Made available in DSpace on 2016-06-02T19:10:02Z (GMT). No. of bitstreams: 1 2812.pdf: 9864316 bytes, checksum: 6d509e89f2d84a8ed7d917440c6d2905 (MD5) Previous issue date: 2009-12-15 / Universidade Federal de Sao Carlos / Porcelain tile is a type of ceramic tile which has shown the highest worldwide expansion in recent years due to the excellent technical and esthetic qualities of the product, which have augmented the possibilities of its use in a wide variety of applications. Among the various types of porcelain tiles today, polished porcelain tile stands out because consumers greatly appreciate the esthetic effect of its characteristically high gloss. However, polishing exposes part of the material s closed pores and facilitates the impregnation of dirt when the product is in use, which may compromise one of its most important properties, i.e., stain resistance. Staining of polished porcelain tile does not depend only on the occurrence of closed pores on the surface of the product but also on other characteristics such as the size and morphology of the pores. This research work aimed to investigate the characteristics of the pores that most contribute to staining and to ascertain how processing variables act in the formation of the material s porous microstructure. The methodology employed to deal with the theme differs from that of other works reported in the literature, since it is based on the characterization of porosity throughout all the stages of processing (green compact to end product) and on a systematic study of several process variables responsible for pore formation (granulometric distribution and particle size distribution). The main experimental techniques used in the development of this study were scanning electron microscopy, digital optical microscopy, image analysis (software), mercury porosimetry, diffuse reflectance spectrophotometry, X-ray sedimentometry, helium gas pycnometry, and mechanical profilometry. In addition to achieving the initial objectives, the results indicated several viable alternatives for reducing the staining tendency of polished porcelain tile. / O porcelanato é a tipologia de revestimento cerâmico que apresentou maior expansão mundial nos últimos anos. O destaque alcançado deve-se às excelentes qualidades técnicas e estéticas do produto que ampliaram as possibilidades de uso nos mais variados ambientes. Dentre os tipos de porcelanatos produzidos o polido se destaca por oferecer o efeito estético mais apreciado pelos consumidores por causa do elevado brilho característico. Por sua vez, o polimento revela parte dos poros fechados do material e facilita a impregnação de sujeira durante o uso do produto, o que pode comprometer uma de suas propriedades mais importantes: a resistência ao manchamento. O manchamento do porcelanato polido não depende somente da ocorrência de poros fechados na superfície do produto, mas também de outras características como o tamanho e a morfologia. Este trabalho de pesquisa teve como objetivo conhecer as características dos poros que mais contribuem para o manchamento e avaliar como as variáveis de processo atuam na formação da microestrutura porosa do material. A metodologia utilizada para tratar do tema é distinta dos demais trabalhos encontrados na literatura, sendo fundamentada na caracterização da porosidade ao longo das etapas de processamento (compacto verde a produto acabado) e no estudo sistemático de algumas variáveis de processo responsáveis pela formação dos poros (distribuição granulométrica e distribuição do tamanho de partículas). As principais técnicas experimentais empregadas no desenvolvimento do estudo foram: microscopia eletrônica de varredura, microscopia ótica digital, análise de imagens (software), porosimetria de mercúrio, espectrofotometria de reflectância difusa, sedimentometria de raios X, picnometria de gás hélio e perfilometria de contato mecânico. Os resultados obtidos além de atenderem aos objetivos iniciais indicaram algumas alternativas viáveis para reduzir a tendência ao manchamento do porcelanato polido.

Made available in DSpace on 2016-06-02T19:12:02Z (GMT). No. of bitstreams: 1 3197.pdf: 6315859 bytes, checksum: 36b44ae7699dfee5945b8beb022fe8eb (MD5) Previous issue date: 2010-05-24 / Financiadora de Estudos e Projetos / The porcelain stoneware tile is a ceramic product that has presented a great increase on production, since it had excellent technical properties and raised aesthetic performance. To improve its aesthetic characteristics, it is submitted to a polishing process that influences a lot of interested properties of the products, due mainly to changes observed on the superficial roughness. In this way, the roughness was investigated throughout the superficial polishing process of the glazed and unglazed (technical) porcelain stoneware tile and it was correlated with the gloss. For this, the Atomic Force Microscope (AFM) was used, being ideal to measure the roughness in nanometer scale and to visualize the nanotexture of many types of surface materials. The specular part of the gloss was measured through the equipment known as glossmeter. The results achieved shown that the technical porcelain stoneware tile in the first stage is more rough than the glazed. On the technical porcelain stoneware tile the roughness reduction was more accented between the grit 80 and 1000 stages, and the gloss was practically double between the first and the last (POLIDO) stages. The surface covering with the polymeric resin reduced significantly the product gloss, without it causes brusque alterations in superficial roughness. On the glazed porcelain stoneware tile the roughness reduction and the gloss increased occurred mainly between the grit 600 and 1800 stages. Between the grit 1800 and 8000 stages had not observed great changes on the roughness or gloss, showing that the polishing becomes unnecessary from the grit 1800. In general way, the gloss reduction occurred more visibly in stages of polishing with abrasives of larger grains, while the abrasives of smaller grains had given the final gloss, intervene poorly in roughness. The results interpretation had supplied subsidies to a better understanding and control of the process responsible for the final characteristics between the glazed and technical products, and the differences between these typologies. / O porcelanato é um produto cerâmico que apresenta grande expansão na produção, já que possui excelentes propriedades técnicas e um elevado desempenho estético. Para melhorar suas características estéticas, é submetido a um processo de polimento que influencia diversas propriedades de interesse do produto, devido principalmente às mudanças verificadas na rugosidade superficial. Desta forma, a rugosidade foi investigada ao longo do processo de polimento da superfície de porcelanatos esmaltados e não esmaltados (técnicos) e correlacionada com o brilho obtido. Para isso, foi utilizado o Microscópio de Força Atômica (AFM), ideal para medir a rugosidade em escala nanométrica e visualizar a nanotextura de muitos tipos de superfícies de materiais. A parte especular do brilho foi medida por meio do equipamento conhecido por brilhômetro. Os resultados obtidos mostraram que o porcelanato técnico no primeiro estágio analisado é mais rugoso que o esmaltado. No porcelanato técnico a diminuição da rugosidade foi mais acentuada entre os estágios de grit 80 e 1000 e o brilho do produto praticamente dobrou entre o primeiro e último estágio (POLIDO). A aplicação de resina impermeabilizante causou uma diminuição brusca do brilho, sem alterar significativamente a rugosidade. No porcelanato esmaltado a diminuição da rugosidade e o aumento do brilho ocorreram principalmente entre os estágios de grit 600 e 1800. Entre os estágios de grit 1800 e 8000 não foram observadas grandes mudanças na rugosidade, nem tampouco no brilho, mostrando que o polimento torna-se desnecessário a partir do grit 1800. De modo geral, a diminuição da rugosidade ocorreu mais visivelmente nas etapas de polimento com abrasivos de grãos maiores, enquanto os abrasivos de grãos menores deram o brilho final das peças, interferindo pouco na rugosidade. A interpretação dos resultados forneceu subsídios para um melhor entendimento e controle do processo responsável pelas características finais dos produtos esmaltados e técnicos e as diferenças entre estas duas tipologias.

Made available in DSpace on 2016-06-02T19:12:15Z (GMT). No. of bitstreams: 1 3946.pdf: 4466269 bytes, checksum: 9cc3e3c7b0f0399d01e129c31e5dc027 (MD5) Previous issue date: 2011-03-03 / Universidade Federal de Sao Carlos / Considering the various types of ceramic tiles used today, the stoneware tile is distinguished by its aesthetic and technical characteristics, such as: very low water absorption (less than 0.5%), high mechanical strength, high abrasion strenght, high chemical and frost strenght. Commonly, a composition of stoneware tile is constituted by homogeneous mixture of plastic clay(s), kaolin, feldspar, quartz and talc of high purity. This work studied the effect of replacing the plastic clay used in the manufacture of this product, typically a clay, by a mudstone of lower refractoriness. Another object of study was to evaluate the influence of the replacement, even partially, the content of feldspar (which is the raw material most suitable flux and used industrially, around 45% by mass) for nepheline, evaluating the technical characteristics achieved in the final product. For this, emphasis was given to the use of different levels and types of trainers from the liquid phase (feldspar and nepheline) in compositions of bath with the mudstone. For comparison it was characterized, by means of physical tests, the linear shrinkage and water absorption (vitrification curve), and flexural strength of a standard composition, reported in the literature, and new compositions. In addition, it was evaluated the cycle and the level of firing (1200 ° C is the temperature industrial average), verifying the possibility of reducing consumption of natural gas, which represents the main energy source of the production process. / Considerando-se os vários tipos de revestimentos cerâmicos utilizados atualmente, o porcelanato se destaca por sua estética e por suas características técnicas, tais como: baixíssima absorção de água (menor que 0,5%), elevadas resistências mecânica, à abrasão, química e ao gelo. Comumente, uma composição de porcelanato é constituída da mistura homogênea de argila(s) plástica(s), caulim, feldspato, quartzo e talco, de elevada pureza. Neste trabalho estudou-se o efeito da substituição da argila plástica utilizada na fabricação desse produto, tipicamente uma argila caulinítica, por um argilito de menor refratariedade. Outro objeto de estudo foi avaliar a influência da substituição, mesmo que parcial, do teor de feldspato (que corresponde à matéria-prima fundente mais indicada e utilizada industrialmente, em torno de 45% em massa) por nefelina, avaliando-se as características técnicas alcançadas no produto final. Para isto, ênfase foi dada à utilização de diferentes teores e tipos de formadores de fase líquida (feldspato e nefelina) em composições de massas com o argilito. Para comparação caracterizou-se, por meio de ensaios físicos, a retração linear de queima e absorção de água (curva de gresificação), e a resistência mecânica à flexão de uma composição padrão, reportada na literatura, e das novas composições. Além disso, avaliou-se o ciclo e o patamar de queima (1200°C é a temperatura industrial média), verificando-se a possibilidade de redução de consumo de gás natural, que representa a principal fonte energética do processo produtivo.

Made available in DSpace on 2016-06-02T19:12:18Z (GMT). No. of bitstreams: 1 4206.pdf: 3029951 bytes, checksum: d95d50e3aa33adb881af74f67cd3abbb (MD5) Previous issue date: 2011-12-05 / Financiadora de Estudos e Projetos / Given the importance of planarity of the tiles for covering of floor and walls, this work aims to identify the influence of engobe layer on the behavior of central curvature, and from then on, allowing a greater understanding of the phenomenon of coupling support-engobe-enamel. The engobes are currently used as intermediate layer of ceramic tiles. Among the functions provided by engobes, some can be highlighted, hide the color of the ceramic, eliminate surface defects, to prevent reactions between the substrate and the ceramic glaze. In addition, the engobe also have a role in the coupling between substrate and enamel, but this is one of the least studied in the literature. To conduct the study, distinct engobes compositions were formulated, with planned variations in their behavior during the burning (fusibility and thermal expansion). With the help of the technique of design of experiments (DOE) with 2k factorial analysis, it was possible to study the effect of these variables on the central curvature. Results helped to understand the effect of each variable and the role of engobe on the flatness of the ceramic tiles. From the analysis of the results obtained it was suggested a statistical method that can help reduce the central curvature of the tiles from the knowledge of the characteristics of the engobe to the same type of enamel. / Devido à importância da planaridade das placas cerâmicas para revestimento de pisos e paredes, o presente trabalho visa identificar a influência da camada de engobe sobre o comportamento da curvatura central e, a partir de então, permitir uma maior compreensão do fenômeno de acoplamento suporte-engobe-esmalte. Os engobes são utilizados atualmente como camada intermediária nas placas de revestimentos cerâmicos. Dentre as funções apresentadas pelos engobes, podem ser destacadas algumas como: ocultar a cor do suporte cerâmico, eliminar defeitos superficiais e impedir reações entre o suporte e o esmalte cerâmico. Além disso, o engobe também têm papel no acoplamento entre suporte e esmalte, porém este é um dos aspectos menos tratado na literatura. Para a realização do estudo, foram formuladas distintas composições de engobes, com variações planejadas nas características de comportamento durante a queima (fusibilidade e expansão térmica linear). Com o auxílio da técnica de planejamento de experimentos (DOE) com análise fatorial 2k estudou-se o efeito dessas variáveis sobre a curvatura central. Os resultados permitiram a compreensão do efeito de cada uma das variáveis e do papel do engobe sobre a planaridade das placas cerâmicas. Partindo das análises dos resultados obtidos, sugeriu-se um método estatístico que possa auxiliar na redução das curvaturas centrais das placas cerâmicas à partir do conhecimento das características do engobe, para mesma tipologia de esmalte.

Submitted by Aelson Maciera (aelsoncm@terra.com.br) on 2017-04-03T18:22:29Z No. of bitstreams: 1 TeseLRSC.pdf: 19321865 bytes, checksum: 59c8299f94b51244447ce153f6f78a35 (MD5) / Approved for entry into archive by Ronildo Prado (ronisp@ufscar.br) on 2017-04-18T14:13:01Z (GMT) No. of bitstreams: 1 TeseLRSC.pdf: 19321865 bytes, checksum: 59c8299f94b51244447ce153f6f78a35 (MD5) / Approved for entry into archive by Ronildo Prado (ronisp@ufscar.br) on 2017-04-18T14:13:11Z (GMT) No. of bitstreams: 1 TeseLRSC.pdf: 19321865 bytes, checksum: 59c8299f94b51244447ce153f6f78a35 (MD5) / Made available in DSpace on 2017-04-18T18:09:37Z (GMT). No. of bitstreams: 1 TeseLRSC.pdf: 19321865 bytes, checksum: 59c8299f94b51244447ce153f6f78a35 (MD5) Previous issue date: 2016-09-09 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / In recent years porcelain stoneware tiles showed the highest growth in production and consumption in ceramic industry sector. To achieve low porosity, which ensures the high performance of the product, is required the formation of large amount of liquid phases during sintering and the flow of these liquids are responsible for the undesirable pyroplastic deformation. Some factors exacerbate the problem: large and rectangular shapes and faster firing cycles. Moreover, the production of tiles through a more sustainable route, the dry route, lacks studies evaluating the effects of processing method on pyroplastic deformation. Thus, this study aimed to contribute to reducing the incidence of pyroplastic deformations in porcelain stoneware tiles, in order to identify the main variables involved and suggest maneuvers for achieve this goal. In the first stage, technical porcelain stonewares were formulated using common raw materials in this type of manufacturing and prepared by wet route. The main difference between the batches was that 10% of the feldspar was replaced with other raw materials such as potash feldspar and quartz in different granulometries in order to change the characteristics of the liquid phases and to minimize pyroplastic deformation. The characterization of the batches before and after firing, as well the assessment of physical and chemical / mineralogical effects of the raw materials on deformation behavior was essential to identify the variables prevalent in deformation. In second stage some batches from previous step were prepared by dry route method, and then the same tests were performed in order to evaluate the effects of processing route on pyroplastic deformation. The results indicated that batches prepared by dry processing route are less likely to deformation mainly due to heterogeneity of microstructure. In both stages, it was found out that the viscosity of the liquid phase formed during firing is the variable that affects most significantly the pyroplastic deformation of the porcelain obtained by both processing routes studied. / Os porcelanatos apresentaram nos últimos anos o maior crescimento em produção e consumo do setor de revestimentos cerâmicos. Para atingir a baixa porosidade, a qual garante o alto desempenho do produto, é necessário que durante a sinterização seja formada grande quantidade de fases líquidas e o fluxo dos líquidos formados é responsável pela indesejável deformação piroplástica. Formatos retangulares, grandes dimensões, espessuras reduzidas e ciclos térmicos rápidos agravam o problema. Além disso, a produção de porcelanatos por uma rota mais sustentável, a via seca, não apresenta estudos que avaliem os efeitos do processamento sobre a deformação. Assim, este estudo objetivou contribuir para reduzir a incidência de deformações piroplásticas em porcelanatos, buscando identificar as principais variáveis envolvidas e sugerir alternativas que permitam atingir esse objetivo. Na primeira etapa do trabalho foram formuladas massas de porcelanatos técnicos preparadas por via úmida, substituindo-se 10% do feldspato utilizado na massa de referência (STD) por matérias-primas como o quartzo e feldspato potássico em granulometrias diferenciadas com o objetivo de alterar as características das fases líquidas de modo a minimizar a deformação piroplástica. A caracterização das massas antes e após a queima, bem como a avaliação dos efeitos físicos e químico/mineralógicos das matérias-primas sobre o comportamento de deformação foram essenciais para identificar as variáveis predominantes na deformação. Na segunda etapa algumas massas da etapa anterior foram preparadas pelo método de via seca, realizando posteriormente os mesmos ensaios, permitindo avaliar os efeitos do processamento sobre a deformação. Os resultados indicam que massas preparadas por via seca apresentam menor tendência a deformar piroplasticamente devido principalmente à heterogeneidade da microestrutura. Nas duas etapas do trabalho, verificou-se que a viscosidade das fases líquidas formadas durante a queima é a variável que afeta de forma mais significativa a deformação piroplástica dos porcelanatos obtidos pelas duas rotas de processamento estudadas.

A Dissertação de Mestrado em questão consiste na avaliação do uso de revestimentos cerâmicos de fachada fundamentada no estudo de caso para edifícios residenciais multifamiliares, caracterizado por prédios de apartamentos, no Município de São Paulo, região Sul, cujos lançamentos ocorreram entre 1994 e 1998. Para tanto, abordam-se inicialmente antecedentes do uso destes materiais em fachadas de edifícios no Brasil. Posteriormente são abordadas as principais características dos materiais componentes dos revestimentos cerâmicos, enfatizando suas características quando aplicados em fachadas. São explicitadas, ainda, considerações para a elaboração de projetos de revestimentos cerâmicos de fachadas, bem como para sua execução, destacando também as principais patologias que os afetam. Finalmente, é realizada uma análise do uso dos revestimentos cerâmicos em fachada, no cenário definido, acompanhada de registros fotográficos, apresentados na forma de fichas para cada bairro levantado. Acompanha também esta análise uma pesquisa realizada entre os escritórios de arquitetura responsáveis pelos projetos arquitetônicos dos edifícios em questão, visando as condicionantes de projeto para o uso dos revestimentos cerâmicos. Conclui-se com abordagens vinculadas ao estado da arte sobre o uso dos Revestimentos Cerâmicos de Fachadas baseado na pesquisa de campo e opiniões dos arquitetos. / This Dissertation is about an evaluation of the use of ceramic tiles in facades of buildings, based on the study of housing buildings located at the southern region of the city of Sao Paulo, which were built between 1994 and 1998. At the beginning, the historic aspects of use of ceramic tiles in facades are reviewed, specifically in Brazil. Later on, the main characteristics of the components of ceramic tiles in coverings are studied, emphasizing the resulting characteristics when applied to facades. The study also describes considerations for both the elaboration and implementation of projects of ceramic tile facade coverings including the main pathologies that may affect them. An analysis on the use of ceramic tile facade coverings in a specific scenery is included. Photographic files of each neighborhood are attached to this section as well as a research among architecture offices who were responsible for the projects of those buildings. Finally you will find approaches related to the state -of-art when using ceramic tile facade coverings based on an in situ research and on architect’s opinions.

O aumento da capacidade de penetração dos novos projéteis, utilizados tanto em operações de guerra como na violência urbana, tem obrigado o desenvolvimento contínuo de materiais mais resistentes e mais leves no emprego de blindagens. Na aplicação aeronáutica, os fatores peso e eficiências balísticas são extremamente críticos. Uma blindagem tem que oferecer proteção contra calibres de munição antiaérea sem acrescentar muito peso, para que a autonomia e capacidade de carregar armamentos não sejam limitadas. As blindagens que melhor desempenham esse papel são do tipo cerâmica/compósito. Contudo uma grande quantidade de combinações é possível, variando o tipo de cerâmica e de compósito. No presente trabalho foram abordados dois tipos de estudos. O primeiro estudo abordado é um modelo analítico que representa o impacto de um projétil sobre uma blindagem cerâmica/compósito, cuja simulação foi rodada em MATLAB V.5. Na simulação, os valores da V50 foram obtidos para os painéis de Al2O3/aramida e B4C/aramida contra os projéteis 7,62x51mm AP e 0,50 pol. NATO AP, respectivamente. O ensaio do painel SiC/aramida contra 0,50 pol. NATO AP serviu para calibrar a simulação e determinar o valor da deformação máxima da base, que é o critério de falha do modelo. Os resultados da simulação comparados com os resultados obtidos nos ensaios foram bem próximos, indicando que o modelo analítico é representativo. O segundo estudo é uma análise da vulnerabilidade de uma aeronave. Desta forma, um cone de ameaças é definido tendo a aeronave no seu vértice e os inimigos distribuídos aleatoriamente em sua base. Através de composição vetorial de velocidade calculam-se a velocidade de impacto e a seção oblíqua do projétil paralela ao plano da aeronave. Dessa forma é possível determinar a espessura necessária para proteger aquela área, utilizando a simulação, e assim otimizar a blindagem para que ela tenha o melhor quociente desempenho balístico/peso.

Neste trabalho é desenvolvido um modelo de blindagem balística mista composta por uma parte cerâmica (alumina), e uma parte de compósito (polietileno de ultra alto peso molecular). Paralelamente, também foi modelada a munição à qual a blindagem objetiva proteger. O modelo foi aplicado a alvos compostos somente da base de polietileno de ultra alto peso molecular, e a alvos mistos contendo cerâmica e compósito. Quando a blindagem apresentou uma V50, velocidade com 50% de chance de penetração, da ordem de 700m/s, a simulação obteve erros inferiores a 5%. Já quando a blindagem apresentou uma V50 mais baixa, cerca de 500m/s, a simulação obteve erros maiores, superiores a 15%, mas mesmo assim foi possível prever que a blindagem não era eficiente para esse tipo de solicitação.

Compósitos híbridos polímero/cerâmica têm sido bastante utilizados em painéis de blindagem balística por serem materiais que possuem capacidade de absorver impactos de alta velocidade. A eficiência de absorver impactos sucessivos e a extensão dos danos colaterais do impacto está relacionada a diversos fatores entre eles, um que tem um papel fundamental, é a interface da camada cerâmica com a camada polimérica. A natureza do adesivo utilizado e das interações estabelecidas, aliada a força de adesão e, as morfologias da camada interfacial, entre outras variáveis, podem determinar a intensidade da propagação de energia residual. Estes fatos podem afetar os modos de fragmentação da cerâmica, a capacidade do material resistir a um segundo impacto e, sobretudo interferir no tamanho e na geometria do cone residual resultante da deformação plástica da camada polimérica. Neste trabalho, analisa-se a influência da interface adesiva no desempenho balístico de materiais híbridos constituídos de compósito de fibras de polietileno de ultra-alta massa molar (UHMWPE) /matriz polimérica (Dyneema ), tecido de fibras de aramida (Kevlar ) e a cerâmica alumina. São avaliados adesivos de natureza química distinta, à base de poliuretano, epóxi e silano. A alumina é preparada e caracterizada por ensaios de massa específica, resistência à flexão, dureza Vickers, difração de raios X e Microscopia eletrônica de varredura (MEV), cujos resultados indicam que a mesma possui propriedades adequadas para aplicação balística. A caracterização da interface adesiva é realizada por meio do teste de resistência ao despelamento (T-Peel) e a superfície pós-teste é caracterizada por microscopia óptica e espectroscopia na região do infravermelho com transformada de Fourier (FT-IR). Estes testes ressaltam que no compósito utilizando Dyneema , a resistência ao despelamento foi parecida para todos os adesivos utilizados indicando que o rompimento ocorre entre as camadas do substrato polimérico. Já para as amostras com Kevlar , o adesivo PU hot melt apresenta maior adesão enquanto que o adesivo a base de silano é o menos eficiente dentre os utilizados. Ensaios balísticos foram realizados em painéis montados com adesivos selecionados no ensaio de adesão: PU hot melt (maior aderência), silano (menor aderência) e epóxi (intermediária). O desempenho dos painéis balísticos, no que diz respeito à extensão dos danos colaterais, varia de acordo com os adesivos utilizados. A força adesiva, assim como a rigidez do adesivo, influencia na transferência de energia de impacto e consequentemente nas dimensões da deformação da camada posterior e na integridade da placa cerâmica adjacente à que sofreu o impacto.

As atividades de manutenção, que dependem das decisões tomadas nas diversas etapas do processo de produção dos edifícios, têm por objetivo maximizar o desempenho de cada subsistema que o constitui. A manutenção de cada um destes subsistemas está associada a uma série de atividades programadas que devem prolongar sua vida útil a um custo compensador. Dentro deste contexto, a manutenção do revestimento de fachadas, em particular a limpeza dos revestimentos cerâmicos, reveste-se de grande importância uma vez que este subsistema não apenas está exposto a vários agentes de degradação, mas também está intimamente relacionado com a estética e a proteção do edifício. A pesquisa desenvolvida discute teoricamente os principais tipos de sujidades presentes nos revestimentos de fachada de edifícios e apresenta os principais métodos de limpeza destes revestimentos. Após o estudo teórico dos aspectos relacionados com a limpeza, aborda, por meio de estudo experimental de laboratório e de estudos de caso, a limpeza de revestimento cerâmico de fachada de edifícios. O trabalho demonstrou a necessidade da elaboração de uma norma técnica que aborde a especificação de métodos de limpeza de revestimentos de fachada, abrangendo procedimentos, produtos e técnicas. Além disso, notou-se a ineficácia de determinados produtos anti-pichação e de limpeza para determinadas condições de uso. / The maintenance activities, which depend on the decisions made in the several stages of the production process, aim to maximize the performance of each subsystem of building. The maintenance of each one of these subsystems is associated with a series of programmed activities that must draw out their service life in compensating cost. In this context, the maintenance of façade claddings, particularly, the cleaning of ceramic tiles claddings, assumes great importance, since this subsystem is not only exposed to some degradation agents, but it is also intimately related to the aesthetic and the protection of the building. This research theoretically emphasizes the main types of soiling existing in façade claddings of buildings and it presents the main methods of cleaning of these claddings. After the theoretical study of the aspects related to cleaning, it broaches, by means of laboratory experimental tests and case studies, the cleaning of ceramic tiles claddings in façades of buildings. This research discussed the necessity of the elaboration of a technical standard involving the specification of cleaning methods for façade claddings, including procedures, products and techniques as well. Moreover, it was noticed the inefficacy of certain anti-graffi i products and cleaning products in certain situations of use.