Avaliação da influência do calor e da luz solar na densidade de filmes radiográficos impressos / Evaluation of the influence of heat and sunlight on density of printed radiographic films

Orientador: Frab Norberto Bóscolo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T13:39:06Z (GMT). No. of bitstreams: 1
Frazao_MarcoAntonioGomes_D.pdf: 4262109 bytes, checksum: 0e3256f8a0dd02738990d526d5a2329b (MD5)
Previous issue date: 2012 / Resumo: Com este estudo, teve-se a proposta de avaliar a modificação da densidade de 4 cores (branco, cinza claro, cinza escuro e preto) em filmes radiográficos impressos por duas tecnologias dry seca: termográfica (AGFA) e fototermográfica (KODAK). Para isso, foi utilizada uma amostra formada por 18 grupos com 6 corpos de prova para cada uma das tecnologias de impressão totalizando um experimento com 216 corpos de prova submetidos às temperaturas de 40ºC, 60ºC e 80ºC, pelos tempos de 30, 60 e 120 minutos com e sem a exposição solar. Nestes foram realizadas analises densitométricas antes e depois da exposição aos fatores estudados e os dados obtidos submetidos aos testes estatísticos de: Kruskal Wallis, Mann-Whitney e Wilcoxon para dados pareados com nível de significância de 5%. Pôde-se observar que as cores avaliadas impressas no filme pela tecnologia termográfica (AGFA) modificam sua densidade a partir de combinações de exposição a 60ºC e 120 minutos e a 80ºC e 30 minutos sem a exposição ao sol e a partir de 40ºC e 30 minutos com exposição solar, e no filme impresso pela tecnologia fototermográfica (KODAK) modifica sua densidade a 40ºC a partir de 30 minutos com e sem a exposição solar. Concluiu-se que o aumento da temperatura de armazenamento bem com a exposição à luz solar modificam a densidade dos filmes radiográficos impressos pelas tecnologias dry seca avaliadas / Abstract: The purpose of this study was to evaluate the density modification of 4 colors (white, light gray, dark gray and black) in films printed by two dry technologies: thermographic (AGFA) and photothermographic (KODAK). A sample consisting of 18 groups with six specimens per printing technologies was used, totaling an experiment of 216 evaluated specimens when subjected to temperatures of 40°C, 60°C and 80°C, for periods of 30, 60 and 120 minutes with and without sunlight exposure. These specimens were submitted to densitometric analysis before and after exposure to the studied factors and data were subjected to the following statistical tests: Kruskal Wallis, Mann-Whitney and Wilcoxon for paired data. It was observed that the evaluated colors printed on the film by thermographic technology (AGFA) modify their density at exposures to 60°C and 120 minutes, and without sunlight exposure at the temperature of 80°C after 30 minutes, and with sunlight exposure from 40°C and 30 minutes, and the film printed by photothermographic technology (KODAK) modifies its density at 40°C from 30 minutes with and without sunlight exposure. It was concluded that the increase of storage temperature and sunlight exposure modify the density of radiographic films printed by dry technologies / Doutorado / Radiologia Odontologica / Doutor em Radiologia Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288919
Date22 August 2018
CreatorsFrazão, Marco Antonio Gomes, 1975-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Boscolo, Frab Norberto, 1942-, Perez, Flávia Maria de Moraes Ramos, Chilvarquer, Israel, Haiter Neto, Francisco, Daruge Junior, Eduardo
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Radiologia Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format54 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds