Advanced BaZrO3-BaCeO3 Based Proton Conductors Used for Intermediate Temperature Solid Oxide Fuel Cells (ITSOFCs)

Bu, Junfu January 2015 (has links)
In this thesis, the focus is on studying BaZrO3-BaCeO3 based proton conductors due to that they represent very promising proton conductors to be used for Intermediate Temperature Solid Oxide Fuel Cells (ITSOFCs). Here, dense BaZr0.5Ce0.3Y0.2O3-δ (BZCY532) ceramics were selected as the major studied materials. These ceramics were prepared by different sintering methods and doping strategies. Based on achieved results, the thesis work can simply be divided into the following parts: 1) An improved synthesis method, which included a water-based milling procedure followed by a freeze-drying post-processing, was presented. A lowered calcination and sintering temperature for a Hf0.7Y0.3O2-δ (YSH) compound was achieved. The value of the relative density in this work was higher than previously reported data. It is also concluded that this improved method can be used for mass-production of ceramics. 2) As the solid-state reactive sintering (SSRS) represent a cost-effective sintering method, the sintering behaviors of proton conductors BaZrxCe0.8-xLn0.2O3-δ (x = 0.8, 0.5, 0.1; Ln = Y, Sm, Gd, Dy) during the SSRS process were investigated. According to the obtained results, it was found that the sintering temperature will decrease, when the Ce content increases from 0 (BZCLn802) to 0.3 (BZCLn532) and 0.7 (BZCLn172). Moreover, the radii of the dopant ions similar to the radii of Zr4+ or Ce4+ ions show a better sinterability. This means that it is possible to obtain dense ceramics at a lower temperature. Moreover, the conductivities of dense BZCLn532 ceramics were determined. The conductivity data indicate that dense BZCY532 ceramics are good candidates as either oxygen ion conductors or proton conductors used for ITSOFCs. 3) The effect of NiO on the sintering behaviors, morphologies and conductivities of BZCY532 based electrolytes were systematically investigated. According to the achieved results, it can be concluded that the dense BZCY532B ceramics (NiO was added during ball-milling before a powder mixture calcination) show an enhanced oxygen and proton conductivity. Also, that BZCY532A (NiO was added after a powder mixture calcination) and BZCY532N (No NiO was added in the whole preparation procedures) showed lower values. In addition, dense BZCY532B and BZCY532N ceramics showed only small electronic conductivities, when the testing temperature was lower than 800 ℃. However, the BZCY532A ceramics revealed an obvious electronic conduction, when they were tested in the range of 600 ℃ to 800 ℃. Therefore, it is preferable to add the NiO powder during the BZCY532 powder preparation, which can lower the sintering temperature and also increase the conductivity. 4) Dense BZCY532 ceramics were successfully prepared by using the Spark Plasma Sintering (SPS) method at a temperature of 1350 ℃ with a holding time of 5 min. It was found that a lower sintering temperature (&lt; 1400 ℃) and a very fast cooling rate (&gt; 200 ℃/min) are two key parameters to prepare dense BZCY532 ceramics. These results confirm that the SPS technique represents a feasible and cost-effective sintering method to prepare dense Ce-containing BaZrO3-BaCeO3 based proton conductors. 5) Finally, a preliminary study for preparation of Ce0.8Sm0.2O2-δ (SDC) and BZCY532 basedcomposite electrolytes was carried out. The novel SDC-BZCY532 based composite electrolytes were prepared by using the powder mixing and co-sintering method. The sintering behaviors, morphologies and ionic conductivities of the composite electrolytes were investigated. The obtained results show that the composite electrolyte with a composition of 60SDC-40BZCY532 has the highest conductivity. In contrast, the composite electrolyte with a composition of 40SDC-60BZCY532 shows the lowest conductivity. In summary, the results show that BaZrO3-BaCeO3 based proton-conducting ceramic materials represent very promising materials for future ITSOFCs electrolyte applications. / <p>QC 20150423</p>
12

Stabilité et vieillissement des études de nickelates base praséodyme comme cathodes pour oxyde solide piles à combustible / Stability and ageing studies of praseodymium-based nickelates as cathodes for Solid Oxide Fuel Cells

Vibhu, Vaibhav 12 February 2016 (has links)
Ce travail de thèse est consacré à l’étude des nickelates La2-xPrxNiO4+δ, comme nouveaux matériauxde cathodes pour piles à combustible haute température, SOFC, et en particulier à la caractérisationde leur stabilité chimique et leur comportement en fonctionnement. En effet, du fait de leurpropriété de conduction mixte ionique et électronique, MIEC, les nickelates de structure typeK2NiF4, Ln2NiO4+δ (Ln = La, Pr, Nd), correspondant au terme n = 1 de la série de Ruddlesden-Popper (An+1MnO(3n+1)), sont des matériaux prometteurs pour des fonctionnements à températureintermédiaire, IT-SOFC (T < 800 °C). Compromis entre la stabilité chimique de La2NiO4+δ et lestrès bonnes performances électrochimiques de Pr2NiO4+δ, les phases La2-xPrxNiO4+δ, ont étésynthétisées et leurs propriétés physico-chimiques, de transport et électrochimiques ont étédéterminées. L’étude approfondie des caractéristiques des électrodes par spectroscopied’impédance en cellules symétriques a été réalisée à courant nul et sous polarisation anodique etcathodique sur des périodes d’un mois. De façon surprenante, même après la dissociation complètede Pr2NiO4+δ en PrNiO3-δ, Pr4Ni3O10+δ et Pr6O11, la résistance de polarisation ne montre pas dechangement significatif. L’étude de PrNiO3-δ et Pr4Ni3O10+δ, comme matériau de cathode pour pilesà combustible, démontre l’excellent comportement de la phase Pr4Ni3O10+δ et ceci en cellulesymétrique (Rp (Pr4Ni3O10+δ) = Rp (Pr2NiO4+δ) = 0.15 Ω.cm² à 600 ° C) et cellule complète (1.6W.cm-2 at 800 °C). / This PhD work is dedicated to stability and ageing studies of Praseodymium based nickelates ascathodes for Solid Oxide Fuel Cells (SOFCs). With this respect Ln2NiO4+δ (Ln=La, Pr or Nd)compounds with the K2NiF4 type structure act as alternative cathode materials for IT-SOFC due totheir mixed ionic and electronic conductivity (i.e. MIEC properties). Pr2NiO4+δ shows excellentelectrochemical properties at intermediate temperature (i.e. low polarization resistance Rp value, Rp= 0.03 Ω.cm² at 700 °C), while La2NiO4+δ exhibits higher chemical stability. So, the properties ofLa2-xPrxNiO4+δ nickelates were investigated with the aim to find best compromise between chemicalstability and electrochemical performances. After synthesis, the physical and chemical properties aswell as their transport and electrochemical properties have been determined. Measurements of thepolarization resistance of symmetrical half-cells have been carried out by impedance spectroscopy.Then, the chemical stability and the electrochemical performance of the materials have been studiedfor duration up to one month. As an interesting point, even after complete dissociation of Pr2NiO4+δinto PrNiO3-δ,Pr4Ni3O10+δ and Pr6O11, the polarization resistance does not show significant change.So finally, two new materials PrNiO3-δ and Pr4Ni3O10+δ were investigated as SOFCs cathodeshowing very promising results for Pr4Ni3O10+δ in symmetrical cell (Rp (Pr4Ni3O10+δ) = Rp(Pr2NiO4+δ) = 0.15 Ω.cm² à 600 ° C) and complete cell (1.6 W.cm-2 at 800 °C).