Thesis (Ph. D.)--Missouri University of Science and Technology, 2009. / Vita. The entire thesis text is included in file. Title from title screen of thesis/dissertation PDF file (viewed August 10, 2009) Includes bibliographical references.

Thesis (Ph. D.)--University of Rhode Island, 2006. / Typescript. Includes bibliographical references (leaves 126-134).

Thesis (M.S.)--Ohio University, November, 2004. / Title from PDF t.p. Includes bibliographical references (leaves 74-83).

No description available.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Bactérias redutoras de sulfato (BRS) possuem um papel importante na corrosão de ligas metálicas expostas em hábitats marinhos, óleos e solos úmidos. A redução do sulfato por estas bactérias resulta na produção de H2S, podendo influenciar os processos anódico e catódico na corrosão de materiais. Neste trabalho, o comportamento da corrosão microbiológica no aço carbono AISI 1020 foi avaliada em meio Postgate C, na presença e na ausência de BRS, as quais foram isoladas da camada de ferrugem presente numa tubulação submersa da Baía de Guanabara RJ. A taxa de corrosão e o comportamento eletroquímico do aço nas duas condições foram investigados através dos métodos de perda de massa e de polarização potenciodinâmica. A formação do biofilme e dos produtos de corrosão na superfície do aço foram observados por microscopia eletrônica de varredura (MEV) e por espectroscopia de energia dispersiva (EDS). Em complementação, foi realizada a quantificação das BRS (planctônicas e sésseis) pelo método do número mais provável (NMP). A presença de BRS no meio ocasionou o deslocamento do potencial de corrosão para valores mais negativos em todos os tempos de ensaio estudados, indicando um aumento no processo corrosivo. Nos ensaios de perda de massa, a taxa de corrosão do aço carbono foi maior na ausência de BRS, provavelmente devido à formação de um biofilme na superfície do metal nos ensaios com inóculo, e a uma menor tendência de haver corrosão generalizada neste tipo de meio. As micrografias de MEV revelaram a presença de agregado celular na superfície do aço carbono durante o experimento, e a presença de pites profundos após remoção do biofilme, mostrando prevalência deste tipo de corrosão. Com 35 dias de ensaio, a densidade de corrente de corrosão aumentou na presença de BRS / Sulfate-reducing bacteria (SRB) play an important role in the corrosion of alloys exposed in marine habitats, wet soils and oils. The sulfate reduction by these bacteria results in production of H2S, which may influence processes in the anodic and cathodic corrosion of materials. In this work, the behavior of microbial corrosion in carbon steel AISI 1020 was evaluated in Postgate C medium, in the presence and absence of SRB, which were isolated from a layer of rust on a pipeline submerged in Guanabara Bay - Rio de Janeiro. The corrosion rate and the electrochemical behavior of steel in the two conditions were investigated by weight loss and potentiodynamic polarization methods. Biofilm formation and corrosion products on the steel surface were observed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). In addition, the quantification of BRS (planktonic and sessile) was carried out by the most probable number method (MPN). The presence of SRB in the medium caused the shift of corrosion potential to more negative values in all experimental times studied, indicating an increase in corrosion. In the weight loss tests, the corrosion rate was higher in the absence of BRS, probably due to the formation of a biofilm on the metal surface in the tests with inoculum, and to a smaller trend of general corrosion with this kind of medium. SEM micrographies revealed the presence of cellular aggregates on the surface of mild steel during the experiment and the presence of deep pittings after the biofilm removal, showing that this kind of corrosion was prevalent . With 35 days of asseys, the corrosion current density increased in the presence of BRS

Microbiologically Influenced Corrosion (MIC) is a process influenced by microbial presence and their metabolic activities. This study examined the microbial effects on metal corrosion under different environmental conditions with nutrient supplements. Experiments were conducted by inserting stainless steel 304 and mild steel coupons (2.5 x 2.5 cm²) into loam soil and a simulated seawater/sediment system with various nutrient conditions (sterilized, without supplement, 5 mM NaNO₃ or NH₄NO₃). Two mild and stainless steel coupons were removed monthly and the corrosion rate was evaluated based on the weight loss. Bacterial populations were enumerated using the most probable number (MPN) technique. The presence and adhesion of microbes on mild steel coupons were examined using Scanning Electron Microscopy (SEM). The extent of the corrosion process on the surface of the metal coupons were visualized by using the Stereo Microscope. The elemental composition of the corrosion products formed on the coupon surface were determined by Energy Dispersive X-Ray analyses. Isolation and identification of aerobic microorganisms were conducted and examined for its potential in either accelerating or inhibiting corrosion. The bacterial populations present on the mild steel surface were analyzed by fluorescent in situ hybridization. Denaturing gradient gel electrophoresis (DGGE) analyses of PCR-amplified 16S rDNA fragments were conducted to determine the microbial community complexity of the biofilm. Greater weight losses of mild steel in loam soil and the seawater/sediment system with NaNO₃ (48.86 mg/g and 19.96 mg/g of weight loss, respectively after 20 weeks) were observed with total heterotrophic bacterial population presented (106.695 MPN/ml and 0.11187 MPN/ml respectively) compared to the autoclaved control (7.17845 mg/g and 0.12082 mg/g of weight loss respectively). Supplementation of 5 mM NH₄NO₃ increased the total heterotrophic bacterial population and resulted in a decrease in weight loss measurements on the stainless steel coupons (211.4 MPN/ml with a 0.01 mg/g weight loss) after 20 weeks compared to the non-autoclaved loam soil and loam soil supplemented with NaNO₃ (139.2 MPN/ml and 134.9 MPN/ml respectively with no weight loss). SEM images of the mild steel coupons confirmed the presence and adherence of bacteria on the metal surface. Stereo microscopic images displayed reddish-brown deposits and pitting on the coupon surface. Isolation, identification and sequence analysis revealed that most microorganisms were the Bacillus species. This group of microorganisms are iron-oxidizing bacteria that could also promote the corrosion process. After 20 weeks of incubation, the total SRB cell counts were lower in samples supplemented with NaNO₃ in both loam soil and the seawater/sediment system. This study also indicated that the isolated aerobic microorganisms do play a role in the corrosion process in both stainless and mild steel. DGGE analysis revealed microbial diversity in the corrosion products especially those affiliated to the bacterial phyla Firmicutes and Gamma-Proteobacteria. Fluorescent in situ hybridization analysis allowed for an overall estimation of Eubacteria and sulphate-reducing bacteria present in the biofilm formed on the surface of mild steel. The current study indicates that the addition of nitrates did not significantly reduce the rates of corrosion of both mild and stainless steel. However, it does seem that environmental conditions did pose as an important factor in the corrosion process. Therefore, further studies need to be implemented to analyze the environmental type, microbial composition and optimization of the concentration of nitrates for possible mitigation of metal corrosion. To optimize MIC prevention and control, collaboration between engineers and microbiologists proves advantageous to develop an environmentally sound and potentially cost-effective approach to control corrosion. / Thesis (Ph.D.)-University of KwaZulu-Natal, Westville, 2012.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Bactérias redutoras de sulfato (BRS) possuem um papel importante na corrosão de ligas metálicas expostas em hábitats marinhos, óleos e solos úmidos. A redução do sulfato por estas bactérias resulta na produção de H2S, podendo influenciar os processos anódico e catódico na corrosão de materiais. Neste trabalho, o comportamento da corrosão microbiológica no aço carbono AISI 1020 foi avaliada em meio Postgate C, na presença e na ausência de BRS, as quais foram isoladas da camada de ferrugem presente numa tubulação submersa da Baía de Guanabara RJ. A taxa de corrosão e o comportamento eletroquímico do aço nas duas condições foram investigados através dos métodos de perda de massa e de polarização potenciodinâmica. A formação do biofilme e dos produtos de corrosão na superfície do aço foram observados por microscopia eletrônica de varredura (MEV) e por espectroscopia de energia dispersiva (EDS). Em complementação, foi realizada a quantificação das BRS (planctônicas e sésseis) pelo método do número mais provável (NMP). A presença de BRS no meio ocasionou o deslocamento do potencial de corrosão para valores mais negativos em todos os tempos de ensaio estudados, indicando um aumento no processo corrosivo. Nos ensaios de perda de massa, a taxa de corrosão do aço carbono foi maior na ausência de BRS, provavelmente devido à formação de um biofilme na superfície do metal nos ensaios com inóculo, e a uma menor tendência de haver corrosão generalizada neste tipo de meio. As micrografias de MEV revelaram a presença de agregado celular na superfície do aço carbono durante o experimento, e a presença de pites profundos após remoção do biofilme, mostrando prevalência deste tipo de corrosão. Com 35 dias de ensaio, a densidade de corrente de corrosão aumentou na presença de BRS / Sulfate-reducing bacteria (SRB) play an important role in the corrosion of alloys exposed in marine habitats, wet soils and oils. The sulfate reduction by these bacteria results in production of H2S, which may influence processes in the anodic and cathodic corrosion of materials. In this work, the behavior of microbial corrosion in carbon steel AISI 1020 was evaluated in Postgate C medium, in the presence and absence of SRB, which were isolated from a layer of rust on a pipeline submerged in Guanabara Bay - Rio de Janeiro. The corrosion rate and the electrochemical behavior of steel in the two conditions were investigated by weight loss and potentiodynamic polarization methods. Biofilm formation and corrosion products on the steel surface were observed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). In addition, the quantification of BRS (planktonic and sessile) was carried out by the most probable number method (MPN). The presence of SRB in the medium caused the shift of corrosion potential to more negative values in all experimental times studied, indicating an increase in corrosion. In the weight loss tests, the corrosion rate was higher in the absence of BRS, probably due to the formation of a biofilm on the metal surface in the tests with inoculum, and to a smaller trend of general corrosion with this kind of medium. SEM micrographies revealed the presence of cellular aggregates on the surface of mild steel during the experiment and the presence of deep pittings after the biofilm removal, showing that this kind of corrosion was prevalent . With 35 days of asseys, the corrosion current density increased in the presence of BRS

Microbial-influenced corrosion (MIC) has been widely recognized as a significant economic and environmental problem in the oil and gas industry. MIC can be classified into two types based on the mechanisms: the extracellular electron transfer MIC (EET-MIC) and the metabolite MIC (M-MIC). The first includes electroactive bacteria that facilitate EET, while the latter includes bacteria that secrete corrosive metabolites. Sulfate-reducing bacteria (SRB) is believed to cause EET-MIC in carbon steel, a widely used metal in the oil and gas industry. In previous electroactive bacteria studies, nanowires have been shown to facilitate EET by acting as electron mediators. This study investigates the use of magnetite nanowires as electron mediators to accelerate EET-MIC of C1020 by Desulfovibrio vulgaris. The addition of 40 ppm (w/w) nanowires to carbon steel incubated with D. vulgaris, corrosive SRB species, for seven days resulted in 45% weight loss and 57% deeper pitting of carbon steel. Furthermore, electrochemical measurements of open circuit potential, linear polarization resistance and potentiodynamic polarization were found to be parallel with weight loss and pitting results. Therefore, these findings highlight the possibility of using magnetic nanowires as an electron mediator with high efficiency and selectivity to EET-MIC for future MIC studies and applications.

No description available.

No description available.