Orientador: Rosiane Lopes da Cunha / Texto em português e inglês / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-20T12:57:32Z (GMT). No. of bitstreams: 1
Picone_CarolinaSiqueiraFranco_D.pdf: 4074904 bytes, checksum: 1a2779daa118fabb35ba241a8f6bf16f (MD5)
Previous issue date: 2012 / Resumo: As nano partículas possuem grande potencial para a liberação controlada de bioativos, porém ainda são pouco exploradas na área de alimentos. Neste trabalho foi estudada a formação de nanopartículas a partir da autoagregação de surfactantes, associação surfactante-polissacarídeo e complexação eletrostática entre diferentes polissacarídeos, no caso, quitosana e gelana. A compreensão das interações moleculares responsáveis pela formação das partículas e o conhecimento das variáveis que afetam sua formação permitem predizer e controlar suas propriedades. Tais interações dependem fortemente das características de cada macromolécula, como flexibilidade, estado conformacional e densidade de cargas que são diretamente afetadas pelas condições físico-químicas do meio como pH, força iônica e temperatura. Por isso, este trabalho foi dividido em três etapas. (I) Inicialmente foi avaliado o comportamento em solução dos polissacarídeos utilizados posteriormente para a formação de complexos. Os efeitos do pH e da temperatura nas características reológicas e no estado conformacional de soluções puras de gelana e quitosana foram estudados. A agregação da gelana foi mais sensível às alterações do meio que a quitosana. (II) Na segunda etapa, nanopartículas foram formadas por autoassociação de polissorbatos na presença de quitosana. A influência do comprimento da cauda hidrofóbica do surfactante e do pH do meio nas propriedades das partículas foi estudada por espalhamento de luz, reologia, condutivimetria e microscopia de luz polarizada. O tamanho e estrutura das partículas formadas pelo surfactante de menor cadeia hidrofóbica foram mais favoráveis à associação com a quitosana. O pH do meio (3,0 ou 6,7) não influenciou de maneira significativa as características das partículas. O efeito da concentração de quitosana na estrutura e tamanho de partículas foi analisado. Maiores concentrações levaram a viscosidades mais elevadas, impedindo a agregação das micelas e formando partículas menores. (III) No terceiro estudo, nanopartículas foram obtidas pela complexação eletrostática de gelana e quitosana. Os efeitos da razão de concentração de cada polissacarídeo, do tempo de estocagem a 25 °C e da presença de um surfactante nãoiônico (polissorbato) no tamanho, carga e quantidade de partículas formadas foram avaliados. Devido à menor densidade de carga e flexibilidade da gelana, maior quantidade deste polissacarídeo foi necessária para obtenção de partículas neutras. De forma geral, as partículas apresentaram aumento de tamanho ao longo das primeiras 100 horas após o preparo e não foram observadas mudanças significativas das propriedades das partículas devido à adição de surfactante. O método de preparo das amostras também foi estudado. Partículas preparadas pela mistura das soluções de polissacarídeos em dois passos foram consideravelmente maiores que as preparadas pela mistura em uma única etapa. Este trabalho confirmou a possibilidade de formação de nanopartículas promissoras para a encapsulação de bioativos em alimentos a partir da associação de biopolímeros e surfactantes, cujas propriedades poderiam ser moduladas em função da composição e condições de processo / Abstract: Nanoparticles are promising vehicles for bioactive delivery, but their potential has not been fully explored by the food industry. This work studied the formation of nanoparticles by self-assembly of surfactants, polysaccharide-surfactant association, and electrostatic complexes formed by different polysaccharides, especially chitosan and gellan gum. The knowledge of molecular interactions and the variables that affect particle formation allows predicting and controlling the properties of nanoparticles. These interactions depend on the characteristics of each macromolecule such as conformation, charge density and flexibility, which are affected by the physicol-chemical properties of the solution, such as pH, ionic strength and temperature. This work was divided in three parts: (I) Firstly it was studied the behaviour of each polysaccharide alone. The influence of the pH and temperature on the rheological properties and structural conformation of the pure gellan and chitosan samples was determined. Gellan aggregation was more strongly affected by such variables than chitosan. (II) In the second part, nanoparticles were obtained by polysorbate-chitosan association. The effect of the length of surfactant tail and the solution pH on the particle properties was studied by dynamic light scattering, rheological and conductivity measurements and polarizing microscopy. The size and structure of nanoparticles composed by the shorter surfactant were more appropriated to chitosan assembly. The pH (6.7 or 3.0) did not affect significantly the particle properties. The effects of chitosan concentration on particle structure and size were studied. Greater chitosan concentration led to smaller particles due to the increase in viscosity values which prevented micelles aggregation. (III) In the third study nanoparticles were produced by electrostatic complexation of chitosan and gellan gum. Particle size, charge density, stability and complexes number were evaluated as a function of polysaccharide concentration, chitosan:gellan ratio and the presence of a non-ionic surfactant. Due to the stiffness and low charge density of gellan gum, a greater amount of such polysaccharide was necessary to obtain neutral particles. Overall particles showed an increase in size during 100 hours of storage at 25 °C, but no significant changes on particle properties were observed due to surfactant addition. The methodology of particle preparation was also evaluated. Particles prepared by 2 mixing steps were markedly larger than those prepared by mixing polysaccharides in a single step (all together). This work showed that it is possible to produce nanoparticles with promising application on bioactive delivery by biopolymer-surfactant association, since their properties could be modulated as a function of composition and process conditions / Doutorado / Engenharia de Alimentos / Doutor em Engenharia de Alimentos
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/254194 |
Date | 20 August 2018 |
Creators | Picone, Carolina Siqueira Franco, 1983- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Cunha, Rosiane Lopes da, 1967-, Cavallieri, Angelo Luiz Fazani, Ushikubo, Fernanda Yumi, Torre, Lucimara Gaziola de la, Telis, Vania Regina Nicoletti |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Alimentos, Programa de Pós-Graduação em Engenharia de Alimentos |
Source Sets | IBICT Brazilian ETDs |
Language | Multilíngua, poreng |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 151 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0121 seconds