu por meio da análise dos exames radiográficos inicial e após 12 meses de acompanhamento; através de dois métodos: avaliação radiográfica qualitativa e quantitativa. A análise qualitativa foi realizada por um único examinador devidamente calibrado (Kappa = 0,837) com o uso de negatoscópio em sala escura e lupa de aumento 10x, e considerou como sucesso do tratamento a regressão ou paralisação da lesão; e insucesso, a evolução da lesão cariosa. A análise quantitativa se deu por meio da comparação entre os coeficientes de densidade radiográfica obtidos através do software DIGORA®, observando aumento (sucesso) ou diminuição (insucesso) dos coeficientes de densidade. Após a avaliação qualitativa, observou-se sucesso do tratamento em 64,3% dos casos (n=9) do grupo Gciv e 85,7% (n=12) do grupo Gres, sem diferença estatística entre os grupos (p=0,39). A avaliação quantitativa mostrou que no Gres foi observado um aumento significante dos coeficientes de densidade (p=0,003) e no Gciv se observou uma estabilidade dos coeficientes após 12 meses (p=0,49). Desta forma, pode-se concluir que, nas condições deste estudo, o uso de selantes de sulcos e fóssulas mostrou-se eficaz no tratamento de lesões cariosas. / This study examined the effect of two sealants in the treatment of non-cavitated occlusal carious lesions, regarding to the progression or arresting of the lesions in permanent molars in adolescents 11 to 15 years age. The sample consisted of 28 teeth: 14 sealed with resin-based sealant (Fluroshield®, Denstply), Gres group, and 14 sealed with glass ionomer sealant (RIVA Protect®, SDI), Gciv group. Caries progression was monitored by radiographic examination, using two methods: qualitative and quantitative trough radiographic evaluation. Qualitative analysis was performed by a single calibrated examiner (Kappa = 0.837) using light box in a darkened room and 10x magnifying glass, and considered as success treatment the regression or interruption of the injury caries, and failure treatment, the evolution of the lesion carious. Quantitative analysis occurred by comparing the radiographic density coefficient obtained through software DIGORA®, observing increased (success) or decreased (failure) of the coefficients. After the qualitative evaluation, it was observed success of treatment in 64.3% (n = 9) of Gciv group and 85.7% (n = 12) on Gres group, with no statistical difference between the them (p=0,39). The quantitative analysis showed in Gres group a significant increase in the density coefficient (p = 0.003) and in the Gciv group the stability of coefficients after 12 months (p = 0.49). It can be concluded that under the conditions of this study, the use of sealants proved to be effective in the treatment of occlusal carious lesions.

Indiana University-Purdue University Indianapolis (IUPUI) / Background: The ability of sealants to prevent caries is directly related to the sealant being retained in teeth. The longer the material remains bonded to the occlusal surface, the more protection it provides to the tooth. Objective: The aim of this in-vitro study was to evaluate the influence of pit and fissure morphologies and sealant viscosity on sealant penetration and micro-leakage. 82 Study Hypothesis: The low viscosity dental sealant will express better penetration ability and less microleakage in permanent molars with any pit and fissure morphology than the high viscosity sealant. Material and methods: Permanent extracted molars (n = 150) were distributed into two groups based on two types of sealant (high and low viscosity) Permanent extracted molars (n = 150) were selected using the International Caries Detection Assessment system (ICDAS) criteria 0-1. Teeth were stored in 0.1-percent thymol and distilled water. Teeth were assigned to three subgroups according to the fissure’s morphology. Enamel was etched with 35-percent phosphoric acid for 30 seconds; two different light cured sealants were placed, Group A: Delton and Group B: Ultra X Plus. Specimens were thermocycled for 500 cycles between two water baths, having a 40°C temperature differential (4°C to 48°C). Teeth were coated with nail varnish and wax, except in the occlusal areas. All specimens were immersed in 1-percent methylene blue dye at 37°C for 24 hours. Specimens were sectioned longitudinally in a bucco-lingual direction, and the sections were photographed and analyzed by a previously trained examiner for fissure morphology, sealant penetration, and microleakage using a standardized grading system. Data were entered and statistically analyzed, at the 5-percent significance level. Results: Viscosity of sealant and morphology of fissures had significant effects on sealant penetration (p < 0.001). The interaction between viscosity of sealant and morphology of fissures was not significant (p = 0.4236). The sealant penetration for Delton was significantly higher than the UltraSeal XT Plus (p < 0.0001). The sealant penetration for fissure I-type was significantly lower than fissures U and V-types (p < 0.0001). Sealant penetration for Y-type was significantly lower than U and V-types (p < 83 0.0001). However, the viscosity of sealant and morphology of fissures did not have significant effect on microleakage (p = 0.5891 and p = 0.4857). The interaction between the viscosity of the sealant material and the morphology of pit and fissures was not significant (p = 0.6657). Conclusion: The results of the present study indicated the viscosity of the sealant and the morphology did not affect the microleakage. On the other hand, the viscosity of sealant affected the penetration ability of dental sealant. The low viscosity dental sealant (Delton) exhibited a better penetration than the high viscosity sealant (UltraSeal XT Plus). As the morphology of pit and fissure directly affected the penetration ability, the fissures types U and V exhibited a better penetration than fissure types Y and I.