Purpose: To compare the in-vitro shear bond strengths of a new paste-paste formulation of resin-modified glass-ionomer cement (Rm-GIC) to an exising powder-liquid formulation. The study will test the hypothesis that the new paste-paste formulation of Rm-GIC (Fuji-Cem ™, GC Corp, Tokyo, Japan) has the same bond strength as an existing popular powder-liquid formulation of Rm-GIC (Rely-X ™ Luting Cement, 3M, St. Paul, MN)Materials and Methods: A total of 33 human molars were sectioned parallel to the occlusal surface to expose mid-coronal dentin and mounted parallel to the bond shearing device on the universal testing machine (Instron). For Group I samples (Rely-X, n=15), the powder and liquid were measured and adjusted to achieve a ratio of 1.6 and mixed for 30 seconds as recommended by the manufacturer. For Group II (Fuji-Cem, n=18), the paste-paste was expressed from the paste-dispenser provided by the manufacturer and mixed for 10 seconds as recommended. After testing, the teeth from group II were bonded on a different site with the same material but mixed for 20 seconds (n=18). To ensure a uniform flow and bond surface area, the mixed cement was syringed into a cylindrical mould (diameter 2.38mm, height 2mm) and allowed to set under constant force. All samples were subjected to fracture by shear loading on a universal testing machine (Instron) at a uniform crosshead speed of .02" per minute and expressed as MPa. Values were analyzed at the pResults: Wilcoxon rank sums test showed significantly higher shear bond strength values for Rely-X compared to Fuji-Cem mixed both at 10 seconds and 20 seconds. Mixing for 20 seconds resulted in stronger bonds for Fuji-Cem compared to 10 seconds, but was still significantly lower than Rely-X.Conclusions: Within the limitations of the study, the Rely-X powder-liquid formula shows a significantly stronger dentin shear bond strength when compared to the new paste-paste formula of resin-modified glass ionomer cement, Fuji-Cem.

Os ionômeros de vidro vêm sendo utilizados largamente na odontologia com diversas funções. Suas formulações sofreram alterações durante os anos, como a incorporação de componentes resinosos, para a melhoria de suas propriedades físicas e aumento do tempo de trabalho. Com isso, o estudo teve como objetivo avaliar o grau de conversão e a microdureza Knoop dos cimentos de ionômero de vidro modificados por resina (Rely X Luting e Vitremer, ambos da 3M ESPE) de acordo a forma de polimerização (química ou fotopolimerável por lâmpada halógena Ultralux EL ? Gnatus e LED LEC 1000 ? MMOptics) e o tempo de armazenagem. Três espécimes de cada material, autopolimerizável e fotopolimerizável, e tipo de fotopolimerização (por luz halógena e LED) foram confeccionados para cada tempo experimental de 6 horas, 1, 2, 3, 5, 7 ,11 e 14 dias (n=72). Os espécimes foram armazenados em ambiente escuro a 37°C durante esses períodos. Os 72 espécimes foram analisados pela espectroscopia FT-IR para a medição do grau de conversão (GC). Três espécimes de cada material e tipo de polimerização (n=9) foram confeccionados para a medição da microdureza, com um penetrador diamantado piramidal, tipo Knoop, carga estática de 50 gramas por 30 segundos. Os resultados encontrados demonstraram que o material fotopolimerizado com LED apresentou os maiores valores do grau de conversão e da microdureza. O grau de conversão aumentou com o tempo de armazenagem enquanto a microdureza obteve os maiores resultados entre 24-48 horas. Os resultados permitiram concluir que para os cimentos de ionômero de vidro modificados por resina, Vitremer e Rely X Luting, o material fotopolimerizável onde se utilizou o LED apresentou os melhores resultados e que a microdureza Knoop foi ineficaz para predizer o grau de conversão. / Glass ionomer cement have been widely used for many functions. Over the years, some alterations have been made to improve some physico-mechanical properties and to prolong working time. The purpose of this study was to evaluate the relation of the degree of conversion (DC) and Knoop microhardness of resin modified glass ionomer cements (Rely X Luting and Vitremer - 3M ESPE) with polymerization type (chemical curing and light curing reactions, using halogen light or LED) and time of storage. Three specimens of each material, self-cured and light-cured, and light-curing type (halogen light or LED) were prepared for each period of time (n=72). Specimens were stored in dark and dry conditions, at 37oC, during 6 hours, 1, 2, 3, 5, 7, 11 and 14 days. All the specimens were analyzed by FT-IR spectroscopy to measure the DC. Three specimens of each material and polimeryzation type (n=9) were prepared for the microhardness determination, equipped with a Knoop indenter, 50g load for 30 seconds. Results showed that higher values of DC and Knoop microhardness were found on the LED light-cured material. DC values increased with storage time while the Knoop microhardness achieved its higher values between 24-48 hours. Results showed that the LED light-curing unit used to polymerize the resin modified glass ionomer cement Vitremer achieved better values of DC, between light and self-cured materials, and that the Knoop microhardness could not predict the DC.

Os ionômeros de vidro vêm sendo utilizados largamente na odontologia com diversas funções. Suas formulações sofreram alterações durante os anos, como a incorporação de componentes resinosos, para a melhoria de suas propriedades físicas e aumento do tempo de trabalho. Com isso, o estudo teve como objetivo avaliar o grau de conversão e a microdureza Knoop dos cimentos de ionômero de vidro modificados por resina (Rely X Luting e Vitremer, ambos da 3M ESPE) de acordo a forma de polimerização (química ou fotopolimerável por lâmpada halógena Ultralux EL ? Gnatus e LED LEC 1000 ? MMOptics) e o tempo de armazenagem. Três espécimes de cada material, autopolimerizável e fotopolimerizável, e tipo de fotopolimerização (por luz halógena e LED) foram confeccionados para cada tempo experimental de 6 horas, 1, 2, 3, 5, 7 ,11 e 14 dias (n=72). Os espécimes foram armazenados em ambiente escuro a 37°C durante esses períodos. Os 72 espécimes foram analisados pela espectroscopia FT-IR para a medição do grau de conversão (GC). Três espécimes de cada material e tipo de polimerização (n=9) foram confeccionados para a medição da microdureza, com um penetrador diamantado piramidal, tipo Knoop, carga estática de 50 gramas por 30 segundos. Os resultados encontrados demonstraram que o material fotopolimerizado com LED apresentou os maiores valores do grau de conversão e da microdureza. O grau de conversão aumentou com o tempo de armazenagem enquanto a microdureza obteve os maiores resultados entre 24-48 horas. Os resultados permitiram concluir que para os cimentos de ionômero de vidro modificados por resina, Vitremer e Rely X Luting, o material fotopolimerizável onde se utilizou o LED apresentou os melhores resultados e que a microdureza Knoop foi ineficaz para predizer o grau de conversão. / Glass ionomer cement have been widely used for many functions. Over the years, some alterations have been made to improve some physico-mechanical properties and to prolong working time. The purpose of this study was to evaluate the relation of the degree of conversion (DC) and Knoop microhardness of resin modified glass ionomer cements (Rely X Luting and Vitremer - 3M ESPE) with polymerization type (chemical curing and light curing reactions, using halogen light or LED) and time of storage. Three specimens of each material, self-cured and light-cured, and light-curing type (halogen light or LED) were prepared for each period of time (n=72). Specimens were stored in dark and dry conditions, at 37oC, during 6 hours, 1, 2, 3, 5, 7, 11 and 14 days. All the specimens were analyzed by FT-IR spectroscopy to measure the DC. Three specimens of each material and polimeryzation type (n=9) were prepared for the microhardness determination, equipped with a Knoop indenter, 50g load for 30 seconds. Results showed that higher values of DC and Knoop microhardness were found on the LED light-cured material. DC values increased with storage time while the Knoop microhardness achieved its higher values between 24-48 hours. Results showed that the LED light-curing unit used to polymerize the resin modified glass ionomer cement Vitremer achieved better values of DC, between light and self-cured materials, and that the Knoop microhardness could not predict the DC.