Orientador: Mario Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-25T16:27:57Z (GMT). No. of bitstreams: 1
SouzaJunior_EduardoJoseCarvalhode_D.pdf: 1265761 bytes, checksum: 1e110af2f222e502411203feb253160f (MD5)
Previous issue date: 2014 / Resumo: O objetivo neste estudo foi analisar o efeito de diodos emissores de luz (LEDs) nas propriedades físicas, químicas, resistência da união (RU), adaptação marginal (AM) e na durabilidade de restaurações realizadas com adesivos experimentais contendo diferentes fotoiniciadores. Uma resina modelo contendo uma mistura de BisGMA/HEMA (60/40 em peso) e dimetil amino etil metacrilato (co-iniciador) foi preparada com os diferentes fotoiniciadores: CQ (Canforoquinona), PPD (1-Fenil-1,2-Propanodiona) e BAPO (Óxido bis-alquil fosfínico), além da associação entre eles. As amostras foram fotoativadas por duas fontes de luz LED, uma de 2° geração (Radii Cal, SDI) e outra de 3° geração (Bluephase G2, Ivoclar Vivadent). A irradiância foi aferida a partir de medidas em potênciômetro e a densidade energética foi padronizada em 48J/cm2. As propriedades avaliadas foram o grau de conversão (GC), cinética de polimerização (CI), análise da permeabilidade dentinária (PMD), sorção (SO) e solubilidade (SL), resistência flexural (RF), módulo flexural (MF) e amarelamento (YL). Para o teste de RU, o ensaio de microtração foi realizado em dentina plana de 70 molares humanos, avaliados após 24 horas e após 1 ano de armazenamento em água a 37ºC. A AM foi mensurada por meio de réplicas das margens superficial e interna de 70 molares humanos, analisadas em microscopia eletrônica de varredura (MEV). Os ensaios de GC, PMD, SO, SL, RF, MF e AM foram submetidos à análise de variância dois fatores, enquanto a RU foi submetida à análise de variância dois fatores (fotoiniciadores e fontes de luz), com medidas repetidas no tempo. Após, todas as médias foram comparadas pelo teste de Tukey ('alfa' = 5%). Os adesivos contendo os fotoiniciadores alternativos, em especial BAPO e BAPO/amina monstraram maior potencial de polimerização, evidenciado pela cinética de conversão. Ainda, os fotoiniciadores alternativos promoveram melhor selamento dentinário, sorção e solubilidade similares e propriedades físico-químicas com melhor desempenho quando comparados aos adesivos convencionais contendo CQ. Em relação à resistência de união, os adesivos contendo BAPO promoveram os melhores desempenhos em até um ano de degradação hidrolítica / Abstract: The aim of this study was to evaluate the effect of light emitting diodes (LEDs) on the physical-chemical properties, bond strength (BS) and marginal adaptation (MA) of experimental adhesives containing diferent photo-initiators. A model resin containing a mixture of BisGMA/HEMA (60/40 wt%) and DMAEMA (co-iniciator) was prepared using different photo-initiators: CQ (Camphorquinone), PPD (1-Phenyl-1,2-Propanedione) e BAPO (Bisalquylphosphine oxide) and their association. The specimens were photoactivated by two LEDs, one monowave (Radii Cal, SDI) and other polywave (Bluephase G2, Ivoclar Vivadent). Irradiance was measured in potenciometer and the energy dose was standardized. The following properties were analyzed: degree of conversion (DC) and for the curing kinetics (CI), dentin permeability (DPM), water sorption (SO), water solubility (SL), flexural strength (FS), flexural modulus (FM) and yellowing (YL). For the BS test, the microtensile test was realized in 70 molars with planned dentin, immediately or after 1-year of water storage. The MA, superficial and internal marginal adaptation measurements were realized by epoxy replicas of the bonded margins using the scanning eléctron microscopy. DC, DPM, SO, SL, FS, FM and AM were submitted to a two-way ANOVA and BS to a two-way repeated measurement ANOVA. Next, the analyzes were submitted to the Tukey¿s test ('alfa' = 5%). The adhesives containing the alternative photoinitiators, such as BAPO and BAPO/amine showed a higher curing potential, promoted by the curing kinetics. Moreover, these alternative photoinitiators showed a better dentin sealing, with similar sorption and solubility values and high physical-mechanical properties when compared to the other groups based in CQ. In relation to the bond strength, the BAPO containing adhesives promoted higher performance even after 1-year of hydrolytic degradation / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288108 |
Date | 25 August 2018 |
Creators | Souza Júnior, Eduardo José Carvalho de, 1985- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sinhoreti, Mário Alexandre Coelho, 1969-, Briso, Andre Luiz Fraga, Guiraldo, Ricardo Danil, Correr Sobrinho, Lourenço, Lima, Adriano Fonseca de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
Source Sets | IBICT Brazilian ETDs |
Language | Inglês |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 85 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.084 seconds