Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2016. / Made available in DSpace on 2016-09-20T04:26:14Z (GMT). No. of bitstreams: 1
341092.pdf: 7453597 bytes, checksum: 8acacedccc72534f3475caa2270543b6 (MD5)
Previous issue date: 2016 / Este estudo avaliou o grau de conversão (DC) pela técnica FTIR-ATR e a nanodureza pela técnica de Oliver e Phar de um cimento resinoso de cura dual (RelyX Ultimate, 3M ESPE) fotoativado através de diferentes espessuras da resina nanocerâmica (NCR) LAVA Ultimate (3M ESPE) (0mm, 1mm, 2mm e 5mm), com diferentes tempos de fotoativação (20s e 40s) à uma irradiação constante de 1100mW/cm², imediatamente após a fotoativação e após 24 horas. Os dados coletados foram analisados por uma análise de variância de 3 fatores para medidas repetidas e os efeitos das interações foram analisados pelo teste de Sidak. Para o DC, os resultados mostraram que todos os fatores influenciam significativamente (p<0,001), sendo os maiores graus de conversão são obtidos após 24 horas (p<0,001), com a menor espessura de NCR (p<0,001) e fotoativação por 40s (p<0,001). Também ficou constatada a interação dupla entre todos estes fatores (p<0,001), mas o resultado da interação tripla foi não significativo (p=0,104). Quanto à nanodureza, todos os fatores estudados influenciaram a nanodureza (p<0,001), assim como a interação dupla entre eles (p<0,001) e a interação tripla entre os fatores (p<0,001).<br> / Abstract : This study evaluated the degree of conversion (DC) by FTIR-ATR technique and nanohardness by Oliver and Phar technique of a dual cured resin cement (RelyX Ultimate, 3M ESPE) photoactivated through different thicknesses of nanoceramic resin (NCR) LAVA Ultimate (3M ESPE) (0 mm, 1 mm, 2 mm and 5 mm) with different curing times (20s and 40s) at a constant irradiation 1100mW / cm², immediately after curing and after 24 hours. The collected data was analyzed by 3-way ANOVA repeated measures and the effects of the interactions were analyzed by Sidak test. DC results were significant to all factors (p <0.001), and the highest degrees of conversion are obtained after 24 hours (p <0.001), low thickness NCR (p <0.001) and 40 seconds light cure (p <0.001). It was also found double interaction between all of these factors (p <0.001), but the result of the triple interaction was not significant (p = 0.104). Nanohardness was influenced by all these factors (p <0.001), as well as double interaction between them (p <0.001) and triple interaction between factors (p <0.001).
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/167845 |
| Date | January 2016 |
| Creators | Chraim, Gustavo Georges de Mattos |
| Contributors | Universidade Federal de Santa Catarina, Lopes, Guilherme Carpena, Araújo, Élito |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 77 p.| il., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds