Conventional liquid lubricants are faced with limitations under extreme cyclic operating conditions, such as in applications that require lubrication when changing from atmospheric pressure to ultrahigh vacuum and ambient air to dry nitrogen (e.g., satellite components), and room to elevated (>500°C) temperatures (e.g., aerospace bearings). Alternatively, solid lubricant coatings can be used in conditions where synthetic liquid lubricants and greases are not applicable; however, individual solid lubricant phases usually perform best only for a limited range of operating conditions. Therefore, solid lubricants that can adequately perform over a wider range of environmental conditions are needed, especially during thermal cycling with temperatures exceeding 500°C. One potential material class investigated in this dissertation is lubricious oxides, because unlike other solid lubricant coatings they are typically thermodynamically stable in air and at elevated temperatures. While past studies have been focused on binary metal oxide coatings, such as ZnO, there have been very few ternary oxide and no reported quaternary oxide investigations. The premise behind the addition of the third and fourth refractory metals Ti and Zr is to increase the number of hard and wear resistant phases while maintaining solid lubrication with ZnO. Therefore, the major focus of this dissertation is to investigate the processing-structure-tribological property relations of composite ZnO, TiO2 and ZrO2 phases that form ternary (ZnTi)xOy and quaternary (ZnTiZr)xOy nanocrystalline coatings. The coatings were processed by atomic layer deposition (ALD) using a selective variation of ALD parameters. The growth structure and chemical composition of as-deposited and ex situ annealed ternary and quaternary oxide coatings were studied by combined x-ray diffraction/focused ion beam microscopy/cross-sectional transmission electron microscopy, and x-ray photoelectron spectroscopy/Auger electron spectroscopy, respectively. It was determined that the structure varied from purely nanocrystalline (ternary oxides) to composite amorphous/nanocrystalline (quaternary oxides) depending on ALD parameters and annealing temperatures. In particular, the ZnTiO3 ilmenite phase with (104) textured nanocolumnar grains, exhibiting high stacking fault/partial dislocation densities >1012/cm2, was responsible for the excellent tribological behavior. Steady-state sliding friction coefficients down to 0.12 in humid air and 0.2 in dry nitrogen were measured along with sliding and fretting wear factors in the range of 10-6 to 10-7 mm3/N·m, even after ex situ annealing to 550°C. Additionally, the quaternary oxide phase Zn(Ti,Zr)O3 in solid solution exhibited a low fretting wear rate of 1x10-6 mm3/N·m. In contrast, certain phases, such as Zn2TiO4 cubic spinel, that form at annealing temperatures >550°C were responsible for high friction and wear. Mechanistic studies using the above techniques revealed low friction and wear-reducing surfaces and subsurfaces were due to different velocity accommodation modes (VAM). In the case of the ternary system, sliding-induced plastic deformation was possible when ZnTiO3 (104) stacking faults, bordered by partial dislocations, serve as a pathway for the dislocations to glide parallel to the sliding direction and hence achieve low friction and wear via an intrafilm shear VAM. It was evident that the individual nanocolumnar ZnTiO3 grains were plastically sheared as opposed to being fractured during wear. Conversely for the quaternary system, an interfacial sliding VAM between the counterface and a mechanically mixed layer (tribofilm) composed of the refined coating and counterface material, that also served as a source for the formation of cylindrical rolls, was responsible for wear reduction. Therefore, these lubricious oxides are a potential candidate for solid lubrication at high temperatures (up to 550 °C) and in space environments.

The future energy demand will require a change in the current energy supply. In this regard, the production of hydrogen by photoelectrochemical solar cells is a promising alternative because the fuel is obtained from water and, importantly, its combustion is free of carbon. Many metal oxides, including those having a complex stoichiometry (i.e. ternary oxides) behave as semiconductors and present good stability in aqueous environments, making them attractive candidates for water splitting devices. This thesis focuses on the preparation and study of ternary metal oxide materials as photoelectrodes for water splitting, with emphasis on photocathodes. These materials must meet the requirements for a practical device: low cost, non-toxicity, made of Earth abundant elements, environmentally friendly, etc. The thesis also aims at the study of strategies to improve their photoelectrochemical response. lt comprises the investigation of the kinetics of hydrogen generation reaction and the characteristics of the electrode solution interface by photoelectrochemical impedance spectroscopy. The main points can be summarized as: (i) the effect of an electrochemical oxidative pretreatment in CuFe2Ü4 photocathodes (ii) the investigation of water splitting mechanisms in CaFe2Ü4 photocathodes, (iii) the effect of metal doping in LaFeO3 photocathodes (iv) the study of the photoelectrochemistry of compact and nanoparticulate YFeO3 photocathodes and (v) the effect of a reductive electrochemical treatment in NiTiO3 photoanodes, and comparison with the effect of the treatment in anatase electrodes.