Conselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPq / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / In this work, CaF2, SrF2 and LiCaAlF6 pure and doped with rare earths were produced by microwave-assisted hydrothermal synthesis, which is a promising method to produce nanostructured powders in a simple, low cost and fast way. The samples were produced with or without using chelating agent and synthesized at low temperature, under pressure and a short time period. The crystalline phases of the samples were identified by X-ray diffraction (XRD) and the morphology of the particles was determined by scanning electron microscopy (SEM). The particles present similar morphology to CaF2 and SrF2 samples produced with and without using chelating agent. While the LiCaAlF6 samples presented a different morphology when produced with EDTA. The study of the chemical composition of CaF2 was performed by X-ray Photoelectron Spectroscopy (XPS) and the results indicated the presence of reasonable amounts of hydroxyl groups and oxygen ions in the samples produced with chelating agent. Optical study was conducted by emission and excitation spectra to understand the band structure and to determine the band gap of the materials. The emission spectrum showed that the CaF2 and SrF2 presents an intrinsic luminescence with an band at approximately 300 nm associated with the exciton emission. The fundamental absorption associated to the band gap was estimated at 11.7 eV for CaF2, 10.9 eV for SrF2 and 12.1 eV for LiCaAlF6. The emission and excitation spectra were measured in the Toroidal Grating Monochromator (TGM) beamline of the Brazilian Synchrotron Light Laboratory (LNLS) and the results shown evidences that the formation energy of the exciton and band gap energy are smaller than the ones for the single crystal. / Neste trabalho, CaF2, SrF2 e LiCaAlF6 puros e dopados com terras raras foram produzidos pelo método hidrotermal assistido por micro-ondas, o qual é um método promissor para produzir pós nanoestruturados de uma forma simples, com baixo custo e rápida. As amostras foram produzidas com e sem agente quelante e sintetizadas em baixa temperatura, sob pressão e curto período de tempo. As fases cristalinas das amostras foram identificadas por Difração de Raios X (DRX) e a morfologia das partículas determinada por microscopia eletrônica de varredura (MEV). As partículas apresentaram morfologias semelhantes para as amostras de CaF2 e SrF2 produzidas com e sem o uso do agente quelante. Enquanto que as amostras de LiCaAlF6 apresentaram uma morfologia diferente ao adicionar agente quelante. O estudo da composição química do CaF2 foi realizado por espectroscopia de fotoelétrons excitados por raios X (XPS) e os resultados indicaram a presença de uma quantidade razoável de grupos OH e íons de oxigênio na amostra produzida com agente quelante. Os estudos ópticos foram conduzidos por meio dos espectros de emissão e excitação para compreender a estrutura de bandas e determinar o band gap dos materiais. Os espectros de emissão mostraram que o CaF2 e o SrF2 apresentam luminescência intrínseca com uma banda em aproximadamente 300 nm associada a emissão do éxciton. A absorção fundamental associada ao band gap foi estimada em 11,7 eV para o CaF2, 10,9 eV para o SrF2 e 12,1 para o LiCaAlF6. Os espectros de emissão e excitação foram realizados na linha de luz TGM do Laboratório Nacional de Luz Sincrotron (LNLS) e os resultados mostraram evidências de que a energia de formação do éxciton e a energia do band gap são menores do que para o monocristal.

O tecido ósseo possui alto grau de rigidez e resistência à pressão, característica relacionada às suas funções de proteção, sustentação e locomoção. Patologias como periodontite, artrite reumatóide e osteoporose decorrem do desequilíbrio da dinâmica óssea, que ocorre quando os osteoclastos estão em maior atividade em relação aos osteoblastos. O fluoreto (F-) é incorporado nos tecidos mineralizados após ingestão e a sua administração aumenta a formação óssea in vivo, de maneira dependente da dose e da linhagem dos animais. As linhagens A/J e 129P3/J possibilitam a análise dos fenômenos moleculares envolvidos na suscetibilidade e resistência de células ósseas aos efeitos do F- no osso. Neste estudo, avaliou-se a administração in vivo de F- na osteoclastogênese, através da análise da atividade da enzima fosfatase ácida resistente ao tartarato (TRAP), contagem de células TRAP- positivas e quantificação da atividade das metaloproteinases MMP-2 e -9. Para tal, células hematopoiéticas provenientes da medula óssea de camundongos das linhagens 129P3/J e A/J foram cultivadas com M-CSF e RANKL em associação ou não com F-, nas concentrações de 10- 9, 10-7, 10-5, 5x10-5, 5x10-5, 10-4 e 10-3 M. Os dados mostraram que a atividade da TRAP foi semelhante entre as células das duas linhagens de animais, independente do F-. Concomitante à diferenciação osteoclástica, o tratamento das células com F-, independente da concentração, aumentou significativamente a atividade da TRAP em células da linhagem A/J. O aumento da atividade de TRAP foi associada com o aumento do número de osteoclastos formados, na concentração de 10-3 M F-. Já em células dos animais 129P3/J, o F- não alterou a atividade da TRAP bem como a osteoclastogênese. A atividade de MMP-9 foi aumentada em relação à da MMP-2, porém ambas não foram moduladas pelo F-, independente da linhagem. Assim, concluiu-se que as células de ambas as linhagens não diferem com relação à diferenciação de osteoclastos, mas respondem diferentemente ao F-, sendo as células dos animais A/J e 129P3/J sensíveis e resistentes à osteoclastogênese induzida pelo F-, respectivamente. / The bone tissue has a high degree of rigidity and pressure resistance, characteristic related to its protection, support and locomotion functions. Diseases such as periodontitis, osteoporosis and rheumatoid arthritis arise from dynamic bone imbalance that occurs when osteoclasts present increased activity compared to osteoblasts. Fluoride (F-) is incorporated in mineralized tissues after ingestion and its administration increases in vivo bone formation in dose and strain-dependent manner. The strains A/J and 129P3/J make possible the analysis of molecular phenomena involved in susceptibility and resistance of bone cells to the effect of F- in bone. In this study, we evaluated the effect of F- on the in vitro osteoclastogenesis, by analyzing the fosfatase tartrate-resistant acid (TRAP) activity, TRAP positive cell counts and the activity of MMP-2 and -9 measurements in A/J and 129P3/J differentiated hematopoietic stem cells. Hematopoietic cells were differentiated with M-CSF and RANKL and treated or not with F- in the concentrations of 10-9, 10-7, 10-5, 5x10-5, 5x10-5, 10-4 and 10-3 M.The data show that TRAP activity, an osteoclast marker, was similar between cells from both strains of mice, regardless of F-. In addition, the treatment of A/J cells with F- significantly increased TRAP activity, in a dose-independent manner. This was accompained by the increased TRAP+-osteoclast counts, at 10-3 M F- dose. However, while the MMP-9 activity was aumented when compared to MMP-2, it was not altered by F-, regardless of the strain. Thus, we concluded that cells from both strains do not differ regarding the osteoclast differentiation potential, but they respond differently to F-, whereas A/J and 129P3/J cells are sensitive and resistant to F--induced osteoclastogenesis, respectively.

A cidade de Ribeirão Preto é abastecida com água proveniente do Aquífero Guarani, sendo apenas fluoretada e clorada antes da distribuição. O objetivo desse trabalho foi avaliar a qualidade da água que a população está consumindo com relação às concentrações de fluoreto, chumbo e ferro. Além disso, foi investigada se a concentração de ferro poderia ser utilizada como marcadora da contaminação por chumbo na água potável. Foram investigadas 145 residências de 4 bairros antigos de Ribeirão Preto (casas com mais de 40 anos), havendo pelo menos uma criança moradora por residência. Um bairro novo (menos de 10 anos) foi escolhido para controle. Amostras de água foram coletadas na torneira da cozinha e do quintal, sendo a 1ª alíquota coletada após pelo menos 6 h de estagnação e a 2ª alíquota após 5 minutos de escoamento. A concentração dos íons fluoreto foi determinada por eletrodo combinado íon-seletivo e cromatografia iônica; chumbo por ET AAS e ICP-MS; e ferro por espectrofotometria. As concentrações de fluoreto nas amostras (n = 281) variaram de 0,052 a 1,01 mg L-1. Considerando apenas 1 algarismo significativo e as amostras provenientes da cozinha, observou-se que 30% das casas estiveram fora do padrão de potabilidade estabelecido pela Resolução SS-65 (2005), isto é, de 0,6 a 0,8 mg L-1. Considerado 2 algarismos, essa percentagem passou para 45%. Um baixo consumo de fluoreto pelas crianças pode não prevenir eficientemente a formação de cáries, enquanto que concentrações elevadas podem levar à fluorose dentária. As concentrações de chumbo variaram de 0,025 a 58,4 µg L-1 (n = 562), sendo que a concentração máxima permitida pela Portaria 2.914 (Ministério da Saúde) é de 10,0 µg L-1. Para todas as casas avaliadas, as concentrações de chumbo na água da torneira da cozinha não ultrapassaram 5,00 µg L-1, caracterizando um baixo risco de contaminação por chumbo por essa via. Para 2 alíquotas de água coletadas na torneira do quintal, a concentração de chumbo ultrapassou o limite tolerável para chumbo, porém, o uso dessa água para ingestão é pouco usual. Possivelmente a contaminação observada seja oriunda da própria torneira e outras partes metálicas, pois após escoamento da água por 5 minutos, a concentração de chumbo caiu dentro dos valores permitidos. As concentrações de ferro variaram de 13,40 a 4.119 µg L-1 (n = 189; 1ª alíquota), sendo a concentração máxima permitida de 300 µg L-1 (Portaria 2.914). Em 4 casas a água do quintal apresentou concentração superior a permitida, mas na água da cozinha a concentração foi de 8 a 66 vezes menor. Isso indica que a torneira do quintal pode ser uma grande fonte de contaminação de ferro. Apesar do coeficiente de correlação linear entre a concentração de ferro e chumbo na água ser estatisticamente significativo (r = 0,410; n = 184), essa correlação foi relativamente baixa para sugerir o uso do ferro como marcador da contaminação por chumbo. / The city of Ribeirão Preto is supplied with water from the Guarani Aquifer, that is only fluoridated and chlorinated before distribution. The objective of this study was to evaluate the quality of drinking water that the population is consuming with respect to the concentrations of fluoride, lead and iron. Furthermore, it was investigated if the concentration of iron could be used as a marker to infer lead contamination in drinking water. We investigated 145 residences with more than 40 years of age in 4 districts of Ribeirão Preto, with at least one resident child. One new district (less than 10 years) was selected as a control group. Water samples were collected from the kitchen and the yard taps. The 1st aliquot was collected after at least 6 h of stagnation and the 2nd after leaving the water running for 5 minutes. The concentration of fluoride ions was determined by combined ion-selective electrode and ion chromatography; lead by ET AAS and ICP-MS; and iron by spectrophotometry. The fluoride concentrations in the samples varied from 0.052 to 1.01 mg L-1 (n = 281). Considering only 1 significant digit and the kitchen samples, it was observed that 30% of the homes did not attend the legislation for fluoride in drinking water (Resolution SS-65, 2005), that is, from 0.6 to 0.8 mg L-1. Considering 2 significant digits, this percentage increased to 45%. A low intake of fluoride by children cannot effectively prevent the formation of dental caries, while high concentrations can cause dental fluorosis. Lead concentrations ranged from 0.025 to 58.4 µg L-1 (n = 562), and the maximum permited by the law 2,914 (Ministry of Health) is 10.0 µg L-1. For all homes investigated, lead concentrations from the kitchens tap water did not exceed 5.00 µg L-1, showing there is a low risk of lead contamination through this pathway. For 2 aliquots of water collected from the yards tap, the concentration of lead exceeded the tolerable limit, however, the use of this water for ingestion is unusual. Possibly this contamination might come from the tap itself and from others metal parts, because after running the water for 5 minutes the lead concentration fell below the permitted value. Iron concentrations varied from 13.40 to 4,119 µg L-1 (n = 189, 1st aliquot), and the tolerable limit is 300 µg L-1 (law 2.914). In 4 houses the water from the year tap had concentrations above the limit, while in the kitchen water iron concentrations were from 8 to 66 times lower. This indicates that the tap material from the yard can be a large source of iron contamination. Although the linear correlation coefficient between iron and lead concentrations in the drinking water was statistically significant (r = 0.410; n = 184), this correlation was relatively low to suggest the use of iron as a marker of contamination by lead.

Estudos têm avaliado a eficiência de diferentes tipos de laser no aumento da resistência ácida e na redução da solubilidade do esmalte dentário. O objetivo do presente estudo clínico longitudinal foi avaliar o comportamento do laser de CO2 associado, ou não, à aplicação tópica de fluoreto acidulado na prevenção de lesões de cárie em fossas e fissuras de primeiros molares permanentes parcialmente irrompidos. Foram selecionadas 61 crianças de alto risco a cárie dentária, de 6 a 8 (7,1 ± 0,8) anos de idade, apresentando os quatro primeiros molares permanentes parcialmente irrompidos e hígidos. Cada primeiro molar recebeu aleatoriamente um dos tratamentos avaliados nas fossas e fissuras: (L) - laser de CO2 (0,066J/cm2); (FL) - gel fluoretado acidulado a 1,23% e laser de CO2 (0,066J/cm2); (V) - verniz fluoretado a 5%; (S) selante (controle). Os dentes foram avaliados aos 3, 6, 12 e 18 meses após a realização dos tratamentos, por meio de exame visual direto e avaliador calibrado e \"cego\" aos tratamentos (Kappa 0,70). Foi utilizado o indíce ICDAS-II para avaliação da manutenção da higidez, presença de lesão de mancha branca ativa e de lesões cavitadas em esmalte e/ou dentina. Para avaliação da retenção do selante, foram utilizados os critérios visuais modificados de Yildiz et al. (2004). Foi aplicada a análise de sobrevida de Kaplan-Meyer. O hazard ratio dos tratamentos foram estimados utilizando-se shared frayilt models com distribuição gama, considerando-se o paciente como conglomerado. O modelo também evidenciou que a correlação intra-paciente foi significante (p = 0,0022), com covariância de 0,8425 (erro padrão = 0,3208). Clinicamente, não houve diferença significante entre os tratamentos (L), (LF) e (V) após 18 meses de avaliação. Para o tratamento (S), observou-se a maior taxa de desenvolvimento de lesões de cárie. Após análise longitudinal de 18 meses, pode-se concluir que a aplicação do laser de CO2, independentemente do uso associado ao fluoreto, foi eficiente na prevenção de lesões de cárie em fossas e fissuras de molares parcialmente irrompidos, em crianças de alto risco à cárie. / Studies have evaluated the efficiency of different laser systems in increasing strength and reducing the acid solubility of dental enamel. The aim of this longitudinal clinical study was to evaluate the CO2 laser combined or not to the topical application of acidulated fluorides in preventing caries in pits and fissures of partially-erupted first permanent molars. It were selected 61 children at high caries-risk, with 6-8 (7.1 ± 0.8) years old, with the four first permanent molars partially erupted and healthy. Each first molar randomly received one of the tested treatments in pits and fissures: (L) - CO2 laser (0.066 J/cm2), (FL) - acidulated fluoride gel 1.23% and CO2 laser (0.066 J/cm2) (V) - 5% fluoride varnish, (S) - sealant (control). The teeth were evaluated at 3, 6, 12 and 18 months after treatment, through direct visual examination and by a calibrated operator blinded to the treatments (Kappa 0.70). The ICDAS-II index was used to assess the soundness of tooth structure, presence of white spot lesions and cavitated enamel and/or dentin lesions. The Yildiz et al. (2004) visual modified criteria was used to evaluate the retention of sealant. The Kaplan-Meyer survival analysis was used. The hazard ratio of the treatments was estimated using frayilt shared models with gamma distribution, considering the patient as a conglomerate. The model also showed that intra-patient correlation was significant (p = 0.0022), with covariance of 0.8425 (standard error = 0.3208). Clinically, there was no significant difference between (L), (LF) and (V) treatments after 18 months of evaluation. For (S) treatment, there was a higher rate of caries development. After long-term analysis of 18 months, it can be concluded that the application of CO2 laser, regardless of use with fluoride, was effective in preventing caries in pits and fissures of partially-erupted molars in children at high caries-risk.

O presente trabalho teve como objetivo avaliar in vitro o efeito de diferentes densidades de energia da irradiação com lasers de CO2 e Nd:YAG sobre o esmalte e dentina quando submetidos a erosão (fase 1) e depois avaliar o efeito do melhor parâmetro associado ao fluoreto na diminuição da erosão dentária, quando aplicados sobre esmalte e dentina hígidos e previamente erodidos (fase 2). Além disso, na fase 1 foi avaliado o efeito do recobrimento das estruturas dentárias com pigmento (corante foto absorvente) no desempenho do laser de Nd:YAG. Na fase 1, 130 blocos de esmalte e 130 blocos de dentina (dente bovino), foram igualmente e aleatoriamente divididos em 13 grupos (n = 10): C- sem tratamento (controle), Nd1 e Nd5- irradiação com laser Nd:YAG (42,45 J/cm2), Nd2 e Nd6- irradiação com laser Nd:YAG (56,6 J/cm2), Nd3 e Nd7- irradiação com laser Nd:YAG (84,9 J/cm2), Nd4 e Nd8- irradiação com laser Nd:YAG (99,05 J/cm2), CO1 - irradiação com laser CO2 (esmalte: 7,2 J/cm2; dentina: 3,6 J/cm2), CO2 - irradiação com laser CO2 (esmalte: 14,4 J/cm2; dentina: 7,2 J/cm2), CO3 - irradiação com laser CO2 (esmalte: 21,4 J/cm2; dentina: 10,7 J/cm2) e CO4 - irradiação com laser CO2 (esmalte: 28,8 J/cm2, dentina: 14,4 J/cm2). Nos grupos Nd5-9 foi feita aplicação de corante a base de carvão antes da irradiação com laser Nd:YAG. Antes da irradiação os blocos tiveram 2/3 de suas superfícies protegidas com esmalte cosmético para realização da perfilometria. Após a irradiação, os blocos foram submetidos à ciclagem erosiva, composta por 4 imersões diárias em bebida ácida por 2 minutos, seguida pela imersão em saliva artificial por 2 h, durante 5 dias. A perda de esmalte e dentina foram avaliados por meio da perfilometria após a aplicação do laser e após o 1º e 5º dia de ciclagem erosiva. Na segunda fase foi utilizado o grupo que obteve o melhor resultado numérico ou estatístico quanto à diminuição do desgaste. Assim 120 blocos de cada tipo de substrato foram divididos em 12 grupos (n = 10): C - controle sem erosão prévia; C+EP - controle com erosão prévia; Nd:YAG - irradiação com laser Nd:YAG (esmalte: 56,6 J/cm2 e dentina: 42,45 J/cm2); EP+Nd:YAG - erosão prévia seguida da irradiação com laser Nd:YAG; F - aplicação de AmF (1% F); EP+F - erosão prévia e posterior aplicação de AmF (1% F); Nd:YAG+F - irradiação com laser Nd:YAG e posterior aplicação de AmF (1% F); EP+Nd:YAG+F - erosão prévia seguida da irradiação com laser Nd:YAG e posterior aplicação de AmF (1% F); CO2 - irradiação com laser CO2 (esmalte: 28,6 J/cm2 e dentina: 10,7 J/cm2); EP+CO2 - erosão prévia seguida da irradiação com laser CO2; CO2+F - irradiação com laser CO2 e posterior aplicação de AmF (1% F); EP+CO2+F - erosão prévia seguida da irradiação com laser CO2 e posterior aplicação de AmF (1% F). Assim como na 1ª fase, antes da irradiação, os blocos foram protegidos (2/3) e após os tratamentos, os blocos foram submetidos à ciclagem erosiva previamente descrita. Os blocos foram avaliados por perfilometria como descrito. Os resultados foram submetidos à ANOVA ou Kruskal Wallis e Teste de Tukey (p<0,05), sendo que os dois tipos de lasers foram avaliados separadamente. Os diversos parâmetros do laser Nd:YAG não apresentam efeito preventivo em relação à erosão dentária independentemente do corante foto absorvente. Para o CO2 apenas as densidades de energia de 28,8 J/cm2 para o esmalte e 10,7 J/cm2 para a dentina apresentaram este efeito. A estrutura dentária previamente erodida resulta em maior desgaste quando comparada à estrutura hígida. A utilização de fluoreto na maioria das situações apresentou efeito preventivo em relação à erosão, no entanto a associação do fluoreto ao laser não apresentou efeito sinérgico, tendo sido observada uma diminuição do efeito preventivo do fluoreto. Considerando esses resultados, para os pacientes com risco de erosão dentária, a aplicação de fluoreto ainda é o tratamento com melhor resultado preventivo em relação à erosão dental. / This study aimed to evaluate the in vitro effect of different irradiation power densities of CO2 and Nd:YAG lasers on enamel and dentine when eroded (phase 1). To evaluate the effect of fluoride associated with the best parameter of laser able to reduce dental erosion considering sound and previously eroded enamel and dentine (phase 2). Furthermore, in phase 1 the application of an absorbing photo dye was evaluated on the performance of Nd:YAG. In phase 1, 130 enamel blocks and 130 dentine blocks, were equally and randomly divided into 13 groups (n = 10): C -untreated (control), Nd1 and Nd5 - irradiation with Nd:YAG laser (42.45 J/cm2), Nd2 and Nd6 - irradiation with Nd:YAG laser (56.6 J/cm2), Nd3 and Nd7 - irradiation with Nd:YAG laser (84.9 J/cm2), Nd4 and Nd8 - irradiation with Nd:YAG laser (99.05 J/cm2), CO1 - CO2 laser irradiation (enamel: 7.2 J/cm2; dentine: 3.6 J/cm2), CO2 - CO2 laser irradiation (enamel: 14.4 J/cm2; dentine: 7.2 J/cm2), CO3 - CO2 laser irradiation (enamel: 21.4 J/cm2; dentine: 10.7 J/cm2) and CO4 - CO2 laser irradiation (enamel: 28.8 J/cm2, dentine: 14.4 J/cm2). In groups Nd5 to 9 coal-paste dye was applied before Nd:YAG laser irradiation. Before irradiation 2/3 of the blocks surfaces were protected with nail varnish for performing the profilometry. After irradiation, the blocks were submitted to four erosive 2-min cycles, followed by immersion in artificial saliva for 2 h for 5 days. Enamel and dentine losses were evaluated by profilometry after laser application and after 1 and 5 days of erosive cycling. In the second phase, the group that obtained the best numerical or statistical result was used. So 120 enamel and dentine blocks were divided into 12 groups (n = 10): C - control without prior erosion; C+EP - control with prior erosion; Nd:YAG - laser irradiation with Nd:YAG (enamel: 56.6 J/cm2 and dentin: 42.45 J/cm2); EP+Nd:YAG - prior erosion followed by Nd:YAG irradiation; F - AmF (1% F) application; F+EP - erosion prior subsequent AmF (1% F) application; Nd:YAG+F - irradiation with Nd:YAG laser and subsequent AmF (1% F) application; EP+Nd:YAG+F - prior erosion followed by Nd:YAG irradiation and subsequent AmF (1% F) application; CO2 - CO2 laser irradiation (enamel: 28.6 J/cm2 and dentin: 10.7 J/cm2</sub); EP+CO2 - prior erosion followed by CO2 laser irradiation , F+CO2 - CO2 laser irradiation and subsequent AmF (1% F) application; F+EP+CO2 - erosion prior CO2 laser irradiation and subsequent AmF (1% F) application. As in stage 1, before irradiation, the blocks were protected (2/3) and after the treatments, the blocks were subjected to erosive cycling as previously described. The dental loss was evaluated by profilometry as described. The lasers were analyzed separated. The results were submitted to ANOVA or Kruskal Wallis (as passed or not in the normal curve) and Tukey test (p<0.05). The various parameters of Nd:YAG laser did not present effect in relation to dental erosion regardless of the use of photo absorbent dye. In relation to CO2 laser only the energy densities of 28.8 J/cm2 for enamel and 10.7 J/cm2 for dentin showed some preventive effect. The previously eroded substrate resulted in greater wear when compared to sound one. Generally, fluoride had some preventive effect against erosion. However, the combination of fluoride to the laser showed no synergistic effect, since it was observed a decrease in fluoride preventive effect. Considering these results, for patients at high risk for dental erosion, application of fluoride is still the best preventive treatment.

Fluoreto presente em águas de abastecimento, pode ser determinado por titulação condutométrica, usando-se La(NO3)3 como titulante. O método proposto no presente trabalho exige a separação prévia de fluoreto da amostra, por destilação a 135&#186;C. O pH do destilado é ajustado entre 5,5 - 6,0; etanol é adicionado até atingir-se a proporção de 50%, titulando-se a solução resultante com La(NO3)3. Nessas soluções, fluoreto nas concentrações de 500 ppb e 2,0 ppm podem ser determinadas com precisões de 5% e 4%, respectivamente. Amostras naturais foram analisadas condutometricamente pelo método proposto, potenciometricamente com eletrodo íon seletivo de fluoreto, obtendo-se resultados compatíveis. / Fluoride ions in drinking water can be easily determined by condutometric titraction using La(NO3)3 as titrant. The sample must be destilled in H2S04 previously to separate the fluoride ions, at 1350 C. The destillated, in 50% ethanol is titrated with La(NO3)3 In these conditions, fluoride ions at the concentrations of 500 ppb and 2,0 ppm are determined with accuracy of, respectively, 5% and 4%. Natural samples of drinking water were analysed by this method and by the ion-selective method, with agreement among the results.

Submitted by Mirian Silva (mirian.pereira@uniceub.br) on 2015-10-08T23:33:03Z No. of bitstreams: 1 Influencia do tempo (6) ok.pdf: 358016 bytes, checksum: 31f9923438aa951579acb64080ccce3b (MD5) / Made available in DSpace on 2015-10-08T23:33:03Z (GMT). No. of bitstreams: 1 Influencia do tempo (6) ok.pdf: 358016 bytes, checksum: 31f9923438aa951579acb64080ccce3b (MD5) Previous issue date: 2012 / A dosagem da glicemia é empregada para estudo do metabolismo da glicose tanto no controle de produção, consumo e também no armazenamento, assim podem ser diagnosticados os diversos estados de hiperglicemia e hipoglicemia, podendo ser medidos por exames laboratoriais utilizando sangue venoso. É visto que após a coleta do sangue, as células sanguíneas continuam a degradar a glicose gerando um decréscimo de aproximadamente 10mg/dL por hora à temperatura ambiente a não ser que se adicione um preservativo, sendo o fluoreto o mais indicado por ser inibidor da glicólise. Este estudo teve por objetivo comparar o uso de dois anticoagulantes diferentes (fluoreto e EDTA) para avaliar a estabilidade da glicemia em temperatura ambiente e ainda correlacionar as glicemias obtidas para os dois tipos de anticoagulantes determinando a diferença entre elas devido ao fator de tempo. Para a realização do trabalho foram coletadas 30 amostras de sangue total por punção venosa de voluntários de ambos os sexos sem restrição de idade e sem necessidade de jejum. Os resultados obtidos confirmaram que na primeira hora houve a queda de aproximadamente 10mg/dL para os dois anticoagulantes utilizados, seguido de estabilização com o anticoagulante fluoreto e um decréscimo progressivo com o uso do anticoagulante EDTA. Isto concorda com o fato de que o tempo é um fator determinante na dosagem da glicemia influenciando na estabilidade da amostra e na confiabilidade dos resultados podendo gerar resultados não verdadeiros.

Orientador: Cristina Antoniali Silva / Banca: Robson Frederico Cunha / Banca: Adriana Balbina Paoliello Paschoalato / Resumo: Em pesquisa anterior, verificamos que ratos espontaneamente hipertensos (SHR) apresentam menor fluxo salivar estimulado que ratos normotensos Wistar, o que poderia levar ao maior índice de doença cárie nestes animais. O objetivo deste estudo foi avaliar o efeito do tratamento crônico com fluoreto de sódio (NaF) nos parâmetros bioquímicos da saliva e plasma, nos ossos e na mineralização de dentes incisivos de SHR. Foram utilizados ratos Wistar e SHR aos 3 meses de vida. O tratamento foi feito com solução de NaF (20 ppm) por 30 dias, na água de beber. A medida da pressão arterial sistólica (PAS) foi realizada pelo método indireto de pletismografia de cauda. Para a coleta da saliva, o fluxo salivar foi estimulado com nitrato de pilocarpina e os animais foram colocados em prancha inclinada e a saliva coletada por 15 minutos. As concentrações salivares e plasmáticas de fluoreto foram determinadas com eletrodos específicos e as de cálcio utilizando um kit comercial específico. A determinação da concentração de proteínas totais foi realizada pelo método de Lowry e a atividade da amilase salivar utilizando kit comercial. A análise de flúor na superfície do fêmur foi feita pelo método direto e a análise no fêmur pelo método de Taves. A microdureza dos dentes incisivos foi determinada utilizando microdurômetro com penetrador tipo Knoop. Os resultados foram avaliados e a diferença estatística foi considerada quando p<0,05. A PAS e o peso dos animais não foram alterados pelo tratamento. O reduzido fluxo salivar de SHR apresentou-se aumentado em SHR tratados. A concentração de flúor na saliva e plasma aumentou com o tratamento em ratos Wistar, no entanto em SHR este aumento foi observado apenas no plasma. Apesar do aumento no fluxo ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In previous research we found that spontaneously hypertensive rats (SHR) have lower stimulated salivary flow than normotensive Wistar, which could lead to a higher rate of caries in these animals. The aim of this study was to evaluate the effect of chronic treatment with sodium fluoride (NaF) in the biochemical parameters of saliva and plasma, bone and mineralization in incisor teeth of SHR. Were used SHR and Wistar rats at 3 months of life. The treatment was made with NaF solution (20 ppm) for 30 days in drinking water. The measurement of systolic blood pressure (SBP) was performed by the indirect method of tail plethysmography. To collect saliva, salivary flow was stimulated with pilocarpine nitrate and the animals were placed on an inclined board and saliva collected for 15 minutes. Salivary and plasma concentrations of fluoride were determined with specific electrodes and calcium using a specific commercial kit. The determination of total protein concentration was performed by the method of Lowry and salivary amylase activity using a commercial kit. The analysis of fluoride on the surface of the femur was made by the direct method and analysis in the femur by the method of Taves. The microhardness of incisors was determined using Knoop microhardness with indenter type. The results were evaluated and differences were considered when p <0.05. The SBP and the weight of the animals were not affected by treatment. The reduced salivary flow in SHR were enlarged in treated SHR. The fluoride concentration in saliva and plasma increased with treatment in Wistar rats, however, in SHR the increase was only observed in plasma. Despite the increase in salivary flow that occurs after treatment with NaF, the concentration of fluoride in saliva is not altered in SHR. The calcium concentration decreased in saliva and plasma in SHR group after treatment, what ... (Complete abstract click electronic access below) / Mestre

O aumento da prevalência de lesões erosivas tem levado a um crescente interesse por medidas preventivas e para controle de tais lesões. Este estudo avaliou in vitro e in situ o efeito da associação de fluoretos à irradiação com laser de CO2 na permeabilidade do esmalte dental erodido. Para o experimento in vitro, foram selecionados oitenta fragmentos (n=10) de esmalte bovino (3x2x2 mm). Para formação de lesão de erosão, os espécimes foram submetidos a desafios ácidos iniciais duas vezes ao dia, durante dois dias, através de um regime alternado de erosão e remineralização. Para isso, os espécimes foram imersos individualmente em 20 ml de suco de laranja (pH 3,84) por 5 min sob agitação, enxaguados com água deionizada e armazenados em saliva artificial por 4 h. Os espécimes com as lesões de erosão pré-formadas foram divididos em 4 grupos para serem submetidos aos diferentes tratamentos: amina fluoretada (AmF), tetrafluoreto de titânio (TiF4), fluoreto de sódio (NaF) e placebo. Metade dos espécimes foi irradiada no modo contínuo com laser de CO2 ( &lambda;= 10.6 µm; 2.0 W). Após a realização dos tratamentos, foram simulados novos desafios erosivos durante 2 dias, utilizando o mesmo protocolo descrito anteriormente. Terminadas as ciclagens, os espécimes foram preparados para a avaliação da permeabilidade, sendo submetidos ao método de coloração histoquímica. Uma vez obtidos os resultados do estudo in vitro, foi conduzido um experimento in situ constituído por um delineamento crossover, com duas fases de 5 dias cada. No estudo in situ, os fatores em estudo foram os tratamentos (TiF4 e placebo) e a aplicação do laser de CO2 (presente ou ausente.) Os fragmentos de esmalte bovino foram montados em dispositivo palatino para serem instalados nos participantes para a realização dos desafios erosivos, através da ingestão de 10 alíquotas de 25 ml cada, (9, 11, 13 e 15h). A avaliação da permeabilidade foi realizada conforme descrita para o estudo in vitro. Os dados foram analisados através da ANOVA e Tukey. No estudo in vitro, houve interação significativa entre fluoreto e laser (p=0,0152). Quando os géis fluoretados foram aplicados sozinhos, TiF4 promoveu menor permeabilidade do esmalte do que aquela observada após a aplicação do placebo, enquanto resultados intermediários foram encontrados para os géis de NaF e AmF. Redução na permeabilidade do esmalte foi observada quando a aplicação dos fluoretos foi associada à irradiação com laser de CO2 . No estudo in situ, houve efeito significativo da interação entre os fatores fluoreto e laser de CO2 (p = 0,0002). Em relação ao placebo, a aplicação do TiF4 reduziu significativamente a permeabilidade do esmalte, para substratos irradiados ou não. Mediante a aplicação do placebo, o laser foi capaz de reduzir significativamente a permeabilidade do esmalte, porém, quando se utilizou o TiF4, a aplicação do laser não implicou em redução da permeabilidade. Combinada à aplicação de gel fluoretado, a irradiação com laser de CO2 pode representar uma medida adjuvante no controle da permeabilidade do esmalte erodido. / The increased prevalence of erosive lesion has led to a growing interest of preventive means and to control such lesions. This study evaluated in vitro and in situ the effect of fluoride compounds combined with a CO2 laser on permeability of eroded dental enamel. To in vitro experiment, 80 bovine enamel slabs (n=10) were selected. To create erosion-like lesions, specimens were submitted to inicial erosive challenges, twice a day, during two days, through an alternating erosive and remineralizing regimen. For that, specimens were immersed in 20 ml of orange juice (pH 3.84) for 5 min under agitation, rinsed with deionized water and stored in artificial saliva for 4 h. Specimens with pre-formed lesions were divided into four groups to be treated with different fluoride gels: amine fluoride (AmF), titanium tetrafluoride (TiF4 ), sodium fluoride (NaF) and placebo. Half of the specimens were irradiated with CO2 laser ( &lambda;= 10.6 µm; 2.0 W).Then, specimens were further cycled twice through the previously described erosive-remineralizing regimen. After cycled, specimens were subjected to permeability assessment. Once the results of in vitro study were obtained, an in situ experiment, consisting of a crossover design, with 2 phases of 5 days each, was performed. To in situ study, factors involved were treatments (TiF4 and placebo) and CO2 laser irradiation (present or absent). Bovine enamel slabs (n=10) were placed in palatal device to perform erosive challenges. Volunteers ingested orange juice as 250 mL volumes 4 times per day (9,11,13,15h). Permeability assessment was performed as described to in vitro study. Data were analyzed by ANOVA and Tukey. In vitro study demonstrated significant interaction between fluoride and laser (p = 0,0152). When fluoride gels were applied alone, TiF4 provided to enamel lower permeability than that observed following placebo application, while intermediate results were found to NaF and AmF gels. Reduction of enamel permeability was observed when fluorides were combined to CO2 laser irradiation. To in situ study, there was significant interaction between fluoride and laser (p=0,0002). When compared to placebo, TiF4 application reduced significantly enamel permeability, regardless of irradiation. Through application of placebo, laser was able to reduce significantly enamel permeability; however, when TiF4 was applied, laser irradiation did not decreased permeability. Combined to fluoride gel application, CO2 laser irradiation can represent an adjunctive way in controlling eroded enamel permeability.

Entre as várias terapêuticas propostas para o tratamento da osteoporose, a administração de altas doses de fluoreto é uma alternativa que ainda apresenta controvérsia na literatura. O fluoreto se destaca por influenciar na atividade dos osteoblastos, os quais são responsáveis por mediar a síntese de moléculas que compõem o osso. No entanto, o mecanismo de ação do fluoreto em células do tecido ósseo (osteoblastos, osteócitos e osteoclastos) ainda não está bem esclarecido. Neste trabalho foram utilizados camundongos com diferentes densidades ósseas, sendo 32 da linhagem C57BL/6J (menor densidade óssea) e 32 da linhagem C3H/HeJ (maior densidade óssea) com 60 dias de vida, os quais receberam água deionizada ou água com 50 ppm de fluoreto (na forma de NaF). Realizou-se os procedimentos cirúrgicos extraindo o incisivo superior esquerdo e posteriormente os animais foram eutanasiados 7, 14, 21 e 28 dias após a extração. Imediatamente após a eutanásia, foi removida a peça com alvéolo dental esquerdo. Foram feitas análises descritiva e morfométrica das lâminas obtidas (coloração em Hematoxilina Eosina). Foi utilizada análise ANOVA a quatro critérios seguida da análise de Tukey (p<0,05). Em geral, para todos os grupos, a análise histológica mostrou neoformação óssea à partir das paredes do alvéolo e formação de ilhotas ósseas invadindo o centro dos alvéolos, substituindo o tecido conjuntivo existente. O tecido ósseo neoformado substituiu aos poucos o tecido conjuntivo ao longo dos períodos experimentais, sendo esse fenômeno ligeiramente mais evidente nos camundongos da linhagem C57BL/6J. A análise morfométrica confirmou os achados histológicos em relação à quantidade de tecido ósseo neoformado e mostrou diminuição do tecido ósseo neoformado no último período (28 dias) nos animais C3H/HeJ (grupos controle e experimental). Concluimos que o processo de reparo ósseo alveolar é semelhante nas duas linhagens estudadas, porém apresentam padrão de formação óssea diferentes entre elas. O fluoreto parece influenciar as etapas do processo de reparo alveolar nas duas linhagens, aumentando a quantidade de osso neoformado, no entanto, a linhagem de camundongos C57BL/6J é mais propensa aos efeitos do flúor. / Among the various therapeutic proposals for the osteoporosis treatment, the administration of high doses of fluoride is an alternative that still has controversies in literature. Fluoride is highlighted by influencing the activity of osteoblasts, which are responsible for mediating the synthesis of bone. But, the mechanism of action of fluoride on bone cells (osteoblasts, osteocytes and osteoclasts) is not well understood. This way, this study aims to evaluate the alveolar bone repair in rats under the effect of fluoride (NaF) administered in the water. This work were used four groups of strains C57BL/6J mice (total of 32) and C3H/HeJ (total of 32) for 60 days, which received deionized water or water with 50 ppm of fluoride. The surgical procedures were made by extracting the upper left incisor and then the animals were euthanized 7, 14, 21 and 28 days. Histological analysis (Hematoxylin Eosin staining), by light microscopy, were made. The statistical analysis were made using the statistical test one-way ANOVA complemented by Tukey\'s test (p <0.05). Generally, for all groups, the histological analysis showed a new bone formed from the alveolar walls, replacing the connective tissue. The newly formed bone tissue gradually replaces the connective tissue over time; wich was more evident in C57BL/6J mice. Morphometric analisys confirmed the histological findings of the new bone formed and showed a decrease in the new formed bone in the last period (28 days) of the C3H/HeJ animals. We concluded that the process of alveolar repair is similar when it respects to the stages of repair, however they presents different pattern of new bone formation. The fluoride influences the stages of alveolar repair in both lineages, increasing the amount of bone formed, however the mice lineage of C57BL/6J is more prone to the effects of fluoride.