Orientador: Mario Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-25T16:27:57Z (GMT). No. of bitstreams: 1 SouzaJunior_EduardoJoseCarvalhode_D.pdf: 1265761 bytes, checksum: 1e110af2f222e502411203feb253160f (MD5) Previous issue date: 2014 / Resumo: O objetivo neste estudo foi analisar o efeito de diodos emissores de luz (LEDs) nas propriedades físicas, químicas, resistência da união (RU), adaptação marginal (AM) e na durabilidade de restaurações realizadas com adesivos experimentais contendo diferentes fotoiniciadores. Uma resina modelo contendo uma mistura de BisGMA/HEMA (60/40 em peso) e dimetil amino etil metacrilato (co-iniciador) foi preparada com os diferentes fotoiniciadores: CQ (Canforoquinona), PPD (1-Fenil-1,2-Propanodiona) e BAPO (Óxido bis-alquil fosfínico), além da associação entre eles. As amostras foram fotoativadas por duas fontes de luz LED, uma de 2° geração (Radii Cal, SDI) e outra de 3° geração (Bluephase G2, Ivoclar Vivadent). A irradiância foi aferida a partir de medidas em potênciômetro e a densidade energética foi padronizada em 48J/cm2. As propriedades avaliadas foram o grau de conversão (GC), cinética de polimerização (CI), análise da permeabilidade dentinária (PMD), sorção (SO) e solubilidade (SL), resistência flexural (RF), módulo flexural (MF) e amarelamento (YL). Para o teste de RU, o ensaio de microtração foi realizado em dentina plana de 70 molares humanos, avaliados após 24 horas e após 1 ano de armazenamento em água a 37ºC. A AM foi mensurada por meio de réplicas das margens superficial e interna de 70 molares humanos, analisadas em microscopia eletrônica de varredura (MEV). Os ensaios de GC, PMD, SO, SL, RF, MF e AM foram submetidos à análise de variância dois fatores, enquanto a RU foi submetida à análise de variância dois fatores (fotoiniciadores e fontes de luz), com medidas repetidas no tempo. Após, todas as médias foram comparadas pelo teste de Tukey ('alfa' = 5%). Os adesivos contendo os fotoiniciadores alternativos, em especial BAPO e BAPO/amina monstraram maior potencial de polimerização, evidenciado pela cinética de conversão. Ainda, os fotoiniciadores alternativos promoveram melhor selamento dentinário, sorção e solubilidade similares e propriedades físico-químicas com melhor desempenho quando comparados aos adesivos convencionais contendo CQ. Em relação à resistência de união, os adesivos contendo BAPO promoveram os melhores desempenhos em até um ano de degradação hidrolítica / Abstract: The aim of this study was to evaluate the effect of light emitting diodes (LEDs) on the physical-chemical properties, bond strength (BS) and marginal adaptation (MA) of experimental adhesives containing diferent photo-initiators. A model resin containing a mixture of BisGMA/HEMA (60/40 wt%) and DMAEMA (co-iniciator) was prepared using different photo-initiators: CQ (Camphorquinone), PPD (1-Phenyl-1,2-Propanedione) e BAPO (Bisalquylphosphine oxide) and their association. The specimens were photoactivated by two LEDs, one monowave (Radii Cal, SDI) and other polywave (Bluephase G2, Ivoclar Vivadent). Irradiance was measured in potenciometer and the energy dose was standardized. The following properties were analyzed: degree of conversion (DC) and for the curing kinetics (CI), dentin permeability (DPM), water sorption (SO), water solubility (SL), flexural strength (FS), flexural modulus (FM) and yellowing (YL). For the BS test, the microtensile test was realized in 70 molars with planned dentin, immediately or after 1-year of water storage. The MA, superficial and internal marginal adaptation measurements were realized by epoxy replicas of the bonded margins using the scanning eléctron microscopy. DC, DPM, SO, SL, FS, FM and AM were submitted to a two-way ANOVA and BS to a two-way repeated measurement ANOVA. Next, the analyzes were submitted to the Tukey¿s test ('alfa' = 5%). The adhesives containing the alternative photoinitiators, such as BAPO and BAPO/amine showed a higher curing potential, promoted by the curing kinetics. Moreover, these alternative photoinitiators showed a better dentin sealing, with similar sorption and solubility values and high physical-mechanical properties when compared to the other groups based in CQ. In relation to the bond strength, the BAPO containing adhesives promoted higher performance even after 1-year of hydrolytic degradation / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Luís Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T23:46:46Z (GMT). No. of bitstreams: 1 SouzaJunior_EduardoJoseCarvalhode_M.pdf: 3521538 bytes, checksum: c8b050fbf4fb259c0dc4d1925121d22a (MD5) Previous issue date: 2011 / Resumo: Os objetivos deste estudo foram: a) avaliar o efeito do condicionamento seletivo do esmalte cavosurperficial e da fonte de luz LED na resistência à microtração em dentina de restaurações Classe I em compósito utilizando adesivos autocondicionantes; b) avaliar a dureza Knoop (KHN) de restaurações de cavidades Classe I em compósito utilizando adesivos autocondicionantes fotoativados com diferentes fontes de luz LED; c) Avaliar a formação de fendas antes e após ciclagem termomecânica de restaurações em compósito fotoativadas por LED e utilizando adesivos autocondicionantes em diferentes protocolos de aplicação. No experimento 1, noventa e seis cavidades Classe I foram preparadas em molares humanos, e restauradas com compósito micro-híbrido. Os espécimes foram distribuídos em 12 grupos (n=8), de acordo com a fonte de luz LED (Radii-Cal - RD, Flash Lite 1401 - FL e Ultra-Lume 5 - UL), sistema adesivo autocondicionante (Clearfil SE Bond - CSE e Clearfil S3 Bond - S3) e condicionamento seletivo do esmalte com ácido fosfórico (com e sem). Após o acabamento e polimento das restaurações as mesmas foram submetidas à fadiga termo-mecânica e os palitos para o ensaio de microtração foram obtidos da interface de união entre a parede pulpar dentinária e a restauração. Após o teste mecânico os dados foram submetidos à análise estatística (ANOVA três fatores e teste de Tukey com ?=0.05). O condicionamento seletivo do esmalte para o S3 diminuiu a resistência de união em dentina e não afetou o desempenho do CSE. Além disso, o LED de terceira geração promoveu maiores valores de resistência à microtração para o adesivo de dois passos. Para o S3 as fontes de luz promoveram resistência adesiva semelhante em dentina. No estudo 2, utilizou-se o mesmo método de preparo das amostras do primeiro estudo, formando-se 6 grupos (n=16) pela interação entre os fatores em estudo, LED (RD, FL e UL), sistema adesivo autocondicionante (CSE e S3). As parcelas subdivididas foram diferentes profundidades (superficial, média e profunda). Após a confecção das restaurações, as mesmas também foram submetidas à fadiga termo-mecânica e em seguida, seccionadas no sentido longitudinal para avaliação da KHN nas diferentes profundidades. Após análise estatística (ANOVA dois fatores com parcela subdividida e teste de Tukey com ?=0.05), observou-se que o LED de terceira geração promoveu valores de KHN semelhante aos aparelhos de pico único e que a região superficial, em geral, apresentou melhor qualidade de polimerização. No estudo 3, utilizou-se 192 terceiros molares, onde cavidades Classe I foram preparadas e restauradas com o mesmo método utilizado no primeiro estudo, 12 grupos (n=16) pela interação entre os fatores em estudo, LED (RD, FL e UL), sistema adesivo autocondicionante (CSE e S3) e condicionamento seletivo do esmalte com ácido fosfórico (com e sem), antes e após a termociclagem. Após a restauração, réplicas em resina epóxica foram confeccionadas e as margens foram analisadas em microscópio eletrônico de Varredura (MEV). Após submeter os espécimes da restauração à fadiga termo-mecânica, novamente réplicas em resina epóxica foram feitas e analisadas em MEV. Após análise estatística (Kruskal Wallis e teste de Wilcoxon pareado, ?=0.05), observou-se que o condicionamento seletivo do esmalte promoveu maior integridade marginal para o S3, mostrando ser um passo adicional eficiente na técnica de aplicação desse adesivo em restaurações Classe I em compósito. Além disso, a formação de fendas para adesivo autocondicionante de dois passos não foi influenciado pelo condicionamento ácido prévio do esmalte, nem pelo LED utilizado para fotoativação / Abstract: The aim of this work was to: a) evaluate the effect of enamel selective enamel etching and LED curing units on dentin microtensile bond strength of Class I composite restorations; b) evaluate the effect of different LED light units and self-etch adhesives on the Knoop hardness profile (KHN) of Class I composite restorations; c) evaluate the gap formation before and after thermomechanical loading of Class I composite restorations photocured by LED and using different application protocols of self-etch adhesives systems. In experiment 1, ninety-six Class I cavities were made in human molars and restored with a microhybrid composite. For the restorative procedure, teeth were assigned in 12 groups (n=8) formed by the studied factors interactions, LED curing unit (Radii-Cal - RD, Flash Lite 1401 -FL and Ultra-Lume 5 - UL), self-etch adhesives (Clearfil SE Bond - CSE and Clearfil S3 Bond - S3) and selective enamel acid etching (with and without). After finishing and polishing approach, specimens were submitted to thermo-mechanical ageing and sticks were obtained from the bonding interface between adhesive and pulpal wall which were submitted to a microtensile load in a universal testing machine. After statistical analysis, (three-way ANOVA and Tukey test with ?=0.05) it was shown that the pre-etched enamel approach for Clearfil S3 decreased dentin bond strength while it did not affect the bond performance of Clearfil SE. Thus, the polywave LED promoted higher microtensile bond strength values for the two-step adhesive. When Clearfil S3 was used, the light curing units yielded similar dentin bond strength. In the experiment 2, 96 Class I cavities were prepared in the same way as the previous experiment. Teeth were assigned to 18 groups (n=8) by the interaction among the studied factors, LED curing source (RD, FL and UL), self-etch bond system (CSE and S3), depth (superficial, medium and deep). After the restorative procedure, specimens were submitted to thermo-mechanical ageing and then sectioned in the longitudinal direction for the Knoop hardness measurement in the different depths. Data were submitted to three-way ANOVA and Tukey test with a pre-set alpha of 0.05). The results showed that the third generation LED promoted similar KHN values to the single-peak ones and the superficial surface, in general, presented greater cure quality compared to the others surface depths. In the experiment 3, 192 third molars were used and Class I preparations were restored in the same way as the first study. Specimens were assigned to 12 groups (n=16) formed by the studied factors interaction, LED (RD, FL and UL), self-etch adhesives (CSE and S3), selective enamel acid etching (with and without) and before and after thermomechanical loading. After the restoration procedure, epoxy resin replicas were made and the marginal adaptation was analyzed in a scanning electron microscope (SEM). Then specimes were submitted to thermalmechanical loading and again, epoxy resin replicas were made and analyzed by SEM. After statistical analysis (Kruskal Wallis and Wilcoxon matched-pairs signed-ranks test, with a pre-set alpha of 0.05), it was shown that selective enamel etching yielded higher marginal integrity for S3, showing to be an efficient additional step for the bonding technique of this adhesive in Class I composite restorations. Also, the two-step self-etch adhesive gap formation was not influenced by the selective enamel etching, neither by the LED curing light / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Luís Alexandre Maffei Sartini Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T22:44:51Z (GMT). No. of bitstreams: 1 Humel_MariaMalerbaColombi_D.pdf: 11561780 bytes, checksum: 79e3ed8605dc03bf07a59b8bb75596c5 (MD5) Previous issue date: 2013 / Resumo: Este estudo teve como objetivo avaliar a influência de diferentes concentrações destas soluções na resistência à flexão (FS), módulo de Elasticidade (E) e grau de conversão (DC) de sistemas adesivos convencionais, e ainda, sua influência na cinética (K) e taxa de conversão (RP). Para isso foram realizados dois trabalhos experimentais, sendo que no primeiro avaliaram-se as quantidades de primer nos adesivos, e no segundo trabalho avaliou-se a influência das soluções de enxague de cavidade, água, EtOH e CHX, quando em excesso, nos sistemas adesivos. Para se avaliar as diferentes concentrações do primer residual dois adesivos foram manipulados, M1 e M2 e testados com quatro concentrações de primer: 0, 5, 10 e 15%. Já para se avaliar o excesso de água, EtOH e CHX, dois adesivos foram testados: M1, adesivo manipulado, e o adesivo comercial SBMP; diluídos com 0, 2 e 9% para cada uma das soluções. Para se avaliar as propriedades mecânicas, nos dois estudos, foram preparadas amostras a partir de moldes de silicone em forma de barras (7 x 2 x 1mm) e após armazenamento por 24h, foram testadas em máquina de ensaio mecânico para o teste de FS a uma velocidade de 0,5 mm/min. DC foi mensurado utilizando Espectroscopia Transformada Infravermelha de Fourier (FTIR). Para cinética de conversão, a polimerização em cada diluição foi monitorada por FTIR pelo tempo de 60s, sendo que a conversão foi calculada a cada dois 2s de polimerização, avaliando-se também RP. No primeiro estudo, as diferentes concentrações da diluição com primer não mostrou diferença no teste de FS entre os adesivos testados, independente da concentração avaliada. Os dois adesivos testados apresentaram redução nos valores de DC com o aumento das quantidades de primer, sendo o adesivo M2 o mais susceptível às diluições. No segundo trabalho, para as diluições com água, EtOH, independente da quantidade testada, uma redução nas propriedades mecânicas e DC puderam ser observadas. As diluições em água e CHX alteraram mais as propriedades mecânicas quando comparadas as diluições com EtOH. Para K e RP com o aumento da concentração de primer residual todos adesivos apresentaram redução quando se avaliou os gráficos de conversão. Para as diluições em água, o aumento de sua concentração levou a queda progressiva na K e as diluições com CHX apresentaram menor influência na K, com redução apenas para 9% de diluição. Porém, para as diluições em EtOH houve aumento na K e RP especialmente para o adesivo SBMP. Assim, para o primeiro estudo, os resultados sugerem que as diferentes quantidades de primer usadas na diluição do adesivo não influenciam as propriedades mecânicas dos adesivos testados, porém, interferem na sua reação química de polimerização, uma vez que a velocidade reação foi reduzida (K e RP). Por outro lado, no segundo estudo, para as soluções residuais de água, EtOH e CHX, uma diminuição nas propriedades mecânicas dos adesivos ocorreu somente quando quantidades residuais de 9% foram simuladas. No entanto, pequenas quantidades de EtOH e CHX parecem não afetar as propriedades e velocidade de reação de polimerização dos adesivos / Abstract: The present study evaluates the influence of these solutions in different concentrations on flexural strength (FS), elastic modulus (E) and degree of conversion (DC) of conventional adhesives evaluating also the kinetic of conversion (K) and rate of polymerization (RP). Two distinct experiments were plotted, the first one evaluating the primer amount diluted in adhesives, and the second experiment evaluating rinse solutions amounts like water, ethanol and chlorexidine diluted in different adhesives. For different concentrations of primer solutions, two manipulated adhesives; M1 and M2 were tested at 0, 5, 10 and 15% of dilution. For different concentrations of water, ethanol (EtOH) and chlorexidine (CHX) dilutions, two adhesives were evaluated: M1, a manipulated adhesive, and the SBMP; diluted at 0, 2 and 9% of dilutions. Both studies, for mechanical properties, specimens were obtained by silicon mold bars (7 x 2 x 1mm), and after 24h, FS were performed at Mechanical Test Machine at cross speed of 0.5 mm/min. DC were measured with a Fourier Transformed Infrared Spectroscopy (FTIR). For K test, Infrared Spectroscopy monitored each 2 seconds of conversion for 60sec of polymerization, and the RP were evaluated. The first experiment, for different concentrations of primer dilutions, the FS for all adhesives tested was not affected by primer concentrations. All adhesives tested showed a decrease for DC as increased the primer dilution, with M2 presenting as the most sensitive for primer concentration. For second experiment, for all concentrations dilution of water, EtOH and CHX, a decrease on mechanical properties and DC was noted. Water and chlorexidine seems to affect more mechanical properties when compared to EtOH results. For K and RP results, increasing primer concentration, all adhesives presented a decrease of conversion and RP. For water dilutions, increasing water concentrations on tested adhesives, a progressive decrease could be noted on K graphics. CHX dilutions presented less influence on K, with decreasing RP and K only with 9% dilution. Although, EtOH dilutions presented an improve K as the RP, especially to SBMP adhesive. The results suggested that mechanical properties were not affected regardless of the primer amount diluted on adhesives, interfering only on chemistry of polymer reaction, once reaction speedy were affected (K and RP). However, for second experiment, a decrease on mechanical properties of adhesive solutions could be noted only when extreme amounts of residual solution where diluted. Notwithstanding, at lowest concentrations, EtOH and CHX seems not interfere on K and RP of adhesives / Doutorado / Dentística / Doutora em Clínica Odontológica

<p>U savremenoj restaurativnoj stomatologiji dentalni kompoziti su materijal izbora za rekonstrukciju izgubljenog čvrstog zubnog tkiva. Kako je u kliničkoj praksi primećeno, pozitivna svojstva svetlosno-aktiviranih dentalnih kompozita su ugrožena pojavom polimerizacione kontrakcije kompozitnih ispuna tokom polimerizacije. Naime, tokom svetlosne polimerizacije usled konverzije molekula monomera u dugačke izukr&scaron;tane lance polimera, razvija se napon na adhezivnom spoju kompozitnog ispuna i zida kaviteta. Kada vrednost napona nadma&scaron;i jačinu adhezivne veze kompozita i zida kaviteta, formira se marginalna mikropukotina praćena kliničkim manifestacijama u vidu postoperativne osetljivosti, marginalne diskoloracije ispuna, razvoja sekundarnog karijesa i sledstvenih ireverzibilnih promena pulpe zuba. Cilj istraživanja je bio da se uporedi uticaj primene različitih tehnika postavljanja i svetlosne polimerizacije na marginalnu adaptaciju kompozitnih ispuna. Materijal i metode: Ispitivanje marginalne adaptacije kompozitnih ispuna urađeno je u dentinskim kavitetima, na bukalnim i oralnim povr&scaron;inama humanih trećih molara u laboratorijskim uslovima. Oralni i bukalni deo krunice zuba je bru&scaron;en dijamantskim diskom uz stalno hlađenje radnog polja vodenim mlazom, kako bi se izložila ravna dentinska povr&scaron;ina promera 4x4 mm. Standardizovani cilindrični dentinski kaviteti, dimenzija 3x3 mm, preparisani su dijamantskim cilindričnim svrdlima uz obilno hlađenje radnog polja mlazom vode. Eksperimentalni deo doktorske teze, imajući u vidu postavljeni cilj istraživanja, podeljen je u dva dela. Prvi deo je obuhvatio ukupno 80 dentinskih kaviteta u koje je postavljen isti kompozitni sistem (Adper Single Bond Plus-Filtek Ultimate Flowable), različitim tehnikama postavljanja: u jednom sloju-bulk tehnikom,&nbsp; inkrementalnom tehnikom, prethodno zagrejani kompoziti i eliminisanjem jedinstvene tačke stresa-postavljanjem pin-a. Za svetlosnu polimerizaciju kompozita primenjene su dve tehnike, kontinuirana i diskontinuirana, odnosno polimerizacija sa prekidom od 10 sekundi (dark interval), nakon inicijalnog perioda prosvetljavanja. Drugi deo istraživanja je obuhvatio 20 istovetnih dentinskih kaviteta u kojima su postavljeni bulk-fill kompozitni sistemi (Filtek Bulk Fill Flowable i SDR) uz kontinuiranu svetlosnu polimerizaciju, prema uputstvu proizvođača. Nakon poliranja ispuna, zubi sa postavljenim ispunima svih grupa su čuvani u uslovima 100 % vlažnosti u trajanju od 24 časa u cilju prevencije dehidratacije. Za evaluaciju marginalne adaptacije kori&scaron;ćena je analiza epoksi replika adhezivnog spoja kompozitnog ispuna i dentina skening elektonskom mikroskopijom (SEM). Naime, nakon uzimanja otiska ispuna i okolnog dentina polivinilsiloksanom izrazito niske viskoznosti (Ghenesyl, Super Light Body, Lascod, Florence, Italy), izlivene su replike u epoksi smoli koje su pripremljene za SEM analizu (Jeol, JSM-6460 Low Vacuum, Tokyo, Japan). Dužina marginalne pukotine je izmerena u mikrometrima pomoću ImageJ računarskog programa (National Institute of Health, Bethesda, USA) i prikazana procentualno u odnosu na ukupnu dužinu marginalnog spoja ispun-dentin. Međusobno su upoređeni rezultati marginalne adaptacije različitih tehnika postavljanja i polimerizacije kompozitnih ispuna kao i rezultati marginalne adaptacije različitih kompozita postavljenih bulk tehnikom i polimerizovanih kontinuirano. Statističke razlike su obrađivane primenom ne-parametrijskog Mann-Whitney U-testa. Rezultati: Analizom numeričkih rezultata utvrđen je statistički značajno vi&scaron;i kvalitet marginalne adaptacije kada su kompozitni sistemi postavljeni u kavitete eliminisanjem jedinstvene tačke stresa-postavljanjem pin-a i diskontinuirano polimerizovani, u odnosu na ostale ispitane tehnike postavljanja. Statistčki značajno niži kvalitet marginalne adaptacije utvrđen je u grupi ispuna postavljenih uz prethodno zagrevanje i diskontinuirano polimerizovanih. Nisu dobijene statistički značajne razlike u kvalitetu marginalne adaptacije kompozitnih ispuna postavljenih različitim tehnikama u dentinske kavitete, uz istovetni, kontinuirani režim svetlosne polimerizacije. Nisu dobijene statistički značajne razlike u kvalitetu marginalne adaptacije između kompozitnih ispuna postavljenih istom tehnikom, uz različit režim svetlosne polimerizacije. Nisu dobijene statistički značajne razlike u vrednostima marginalne adaptacije između dva ispitana bulk-fill kompozitna sistema. Takođe, ni njihovim poređenjem sa vrednostima marginalne adaptacije kompozitnih ispuna postavljenih bulk tehnikom i polimerizovanih kontinuirano nisu dobijene statistički značajne razlike. Zaključak: Tehnika postavljanja i polimerizacije značajno utiče na kvalitet marginalne adaptacije kompozitnih ispuna u dentinskim kavitetima. Novi proizvod na trži&scaron;tu ne znači uvek i bolja svojstva materijala u pogledu kvaliteta marginalne adaptacije.</p> / <p>In contemporary restorative dentistry, dental composites become material of choice for reconstruction of lost tooth structure. In clinical practice it is noticed that positive properties of light-activated composites are compromised by polymerization shrinkage appearance during polymerization. The conversion of monomer molecules into polymer network is accompanied by stress transmitting to the adhesive bond what leads to the formation of microgap with clinical symptoms such as postoperative sensitivity, marginal discoloration, secondary caries and pulp pathology. The aim of this study was to compare the influence of different placing and light polymerization techniques on marginal adaptation of composite restorations. Material and Methods Examination of marginal adaptation of composites was done in dentin cavities, prepared on the buccal and oral surfaces of human third molars in laboratory conditions. The buccal and oral enamel was ground using model trimmer under running water to expose a flat dentin surface area dimension 4x4mm. Standardized cylindrical cavities (3 mm diameter, 3 mm deep) with all dentin margins were prepared using diamond cylindrical burs with copious water cooling of the working field. Taking into account the goal of this study, research was consisted of two parts. First part included 80 dentin cavities with composite system (Adper Single Bond Plus-Filtek Ultimate Flowable) placed using different placing techniques: bulk, incremental, preheated composite and by elimination of singular stress point-with pin. There were applied two light-activation techniques: continuous (40 seconds) and discontinuous (2 seconds of activation, followed by 10 seconds of dark interval, and then the polymerization is set continuously). Second part of this study included 20 the same manner prepared dentin cavities with bulk-fill composites (Filtek Bulk Fill Flowable i SDR) placed and continuously polymerized, according to the manufactures instructions. After polishing, the restored teeth were stored in a container with 100% relative humidity for 24 h to prevent dehydration. Evaluation of marginal adaptation was done using SEM analysis of replicas. After making impressions with low viscosity polyvinyl siloxane material (Ghenesyl, Super Light Body, Lascod, Florence, Italy), epoxy resin replicas were prepared for SEM analysis (Jeol, JSM-6460 Low Vacuum, Tokyo, Japan). The length of marginal gap was measured with ImageJ software (National Institute of Health, Bethesda, USA) and shown in percentage relative to total length of the margin composite/dentin. Results of marginal adaptation were compared according to application of different placing and polymerization techniques and also results of marginal adaptation of different composites bulk placed and continuously polymerized. Statistical differences were calculated using the non-parametric Mann-Whitney U-test. Results: With statistical significance there was better quality of marginal adaptation when composite was placed with pin in order to eliminate singular stress point and discontinuously polymerized, compared to other applied placing and polymerization techniques. Contrary, there was significantly higher percentage of marginal gap obtained when using pre-heated, discontinuous polymerized composites. Marginal adaptation of composite materials placed in dentin cavities using different techniques and same, continuously polymerization technique didn&rsquo;t show statistically different results. Marginal adaptation of composite materials placed in dentin cavities using same technique and different, continuously or discontinuously polymerization technique didn&rsquo;t show statistically different results. Marginal adaptation of two &ldquo;bulk-fill&rdquo; composite materials didn&rsquo;t show statistically different results. Also, compared to composites placed using bulk technique and polymerized continuously, their lower values of marginal adaptation didn&rsquo;t show significant difference. Conclusion: Placing and polymerization techniques have significant influence on the quality of marginal adaptation of composite restorations in dentin cavities. New product on the market doesn&rsquo;t always mean better marginal adaptation properties.</p>

Submitted by JÚLIO HEBER SILVA (julioheber@yahoo.com.br) on 2018-05-22T17:33:36Z No. of bitstreams: 2 Tese - Andreia Assis Carvalho - 2018.pdf: 4561805 bytes, checksum: 5562226572f75d161d963c396d0c974f (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2018-05-23T11:38:00Z (GMT) No. of bitstreams: 2 Tese - Andreia Assis Carvalho - 2018.pdf: 4561805 bytes, checksum: 5562226572f75d161d963c396d0c974f (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-05-23T11:38:00Z (GMT). No. of bitstreams: 2 Tese - Andreia Assis Carvalho - 2018.pdf: 4561805 bytes, checksum: 5562226572f75d161d963c396d0c974f (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2018-04-20 / Fundação de Amparo à Pesquisa do Estado de Goiás - FAPEG / The objective of this study was to evaluate the clinical behavior of direct composite resin restorations (Class I and II), varying the universal dental adhesive application protocol, using the FDI and USPHS evaluation criteria. It was a randomized, double-blind, mouth5 divided, and sample-based randomized controlled trial. The selected participants should have a Class I and/or II restorative need for at least three dental elements or multiples of three resulting from the presence of carious lesions and/or unsatisfactory restorations. Three protocols for the application of the Single Bond Universal adhesive (3M ESPE) were tested (n=150): CAT (control) = etch-and-rinse + adhesive (n=50); CASE = selective etching in enamel + adhesive (n=50) and Ac = self-etch (n=50). The three groups were similarly restored using Filtek Z350 XT composite resin (3M ESPE) by means of the oblique incremental technique. Clinical evaluations were performed by two evaluators at the baseline (T1) and after 15.8 (±2.7 months) (T2), using the FDI and USPHS criteria. Friedman (between groups at different times), Wilcoxon (between times for each group) and McNemar (between FDI and USPHS criteria) were performed, α=0.05. The Kappa test showed excellent inter-examiner agreement (κ>0.80). For the "superficial staining" property, a statistically significant difference was observed in T2 between the CAT and CASE groups (p=0.01) with higher values for CAT and, when T1 and T2 were compared for each group, there were differences in the CAT group (p=0.001) and in the Ac group (p=0.007) for T2. For the other comparisons between groups and times there were no statistically significant differences, even when the FDI and USPHS criteria were compared (p≥0.05). It can be concluded that the different protocols of universal adhesive application (CAT, CASE and Ac) did not influence the clinical behavior of the restorations evaluated in 15.8 months of evaluation. The FDI and USPHS criteria provided comparable results. / Esse trabalho objetivou avaliar o comportamento clínico de restaurações diretas de resina composta (Classe I e II), variando o protocolo de aplicação do adesivo dentário universal, por meio dos critérios de avaliação FDI e USPHS. Trata-se de um ensaio clínico contrlado randomizado, duplo-cego, boca-dividida e de amostra por conveniência. Os participantes selecionados deveriam ter necessidade restauradora de Classe I e/ou II no mínimo em três elementos dentários ou múltiplos de três, resultantes da presença de lesões cariosas e/ou restaurações insatisfatórias. Três protocolos de aplicação do adesivo Single Bond Universal (3M ESPE) foram testados (n=150): CAT (controle) = Condicionamento ácido total + adesivo (n=50); CASE = Condicionamento ácido seletivo em esmalte + adesivo (n=50) e Ac = autocondicionante (n=50). Os três grupos foram restaurados de forma similar utilizando resina composta Filtek Z350 XT (3M ESPE) por meio da técnica incremental oblíqua. As avaliações clínicas foram realizadas por dois avaliadores no baseline (T1) e após 15,8 (±2,7 meses) (T2), por meio dos critérios FDI e USPHS. Foram realizados os testes Friedman (entre os grupos nos diferentes tempos), Wilcoxon (entre os tempos para cada grupo) e McNemar (entre os critérios FDI e USPHS), α=0,05. O teste Kappa apresentou excelente concordância interexaminadores (κ>0,80). Para a propriedade “manchamento superficial”, observou-se diferença estatisticamente significante no T2 entre os grupos CAT e CASE (p=0,01) com maiores valores para CAT e, quando comparados T1 e T2 para cada grupo, houve diferença no grupo CAT (p=0,001) e no grupo Ac (p=0,007) para T2. Para as demais comparações entre os grupos e tempos não houve diferenças estatisticamente significantes, inclusive quando os critérios FDI e USPHS foram comparados (p≥0,05). Pode-se concluir que os diferentes protocolos de aplicação do adesivo universal (CAT, CASE e Ac) não influenciaram o comportamento clínico das restaurações avaliadas em 15,8 meses de avaliação. Os critérios FDI e USPHS proporcionaram resultados comparáveis entre si.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2016-05-18T14:18:46Z No. of bitstreams: 1 sergioluizmotajunior.pdf: 65970440 bytes, checksum: b08afa740679beb93b85550945b417d2 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2016-07-01T18:47:10Z (GMT) No. of bitstreams: 1 sergioluizmotajunior.pdf: 65970440 bytes, checksum: b08afa740679beb93b85550945b417d2 (MD5) / Made available in DSpace on 2016-07-01T18:47:10Z (GMT). No. of bitstreams: 1 sergioluizmotajunior.pdf: 65970440 bytes, checksum: b08afa740679beb93b85550945b417d2 (MD5) Previous issue date: 2012-02-14 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo do presente estudo foi o desenvolvimento de uma nova ponteira para ser acoplada aos aparelhos fotopolimerizadores utilizados para colagem de bráquetes e acessórios ortodônticos, e teste da efetividade da mesma em ensaio mecânico in vitro. A ponteira é espelhada na superfície interna e baseia-se em conceitos físicos de refração e reflexão de luz. Apresenta como principal vantagem, a redução do tempo clínico necessário para o procedimento de colagem, reduzindo, dessa forma, a possibilidade de contaminação durante o processo. Através do ensaio de resistência mecânica ao cisalhamento e da determinação do Indice Remanescênte de Adesivo (IRA), testou-se a ponteira em uma amostra composta por 120 corpos de prova, sendo a mesma dividida em 2 grupos. No grupo 1 foi utilizado aparelho fotopolimerizador de fonte de luz halógena e no grupo 2 foi utilizado fonte de LED. Cada grupo foi subdividido. Nos subgrupos H1 e L1 utilizou-se a ponteira convencional dos respectivos instrumentos. Nos subgrupos H2 e L2 a colagem foi feita utilizando-se a ponteira desenvolvida. Os valores dos testes de cisalhamento e IRA para os subgrupos foram comparados entre si. Os resultados mostraram que não houve diferença estatisticamente significante, tanto para os ensaios de resistência ao cisalhamento (p>0,05), quanto para o IRA (p>0,05) entre os subgrupos. Conclui-se que 1 - os testes de ensaios mecânicos, assim como a análise do IRA mostraram que a nova ponteira desenvolvida, cumpriu os requisitos necessários à colagem dos acessórios ortodônticos; 2 – o tempo de colagem foi reduzido pela metade, sendo necessária uma só incidência. / The porpose of the present study was the development of a new device to be coupled to light-curing units for bonding orthodontic brackets and accessories and test of its efficacy in “in vitro” mechanical trial. The inner surface of the device is mirrored and is based on physical concepts of light refraction and reflection. The main advantage of such device is the reduced clinical time needed for bonding and the lesser possibility of contamination during the process. 120 bodies of proof were used for testing the shear bond strength of brackets bonded with the device. The Adhesive Remnant Index (ARI) was also determined. The sample was divided into 2 groups. In group 1 a halogen light-curing unit was used and in group 2 a led lightcuring unit was used. Each group was then subdivided. In subgroups H1 and L1, a conventional light guide rod was used. In subgroups H2 and L2 bonding was performed with the mirrored device coupled to the tip of the guide light rod. The values obtained for the shear bond strength and the ARI in the subgroups were compared. Results showed that there was no statistically significant difference for the shear strength (p>0,05) and the ARI (p>0,05) between the subgroups. Conclusions are that 1 - The tests of mechanical trials and the ARI analysis showed that the new device fulfilled the requisites for bonding orthodontic accessories; 2 - time for bonding was reduced to half, being necessary only one light exposure.

Background: The light-cured resin-based pit and fissure sealants success and longevity are enhanced by sufficient curing. Multiple emission peak Light Emitting Diode Light Curing Units offer a wider range of wavelengths and different levels of irradiances to ensure sufficient curing.The irradiance is considered a main curing factor that can affect the material properties. Purpose: The aim of this study was to assess the effect of different settings of a multiwave LED LCU on the degree of conversion and microhardness of a pit and fissure sealant comparing the irradiance of 1000 mW/cm2 to 1400 mW/cm2 and 3200 mW/cm2 irradiances of the LCU using manufacturer’s guidelines for curing times at 2, 4 and, 6 mm distances. Methods: A multiwave LED light curing unit was evaluated on three different irradiance levels 1000 mW/cm2 (S), 1400 mW/cm2 (H), and 3200 mW/cm2 (X). A total of 90 samples made from the fissure sealant were fabricated and divided into eighteen groups (n=5/group). Samples were cured following manufacturer’s guidelines of curing times for each curing mode at 2, 4, or 6 mm distance between the light tip and top of samples. The DC was measured using (ATR-FTIR) spectroscopy. The KHN test was performed on five different locations of each specimen using a hardness tester (Leco LM247AT, MI, USA, software; Confident V 2.5.2). Results: The top DC for H-8 was significantly higher than S-10 at 2 and 4mm, H-20 DC was significantly lower than S-30 at only 2mm. The bottom DC for H-8 was significantly higher than S-10 at 2mm only, H-20 DC was significantly lower than S-30 at 4 and 6mm only. H-8 KHN at top surface was significantly lower than S-10 at 2mm only, H-20 was significantly lower than S-30 at 2 and 6mm only. H-8 KHN at bottom surface was significantly lower than S-10 at 4 and 6mm but significantly higher at 2mm. H-20 was significantly lower than S-30 at 2mm but significantly higher at 4 and 6mm. The top DC for X-3 was significantly lower than S-10 at all curing distances with no significant difference at all curing distances between X-9 and S-30. The bottom DC for X-3 was significantly higher than S-10 at all curing distances with no significant difference between X-9 and S-30. X-3 KHN at top surface was significantly lower than S-10s at all curing distances. X-9 was significantly lower than S-30 at 6mm only. X-3 KHN at bottom surface was significantly lower than S-10 at 2 and 4mm only with no significant difference at all curing distances between X-9 and S-30. Conclusions: Using a multiwave LED LCU to polymerize Delton Opaque resin-based fissure sealants will result in an optimal DC and KHN values for any irradiance level if the curing distance is kept at 4 mm or less and with at least two cycles of the shortest curing time recommended by the manufacturer. Using a multiwave LED LCU with 1000, 1400 or 3200 mW/cm2 irradiance levels with shortest curing times recommended resulted in unsatisfactory DC and KHN levels. LED LCU with high and extra high irradiance levels (1400 and 3200 mW/cm2) can result in high DC and KHN levels when used adequately. Xtra Power mode (3200 mW/cm2) used on shortest curing time (3 seconds) resulted in significantly lower mechanical properties and for that reason it is not recommended to be used.

Made available in DSpace on 2014-08-20T14:30:07Z (GMT). No. of bitstreams: 1 Dissertacao_Caroline_Ely.pdf: 855676 bytes, checksum: 3b493898d992f4952a9932fd00c16707 (MD5) Previous issue date: 2011-01-01 / The aim of this project will be to investigate the influence of the addition of light and co-initiators in self-etching primers, in relation to microtensile bond strength (μTBS) and on morphological pattern of hybrid layer of an experimental adhesive system. An experimental self-etching primer will be formulated and on which will be added the initiators of polymerization, resulting in a total of 6 experimental groups: PCONTROL, PCQ, PQTX, PDPI, PBAR and PSUL. A coating adhesive resin compound by Bis-GMA, TEGDMA and HEMA will be formulated. For μTBS test, forty-eight bovine incisors will be randomized and allocate in the six groups. Vestibular enamel will be grounded to expose the superficial coronal dentin, which that will be polished wet to create a standardized smear layer with 600 grit silicon paper. After rinsing, water will be removed with a piece of absorbent paper, leaving the surface visibly dried. The prepared dentin surfaces will be etched with primer and air-dried, after coating adhesive resin will be applied and light activated. The composite resin will be inserted in two increments and will be light activated according to the manufacturer s recommendations. After storage for 24 hours, the specimens will be sectioned with a refrigerated diamond saw at lowspeed. After check normal distribuition and equal variances as assumptions to carry out parametric statistics data obtained on μTBS, will be submitted to two-way ANOVA (factor time and factor initiator of (polymerization) test to verify differences between means (p<0.05). Fractographic analysis will be performed using optical microscopy to describe failure patterns. The morphological pattern of hybrid layer will be examined by scanning electron microscopy (Shimadzu SSX550), after 24 hours and 2 years of storage, using 3 teeth for each experimental group. Teeth will be sectioned with a refrigerated diamond saw, in order to obtain 2 or 3 slices per tooth, with 2mm thickness. Restorative procedure will take place, following the same steps of sample preparation 9 for μTBS test. Then, samples will pass through a sequence of polishing with grit silicon paper and diamond pastes of different granulations. Between each stage of polishing, samples will be placed in one ultrasonic tank to complete removal of waste. After, will undertake the procedures of decalcification with solution of phosphoric acid 50%, deproteinization with sodium hypochlorite solution 2.5%, dehydration with silica at room temperature for 2 hours and coating with gold/palladium. Finally, images of hybrid layer will be observed in SEM, on 3000 and 5000 fold increas / O objetivo deste projeto será avaliar a influência da adição de iniciadores de polimerização em primer autocondicionante experimental, na resistência de união e no padrão morfológico da camada híbrida de sistemas adesivos. Será formulado um primer experimental modelo, ao qual serão adicionados fotoiniciadores e co-iniciadores, obtendo-se um total de 6 grupos experimentais: PCONTROLE, PCQ, PQTX, PDPI, PBAR e PSUL. Como adesivo de cobertura, será formulado um co-monômero constituído de Bis-GMA, TEGDMA e HEMA. Para o ensaio de resistência de união à microtração (RU) serão utilizados 48 incisivos bovinos, distribuídos aleatoriamente entre os grupos . Na face vestibular dos dentes será realizado desgaste até a exposição de dentina e, posteriormente, polimento com lixa de SiC granulação 600 para padronização da smear layer. O primer será aplicado vigorosamente sobre a dentina previamente seca com papel absorvente e após será realizada a volatilização do solvente com jato de ar. Em seguida o adesivo de cobertura será aplicado e fotoativado com um aparelho fotopolimerizador de lâmpada halógena. A restauração será confeccionada em incrementos de compósito restaurador, fotoativados de acordo com as recomendações do fabricante. Após armazenagem por 24h em água destilada a 37°C, os dentes serão seccionados em cortadeira de precisão a fim de obterem-se palitos de aproximadamente 0,5mm2 de área de secção transversal. A RU em dentina será avaliada após 24h, 1 e 2 anos de armazenagem em água destilada. Os dados obtidos serão avaliados quanto à normalidade e igualdade de variâncias como condição para utilização de análise estatística paramétrica Preenchendo os requisitos anteriores será aplicada Análise de variância segundo dois critérios (fator tempo e fator iniciador de polimerização), e teste complementar de Tukey para detectar diferenças entre médias (α=5%). Os corpos de prova fraturados a partir do ensaio de microtração serão avaliados por microscopia óptica e classificados quanto ao modo de fratura em adesiva, 7 coesiva ou mista. A análise do padrão morfológico da camada híbrida será realizada por microscopia eletrônica de varredura MEV (SSX-550, Shimadzu), após 24 horas e 2 anos de armazenagem, utilizando-se 3 dentes para cada grupo experimental. Os dentes serão seccionados em cortadeira de precisão a fim de obter-se 2 ou 3 fatias por dente, com 2,0 mm de espessura cada uma. Será realizado então o procedimento restaurador, seguindo os mesmos passos utilizados para avaliar a RU. A seguir, as amostras passarão pelo protocolo de polimento com a seqüência de lixas de SiC e, em seguida, com discos de feltro e suspensões diamantadas, em granulações decrescentes.. Após, serão realizados os procedimentos de descalcificação com solução de ácido fosfórico 50% por 5 segundos, desproteinização com solução de hipoclorito de sódio 2,5% por 10 minutos, desidratação com sílica em temperatura ambiente e metalização. Por fim, serão obtidas fotomicrografias da camada híbrida em aumento de 3000 e 5000 vezes, através de Microscopia Eletrônica de Varrredura

Indiana University-Purdue University Indianapolis (IUPUI) / Reduction of the polymerization shrinkage stress inherent of dimethacrylate-based resin composites has been a work in progress since the phenomenon was first described by Dr. Rafael L. Bowen in 1967. Contemporary efforts to modify the composites or the curing protocols for polymerization have proven a challenging task with controversial results. Influenced by existing mathematical models relating exposure, curing time and depth of cure of resin composites, a novel method for the reduction of polymerization shrinkage stress is proposed. By polymerizing through a single aperture mask, a dental light curing unit is transformed from a planar light source to a point light source, and a fully cured, three-dimensional “bullet” shaped curing front is predicted for the cured resin below. So long as the edges of the bullet do not touch the cavity walls or floor, the shrinkage stress of the bullet is not transferred. Follow-up with an unmasked curing unit then fully polymerizes the restoration. By reducing the volume of uncured composite in contact with the cavity walls and floor, shrinkage stress of the restoration is also reduced. The objective of the present study was to demonstrate this curing phenomenon with a model resin composite using masks with aperture diameters of 0.5, 0.4, and 0.25 mm and curing times of 10, 20, 30, and 40 seconds. The resulting curing front was evaluated quantitatively and qualitatively. From this, mathematical models of the curing front were derived. Selected combinations of aperture mask and curing time were then investigated to evaluate the influence of this phenomenon on the degree of conversion, Knoop hardness, and polymerization shrinkage stress of the same model resin composite. Group differences were analyzed using a one-way ANOVA at 5% significance.