Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-05-12Bitstream added on 2014-06-13T20:58:53Z : No. of bitstreams: 1 saavedra_gsfa_me_sjc.pdf: 2452196 bytes, checksum: b3f2463bbb388a1fe5fbb2276e959c7e (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi avaliar três hipóteses: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) associação entre o do processo de neutralização e a limpeza sônica melhora a resistência de união. Confeccionou-se 32 blocos cerâmicos (VM7 VITA Zahnfabrik), os quais foram duplicados em resina composta (W3D Master). Os resultados deste estudo confirmaram que: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) a limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) a associação entre o processo de neutralização e a limpeza sônica melhora a resistência de união. / This study evaluated three hypotheses: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. The present results confirmed that: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-12-11Bitstream added on 2014-06-13T19:05:09Z : No. of bitstreams: 1 saavedra_gsfa_dr_sjc.pdf: 1086992 bytes, checksum: 75c209bde5e5e11f3fb1185fe635e9ab (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi avaliar cinco hipóteses: a) o condicionamento ácido diminui a resistência à flexão de uma cerâmica feldspática; b) a cimentação aumenta os valores de resistência à flexão de uma cerâmica feldspática; c) o processo de neutralização dos precipitados do ácido fluorídrico diminui os valores de resistência à flexão de uma cerâmica feldspática; d) a limpeza sônica (ultra-som) com água deionizada dos precipitados do ácido fluorídrico, formados sobre a superfície cerâmica após o condicionamento ácido, aumenta os valores de resistência à flexão de uma cerâmica feldspática; e) a associação entre o processo de neutralização dos precipitados do ácido fluorídrico e a limpeza sônica melhora a resistência à flexão de uma cerâmica feldspática. Foram confeccionadas 60 barras cerâmicas (20x4x1.2mm) (VM7 VITA Zahnfabrik). Cada barra cerâmica (1face) (exceção G1) foi condicionada (20s) com AF10% (Dentsply), seguida pela lavagem jato ar-água (60s) e secagem. Foram selecionadas aleatoriamente e separadas em 6 grupos(n=10): G1 - Controle (sem tratamento); G2 - condicionamento ácido apenas; G3 – o silano(Porcelain Primer,BISCO) foi aplicado na superfície cerâmica seguido da cimentação resinosa (Rely X ARC/3M); G4 – as barras foram imersas (40s) em solução supersaturada de bicarbonato de sódio, lavadas jato ar-água por (5s) e secas antes da aplicação do silano e cimentação; G5 - limpeza sônica (4min), silano e cimentação; G6 - associação da neutralização e limpeza sônica, seguido da silanização e cimentação. Após armazenagem (água destilada/sete dias a 37ºC), cada conjunto cerâmica/cimento) foi levado ao dispositivo de ensaio, sendo este acoplado em uma máquina de ensaios universal (EMIC) com célula de carga de 10Kgf, velocidade de 1,0mm/min e submetidos ao ensaio mecânico de flexão 3 pontos... / The purpose of this study was to evaluate five hypotheses: a) hydrofluoric acid etching decreases the flexural strength of a feldspathic porcelain; b) cementation increases the flexural strength of a feldspathic porcelain; c) the neutralization process of hydrofluoric acid precipitates decreases the flexural strength of a feldspathic porcelain; d) hydrofluoric acid precipitates cleaning with ultrasonic bath in deionized water, formed on the ceramic surface after acid etching, increases flexural strength values of a feldspathic porcelain; e) the association between the neutralization process of the hydrofluoric acid precipitated and ultrasonic sonic cleaning improves the flexural strength of a feldspathic porcelain. Sixty ceramic bars (20x4x1.2mm) (VM7 VITA Zahnfabrik) were made and each one (1 surface) (except G1) was etched (20s) with HF10% (Dentsply), followed by water spray (60s) and drying. The specimens were randomly divided into 6 groups (n=10): G1 - Control (no treatment); G2 – hydrofluoric acid; G3 – silane(Porcelain Primer,BISCO) was applied on porcelain surface followed adhesive cementation (Rely X ARC/3M); G4 – the bars were immersed on a oversaturated sodium bicarbonate solution (40s), washed by water spray (5s) and drying before silane application and cementation; G5 – ultrasonic cleaning (4min), silane and cementation; G6 – association between neutralization and ultrasonic cleaning, followed by silanization and cementation. After storage (distillated water/ 7 days at 37ºC), each set (ceramic/cement) was carry to test device, which was mounted in universal test machine (EMIC) with a load cell of 10 Kgf, crosshead speed of 1,0mm/min, and submitted to the three-point bending mechanical test (immersed on water at 37 ºC). The flexural strength values and standard deviation (MPa) of the groups were: G1: 73,79±5,83a; G2: 60,65±10,07b; G3: 85,10±12,40a; G4: 80,91± ... (Complete abstract click electronic access below)

Orientador: Estevão Tomomitsu Kimpara / Banca: Rander Pereira Avelar / Banca: Tarcisio José de Arruda Paes / Resumo: O objetivo deste trabalho foi avaliar três hipóteses: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) associação entre o do processo de neutralização e a limpeza sônica melhora a resistência de união. Confeccionou-se 32 blocos cerâmicos (VM7 VITA Zahnfabrik), os quais foram duplicados em resina composta (W3D Master). Os resultados deste estudo confirmaram que: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) a limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) a associação entre o processo de neutralização e a limpeza sônica melhora a resistência de união. / Abstract: This study evaluated three hypotheses: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. The present results confirmed that: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. / Mestre

Description of Ultrasonic Cleaning technology. Description of Non-destructive testing technology process. Design of Ultrasonic Cleaning equipment. Design of equipment for the ultrasonic cleaning machine. Design of non-destructive testing equipment (Liquid Penetrant Inspection and Magnetic Testing). Feasibility study of designed technologies and supporting processes.

This master thesis studies the behaviour of two aluminium alloys in ultrasonic cleaning at two different intensities, as well as the effect of a cleaning solution, Formula 815 GD-NF on the same surface have been studied with respect to surface roughness and material composition. Methods like Light Optical Microscopy (LOM), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and 3D topography using white light interferometry (VSI) was used to study the surface and material composition. It was found that both the ultrasonic cleaning, as well as the solution itself both increase surface roughness of the samples. When crossing a threshold in ultrasonic intensity micro jet cavitation dislodge precipitates, or areas weakened by precipitate to form a large pit. And the following heat from the jet causes the surface to oxidise, becoming more brittle, and be broken up by other cavitation phenomena to cause rapid acceleration of surface roughness in an area originating from the pit.