Orientador: Jose Ricardo de Albergaria Barbosa / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:59:55Z (GMT). No. of bitstreams: 1
Sardinha_SandradeCassiaSantana_D.pdf: 6778496 bytes, checksum: 6e85b28fae3ec96602b176bd2bbce76d (MD5)
Previous issue date: 2003 / Resumo: Este trabalho teve como objetivo analisar, química e topograficamente, a superfície de implantes de titânio comercialmente puro, utilizados atualmente na Odontologia. Foram selecionados oito implantes das seguintes marcas comerciais: Conexão - Sistema de Próteses; Lifecore - Biomedical; AS Technology e S - Serson Internacional. As amostras apresentavam tratamento de superfície, através das técnicas de ataque ácido (Conexão) e plasma sprayde titânio (Lifecore-Biomedical; AS Technology e S - Serson International), sendo divididas em quatro grupos, contendo dois implantes do mesmo lote de cada fabricante. As análises foram realizadas através de Espectroscopia de Fotoelétrons Excitada por Raios-X (XPS) e Microscopia Eletrônica de Varredura (MEV). Os resultados da análise química mostraram os elementos titânio (Ti), oxigênio (O), silício (Si), zinco (Zn), alumínio (AI) e carbono (C). O estudo através do MEV revelou a topografia rugosa da superfície e uniformidade entre as roscas dos implantes. Pode-se concluir, deste modo, que houve impurezas na superfície dos implantes, que todas as amostras apresentaram rugosidade de superfície, mas que há necessidade de outros trabalhos que relacionem a presença desses compostos e sua interferência na osseointegração / Abstract: The aim of this study was to analyze the chemical and topography of the surface of currently utilized implants of commercially pure titanium. A total of eight implants were studied (Conexão - Sistema de Próteses, Lifecore Biomedical, AS Technology, and S - Serson International). Ali samples had treatment of surface. The samples were divided into four groups, containing two implants from the same lot of each manufacturer. The analysis of the samples was performed utilizing spectroscopy and electromicroscopy. Results showed predominance of the elements of titanium, oxygen, zinc, aluminum, silicon, and carbon in ali samples studied. The electromicroscopy showed the rough topography of the surface and uniformity between the implants. In conclusion, there were impurities in the surface of the implants. However, further studies are required to investigate the relationship between these chemical components in the surface of implants and their influence in the process of bony integration / Doutorado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Doutor em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289439 |
Date | 08 January 2003 |
Creators | Sardinha, Sandra de Cassia Santana |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Albergaria-Barbosa, José Ricardo de, 1956-, Bastos, Eider Guimarães, Marcantonio, Elcio, Mazzonetto, Renato, Passeri, Luis Augusto |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 96p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0119 seconds