Bragg reflection waveguides (BRW) or one-dimensional photonic bandgap structures have been demonstrated for phase-matching chi(2) nonlinearities in AlxGa1-xAs. The method exploits strong modal dispersion of a Bragg mode and total internal reflection modes co-propagating inside the waveguide. It is shown that phase-matching is attained among the lowest order modes of interacting harmonics, which allows maximizing the utilization of harmonics powers for nonlinear interactions.
As our first demonstration, we report second-harmonic generation (SHG) of a 2-ps telecommunication pump in a 2.4 mm long slab BRW. The conversion efficiency is estimated as 2.0 %/W.cm^2 with a generated SH power of 729 nW. This efficiency has been considerably improved by introducing lateral confinement of optical modes in ridge structures. Characterizations denote that efficiency of SHG in ridge BRWs can increase by over an order of magnitude in comparison to that of the slab device. Also, we report continuous-wave SHG in BRWs. Using a telecommunication pump with a power of 98 mW, the continuous-wave SH power of 23 nW is measured in a 2.0 mm long device.
Significant enhancements of chi(2) interactions is obtained in the modified design of matching-layer enhanced BRW (ML-BRW). For the first time, we report type-II SHG in ML-BRW, where the second-harmonic power of 60 µW is measured for a pump power of 3.3 mW in a 2.2 mm long sample. Also, we demonstrate the existence of type-0 SHG, where both pump and SH signal have an identical TM polarization state. It is shown that the efficiency of the type-0 process is comparable to type-I and type-II processes with the phase-matching wavelengths of all three interactions lying within a spectral window as small as 17 nm. ML-BRW is further reported for sum-frequency and difference-frequency generations. For applications requiring high pump power, a generalized ML-BRW design is proposed and demonstrated. The proposed structure offsets the destructive effects of third-order nonlinearities on chi(2) processes when high power harmonics are involved. This is carried out through incorporation of larger bandgap materials by using high aluminum content AlxGa1-xAs layers without undermining the nonlinear conversion efficiency.
Theoretical investigations of BRWs as integrated sources of photon-pairs with frequency correlation properties are discussed. It is shown that the versatile dispersion properties in BRWs enables generation of telecommunication anti-correlated photon-pairs with bandwidth tunablity between 1 nm and 450 nm.
Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/29655 |
Date | 29 August 2011 |
Creators | Abolghasem, Payam |
Contributors | Helmy, Amr S. |
Source Sets | University of Toronto |
Language | en_ca |
Detected Language | English |
Type | Thesis |
Page generated in 0.0013 seconds