Untersuchungen zur Hochrateabscheidung harter DLC-Schichten

Graupner, Karola 11 January 2005 (has links) (PDF)
Amorphous, hydrogenated carbon films (a-C:H) have been prepared in a PECVD device from methane and ethine as the source gases.The aim was to deposit films at high growth rates while keeping high hardness (25 ± 3 GPa). Hardness, hydrogen content and surface roughness were investigated dependent on the process conditions. Further investigation showed, that the mechanical properties of the a-C:H films are determined by the energy of the ions and the ratio between the film forming ion and the film forming neutral fluxes. On the basis of the collected data the optimal deposition conditions were determined and suggestions for further improvement of the deposition were made. / Amorphe, wasserstoffhaltige Kohlenstoffschichten (a-C:H) wurden mittels PECVD-Verfahren abgeschieden, wobei Methan und Ethin als Quellgase verwendet wurde. Ziel war dabei die Abscheidung der Schichten mit hohen Aufwachsraten unter Beibehaltung hoher Härten (25 ± 3 GPa). Härte, Wasserstoffgehalt und Oberflächenrauhigkeit der Schichten wurden in Abhängigkeit von den Prozeßbedingungen untersucht. Weitere Untersuchungen zeigten, daß die mechanischen Eigenschaften der a-C:H Schichten von der Energie der Ionen und dem Verhältnis der schichtbildenden Ionen- und Neutralteilchenflüsse bestimmt werden. Auf der Grundlage der gewonnenen Daten können die optimalen Abscheidebedingungen festgelegt, und Vorschläge zur weiteren Verbesserung der Schichtabscheidung gemacht werden.
2

Untersuchungen zur Hochrateabscheidung harter DLC-Schichten

Graupner, Karola 04 January 2005 (has links)
Amorphous, hydrogenated carbon films (a-C:H) have been prepared in a PECVD device from methane and ethine as the source gases.The aim was to deposit films at high growth rates while keeping high hardness (25 ± 3 GPa). Hardness, hydrogen content and surface roughness were investigated dependent on the process conditions. Further investigation showed, that the mechanical properties of the a-C:H films are determined by the energy of the ions and the ratio between the film forming ion and the film forming neutral fluxes. On the basis of the collected data the optimal deposition conditions were determined and suggestions for further improvement of the deposition were made. / Amorphe, wasserstoffhaltige Kohlenstoffschichten (a-C:H) wurden mittels PECVD-Verfahren abgeschieden, wobei Methan und Ethin als Quellgase verwendet wurde. Ziel war dabei die Abscheidung der Schichten mit hohen Aufwachsraten unter Beibehaltung hoher Härten (25 ± 3 GPa). Härte, Wasserstoffgehalt und Oberflächenrauhigkeit der Schichten wurden in Abhängigkeit von den Prozeßbedingungen untersucht. Weitere Untersuchungen zeigten, daß die mechanischen Eigenschaften der a-C:H Schichten von der Energie der Ionen und dem Verhältnis der schichtbildenden Ionen- und Neutralteilchenflüsse bestimmt werden. Auf der Grundlage der gewonnenen Daten können die optimalen Abscheidebedingungen festgelegt, und Vorschläge zur weiteren Verbesserung der Schichtabscheidung gemacht werden.