Dissertação (mestrado)—Universidade de Brasília, Instituto de Química, 2015. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2016-05-16T15:31:15Z
No. of bitstreams: 1
2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2016-07-21T18:34:08Z (GMT) No. of bitstreams: 1
2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Made available in DSpace on 2016-07-21T18:34:08Z (GMT). No. of bitstreams: 1
2015_DanielAndradeMoreira.pdf: 5936294 bytes, checksum: b47ddee8b1d7d84f7efbd5f3de0d31e3 (MD5) / Este trabalho baseia-se na síntese e caracterização de compósitos a partir de nanocristais de NaYF4:Eu ou NaYF4:Tb e nanopartículas de carbono conhecidas como carbon-dots ou carbon-nanodots, também chamados de C-Dots, afim de desenvolver e estudar novos materiais luminescentes. Os compósitos são sintetizados por dois métodos, via coprecipitação, onde foram obtidos materiais nanométricos com diâmetros a partir de 25 nm, com baixa cristalinidade, tempos de vida próximos de 1 ms e rendimentos quânticos abaixo de 1%, para a via hidrotermal, foram obtidos compósitos micrométricos com diâmetro a a partir de 300 nm, cristais de fase hexagonal tempos de vida próximos a 1 ms e rendimentos quânticos abaixo de 1%, os compósitos coprecipitados apresentaram luminescência superior aos tratados hidrotermalmente. Houve variação de concentração de C-Dots nas sínteses, visando morfologias e tamanhos distintos e a relação destes com as propriedades luminescentes do material, maiores concentrações de C-Dots indicaram maior agregação dos compósitos, baixa intensidade luminescente e menores tempos de vida, baixas concentrações geraram compósitos dispersos, com intensidade luminescente e tempos de vida superiores as demais concentrações. / This work is about the synthesis and characterization of composites from nanocrystals of NaYF4:Eu or NaYF4:Tb and nanoparticles of carbon, known as carbon-dot or carbon-nanodots, also called of C-Dots to develop and study new luminescent materials. The composites are sintherized by two differents methods co-precipitation and hydrothermal. Using co-precipitation the materials obtained are nanomerics, with diameter from 25 nm, They have low crystallinity and lifetime next to 1 ms and quantum yeld bellow 1%. Using the hydrothermal method the materials obtained are micrometric composites of hexagonal phase, with diameter from 300 nm, lifetime next to 1 ms and quantum yeld bellow 1%. The co-precipitates composts shows more luminescence than hydrothermal composts. To obtained sizes and differents morphologies and to determine the relation of this and the luminescence properties the concentration of C-Dots in the sinthezys had been varied. Higher concentrations of C-Dots indicates greater aggregation of composites, low luminescent intensity, shorter lifetime and low concentration produced dispersed composites, with intense luminescence and higher lifetime than with others concentration.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/20947 |
Date | 14 December 2015 |
Creators | Moreira, Daniel de Andrade |
Contributors | Silveira Neto, Brenno Amaro da, Rodrigues, Marcelo Oliveira |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0011 seconds