<p>Joints are critical parts of timber structures, transmitting static and dynamic forces between structural members. The ultimate behavior of a loaded building depends strongly on the structural configuration and the capacity of the joints. The collapse of a whole building or less extensive accidents that may occur is usually starting as a local failure inside or in the vicinity of a joint. Such serious failures have recently occurred in our Nordic countries. Especially the collapse of two large glued laminated timber structures clearly indicates the need of an improved joint design. The trend toward larger and more complex structures even further increases the importance of a safer design of the joints.</p><p>An aim of this partly experimental and partly numerically based thesis has been to investigate if steel-to-timber dowel joints are affected by moisture-induced stresses. The experimental results showed that the load-bearing capacity of the joints is reduced by such a moisture influence. Most of the decrease in load-bearing capacity observed was found in joints initially exposed to restrained shrinkage deformations caused by the presence of dowel fasteners in the joint area. The load-bearing capacity was, however, also found to decrease in joints exposed to an initial decrease in moisture without any fasteners present in the specimens during storage before loading. An explanation of this unexpected behavior is that moisture gradients cause tensile stresses. It is shown by numerical simulations that the moisture-induced stresses are so large that they may have a considerable influence on the joint behavior.</p><p>Use of contact-free measurement methods, used in some of the experimental tests, was in many ways found to be superior to traditional measurement techniques, but was also found to be a valuable complement to the numerical analysis performed. From numerical results obtained in combination with results from contact-free measurements several observations of considerable interest were made. For dowel-type joints loaded in tension parallel to the grain a strongly non-uniform strain distribution was found in the joint area. It was further observed that the shear and tensile strains were concentrated close to the fasteners in the joint area. These concentrations will influence the failure mode of the joint. A general observation was that the larger sized joints failed in a brittle manner.</p><p>Keywords: constraint stresses, contact-free measurement, dowel-type joints, humidity variations, moisture-induced deformations, timber structures</p>

Joints are critical parts of timber structures, transmitting static and dynamic forces between structural members. The ultimate behavior of a loaded building depends strongly on the structural configuration and the capacity of the joints. The collapse of a whole building or less extensive accidents that may occur is usually starting as a local failure inside or in the vicinity of a joint. Such serious failures have recently occurred in our Nordic countries. Especially the collapse of two large glued laminated timber structures clearly indicates the need of an improved joint design. The trend toward larger and more complex structures even further increases the importance of a safer design of the joints. An aim of this partly experimental and partly numerically based thesis has been to investigate if steel-to-timber dowel joints are affected by moisture-induced stresses. The experimental results showed that the load-bearing capacity of the joints is reduced by such a moisture influence. Most of the decrease in load-bearing capacity observed was found in joints initially exposed to restrained shrinkage deformations caused by the presence of dowel fasteners in the joint area. The load-bearing capacity was, however, also found to decrease in joints exposed to an initial decrease in moisture without any fasteners present in the specimens during storage before loading. An explanation of this unexpected behavior is that moisture gradients cause tensile stresses. It is shown by numerical simulations that the moisture-induced stresses are so large that they may have a considerable influence on the joint behavior. Use of contact-free measurement methods, used in some of the experimental tests, was in many ways found to be superior to traditional measurement techniques, but was also found to be a valuable complement to the numerical analysis performed. From numerical results obtained in combination with results from contact-free measurements several observations of considerable interest were made. For dowel-type joints loaded in tension parallel to the grain a strongly non-uniform strain distribution was found in the joint area. It was further observed that the shear and tensile strains were concentrated close to the fasteners in the joint area. These concentrations will influence the failure mode of the joint. A general observation was that the larger sized joints failed in a brittle manner. Keywords: constraint stresses, contact-free measurement, dowel-type joints, humidity variations, moisture-induced deformations, timber structures

Joints are critical parts of timber structures, transmitting static and dynamic forces between structural members. The ultimate behavior of e.g. a building depends strongly on the structural configuration and the capacity of its joints. The complete collapse of a building or other less extensive accidents that may occur usually start as a local failure inside or in the vicinity of a joint. Such serious failures have recently occurred in the Nordic countries. Especially the collapses of two large glued-laminated timber (glulam) structures clearly indicate the need of an improved joint design. The trend toward larger and more complex structures even further increases the importance of a safer design of the joints. One aim of this partly experimentally and partly numerically based work has been to investigate if the short term capacity of steel-timber dowel joints loaded parallel to the grain is affected by an initial drying exposure. The experimental results showed that the load-bearing capacity of the joints is indeed reduced by such moisture changes. Moisture induced stresses was mentioned to be the explanation. The key point is that the climates chosen in the present work (20°C / 65% RH and 20°C / 20% RH) are equivalent to service class 1 according to EC5 (Eurocode 5 2004). Thus, EC5 predicts no decrease in load-bearing capacity, in relation to the standard climate used during testing. A decrease in load-bearing capacity in the range of 5-20%, which was found in the present work, is of course not negligible and, therefore, there could be a need to introduce the effect of drying in design codes. Because similar results were also observed for a double-tapered glulam beam, further work should consider timber structures in general. Two numerical methods in order to predict the capacity of multiple steel-timber dowel joints loaded parallel to the grain were tested in the thesis. For the first method, where fracture mechanics (LEFM) concepts were implemented, a good correlation with the experimental results was seen. Also for the second method, where the capacity for a single dowel-type joint as given in EC5 was used as a failure criterion, a good correlation to traditional EC5 calculations of multiple dowel-type joints was seen. One advantage of using numerical methods in design is that the capacity of the joint can be calculated also for cases when the dowels are placed in more complex patterns. From both a structural and an architectural point of view this can be very important. In addition, such numerical methods are effective tools for the structural engineer when considering complicated loading situations in joints, i.e. eccentric loading giving moments in the joint.

Cette thèse est consacrée à la simulation du comportement à la rupture de bois sous des chargements à long terme et sous des conditions d'Humidité Relatives (HR) de l'air variables. Il est connu que le bois est un matériau fortement hygroscopique, ses propriétés mécaniques et de rupture sont en effet très dépendantes de sa teneur en eau. En outre, la stabilité d'une fissure existante dans un élément structural peut être fortement influencée parles variations, en particulier brusques, d'humidité relative qui peut conduire à la rupture inattendue de l'élément.L'approche thermodynamique proposée intègre l'effet de mécanosorption dans l'expression analytique de la déformation, en découplant les déformations mécaniques et celles dues au comportement mécanosorptif du matériau. En outre, la rupture quasi-fragile du matériau boisest traduite par un modèle de zone cohésive dont les paramètres de cohésion sont fonctions de la teneur en eau afin de simuler l’effet de l'humidité sur les propriétés de rupture. Sur cette base, une formulation incrémentale permet l'intégration de l'effet des variations soudaines d’humidité relative (autrement dit, le choc hydrique) sur la zone d’élaboration(zone cohésive) en introduisant un champ de contraintes supplémentaires le long de cette zone. Fonction de la variation de HR, ce champ de contraintes supplémentaires dépend de l'état de contrainte et de l'ouverture de la fissure le long de la zone cohésive, mais également de l'humidité en pointe de fissure (matériau non endommagé). Dans l'analyse par éléments finis, un opérateur tangent algorithmique est utilisé pour résoudre le problème non linéaire en combinant le modèle de mécanosorption et le modèle de zone cohésive et en intégrant l'effet du choc hydrique.La simulation du comportement d'une éprouvette entaillée soumise à un chargement constant et à des variations cycliques de HR montre un fort couplage entre le comportement mécanosorptif et l'effet du choc hydrique HR sur la zone d’élaboration. Ce couplage entraîne une augmentation de la propagation des fissures et conduit à une fissuration plus précoce par rapport à celle obtenue à partir du modèle de mécanosorption seul ou à partir du modèle de zone cohésive en intégrant l'effet des variations soudaines de HR. En outre, le couplage entre le modèle mécanosorptif et le modèle de zone cohésive en intégrant l'effet du chochydrique montre l'intérêt d'une telle approche numérique pour décrire le comportement complexe des éléments de charpente en bois soumis à des conditions climatiques variables,comportement qui ne peut être prédit par une simple superposition des deux modélisations. / This thesis is dedicated to the simulation of the fracture behavior of wood under long-termloading and variable relative humidity conditions. Indeed, wood is well-known to be a highlyhygroscopic material in so far as its mechanical and fracture properties are very dependenton moisture. Moreover, the stability of an existent crack in a structural element can bestrongly affected by the sudden variations of relative humidity (RH) and can lead tounexpected failure of the element.The thermodynamic approach proposed in this thesis includes the mechano-sorptive effect inthe analytical expression of the deformation, by operating a decoupling of the strain in amechanical part and a mechano-sorptive part in material. Moreover, the quasi-brittle fractureof wood is here simulated from a cohesive zone model whose cohesive parameters arefunctions of the moisture in order to mimic the moisture-dependent character of the fractureproperties. On this basis, an increment formulation allows the integration of the effect ofsudden RH variations on the fracture process zone (cohesive zone) by introducing anadditional stress field along this zone. As a function of the RH variation, this additional stressfield depends on not only the stress state and the crack opening along the cohesive zone butalso the material moisture ahead of the zone (undamaged material). In the finite elementanalysis, an algorithmic tangent operator is used to solve the non-linear problem combiningmechano-sorptive model and cohesive zone model including the effect of sudden RHvariations.The simulation of a notched structural element submitted to a constant load and cyclic RHvariations exhibits a strong coupling between the mechano-sorptive behavior and the effectof the RH variations on the fracture process zone (FPZ). This coupling results in an increaseof the crack propagation kinetic and leads to a precocious failure compared to those obtainedfrom the mechano-sorptive model or from the effect of sudden RH variations on the FPZ.Moreover, the coupling between the mechano-sorptive model and the effect of sudden RHvariations on the FPZ which cannot be predicted by a simple superposition of both effects,showing the interest of such a numerical approach in order to describe the complex behaviorof wood structural elements submitted to variable climatic conditions.