Orientador: Gladis Camarini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil / Made available in DSpace on 2018-08-03T21:48:06Z (GMT). No. of bitstreams: 1
FerreiraJunior_EpaminondasLuiz_M.pdf: 5084071 bytes, checksum: 03b184ef71edeef1b61a1e5c4f46715f (MD5)
Previous issue date: 2003 / Resumo: A durabilidade do concreto é dependente de fatores que vão desde a sua produção (tipo de cimento, de agregados, adensamento, tipo de cura, etc.) até a influência do meio ao qual o material está exposto. Este trabalho teve por objetivo avaliar algumas propriedades mecânicas e a durabilidade de concretos produzidos com cimento Portland com elevado teor de escória (CP III) e cimento Portland de alta resistência inicial (CP V -ARI). Os concretos foram submetidos a quatro tipos de cura: normal, imerso em água por 7 dias, ao ar e térmica. Na cura térmica foram empregadas duas temperaturas de cura: 60°C e 80°C. Para avaliação da resistência mecânica, foram realizados ensaios de compressão axial e tração por compressão diametral. Para a durabilidade, foram realizados ensaios de absorção capilar, permeabilidade ao ar, carbonatação natural e acelerada e penetração de cloretos. A microscopia eletrônica de varredura foi usada para observação microestrutura dos compostos hidratados e o efeito dos ensaios acelerados, tendo como variáveis o tipo de cimento e o regime de cura. Os resultados obtidos mostraram que a cura térmica não contribui significativamente para a elevação da resistência nas primeiras idades para os concretos produzidos com CP V-ARI, mas melhora em muito a resistência dos concretos produzidos com CP-III, principalmente na temperatura de 80°C. Quanto à durabilidade, os concretos com CP V -ARI apresentaram bons resultados com relação a carbonatação, mas mostraram resultados mais elevados na absorção e penetração de cloretos. A cura por imersão em água até sete dias mostrou-se satisfatória, atingindo resultados similares em relação à cura normal em todas as propriedades estudadas. Os piores resultados, tanto mecânicos quanto de durabilidade, foram obtidos pelas amostras curadas ao ar, e foram mais prejudiciais nos concretos produzidos com CP III. Concluiu-se que um regime de cura adequado é essencial para garantir a resistência mecânica e a durabilidade dos concretos, e que a resistência mecânica não pode ser usada como parâmetro de durabilidade / Abstract: The durability of concrete depends of factors that change with its production. There is the influence of cement type, aggregates, casting, curing procedures, and the influence of the aggressive environment in which the material is exposed. The aim this work was to study the mechanical performance and durability of concretes made from High Early Strength Cement (HPC) and Blast-furnace Slag Cement (BFSC). Concretes were submitted to different curing conditions: cured in water (standard curing), curing in water up to 7 days (immersion curing), curing in air at ambient temperature and steam curing under atmospheric pressure. In steam curing it were used two curing temperatures: 60°C and 80°C. For assessment of mechanical properties, testing of compressive and tensile strength were determined. Durability was determined by capillary absorption, air permeability, natural and accelerated carbonation, and chloride ion absorption. Scanning electron microscopy was utilized to observe the feature of the hydrated compounds and the effect of the variation the cement type and curing conditions. According to the obtained results, steam curing do not improve the strength at early ages for concretes made from HPC, but it is better for concretes made with BFSC in steam curing at 80°C Concretes made with HPC showed the worst results for chlorides absorption. The immersion curing (in water up to 7 days) showed similar results compared to standard curing for all properties studied. The worst results, for all properties were obtained for samples cured in air, and the concretes made with BFSC were more sensible to curing procedure. In this way, its was conc1uded that curing procedure is essential for reach the development of mechanical properties and durability of concretes, and that mechanical properties cannot be reference for durability / Mestrado / Edificações / Mestre em Engenharia Civil
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/258269 |
| Date | 14 April 2004 |
| Creators | Ferreira Junior, Epaminondas Luiz |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Camarini, Gladis, 1958-, Ducatti, Vitor Antonio, Silva, Maristela Gomes da |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 141p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds