BIOATIVIDADE DE VIDROS NO SISTEMA 2Na2O.1CaO.3SiO2-P2O5Dechandt, Iolanda Cristina Justus 06 March 2015 (has links)
Made available in DSpace on 2017-07-21T19:25:46Z (GMT). No. of bitstreams: 1
Iolanda Cristina Dechandt.pdf: 4265751 bytes, checksum: 63e41222d90f6a9011f71a3cac7991d8 (MD5)
Previous issue date: 2015-03-06 / Fundação Araucária de Apoio ao Desenvolvimento Científico e Tecnológico do Paraná / Progress in medicine has led to an increase in life expectancy of the world population. On the other hand, the properties of certain tissues and organs that compose the human body continues to follow the aging process. Faced with this challenge, biomaterial are developed with new technologies for bone substitutes. In this study we investigated the bioactivity of the glasses system 2Na2O.1CaO.3SiO2 with 0, 3 and 6% P2O5 in weight. The bioactivity was studied by immersion in simulated body fluid solution. Heat treatments were also performed in order to study the bioactivity of these glass-ceramics. Differential scanning calorimetry was performed to determine the glass transition temperatures for the glasses. Through Fourier transform infrared spectroscopy analysis was used to verify the bioactivity. The hardness and elastic modulus of the glasses were determined by the instrumented nanoindentation. X-ray diffraction confirmed the crystalline phases present in the glass ceramic samples. It was observed the formation of a hydroxycarbonate apatite layer after 21 days in samples of glass 2Na2O.1CaO.3SiO2 with 0, 3 and 6% P2O5 in weight. The best condition for the growth of hydroxycarbonate apatite layer in the glass-ceramics was the 2Na2O.1CaO.3SiO2 + 3% P2O5 that received heat treatment of 15 hours at 560° C. We observed the growth of the hydroxycabonate apatite layer after 7 days, and the glass-ceramic 2Na2O.1CaO.3SiO2+6% P2O5 who received heat treatment of 15 hours at 560° C the hydroxycabonate apatite layer was observed after 14 days in vitro novel. It was observed that cristalyzation is reduced with increase P concentration. At glass-ceramics with 6%wt of P2O5 the crystals are richer in Ca than in the stoichiometric glass matrix. In opposition, for 1Na2O2NaO3SiO2 glass-ceramics, the crystals are richer in Na.x / Os avanços na medicina vêm levando a um aumento na expectativa de vida da população mundial, por outro lado o desgaste de certas propriedades de tecidos e órgãos que compõe o corpo humano continua acompanhando o processo de envelhecimento. Frente a esse desafio os biomateriais são desenvolvidos com novas tecnologias para substituir ossos. Nesta pesquisa investigamos a bioatividade dos vidros no sistema 2Na2O.1CaO.3SiO2-P2O5 com 0, 3 e 6% em peso de P2O5. A bioatividade foi investigada pela imersão das amostras em solução de fluido corpóreo simulado. Realizados tratamentos térmicos a fim de verificar a bioatividade em vitrocerâmicas. Por meio da calorimetria exploratória diferencial determinamos os valores de temperatura de transição vítrea dos vidros. Através das análises de Infravermelho por transformada de Fourier pudemos verificar a bioatividade dos vidros. Analises de indentação instrumentada determinaram a dureza e o módulo de elasticidade dos vidros. A difração de raios X nos forneceu as fases cristalinas presentes nas amostras vitrocerâmicas. Foi verificado a formação de uma camada de hidroxicarbonato de apatita após 21 dias nas amostras de vidro 2Na2O.1CaO.3SiO2 com 0, 3 e 6% em peso de P2O5. A melhor condição para o crescimento da camada de hidroxicarbonato de apatita nos vitrocerâmicos foi 2Na2O.1CaO.3SiO2 + 3% P2O5 que recebeu tratamento térmico por 15 horas a 560°C. Nos observamos a camada de hidroxiapatita após 7 dias, e o vitrocerâmico 2Na2O.1CaO.3SiO2+6% P2O5 que recebeu tratamento por 15 horas a camada hidroxiapatita foi observada após 14 dias de ensaio in vitro. Foi observado que a cristalização é reduzida com o aumento da concentração de P. No vitrocerâmico com 6% em peso de P2O5 os cristais são mais ricos em Ca do que na matriz vítrea estequiométrica. Por outro lado, o vitrocerâmico com a fase 1Na2O2NaO3SiO2 os cristais são ricos em Na.
|
2 |
Bioatividade de vidros e vitrocerâmicas do sistema 2Na2O.1CaO.3SiO2 com adições de P2O5, K2O E SrORibeiro, Karen Cristiane 06 March 2018 (has links)
Submitted by Eunice Novais (enovais@uepg.br) on 2018-05-17T18:12:06Z
No. of bitstreams: 2
license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5)
Karen Cristiane Ribeiro.pdf: 2399556 bytes, checksum: 061ec872551f525fe1b25a9dbb51fcb7 (MD5) / Made available in DSpace on 2018-05-17T18:12:06Z (GMT). No. of bitstreams: 2
license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5)
Karen Cristiane Ribeiro.pdf: 2399556 bytes, checksum: 061ec872551f525fe1b25a9dbb51fcb7 (MD5)
Previous issue date: 2018-03-06 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O aumento na expectativa de vida tem levado a busca por materiais que possam melhorar a qualidade de vida. Dentre os materiais mais utilizados para tratamento de problemas no tecido ósseo, os vidros bioativos são os que possuem uma excelente resposta bioativa. A composição 2Na2O.1CaO.3SiO2 (2N1C3S) é um dos poucos sistemas de vidro que apresenta cristalização homogênea no volume e também a sua composição é próxima do vidro Bioglass® 45S5, um dos materiais mais bioativos existentes. Neste trabalho, estudamos a bioatividade do vidro 2N1C3S com adições de P2O5, K2O e SrO através da investigação do tempo para a formação da hidroxicarbonato apatita (HCA) por imersão em fluido corporal simulado (SBF). Foram realizados tratamentos térmicos para avaliação da bioatividade das vitrocerâmicas derivadas desse sistema. As temperaturas de tratamento térmico foram obtidas através da calorimetria exploratória diferencial, em que foram determinadas as temperaturas de transição vítrea e onset de cristalização. A presença de HCA foi investigada por espectroscopia de absorção no infravermelho por transformada de Fourier em função do tempo de imersão. Foi determinada por difração de raios X as fases cristalinas presentes nas amostras vitrocerâmicas. A formação de uma camada de hidroxicarbonato apatita foi observada após 21 dias nas amostras de vidro 2Na2O.1CaO.3SiO2 com 12% em peso de P2O5. As vitrocerâmicas com o menor tempo para o crescimento da camada de hidroxicarbonato apatita em solução SBF foram 2Na2O.1CaO.3SiO2+6% em peso de P2O5 e 10% em peso de SrO que recebeu tratamento térmico a 620°C/16h. Nós observamos a camada de HCA após 15 dias na vitrocerâmica 2Na2O.1CaO.3SiO2+6% em peso de P2O5 e 10% em peso de K2O que recebeu tratamento a 550°C/8h, a camada HCA foi observada após 15 dias e 21 dias para a que recebeu tratamento térmico a 550°C/16h. / The increase in life expectancy has led to the search for materials that can improve the quality of life. Among the materials that are most used to treat problems in bone tissue, bioactive glasses are those that have the greatest bioactive response. The 2Na2O.CaO.3SiO2 (2N1C3S) composition is one of the few glass systems which exhibits homogeneous crystallization in the volume and also its composition is very close to Bioglass® 45S5 glass, one of the most bioactive materials. In this work, we studied the bioactivity of 2N1C3S glass with additions of P2O5, K2O and SrO by investigating the time to formation of the hydroxycarbonate apatite (HCA) by immersion in simulated body fluid (SBF). Thermal treatments were carried out to evaluate the bioactivity of the glass-ceramics. The heat treatment temperatures were obtained by differential scanning calorimetry, in which the glass transition and crystallization onset temperatures were determined. The presence of HCA was investigated by Fourier transform infrared spectroscopy as a function of immersion time in SBH solution. X-ray diffraction were used for the identification of the crystalline phases present in the glass-ceramics. The glass-ceramics with the lowest time for growth of the hydroxycarbonate apatite layer in SBF solution were 2Na2O.CaO.3SiO2+6% in weight of P2O5 and 10% in weight of SrO heat treated for 620°C/16h and 2Na2O.1CaO.3SiO2+6% in weight of P2O5 and 10% in weight of K2O heat treated at 550°C/8h. The HCS layer was observed after 15 days of immersion for both glass-ceramics.
|
Page generated in 0.0578 seconds