Orientador: Maria do Carmo Gonçalves / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-27T15:15:24Z (GMT). No. of bitstreams: 1
Leite_LilianeSamaraFerreira_M.pdf: 4562587 bytes, checksum: 0ee5828360fc15cbd08b98c4070e5bd3 (MD5)
Previous issue date: 2015 / Resumo: Nesse trabalho, nanocristais de celulose (CNC) foram obtidos por hidrólise de fibras de algodão, utilizando-se três diferentes ácidos: ácido sulfúrico, clorídrico e fosfórico. Micrografias obtidas por microscopia eletrônica de varredura (SEM) e transmissão (TEM) confirmaram que as condições de hidrólise empregadas foram adequadas para isolar seus nanocristais. No entanto, foi também possível observar a presença de uma pequena fração de fibras não totalmente hidrolisadas em todas as amostras analisadas. Imagens de microscopia óptica por luz polarizada (PLM) revelaram que o processo de secagem por liofilização dos CNC conduz à formação de aglomerados com dimensões micrométricas. Modificações químicas nas superfícies dos CNC, empregando-se ácido acético e cloreto de hexanoíla, foram conduzidas com o objetivo de diminuir o seu caráter hidrofílico. As modificações foram confirmadas por espectroscopia na região do infravermelho e por imagens de PLM das suspensões dos CNC. Compósitos de acetato de celulose (CA), reforçados com CNC, foram preparados por extrusão, utilizando-se dois procedimentos para a incorporação da carga na matriz: mistura direta e masterbatch, sendo esse último conduzido na tentativa de evitar a etapa de liofilização, onde ocorre a formação de aglomerados de nanocristais. Ensaios mecânicos mostraram que não houve aumento significativo nas propriedades mecânicas para os compósitos preparados por mistura direta. Entretanto, compósitos preparados por masterbatch apresentaram aumento no módulo de Young em torno de 5% e 14%, para composições contendo 10 e 15 % nanocristais em massa, respectivamente. Esses resultados evidenciam a importância das condições de hidrólise para obtenção das nanopartículas, como também da escolha do método de preparação do compósito de forma a promover a menor formação de aglomerados e melhor dispersão da carga na matriz / Abstract: In this work, cotton fiber cellulose nanocrystals (CNC) were obtained by acid hydrolysis using three different acids: sulfuric acid, hydrochloric acid and phosphoric acid. Scanning (SEM) and transmission (TEM) electron micrographs confirmed that the acid hydrolysis conditions used were efficient to isolate their nanocrystals. However, in all samples analyzed, it was possible to observe the presence of some partially hydrolyzed fibers. Polarized Light Microscopy (PLM) showed that the freeze-drying process led to the formation of small CNC agglomerates with micron dimensions. CNC surface functionalization was carried out with the purpose of reducing the hydrophilic character, by using acetic acid and hexanoyl chloride. Chemical modifications at the surface were confirmed by infrared spectroscopy and the hydrophilic character decrease was confirmed by PLM images of the functionalized CNC. Cellulose acetate composites, reinforced with CNC, were obtained by melt extrusion using two techniques for the introduction of reinforcing agent: direct mixing and masterbatch. The latter were carried out prevent CNC agglomeration formation due to the freeze-drying process. Mechanical tests showed that there was no significant increase in of the composites prepared by direct mixing mechanical properties. However, composites prepared from masterbatch showed a 5% and 14% increase in Young's modulus for 10 and 15 wt% CNC content, respectively. These results show the importance of the hydrolysis conditions on the nanoparticle synthesis, as well as the choice of an appropriate reinforcing agent load method so as to avoid agglomeration and increase load dispersion in the matrix / Mestrado / Mestra em Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248727 |
| Date | 27 August 2018 |
| Creators | Leite, Liliane Samara Ferreira, 1988- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gonçalves, Maria do Carmo, 1957-, Lucas, Alessandra de Almeida, Morales, Ana Rita |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 108 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds