• Refine Query
  • Source
  • Publication year
  • to
  • Language
  • 4
  • Tagged with
  • 4
  • 4
  • 4
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • 2
  • About
  • The Global ETD Search service is a free service for researchers to find electronic theses and dissertations. This service is provided by the Networked Digital Library of Theses and Dissertations.
    Our metadata is collected from universities around the world. If you manage a university/consortium/country archive and want to be added, details can be found on the NDLTD website.
1

Field plot conditions for the expression and selection of straw fibre concentration in oilseed flax

Burton, Alison Dana 30 August 2007
In Canada, flax (<i>Linum usitatissimum</i> L.) is grown for its seed oil. However, a major disadvantage associated with growing oilseed flax is that the straw is difficult to incorporate into the soil after harvest. Instead, the majority of flax straw is burned in the field, increasing the workload for farmers, as well as creating air pollution. Agronomic concerns are also associated with burning, since it leaves fields vulnerable to wind and water erosion. A small market exists for Canadian flax straw for making high quality paper products and some plastic composites. However, fibre-based and fibre-using industries are growing world wide, and flax straw fibre is becoming an important product. Flax straw fibre concentration varies among cultivars and environments. Consistently high fibre concentrations are essential if the fibre in oilseed flax is to become an important product for Canadian farmers. This study assembled the agronomic information necessary to select for increased straw fibre concentration in the Crop Development Centre (CDC) Flax Breeding Program. Three experiments were conducted to determine: how seeding rate and row spacing effects straw fibre concentration, the effects of seeding date on straw fibre concentration, and how nitrogen fertilizer rates effects straw fibre concentration. Seeding in mid-May at either an 18 or 36 cm row spacing at a seeding rate of 30 or 45 kg/ha resulted in high straw fibre concentration without reducing other important oilseed characteristics such as seed yield, oil content and straw fibre yield. Nitrogen fertilizer did not have an effect on either straw fibre concentration or straw fibre yield.
2

Field plot conditions for the expression and selection of straw fibre concentration in oilseed flax

Burton, Alison Dana 30 August 2007 (has links)
In Canada, flax (<i>Linum usitatissimum</i> L.) is grown for its seed oil. However, a major disadvantage associated with growing oilseed flax is that the straw is difficult to incorporate into the soil after harvest. Instead, the majority of flax straw is burned in the field, increasing the workload for farmers, as well as creating air pollution. Agronomic concerns are also associated with burning, since it leaves fields vulnerable to wind and water erosion. A small market exists for Canadian flax straw for making high quality paper products and some plastic composites. However, fibre-based and fibre-using industries are growing world wide, and flax straw fibre is becoming an important product. Flax straw fibre concentration varies among cultivars and environments. Consistently high fibre concentrations are essential if the fibre in oilseed flax is to become an important product for Canadian farmers. This study assembled the agronomic information necessary to select for increased straw fibre concentration in the Crop Development Centre (CDC) Flax Breeding Program. Three experiments were conducted to determine: how seeding rate and row spacing effects straw fibre concentration, the effects of seeding date on straw fibre concentration, and how nitrogen fertilizer rates effects straw fibre concentration. Seeding in mid-May at either an 18 or 36 cm row spacing at a seeding rate of 30 or 45 kg/ha resulted in high straw fibre concentration without reducing other important oilseed characteristics such as seed yield, oil content and straw fibre yield. Nitrogen fertilizer did not have an effect on either straw fibre concentration or straw fibre yield.
3

Characterization of flax fibres and the effect of different drying methods for making biocomposites

Tripathy, Ananda Chandra 20 April 2009
As the environmental concern grows, researchers try to find material which can be environmental friendly and biodegradable to some extent. At present, flax fibre cannot fully replace glass fibre. Some attempts have been made to replace the glass fibre.<p> Studies show the physical and mechanical properties of natural fibres are comparable with glass fibre, so it can replace glass fibre in the process of making biocomposites. <p> The properties of biocomposites depend on the fibre used. Research shows that to get a better biocomposite, the fibre has to be chemically treated to improve adhesion between fibre and polymer matrix. After the chemical treatment, the fibre has to be dried to minimum moisture content so the drying of flax fibre is essential in the process of making biocomposites. <p> In this research, oilseed flax fibre is dried and drying characteristics were investigated. After drying, the physical properties of the fibre were tested and analysed.<p> The fibre was dried using three different drying methods, namely, microwave, microwave-convection, and microwave-vacuum environments. Curve fitting with four empirical methods has been carried out to determine the drying constant, coefficient of determination and standard error values. The results showed that microwave-vacuum drying method is more efficient (in terms of final moisture content) than microwave and microwave-convection drying. Although microwave-vacuum drying took the most time and did not result in promising colour values, the maximum moisture removal is achieved because fibres can be dried for a longer period of time with a comparatively low temperature.<p> The results of physical properties were analysed for untreated and treated and dried flax fibre. The tensile strength and elastic modulus of untreated and treated fibre did not show any significant change. Because the diameter of flax fibre cannot be consistent, a range of values can be obtained. The diameter range of fibre bundle 30-300 µm was examined for these tests. The tensile strength obtained from these fibre bundles ranged between 16 to 667 MPa and elastic modulus values were 2 GPa up to 63 GPa.<p> The scanning electron micrograph (SEM) was also analysed for untreated and treated-dried fibre. The fibre which was dried with high power or longer period of time showed black spots, probably due to local heating. The fibre dried with microwave-vacuum developed some black spots which were clearly seen in the SEM.<p> Differential scanning calorimetric data showed a shift in temperature of degradation. In this research, degradation temperature of cellulose was found 350(+/-10)°C for the treated and dried flax fibre.<p> In conclusion, the flax fibre has a potential to be used in biocomposite production. The microwave-vacuum works best for drying where the fibre can be dried up to a less than 1% of moisture content.
4

Characterization of flax fibres and the effect of different drying methods for making biocomposites

Tripathy, Ananda Chandra 20 April 2009 (has links)
As the environmental concern grows, researchers try to find material which can be environmental friendly and biodegradable to some extent. At present, flax fibre cannot fully replace glass fibre. Some attempts have been made to replace the glass fibre.<p> Studies show the physical and mechanical properties of natural fibres are comparable with glass fibre, so it can replace glass fibre in the process of making biocomposites. <p> The properties of biocomposites depend on the fibre used. Research shows that to get a better biocomposite, the fibre has to be chemically treated to improve adhesion between fibre and polymer matrix. After the chemical treatment, the fibre has to be dried to minimum moisture content so the drying of flax fibre is essential in the process of making biocomposites. <p> In this research, oilseed flax fibre is dried and drying characteristics were investigated. After drying, the physical properties of the fibre were tested and analysed.<p> The fibre was dried using three different drying methods, namely, microwave, microwave-convection, and microwave-vacuum environments. Curve fitting with four empirical methods has been carried out to determine the drying constant, coefficient of determination and standard error values. The results showed that microwave-vacuum drying method is more efficient (in terms of final moisture content) than microwave and microwave-convection drying. Although microwave-vacuum drying took the most time and did not result in promising colour values, the maximum moisture removal is achieved because fibres can be dried for a longer period of time with a comparatively low temperature.<p> The results of physical properties were analysed for untreated and treated and dried flax fibre. The tensile strength and elastic modulus of untreated and treated fibre did not show any significant change. Because the diameter of flax fibre cannot be consistent, a range of values can be obtained. The diameter range of fibre bundle 30-300 µm was examined for these tests. The tensile strength obtained from these fibre bundles ranged between 16 to 667 MPa and elastic modulus values were 2 GPa up to 63 GPa.<p> The scanning electron micrograph (SEM) was also analysed for untreated and treated-dried fibre. The fibre which was dried with high power or longer period of time showed black spots, probably due to local heating. The fibre dried with microwave-vacuum developed some black spots which were clearly seen in the SEM.<p> Differential scanning calorimetric data showed a shift in temperature of degradation. In this research, degradation temperature of cellulose was found 350(+/-10)°C for the treated and dried flax fibre.<p> In conclusion, the flax fibre has a potential to be used in biocomposite production. The microwave-vacuum works best for drying where the fibre can be dried up to a less than 1% of moisture content.