Objetivo: Comparar in vitro la resistencia adhesiva de un cemento autoadhesivo con diferentes tipos de tratamientos previos a la superficie dentinaria.
Materiales y métodos: Se utilizaron 60 incisivos de bovino que fueron divididos en 5 grupos (n=12) 1) grupo control, sin tratamiento dentinario; 2) E.D.T.A al 17% (Eufar®) por 60s; 3) Ácido fosfórico al 37% (CondAc 37%) durante 15s más un sistema adhesivo (Adhesivo Adper™ Single Bond 2); 4) Ácido poliacrílico al 10% (Ketac™Bond), durante 10s; 5) Clorhexidina al 2% (Maquira Dental Products) por 60s. Bloques de SR Adoro® (Ivoclar Vivadent AG®) fueron cementados a la dentina, utilizando el cementación autoadhesivo (RelyX™U200). Las muestras se almacenaron en suero fisiológico al 0.09% a 37°C hasta su evaluación. Se realizó una prueba de cizallamiento a una velocidad de cruceta de 1mm/min; los resultados fueron obtenidos en MPa. Se determinó si tuvo distribución normal mediante la prueba de Shapiro-Wilk. Para la comparación de los grupos se utilizó la prueba de Kruskall Wallis.
Resultados: Se encontró diferencias estadísticamente significativas (p=0.0001) al comparar cada uno de los tipos de tratamiento dentinario. El ácido fosfórico al 37% más adhesivo obtuvo la mayor resistencia adhesiva (5.25 ± 4.94) y el ácido poliacrílico al 10% (0.96 ± 1.37) la menor resistencia adhesiva.
Conclusión: Se concluyó que la ultilización de ácido fosfórico más adhesivo mejora la adhesión del cerómero a la dentina cuando se utiliza un cemento autoadhesivo. / Purpose: To compare in vitro shear bond strength of a self-adhesive cement with different treatments previous to the dentin surface.
Material and Methods: 60 bovine incisors were divided into 5 groups (n=12) 1) Control group, without dentin treatment; 2) E.D.T.A 17% (Eufar®) for 60s; 3) Phosphoric acid 37% (CondAc 37%) for 15s and an adhesive system (Adper™ Single Bond 2 Adhesive); 4) Polyacrylic acid 10% (Ketac™Bond), for 10s; 5) Chlorhexidine 2% (Maquira Dental Products) for 60s. SR Adoro® (Ivoclar Vivadent AG®) blocks were cemented to the dentin, using self-adhesive cement (RelyX™U200). The samples were stored at 37°C in 0.09% physiological saline until their evaluation. A shearing test was performed at a crosshead speed of 1mm/min; the results were obtained in MPa. Using Shapiro-Wilk test, it was established if it had normal distribution. The Kruskall Wallis test was used to compared the groups.
Results: Statistically significant differences were found (p=0.0001) comparing each of the dentin treatments. The Phosphoric acid 37% and adhesive system obtained the highest bonding strength (5.25 ± 4.94) and the Polyacrylic acid 10% (0.96 ± 1.37) the lowest bonding strength.
Conclusion: It may be concluded that using phosphoric acid and adhesive improve the adhesion of ceromer to dentin when self-adhesive cement is used.
| Identifer | oai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/620956 |
| Date | 2016 December 1914 |
| Creators | Meza Juárez, Maritza Lucía |
| Contributors | Cafferata Montoya, Paola Antonella |
| Publisher | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Source Sets | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Language | Spanish |
| Detected Language | Spanish |
| Type | info:eu-repo/semantics/bachelorThesis |
| Source | Universidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico UPC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds