Influência da composição e cor de cerâmicas na transmissão de luz e no grau de conversão de cimentos resinosos de ativação dual / Effect of ceramic composition and shade in light transmission and degree of conversion of dual-cure resin cements

O objetivo desta pesquisa foi avaliar a transmitância de diferentes tipos e cores de cerâmicas e seus efeitos no grau de conversão (GC) de dois tipos de cimentos resinosos com modo de polimerização dual. Foram confeccionadas 60 pastilhas com a cerâmica IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) e divididas em 3 grupos: LT, MO e Z, com 20 pastilhas cada um. Nos grupos LT e MO, as pastilhas foram confeccionadas com a cerâmica de dissilicato de lítio de baixa translucidez (LT - low transluscency) e de média opacidade (MO - medium opacity), respectivamente. No grupo Z, as pastilhas foram confeccionadas em zircônia. Cada grupo foi subdividido em 5 subgrupos (n=4), de acordo com a cor da cerâmica: A2; A3,5; B2; C2; D3. No grupo LT, as pastilhas foram prensadas nas cores anteriormente citadas e, nos grupos MO e Z, as pastilhas foram, inicialmente, confeccionadas para simular infraestruturas e, posteriormente, receberem aplicação de cerâmica de revestimento IPS e.max Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) nas mesmas cores. O espectrofotômetro UV 1800 Shimadzu foi utilizado para medir a transmitância de cada espécime de cerâmica (2,0 mm de espessura). Para medir o GC, espécimes dos cimentos resinosos Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) e Rely X U200 (3M ESPE, St. Paul, MN, USA), com espessura de 100 μm, foram fotopolimerizados sob os discos de cerâmica por 40 s. Espécimes dos cimentos fotoativados sem a interposição da cerâmica foram usados como grupo controle. A polimerização dos cimentos foi avaliada através da espectrometria no infravermelho com transformada de Fourier (FTIR) empregando o método de reflexão atenuada total (ATR) imediatamente após a fotopolimerização. Os resultados foram submetidos aos testes ANOVA a 1 critério e Teste de Tukey (α=5%). Os valores de transmitância foram inferiores a 1%, sendo que as do grupo LT apresentaram, em geral, os maiores valores de transmitância, seguidos dos grupos MO e Z. O GC do cimento Variolink II não sofreu influência da interposição da pastilha de cerâmica. Para o cimento Rely X U200, a interposição de alguns tipos/cores de cerâmica (LT A3,5; MO A2; MO A3,5 e Z A3,5) diminuíram o GC em relação ao grupo controle. Concluiu-se que os valores de transmitância e GC foram influenciados pelos tipos/cores de cerâmica. Entretanto, somente o grupo formado pela cerâmica de dissilicato de lítio LT, usando o Rely X U200, apresentou correlação negativa entre transmitância e GC. / The aim of the present study was to evaluate the transmittance of different ceramic types and shades and their effects on the degree of conversion (DC) of two dual-cure resin cements. Sixty discs were fabricated with IPS e.max ceramic (Ivoclar Vivadent, Schaan, Liechtenstein) and divided into three groups (n= 20 in each group): LT, MO and Z. For LT and MO groups discs were fabricated with low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, respectively. Discs from Z group were manufactured of zirconia. Each group was divided into five subgroups (n = 4), according to the ceramic shade: A2; A3,5; B2; C2; D3. In the LT group, specimens were heat-pressed in shades cited above and in the MO and Z groups, the discs were initially fabricated as core materials and then veneered with veneer ceramic (IPS e.max Ceram, Ivoclar Vivadent, Schaan, Liechtenstein) in the same shades. A spectrophotometer UV-1800 Shimadzu was used to determine the transmittance percentage of each ceramic specimen (2.0-mm-thick). For DC measurements, the resin cements (Variolink II - Ivoclar Vivadent, Schaan, Liechtenstein and Rely X U200 - 3M ESPE, St. Paul, MN, USA) specimens (thickness: 100 μm) were photocured under the ceramic discs (2.0-mm-thick) for 40 s. Specimens photocured without the ceramics discs were used as control group. ATR/FTIR spectrometry was used to evaluated the extent of polymerization for all cement specimens immediately after photocuring. The results were submitted to one-way ANOVA and Tukey test (α=5%). The transmittance percentage was less than 1% and the LT group had the highest transmittance values, followed by MO and Z groups. The %DC of Variolink II cement was not influenced by the ceramic disc interposition. For Rely X U200 cement, the interposition of some ceramics types/shades (LT A3,5, MO A2, MO A3,5 and Z A3,5) significantly decreased the %DC compared to control group. It was concluded that the transmittance values and %DC were influenced by the ceramics types/shades. However, only the LT group, using the Rely X U200, showed a negative correlation between transmittance and %DC.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-10032016-110136
Date14 September 2015
CreatorsLuana Menezes de Mendonça
ContributorsLuiz Fernando Pegoraro, Estevão Tomomitsu Kimpara, Pedro Cesar Garcia de Oliveira, Maria Cecilia Veronezi, Linda Wang
PublisherUniversidade de São Paulo, Ciências Odontológicas Aplicadas, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0015 seconds