This thesis contains descriptions and definitions of the Iron Age Proto-Aeolic capitals from Israel - Palestine area. The modern area, which my materials cover is Israel and Jordan. The time period of the capitals is between the 9th century BC and the late 8th or the beginning of the 7th century BC. Attention has been put on issues of typological characteristics, usage and time periods of the capitals and how this, through the new examples, described here for the first time, created a new typology and usage for the Proto-Aeolic capitals.

Este trabalho compreendeu os estudos de síntese química de pós por via úmida, de processamento cerâmico e de redução do óxido de níquel contido nos compósitos de céria dopada com samária e gadolínia, aplicados, principalmente, como anodos de Células a Combustível de Óxido Sólido. A rota adotada para a preparação dos pós com composição Ce0,8(SmGd)0,2O1,9/NiO e proporção em massa de 40 : 60% foi a coprecipitação de hidróxidos associada ao tratamento solvotérmico, utilizando-se como matérias-primas cloretos de cério, níquel, samário e gadolínio. O surfactante aniônico brometo de cetil trimetil amônio (CTAB) também foi utilizado na etapa de precipitação na relação molar Metal / CTAB entre 1 e 3. A influência do solvente orgânico utilizado no tratamento solvotérmico dos pós foi analisada utilizando o etanol, propanol e o butanol, nas condições de temperatura de 150ºC por 16 h, com e sem calcinação a 600ºC por 1h, e moagem em moinho de bolas. As amostras compactadas foram sinterizadas em temperaturas entre 1200 e 1400ºC por 1h. A redução in situ do NiO-SGDC foi estudada na amostra cerâmica preparada nas seguintes condições: síntese por coprecipitação usando ou não o CTAB, tratamento solvotérmico em butanol, calcinação a 600ºC, prensagem e sinterização a 1350ºC por 1h. O processo de redução das amostras sintetizadas em butanol foi avaliado em forno tubular em atmosfera dinâmica de 4%H2/Ar, fixando-se a temperatura a 900°C e variando-se o tempo entre 10 e 120 minutos. A redução também foi relizada nos compósitos sintetizados utilizando o CTAB na proporção Metal/CTAB = 2, tratados termicamente em etanol e butanol, após calcinação, prensagem e sinterização em forno tubular sob atmosfera de H2/Ar em isotermas de 700, 800 e 900°C por períodos entre 2 e 240 minutos. Os pós, as cerâmicas e os compósitos sintetizados em laboratório foram comparados com os materiais compósitos produzidos com pós de origem comercial. A caracterização dos pós foi realizada por difração de raios X (DRX), microscopia eletrônica de varredura (MEV), área de superfície específica por adsorção gasosa de nitrogênio (BET), análise térmica (TG/DTA) e distribuição granulométrica por espalhamento de feixe laser (Cilas). As cerâmicas foram analisadas por microscopia eletrônica de varredura, DRX e medidas de densidade pela técnica de imersão em água (método de Arquimedes). As cerâmicas e os compósitos foram caracterizados eletricamente por medidas de resistência elétrica pelo método de quatro pontas DC. Os resultados mostraram que os pós sem calcinação apresentaram as estruturas cristalinas características da céria e do hidróxido de níquel, e elevada área de superfície específica (80 m2/g). As cerâmicas provenientes dos pós tratados com etanol e propanol apresentaram boa homogeneidade química, estrutural e valores de densidade de 99% em relação a densidade teórica. Verificou-se que 80 a 90% do NiO é reduzido e as porosidades atingidas pelos compósitos são da ordem de 30%. A caracterização elétrica mostrou que a condutividade iônica da fase cerâmica do anodo, sintetizado solvotermicamente em butanol, possui valor de 0,03S.cm-1 na temperatura de 600°C, valor superior aos encontrados na literatura. A caracterização elétrica dos compósitos reduzidos revelou alta condutividade elétrica característica do níquel metálico, indicando percolação adequada da fase de níquel e distribuição homogênea de ambas fases cerâmica e metálica. As rotas de síntese e os materiais estudados são, portanto, adequados para a aplicação como anodo das IT-SOFCs. / This work comprises studies of powder chemical synthesis by wet route, ceramic processing and reduction of nickel oxide added to samaria and gadolinia doped ceria ceramic composite, mainly applied as Solid Oxide Fuel Cells anode. The route adopted for the powders preparation with composition Ce0.8(SmGd)0.2O1.9/NiO and mass ratio of 40:60% was hydroxides coprecipitation and solvothermal treatment, using as start materials the cerium, nickel, samarium and gadolinium chlorides. The anionic surfactant cetyltrimethylammonium bromide (CTAB) was also used in the precipitation stage with the molar ratio Metal/CTAB ranging between 1 and 3. The influence of organic solvent used in the powders solvothermal treatment was analyzed by using ethanol, propanol and butanol at temperature of 150°C for 16h, with and without calcination at 600°C for 1h, and grinding in a ball mill. The compacted samples were sintered at temperatures between 1200 and 1400°C for 1h. The in situ reduction of NiO-SGDC was studied in the samples synthesized by coprecipitation using CTAB and without it, followed by solvothermal treatment in butanol, calcined at 600°C, pressed and sintered at 1350°C for 1h. The reduction procedure was evaluated in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 900°C and time range between 10 and 120 minutes. The composites synthesized using the CTAB in the proportion of Metal/CTAB = 2, followed by solvothermal treatment in ethanol and butanol, after calcining, compaction and sintering, was also reduced in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 700, 800 and 900°C and time range between 2 and 240 minutes. The powders, ceramics and the sinterized cermets syntesized in laboratory were compared to the materials produced with comercial powders. The powders characterization was performed by X-ray diffraction (XRD), scanning electron microscopy (SEM), specific surface area by nitrogen gas adsorption (BET), thermal analysis (TG / DTA) and particle size distribution by scattering beam laser (Cilas). Ceramics were analyzed by scanning electron microscopy (SEM), XRD and density measurements by the technique of immersion in water (Archimedes method). The ceramics and cermets condutivity was characterized by the four probe DC method. The results obtained showed that the powders without calcination presented the crystal structures characteristics of ceria and nickel hydroxide, and high specific surface area (80m2/g) . The ceramic prepared from powders treated with ethanol and propanol had a high chemical and structural homogeneity and density values corresponding to 99% of the theoretical density. It was found that 80 to 90 % of NiO is reduced and the porosity of the composite reached about of 30 %. The anode ceramic phase synthesized solvothermically in butanol presented electrical conductivity of 0.03S.cm-1 at 600°C, higher than found at literature. The reduced cermets electrical characterization showed high electrical conductivity feature of metallic nickel, indicating the nickel phase good percolation and homogeneous distribution of both ceramic and metallic phases. Considering all these results, the synthesis routes and studied materials are suitable for use as the anode IT- SOFCs.

O óxido de cério (CeO2), quando dopado com óxidos de terras raras, tem sua condutividade iônica aumentada, possibilitando seu uso como eletrólito de Células a Combustível de Óxido Sólido de Temperatura Intermediária (IT-SOFC), que são operadas entre 500 e 700°C. Os aditivos ou dopantes mais eficientes para o aumento da condutividade iônica são a samária (óxido de samário Sm2O3) e a gadolínia (óxido de gadolínio Gd2O3), com concentrações molares entre 10 e 20%. Neste contexto foram sintetizados, neste trabalho, pós de composição Ce0,8(SmGd)0,2O1,9 pelas rotas de síntese por coprecipitação de hidróxidos, carbonatos e oxalatos. O efeito do tratamento hidrotérmico foi avaliado para pós precipitados com hidróxido de amônio. Utilizou-se, como matériasprimas, concentrados de terras raras contendo 90% em massa de CeO2 e outro contendo 51% de Sm2O3 e 30% de Gd2O3, ambos provenientes do processamento da monazita. Estes concentrados foram utilizados devido ao menor custo em relação às matérias-primas puras adquiridas comercialmente e a semelhança química dos demais elementos de terras raras contidos. Inicialmente, foram definidas as condições das etapas de coprecipitação e a influência da temperatura de calcinação nas características dos pós e produtos sinterizados. Os resultados obtidos mostraram que os pós calcinados na faixa de temperatura entre 450 e 800ºC apresentam elevada área de superfície específica (90-150 m2.g-1) e estrutura cristalina cúbica tipo fluorita da céria, indicando a formação da solução sólida. Observou-se, por microscopia eletrônica de varredura, que a forma das partículas e dos aglomerados é função do tipo de agente precipitante. As análises dilatométricas indicaram maior taxa de retração em temperatura próxima a 1300-1350ºC. Entretanto, valores elevados de densificação (>95% DT) são obtidos em temperaturas superiores a 1400ºC. A síntese por coprecipitação de hidróxidos seguida pelo tratamento hidrotérmico demonstrou ser uma rota promissora para cristalização, em baixas temperaturas (200oC), de nanopós à base de céria, mantendo-se elevados os valores de área de superfície específica (cerca de 100 m2.g-1). Cerâmicas com densificação superior a 95%DT foram obtidas em menores temperaturas de sinterização (1400oC), quando comparadas às provenientes de pós cristalizados por calcinação. / Cerium oxide (CeO2) when doped with rare earth oxides has its ionic conductivity enhanced, enabling its use as electrolyte for Intermediate Temperature Solid Oxide Fuel Cell (IT-SOFC), which is operated in temperatures between 500 e 700°C. The most effective aditives or dopants for ionic condutivity improvement are (samarium oxide Sm2O3) and gadolinia (gadolinium oxide Gd2O3), fixing the concentration between 10 and 20 molar%. In this work, Ce0,8(SmGd)0,2O1,9 powders have been synthesized by hydroxide, carbonate and oxalate coprecipitation routes. The hydrothermal treatment has been studied for powders precipitated with ammonium hydroxide. A concentrate of rare earths containing 90wt% of CeO2 and other containing 51% of Sm2O3 and 30% of Gd2O3, both prepared from monazite processing, were used as starting materials. These concentrates were used due the lower cost compared to pure commercial materials and the chemical similarity of others rare earth elements. Initially, the coprecipitation and calcination conditions were defined. The process efficiency was verified by ceramic sinterability evaluation. The results showed that powders calcined in the range of 450 and 800°C presented high specific surface area (90 - 150 m2.g-1) and fluorite cubic structure, indicating the solid solution formation. It was observed, by scanning electron microscopy, that morphology of particles and agglomerates is a function of precipitant agent. The dilatometric analysis indicated the higher rate of shrinkage at temperatures around 1300-1350°C. High densification values (>95% TD) was obtained at temperatures above 1400ºC. Synthesis by hydroxides coprecipitation followed by hydrothermal treatment demonstrated to be a promising route for crystallization of ceria nanopowders at low temperatures (200oC). High values of specific surface area were reached with the employment of hydrothermal treatment (about 100 m2.g-1). High density ceramics were obtained at lower temperatures (1400oC), compared to those employed for calcined powders.

O óxido de cério (CeO2), quando dopado com óxidos de terras raras, tem sua condutividade iônica aumentada, possibilitando seu uso como eletrólito de Células a Combustível de Óxido Sólido de Temperatura Intermediária (IT-SOFC), que são operadas entre 500 e 700°C. Os aditivos ou dopantes mais eficientes para o aumento da condutividade iônica são a samária (óxido de samário Sm2O3) e a gadolínia (óxido de gadolínio Gd2O3), com concentrações molares entre 10 e 20%. Neste contexto foram sintetizados, neste trabalho, pós de composição Ce0,8(SmGd)0,2O1,9 pelas rotas de síntese por coprecipitação de hidróxidos, carbonatos e oxalatos. O efeito do tratamento hidrotérmico foi avaliado para pós precipitados com hidróxido de amônio. Utilizou-se, como matériasprimas, concentrados de terras raras contendo 90% em massa de CeO2 e outro contendo 51% de Sm2O3 e 30% de Gd2O3, ambos provenientes do processamento da monazita. Estes concentrados foram utilizados devido ao menor custo em relação às matérias-primas puras adquiridas comercialmente e a semelhança química dos demais elementos de terras raras contidos. Inicialmente, foram definidas as condições das etapas de coprecipitação e a influência da temperatura de calcinação nas características dos pós e produtos sinterizados. Os resultados obtidos mostraram que os pós calcinados na faixa de temperatura entre 450 e 800ºC apresentam elevada área de superfície específica (90-150 m2.g-1) e estrutura cristalina cúbica tipo fluorita da céria, indicando a formação da solução sólida. Observou-se, por microscopia eletrônica de varredura, que a forma das partículas e dos aglomerados é função do tipo de agente precipitante. As análises dilatométricas indicaram maior taxa de retração em temperatura próxima a 1300-1350ºC. Entretanto, valores elevados de densificação (>95% DT) são obtidos em temperaturas superiores a 1400ºC. A síntese por coprecipitação de hidróxidos seguida pelo tratamento hidrotérmico demonstrou ser uma rota promissora para cristalização, em baixas temperaturas (200oC), de nanopós à base de céria, mantendo-se elevados os valores de área de superfície específica (cerca de 100 m2.g-1). Cerâmicas com densificação superior a 95%DT foram obtidas em menores temperaturas de sinterização (1400oC), quando comparadas às provenientes de pós cristalizados por calcinação. / Cerium oxide (CeO2) when doped with rare earth oxides has its ionic conductivity enhanced, enabling its use as electrolyte for Intermediate Temperature Solid Oxide Fuel Cell (IT-SOFC), which is operated in temperatures between 500 e 700°C. The most effective aditives or dopants for ionic condutivity improvement are (samarium oxide Sm2O3) and gadolinia (gadolinium oxide Gd2O3), fixing the concentration between 10 and 20 molar%. In this work, Ce0,8(SmGd)0,2O1,9 powders have been synthesized by hydroxide, carbonate and oxalate coprecipitation routes. The hydrothermal treatment has been studied for powders precipitated with ammonium hydroxide. A concentrate of rare earths containing 90wt% of CeO2 and other containing 51% of Sm2O3 and 30% of Gd2O3, both prepared from monazite processing, were used as starting materials. These concentrates were used due the lower cost compared to pure commercial materials and the chemical similarity of others rare earth elements. Initially, the coprecipitation and calcination conditions were defined. The process efficiency was verified by ceramic sinterability evaluation. The results showed that powders calcined in the range of 450 and 800°C presented high specific surface area (90 - 150 m2.g-1) and fluorite cubic structure, indicating the solid solution formation. It was observed, by scanning electron microscopy, that morphology of particles and agglomerates is a function of precipitant agent. The dilatometric analysis indicated the higher rate of shrinkage at temperatures around 1300-1350°C. High densification values (>95% TD) was obtained at temperatures above 1400ºC. Synthesis by hydroxides coprecipitation followed by hydrothermal treatment demonstrated to be a promising route for crystallization of ceria nanopowders at low temperatures (200oC). High values of specific surface area were reached with the employment of hydrothermal treatment (about 100 m2.g-1). High density ceramics were obtained at lower temperatures (1400oC), compared to those employed for calcined powders.

Este trabalho compreendeu os estudos de síntese química de pós por via úmida, de processamento cerâmico e de redução do óxido de níquel contido nos compósitos de céria dopada com samária e gadolínia, aplicados, principalmente, como anodos de Células a Combustível de Óxido Sólido. A rota adotada para a preparação dos pós com composição Ce0,8(SmGd)0,2O1,9/NiO e proporção em massa de 40 : 60% foi a coprecipitação de hidróxidos associada ao tratamento solvotérmico, utilizando-se como matérias-primas cloretos de cério, níquel, samário e gadolínio. O surfactante aniônico brometo de cetil trimetil amônio (CTAB) também foi utilizado na etapa de precipitação na relação molar Metal / CTAB entre 1 e 3. A influência do solvente orgânico utilizado no tratamento solvotérmico dos pós foi analisada utilizando o etanol, propanol e o butanol, nas condições de temperatura de 150ºC por 16 h, com e sem calcinação a 600ºC por 1h, e moagem em moinho de bolas. As amostras compactadas foram sinterizadas em temperaturas entre 1200 e 1400ºC por 1h. A redução in situ do NiO-SGDC foi estudada na amostra cerâmica preparada nas seguintes condições: síntese por coprecipitação usando ou não o CTAB, tratamento solvotérmico em butanol, calcinação a 600ºC, prensagem e sinterização a 1350ºC por 1h. O processo de redução das amostras sintetizadas em butanol foi avaliado em forno tubular em atmosfera dinâmica de 4%H2/Ar, fixando-se a temperatura a 900°C e variando-se o tempo entre 10 e 120 minutos. A redução também foi relizada nos compósitos sintetizados utilizando o CTAB na proporção Metal/CTAB = 2, tratados termicamente em etanol e butanol, após calcinação, prensagem e sinterização em forno tubular sob atmosfera de H2/Ar em isotermas de 700, 800 e 900°C por períodos entre 2 e 240 minutos. Os pós, as cerâmicas e os compósitos sintetizados em laboratório foram comparados com os materiais compósitos produzidos com pós de origem comercial. A caracterização dos pós foi realizada por difração de raios X (DRX), microscopia eletrônica de varredura (MEV), área de superfície específica por adsorção gasosa de nitrogênio (BET), análise térmica (TG/DTA) e distribuição granulométrica por espalhamento de feixe laser (Cilas). As cerâmicas foram analisadas por microscopia eletrônica de varredura, DRX e medidas de densidade pela técnica de imersão em água (método de Arquimedes). As cerâmicas e os compósitos foram caracterizados eletricamente por medidas de resistência elétrica pelo método de quatro pontas DC. Os resultados mostraram que os pós sem calcinação apresentaram as estruturas cristalinas características da céria e do hidróxido de níquel, e elevada área de superfície específica (80 m2/g). As cerâmicas provenientes dos pós tratados com etanol e propanol apresentaram boa homogeneidade química, estrutural e valores de densidade de 99% em relação a densidade teórica. Verificou-se que 80 a 90% do NiO é reduzido e as porosidades atingidas pelos compósitos são da ordem de 30%. A caracterização elétrica mostrou que a condutividade iônica da fase cerâmica do anodo, sintetizado solvotermicamente em butanol, possui valor de 0,03S.cm-1 na temperatura de 600°C, valor superior aos encontrados na literatura. A caracterização elétrica dos compósitos reduzidos revelou alta condutividade elétrica característica do níquel metálico, indicando percolação adequada da fase de níquel e distribuição homogênea de ambas fases cerâmica e metálica. As rotas de síntese e os materiais estudados são, portanto, adequados para a aplicação como anodo das IT-SOFCs. / This work comprises studies of powder chemical synthesis by wet route, ceramic processing and reduction of nickel oxide added to samaria and gadolinia doped ceria ceramic composite, mainly applied as Solid Oxide Fuel Cells anode. The route adopted for the powders preparation with composition Ce0.8(SmGd)0.2O1.9/NiO and mass ratio of 40:60% was hydroxides coprecipitation and solvothermal treatment, using as start materials the cerium, nickel, samarium and gadolinium chlorides. The anionic surfactant cetyltrimethylammonium bromide (CTAB) was also used in the precipitation stage with the molar ratio Metal/CTAB ranging between 1 and 3. The influence of organic solvent used in the powders solvothermal treatment was analyzed by using ethanol, propanol and butanol at temperature of 150°C for 16h, with and without calcination at 600°C for 1h, and grinding in a ball mill. The compacted samples were sintered at temperatures between 1200 and 1400°C for 1h. The in situ reduction of NiO-SGDC was studied in the samples synthesized by coprecipitation using CTAB and without it, followed by solvothermal treatment in butanol, calcined at 600°C, pressed and sintered at 1350°C for 1h. The reduction procedure was evaluated in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 900°C and time range between 10 and 120 minutes. The composites synthesized using the CTAB in the proportion of Metal/CTAB = 2, followed by solvothermal treatment in ethanol and butanol, after calcining, compaction and sintering, was also reduced in a tubular oven and atmosphere of 4% H2/Ar, setting the temperature at 700, 800 and 900°C and time range between 2 and 240 minutes. The powders, ceramics and the sinterized cermets syntesized in laboratory were compared to the materials produced with comercial powders. The powders characterization was performed by X-ray diffraction (XRD), scanning electron microscopy (SEM), specific surface area by nitrogen gas adsorption (BET), thermal analysis (TG / DTA) and particle size distribution by scattering beam laser (Cilas). Ceramics were analyzed by scanning electron microscopy (SEM), XRD and density measurements by the technique of immersion in water (Archimedes method). The ceramics and cermets condutivity was characterized by the four probe DC method. The results obtained showed that the powders without calcination presented the crystal structures characteristics of ceria and nickel hydroxide, and high specific surface area (80m2/g) . The ceramic prepared from powders treated with ethanol and propanol had a high chemical and structural homogeneity and density values corresponding to 99% of the theoretical density. It was found that 80 to 90 % of NiO is reduced and the porosity of the composite reached about of 30 %. The anode ceramic phase synthesized solvothermically in butanol presented electrical conductivity of 0.03S.cm-1 at 600°C, higher than found at literature. The reduced cermets electrical characterization showed high electrical conductivity feature of metallic nickel, indicating the nickel phase good percolation and homogeneous distribution of both ceramic and metallic phases. Considering all these results, the synthesis routes and studied materials are suitable for use as the anode IT- SOFCs.

Made available in DSpace on 2014-12-17T14:07:19Z (GMT). No. of bitstreams: 1 WilsonJO_TESE.pdf: 5377189 bytes, checksum: 886cb0d3eb97075a3db2f3b7c1a15af0 (MD5) Previous issue date: 2013-10-21 / Fuel cells are considered one of the most promising ways of converting electrical energy due to its high yield and by using hydrogen (as fuel) which is considered one of the most important source of clean energy for the future. Rare earths doped ceria has been widely investigated as an alternative material for the electrolyte of solid oxide fuel cells (SOFCs) due to its high ionic conductivity at low operating temperatures compared with the traditional electrolytes based on stabilized zirconia. This work investigates the effect of gallium oxide (Gallia) as a sintering aid in Eu doped ceria ceramic electrolytes since this effect has already been investigated for Gd, Sm and Y doped ceria electrolytes. The desired goal with the use of a sintering aid is to reduce the sintering temperature aiming to produce dense ceramics. In this study we investigated the effects on densification, microstructure and ionic conduction caused by different molar fraction of the dopants europium (10, 15 and 20%) and gallium oxide (0.3, 0.6 and 0.9%) in samples sintered at 1300, 1350 and 1450 0 C. Samaria (10 and 20%) doped ceria samples sintered between 1350 and 1450 ?C were used as reference. Samples were synthesized using the cation complexation method. The ceramics powders were characterized by XRF, XRD and SEM, while the sintered samples were investigated by its relative density, SEM and impedance spectroscopy. It was showed that gallia contents up to 0.6% act as excellent sintering aids in Eu doped ceria. Above this aid content, gallia addition does not promote significant increase in density of the ceramics. In Ga free samples the larger densification were accomplished with Eu 15% molar, effect expressed in the microstructure with higher grain growth although reduced and surrounded by many open pores. Relative densities greater than 95 % were obtained by sintering between 1300 and 1350 ?C against the usual range 1500 - 1600 0 C. Samples containing 10% of Sm and 0.9% of Ga reached 96% of theoretical density by sintering at 1350 0 C for 3h, a gain compared to 97% achieved with 20% of Sm and 1% of Ga co-doped cerias sintered at 1450 0 C for 24 h as described in the literature. It is found that the addition of gallia in the Eu doped ceria has a positive effect on the grain conductivity and a negative one in the grain boundary conductivity resulting in a small decrease in the total conductivity which will not compromise its application as sintering aids in ceria based electrolytes. Typical total conductivity values at 600 and 700 ?C, around 10 and 30 mS.cm -1 respectively were reached in this study. Samples with 15% of Eu and 0.9 % of Ga sintered at 1300 and 1350 ?C showed relative densities greater than 96% and total conductivity (measured at 700 ?C) between 20 and 33 mS.cm -1 . The simultaneous sintering of the electrolyte with the anode is one of the goals of research in materials for SOFCs. The results obtained in this study suggest that dense Eu and Ga co-doped ceria electrolytes with good ionic conductivity can be sintered simultaneously with the anode at temperatures below 1350 ?C, the usual temperature for firing porous anode materials / As c?lulas a combust?vel s?o tidas como uma das mais promissoras formas de convers?o de energia el?trica devido ao seu alto rendimento e por utilizar o hidrog?nio como combust?vel, considerado por muitos a principal fonte limpa de energia para o futuro. C?ria dopada com terras raras tem sido amplamente investiga como material alternativo para eletr?lito de c?lulas a combust?vel de ?xido s?lido (SOFC) devido sua alta condutividade i?nica em baixas temperaturas de opera??o quando comparado com os tradicionais eletr?litos ? base de zirc?nia estabilizada. Neste seguimento de pesquisa, este trabalho investiga o efeito do ?xido de g?lio (G?lia) como aditivo de sinteriza??o em eletr?litos cer?micos a base de c?ria dopada com eur?pio, uma vez que este efeito j? foi investigado por outros em eletr?litos ? base de c?ria dopada com Gd, Sm e Y. A meta almejada com a utiliza??o do aditivo de sinteriza??o ? reduzir a temperatura de sinteriza??o para a produ??o de cer?micas densas. Neste trabalho investigou-se o efeito na densifica??o, na microestrutura e na condu??o i?nica causado por diferentes fra??es molares do dopante eur?pio (10, 15 e 20%) e do aditivo de sinteriza??o ?xido de g?lio (0,3; 0,6 e 0,9%), em amostras sinterizadas a 1300, 1350 e 1450 0 C. A c?ria co-dopada com 10 e 20% de Sm e com os mesmos teores do aditivo de sinteriza??o g?lia, sinterizadas a 1350, 1450 e 1500 0 C, tamb?m foi investigada, por sua vez, como par?metro de refer?ncia experimental, haja visto que, nesta pesquisa, adotou-se s?nteses pelo m?todo de complexa??o de c?tions enquanto que os trabalhos encontrados na literatura utilizaram o m?todo convencional. Os p?s cer?micos sintetizados foram caracterizados por FRX, DRX e MEV e as amostras cer?micas sinterizadas por sua densidade relativa, MEV e espectroscopia de imped?ncia. Verifica-se que a G?lia com teores at? 0,6% atua como um excelente aditivo de sinteriza??o na c?ria dopada com Eu. Acima deste teor e at? 0,9% a adi??o da g?lia n?o promove significativos aumentos na densidade da cer?mica. Nas amostras livres do Ga, as maiores densifica??es foram alcan?adas com 15% de Eu, efeito manifestado na micro-estrutura com os maiores crescimentos de gr?os, embora ainda reduzidos e circundados por muitos poros abertos. Densidades relativas superiores a 95% da densidade te?rica podem ser obtidas com sinteriza??es entre 1300 e 1350 0 C, contra as usuais 1500 a 1600 0 C. Com a c?ria co-dopada com 10% de Sm e 0,9% de Ga alcan?ou-se neste trabalho 96% da densidade te?rica com sinteriza??o a 1350 0 C por 3h, um ganho em rela??o aos 97% alcan?ados com a c?ria co-dopada com 20% de Sm e 1% de Ga sinterizada a 1450 0 C por 24h conforme encontrado na literatura. Verifica-se que a adi??o da G?lia em eletr?litos ? base de c?ria dopada com Eu apresenta efeito positivo na condutividade do gr?o e negativo na do contorno de gr?o resultando em uma pequena redu??o na condutividade total, a qual n?o compromete sua promissora aplica??o como aditivo de sinteriza??o. Valores t?picos da condutividade total a 600 e 700 0 C, em torno de 10 e 30 mS.cm -1 respectivamente, foram alcan?ados neste trabalho. As amostras de eletr?litos ? base de c?ria co-dopada com 15% de Eu e 0,9% de Ga, sinterizados a 1300 e 1350 0 C, alcan?aram densidades relativas superiores a 96% e condutividade a 700 0 C entre 20 e 33 mS.cm -1 . A sinteriza??o simult?nea do eletr?lito com o anodo ? uma das metas da pesquisa em materiais para SOFCs. Os resultados alcan?ados neste trabalho sugerem que eletr?litos densos ? base de c?ria co-dopada com Eu e Ga podem ser sinterizados simultaneamente com o anodo ? temperatura de sinteriza??o entre 1300 e 1350 0 C, a faixa de temperatura usual de sinteriza??o do anodo poroso