Experimental evaluation of the durability of fly ash-based geopolymer concrete in the marine environment

The construction industry is increasingly turning to the use of environmentally friendly materials in order to meet the sustainable aspect required by modern infrastructures. Consequently, for the last two decades, the expansion of this concept, and the increasing global warming have raised concerns on the extensive use of Portland cement due to the high amount of carbon dioxide gas associated with its production. The development of geopolymer concretes offers promising signs for a change in the way of producing concrete. However, to seriously consider geopolymer binders as an alternative to ordinary Portland cement, the durability of this new material should be evaluated in any comparative analysis. The main purpose of this study was to evaluate the durability characteristics of low calcium fly ash-based geopolymer concretes subjected to the marine environment, compared to ordinary Portland cement concrete with similar exposure. To achieve this goal, 8 molar geopolymer, 14 molar geopolymer and ordinary Portland cement concrete mixes were prepared and tested for exposure in seawater. Compressive strengths in the range of 2900 to 8700 psi (20-60 MPa) were obtained. The corrosion resistance performance of steel-reinforced concrete beams, made of these mixes, was also studied, using an accelerated electrochemical method, with submergence in salt water. The test results indicated that the geopolymer concrete showed excellent resistance to chloride attack, with longer time to corrosion cracking, compared to ordinary Portland cement concrete. / by Jean-Baptiste Edouard. / Thesis (M.S.C.S.)--Florida Atlantic University, 2011. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2011. Mode of access: World Wide Web.

Identiferoai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_3634
ContributorsEdouard, Jean-Baptiste., College of Engineering and Computer Science, Department of Civil, Environmental and Geomatics Engineering
PublisherFlorida Atlantic University
Source SetsFlorida Atlantic University
LanguageEnglish
Detected LanguageEnglish
TypeText, Electronic Thesis or Dissertation
Formatxiv, 116 p. : ill. (some col.), electronic
Rightshttp://rightsstatements.org/vocab/InC/1.0/

Page generated in 0.0017 seconds