Orientador: Agenor Montebello Filho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T05:42:06Z (GMT). No. of bitstreams: 1 Faria_MarceloDanielBrito_D.pdf: 2753888 bytes, checksum: f51d5a94ef8d365d8baf63fde380e7aa (MD5) Previous issue date: 2000 / Resumo: Este estudo teve por objetivo avaliar a localização do canal mandibular em imagens obtidas de crânios secos por meio de exames tomográficos lineares, pluridirecionais e computadorizados de alta resolução em relação com a anatomia óssea topográfica. Foram utilizadas 1I mandíbulas secas de humanos pertencentes a Área de Radiologia da Faculdade de Odontologia de Piracicaba FOP-UNICAMP que possuiam extremo livre posterior e reabsorção óssea alveolar moderada tipo B segundo LINDH, C et al ( 1995 ) . Foram analizados 22 (Vinte e dois) Canais mandibulares Inferiores ( CM) e 88 ( Oitenta e oito) medidas foram realizadas. Em cada mandíbula foram feitas 04 ( medidas) : V1 - que correspondeu a distância do rebordo alveolar remanescente ao centro do CM ; V2 - distância da cortical externa da base mandibular ao centro do CM ; H1 distância do centro do CM à cortical externa lingual; H2 - distância do centro do CM à cortical externa vestibular. Foram confeccionados guias radiográficos nas regiões de interesse antes da exposição, sendo esferas metálicas de 3,0 mm de diâmetro para os exames convencionais e guias com guta percha para as tomografias computadorizadas de alta resolução. Os aparelhos utilizados foram ORTHOPHOS CD PLUS da SIRONA com os programas pl9 e p20 de cortes pluridirecionais transversais com kV de 60 e 09 mA e espessura do corte de 3,0mm, o tomógrafo Linear Denar Quint Sectograph com cefalostato e kV 52 e mA 50 e espessura dos cortes de 2,5mm e intervalo entre os cortes de 3,0mm. O tomógrafo computadorizado de alta resolução foi o SOMA TOM HiQ-S da Siemens com cortes coronais diretos que foi baseado no protocólo de FARIA CR-IMP ( 1999). Após obtidas as imagens foram realizadas as medidas com paquímetro MITUTOYO e comparadas com as peças seccionadas obtidas e nossos resultados após aplicado análise de variância e teste de Tuckey foram para a tomografia linear de: A distância V1- 13,19mm ; V2 - 8,73mm ;H1 - 5,11mm e H2 -6,44mm .Tomografia Computadorizada de : V1 11,12mm ; V2 - 7,55mm ; H1 - 5,22mm e H2 - 6,22mm. Pluridirecional de : VI - I5,85mm ; V2 - 1O,17mm ; HI6,45mm e H2 - 8,l0mm. E os dados anatômicos de V1 - 13,O4mm ; V2 - 8,7mm ; HI- 5,36mm e H2 - 6,18mm .Baseado nos resultados das medidas o canal mandibular à 3,5cm posterior ao forame mentoniano apresentou-se mais próximo da cortical lingual e a técnica que apresentou maior precisão nas medidas quando comparadas com a anatomia óssea topográfica foi a Tomografia Linear, pois esta não apresentou diferença estatisticamente significante. Já a tomografia computadorizada demonstrou dados com uma discrepância mínima em relação a anatomia óssea topográfica apresentando diferença estatísticamente significante nas medidas verticais e a técnica pluridirecional apresentou diferença estatísticamente tanto nas medidas verticais como nas horizontais. Logo nosso estudo conclui que a técnica tomográfica mais apurada no que diz respeito as dimensões verticais e horizontais para o planejamento de implantes osteointegráveis foi a Tomografia Linear / Abstract: The aim of this study was compare the vertical and horizontal dimensions in images obtained from dried skulls by means of three types of tomographic exams: linear; transversal pleuridirectional panoramic and computerized high resolution with bone topographic anatomy. The selection of a precise radiographic method proved to be of great importance in the planning of osteointegradable implants. Such approach would imply the reduction of traumatic lesions to noble structures of the maxillomandibular complex during surgery. With this purpose, eleven dried mandibles ITom the Radiology Department of the Dentistry University of Piracicaba.( FOP, Unicamp) were analyzed. All of these presented an edentuous posterior and type B alveolar bone reabsorption according to LINDH, C et al.( 1995 ). Twenty two inferior alveolar canals ( CAI ) were selected and 88 measurements were accomplished. Four measurements were made on each mandible: V1,which corresponded the distance of the alveolar ridge to the center of the CAI; V2, the distance of the external cortical of the mandibular base to the center of the CAI; RI, the distance of the center of the CAI to the external lingual cortical; m, the distance from the center of the CAI to the external bucal cortical. Radiographic guides were built at regions of interest before the exposition of metallic step ( 4mm diameter) for conventional exams. Also, gutta percha guides were introduced for high resolution computerized tomography making possible the elimination of artifacts. The equipment used were the SIRONA, Orthophos CD plus, with pI9 and p20 programs of transversal pleuridirectional slices (60kV and 09 mA and slice thickness of 3,0 mm), the Linear Denar Quint Sectograph tomographer with cefalostat ( 52kV and 50 mA and slice thickness of 2,5 mm and intervals between slices of 3,0mm) and the Siemens, SOMATOM HiQ-S computerized high resolution tomographer, opting for direct coronal slices that were based on the FARIA CR-IMP ( 1999 ) protoco1. After images were obtained, measurements were made with a MITUTOYO paquimeter and compared to the sliced mandibles. The mean results of the measurements were later applied to varience analysis and Tuckey test. The following results were obtained for linear tomography: VI - 13,19 mm; V2 - 8,73 mm; Hl 5,11mm; H2 - 6,44 mm. As for computed tomography: V1- 11,12 mm; V2 - 7,55 mm; H1 - 5,22 mm; H2 - 6,22 mm; while pleuridirectional tomography: V1- 15,85 mm; V2 - 10,17 mm; H1 - 6,45 mm; H2 - 8,10 mm. Further more, the anatomic measurements: VI - 13,04 mm; V2 - 8,70 mm; H1 - 5,36 mm; H2 - 6, 18mm. These results have not proved a significant statistical difference between the mean results of measurements in linear tomography exams. However, the exams computed tomography, once these presented a minimal discrepancy with a significant statistical different in the vertical mensurement when compared to the real anatomic measurements and pluridirectional presented significant statistical difference in alI of the mensurements Fina1ly, this subject conc1udes that linear tomography was more accurate for dental osteointegradable planning / Doutorado / Radiologia Odontologica / Doutor em Radiologia Odontológica

Orientador : Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T19:31:26Z (GMT). No. of bitstreams: 1 Botega_DanielaMaffei_M.pdf: 2444917 bytes, checksum: 5e47f571486882534d0a9fc484da1e9e (MD5) Previous issue date: 2002 / Resumo: Este estudo teve como objetivo avaliar a força de retenção de dois sistemas de encaixe para Overdentures em função do número de ciclos de união e separação dos componentes. Foram confeccionadas 20 amostras, divididas em 4 grupos, 5 por grupo: 1) Sistema O'ring; 2) Sistema Barra-Clip (Conexão Sistemas de Prótese); 3) Sistema O'ring; e 4) Sistema Barra-Clip (Lifecore Biomedical). As amostras imersas em saliva artificial foram submetidas ao ensaio de ciclagem mecânica em máquina servohidráulica MTS-81 O, realizando-se 5500 ciclos de inserção e remoção (0,8 Hz). Durante o ensaio, os valores da força de retenção foram monitorados em 4 registros por meio de ensaio de tração, utilizando o programa Test Work for Test Star (1 mm/min), e célula de carga de I kN: 1Q­ retenção inicial; 2Q- após 1500 ciclos; 3Q- após 3000 ciclos; e 4Q- após 5500 ciclos. Os dados obtidos foram submetidos à Análise de Variância e aplicado o teste de Tukey (p<0,05). Os resultados mostraram que o grupo 2 apresentou resultados superiores ao 4, sendo estatisticamente significantes (44,61 N e 18,44 N, respectivamente). O grupo 1 apresentou valores inferiores ao grupo 3, sendo estatisticamente significantes, exceto em 1500 ciclos, onde os valores não apresentaram diferença (13,91 N e 19,75 N, respectivamente). O grupo 2 apresentou valores sempre superiores ao grupo I, sendo estatisticamente significantes (44,61 N e 13,91 N). Os grupos 3 e 4 apresentaram valores semelhantes (19,75 N e 18,44 N). Desse modo, conclui-se que: os sistemas avaliados neste estudo apresentaram valores de força de retenção satisfatórios antes e após ensaio de ciclagem mecânica, sendo os mais elevados apresentados pelo grupo 2; o ensaio simulando 5 anos de inserção e remoção da prótese não provocou diminuição nos valores da força de retenção ou fratura dos componentes / Abstract: The aim of this study was to evaluate the strength of two Overdenture attachments systems according to the number of insertion and removal cycles. Twenty samples were prepared, divided in 4 groups, 5 specimens in each group as follows: 1) O'ring System and 2) Bar and Clip System (Conexão Sistemas de Prótese); 3) O'ring System and 4) Bar and Clip System (Lifecore Biomedical). The samples imersed in artificial saliva were submitted to mechanical test using a servohidraulic machine MTS-810, performing 5500 cycles of insertion and removal (0.8Hz). The retention force values were controled during the test, recording the values in 4 intervals, using the tensile test (Test Works for Test Star), with speed of Imm/min., and load cel of 1 kN: lst- initial; 2nd after 1500 cycles; 3rd- after 3000 cycles; and 4th - after 5500 cycles. Data were statistically analysed by Variance Analysis followed by Tukey's test (p<0.05). The results obtained showed that group 2 had higher values than group 4, showing significant difference (44.61 N and 18.44 N, respectivelly). Group 1 showed lower values when compared with group 3, being statistically significant, except in 1500 cycles, where there was no difference between them (13.91 N and 19.75 N, respectivelly). The values of group 2 were always higher than group 1, being differents (44.61 N and 13.91 N). Groups 3 and 4 showed similar values (19.75 N and 18.44 N). The conclusion is that: the systems evaluated in this study showed satisfactory values of retention force before and after the mechanical test, and the highest values belonged to group 2; the simulation of 5 years of insertion and removal did not cause a decrease in the values of retention or the components' fracture / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador : Renato Mazzonetto / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T14:39:35Z (GMT). No. of bitstreams: 1 Cravinhos_JulioCesardePaulo_M.pdf: 1159055 bytes, checksum: f08ec26d27fdeac90561fc608b698f2d (MD5) Previous issue date: 2003 / Mestrado

Orientador: Renato Mazzonetto / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T17:47:20Z (GMT). No. of bitstreams: 1 Sardinha_SandradeCassiaSantana_M.pdf: 6176162 bytes, checksum: 1d0646d2b9cfeffe8d23ed9b139c8ee0 (MD5) Previous issue date: 2001 / Resumo: Este trabalho teve como objetivo analisar histologicamente o comportamento do polímero de mamona, do osso humano desmineralizado e do sulfato de cálcio associados a implantes de titânio comercialmente puro, com 2,6 mm de diâmetro e 6 mm de comprimento. Os experimentos foram realizados em ambas as tíbias de 10 coelhos da raça Nova Zelândia, com idade variando entre 6 e 8 meses e peso médio de 3,9 kg. Nas perfurações realizadas em cada tíbia foram colocados o material e o implante, sendo que na perfuração proximal da tíbia direita o implante permaneceu envolvido apenas por sangue, que serviu como controle. Após o período de 12 semanas os animais foram sacrificados e blocos ósseos contendo os implantes, foram fixados, descalcificados e processados para posterior análise histológica em microscopia óptica comum. Os resultados mostraram neoformação óssea e vascular, sem a presença de reação inflamatória do tipo corpo estranho em todos os grupos estudados, não havendo diferenças teciduais locais entre os mesmos / Abstract: The prupose of this study was to evaluate the histoligic behavior of castor plant oil polymer, demineralized Iyophilized human bone, and calcium sulfate when associated with a commercially pure titanium implant. Ten New Zealand rabbits were utilized in this study. The animal age ranged from 6 and 8 months and the mean weight was 3,9kg. Perforations of 2,6mm of diameter and 6mm of depth were drilled in both tibia of each rabbit. The left proximal and distal, and right distal tibia perforations were filled with castor plant oil polymer, demineralized Iyophilized human bone and calcium sulfate, respectively. Each material was combined with a commercially pure titanium implant. The right proximal tibia perforation was filled with commercially pure titanium implant and blood clot to serve as a control group. After a 12 weeks, the rabbits were sacrificed and paraffin blocks of each specime were histologically analyzed. The results showed that ali three materials evaluated did not impede appropriate angionesis and osteogenesis. In addition, there was no histologic evidence of foreign body reaction in any of the implant sites. We ca conclud that there was no difference among ali groups with respect to the interference with angiogenesis and osteogenesis. Furthermore, there was no histologic evidence of rejection of the three materials studied. / Mestrado / Cirurgia / Mestre em Clínica Odontológica

Orientador: Francisco Humberto Nociti Junior / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T10:59:34Z (GMT). No. of bitstreams: 1 Stefani_CristineMiron_D.pdf: 2230659 bytes, checksum: 65f2d179832aebbd74d049ecbf00415b (MD5) Previous issue date: 2001 / Resumo: O objetivo deste estudo foi avaliar a influência da nicotina sobre o reparo ósseo ao redor de implantes de titânio com diferentes tratamentos de superfície colocados em tíbias de coelhos. Trinta e dois coelhos Nova Zelândia, adultos, fêmeas, sob anestesia geral, receberam dois implantes de titânio em cada tíbia, sendo dois usinados e dois jateados com óxido de alumínio. Os animais foram sorteados para receber um dos seguintes tratamentos: a) solução fisiológica, b) 0,18 mg de nicotina /Kg de peso corporal/dia; c) 0,56 mg/Kg/dia; d) 0,93 mg/Kg/dia, através de injeção subcutânea. Após a inserção dos implantes, aos sete e 14 dias, receberam aplicação intramuscular de solução de calceína a 2%, para marcação do tecido ósseo neoformado. Os animais foram sacrificados 42 dias após a colocação dos implantes. Secções não descalcificadas foram avaliadas histometricamente e através de microscopia de fluorescência para os parâmetros: intensidade da marcação do tecido ósseo neoformado, área relativa do tecido ósseo por rosca do implante e extensão relativa de tecido ósseo em contato direto com a superfície do implante. Os dados obtidos foram comparados estatisticamente pelo teste ANOV A. Houve diferença estatística significativa (p=0,015) para o parâmetro extensão do tecido ósseo em contato direto com a superfície do implante entre os implantes com superfície tratada quando comparados aos de superfície usinada, para os grupos que receberam nicotina C e D (37,85% +- 8,85 e 30,13% +- 4,97; 33,13% +- 8,87 e 27,79% +- 3,93, respectivamente). Dentro das condições experimentais empregadas, foi possível concluir que a nicotina não influenciou o reparo ósseo ao redor dos implantes de titânio para os parâmetros avaliados. E implantes com superfície tratada favoreceram a extensão de tecido ósseo em contato direto com a superfície do implante nos animais tratados com nicotina / Abstract: The present study investigated the possible influence of nicotine on the bone healing process around machined and rough surfaced titanium implants inserted in the tibiae of rabbits. Thirty-two female New Zealand rabbits were included. After anesthesia, the tibiae surface was exposed and two screw-shaped commercially available pure titanium implants 7.0 mm in length and 3.75 mm in diameter were placed bilaterally. A total of 128 implants were inserted: 64 with a rough surface rnish (aluminum oxide blasted) and 64 with a machined surface finish. The animals were randomly assigned to one of the four treatment groups, including daily subcutaneous injections of nicotine: a) saline solution, b) 0.18 mg/Kg, c) 0.56 mg/Kg and d) 0.93 mg/Kg. In order to label regenerated bone a 2% calcein green solution was administered by intramuscularly injection at O, 7, 14 days after implant insertion. After 42 days, the animals were sacrificed and undecalcified sections were prepared. The degree of bone contact with the implant surface, the bone area and the intensity of bone labeling were measured into the limits of the threads of the implant. Two way ANOV A were used to compare the results. Statistically significant difference was found for the degree of bone contact with the implant surface between smooth and rough surfaces finishes for C and D groups (30,13% +- 4,97 and 37,85% +- 8,85; 27,79% +- 3,93 and 33,13% +- 8,87, respectively, P=0,015). Within the limits of the present study, it was concluded that nicotine had no effect on the bone repair around titanium implants inserted in rabbit tibiae, and rough surfaced. In implants improved bone/implant contact for nicotine groups / Doutorado / Periodontia / Doutor em Clínica Odontológica

Orientador: Francisco Humberto Nociti Junior / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T16:33:06Z (GMT). No. of bitstreams: 1 Stefani_CristineMiron_M.pdf: 3647273 bytes, checksum: 0b66f43d875767c639ec815978074434 (MD5) Previous issue date: 1999 / Resumo: o objetivo deste estudo foi avaliar histometricamente em cães, a utilização de uma combinação do fator de crescimento derivado de plaquetas (PDGF) e fator de crescimento semelhante à insulina - 1 (IGF-1) ffente à colocação de implantes dentais imediatos. Oito cães adultos foram utilizados neste estudo. Sob anestesia geral, os segundos, terceiros e quartos pré-molares inferiores (P2, P3, P 4) foram extraídos e os alvéolos mesiais de P3 e P 4 dos dois lados da mandíbula receberam implantes dentais de titânio. Aleatoriamente foram determinados o lado teste e o controle, sendo que para o lado teste os implantes receberam 0,10 m1 de gel de metilcelulose a 4%, contendo 5 ~g/m1 de cada um dos fatores PDGF e IGF-1 antes de sua colocação, enquanto os implantes do lado controle receberam apenas 0,10 m1 de gel de metilcelulose a 4% (placebo). Os cães receberam injeção de solução de calceína verde nos períodos de O, 7, 15, 30, 45, 60, 75 e 90 dias para marcação do tecido ósseo neoformado. Os animais foram sacrificados nos períodos de 3, 8 e 12 semanas após a colocação dos implantes. Secções não descalcificadas foram avaliadas histometricamente para as variáveis área de tecido ósseo por rosca do implante, extensão do tecido ósseo em contato direto com a superfície do implante dental e intensidade da marcação do tecido ósseo neoformado. Os dados obtidos foram comparados estatisticamente pelo teste t de Student «.(=0,05) entre os grupos teste e controle para cada tempo experimental e pelo ANOV A nas comparações intragrupos «.(=0,05). Encontrou-se diferença estatística significativa (p=0,002549) para o parâmetro extensão do tecido ósseo em contato direto com a superfície do implante dental entre os grupos teste (22,4 :!: 13,7%) e controle (17,2 :!: 13,6%) no tempo 3 semanas; e entre 3 e 12 semanas (127,8 :!: 42,59 e 56,7 :!: 26,34 respectivamente, em escala de cinzas) para o grupo. teste na variável intensidade da marcação do tecido ósseo neoformado. Ao final do estudo concluiu-se que a combinação de PDGF e IGF-I, dentro das condições experimentais empregadas, demonstrou participação positiva no período inicial da reparação óssea / Abstract: The purpose of the present study was to evaluate bone repair around dental implants placed into immediate extraction sockets, associated or not with local application of a combination of platelet derived growth factor (pDGF) and insulin like growth factor - 1 (IGF-1) on the imp1ant surface. Eight adult dogs were used. Under sodium pentobarbithal inserted bilatera1ly. Before implantation, two of the four implants received a single application of 5~g/m1 ofPDGF and IGF-1 delivered in 0,10 m1 of 4% methylcellulose gel. During the experimental period a 2% calcein green solution was administered O, 7, 15, 30, 45, 60, 75 and 90 days after implant insertion. The animals were sacrificed by a lethal injection of sodium penthobarbital in the periods of 3, 8 and 12 weeks after implant insertion. Undecalcified sections were obtained, submitted to histometric analysis and the results analysed by statistical t test (a=O,05) and ANOV A in intragroups analyses (a=0,05). Statistically different results between test and control groups (22,4 i: 13,7 and 17,2 i: 13,6%, respectivelly) were observed for bone/implant contact at 3 weeks timepoint and for intensity of labelled new bone between 3 and 12 weeks (127,8 i: 42,59 and 56,7 i: 26,34, gray scale values) intragroup for test group. It was concIuded that the combination of PDGFIIGF-1 at present experimental conditions activelly took part of the inicial phase of bone repair / Mestrado / Periodontia / Mestre em Clínica Odontológica

Orientador : Mauro Antonio de Arruda Nobilo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T19:34:10Z (GMT). No. of bitstreams: 1 Kleine_Alessandra_M.pdf: 4693471 bytes, checksum: b0b2b120d9e930bfce154e58a35bc7aa (MD5) Previous issue date: 2002 / Resumo: Este estudo avaliou o assentamento passivo de infra-estruturas de próteses fixas implanto-suportadas, confeccionadas pelas técnicas do cilindro cimentado e soldado a laser. Para tanto, em um arco mandibular edêntulo, construído em aço-cromo, foram fixados cinco análogos de pilares tipo esteticone. Foram obtidos modelos mestres em gesso tipo V (Exadur@ - Polidental). Sobre os modelos, onde estavam incorporadas as réplicas de pilares, foram realizados os procedimentos de enceramento. Foram confeccionadas 20 estruturas metálicas fundidas em titânio comercialmente puro (Tritan@-Dentaurum Pforzhein - Germany), divididas em dois grupos, onde foram confeccionados alívios internos nas estruturas, que permitiram a adaptação dos cilindros de titânio (1 1 l-CNB Conexão Sistemas de Próteses). No grupo dos cilindros soldados, estes foram fixados com resina acrílica (Duralay@) e posteriormente soldados a laser. No grupo dos cilindros cimentados, apenas o cilindro central foi soldado a laser, e os demais cimentados com cimento resinoso (Panavia F@ - Kuraray Co.) As mensurações foram realizadas com auxílio de um microscópio mensurador (STM Digital- Olympus - Japan), com precisão de 0,0005 mm. Os resultados foram submetidos à análise de variância (ANOV A) e ao teste estatístico F, em nível de 5% de probabilidade, demonstrando que para a posição central, o assentamento passivo foi melhor para o grupo «cimentado" (desajuste médio de 25,60::t12,54!J.m) em relação ao grupo «soldado" (99,06::t50,47!J.ffi), p<0,05. Do mesmo modo, em relação à posição distal, o desajuste médio foi menor para o grupo "cimentado" (29,17::t16,16!J.m) em relação ao grupo "soldado" (70,21::t56,70!J.m), p<0,05. A técnica dos cilindros cimentados foi a que apresentou melhores resultados de assentamento passivo / Abstract: The aim of this study was to evaluate the passive fit of fixed implant supported prosthesis titanium frameworks using the cemented cylinder and laser welded cylinder techniques. Thus, in an edentulous mandibular arch, constructed with "chromium steel", five analogous were fixed, parallels, 10mm apart, center to center. Twenty master casts were obtained in dental stone type V (Exadur@ - Polidental). Above the casts where the implant replies were incorporated, the procedures of waxing were made. Twenty frameworks were made and cast in commercially pure titanium (Tritan@-Dentaurum, Pforzhein-Germany) and divided in two groups. In both of then "small canals" were made in the frameworks, that permitted the titanium cylinders' fit. In the laser welded cylinders' group, alI the samples were fixed with acrylic resin (Duralay@-Reliance Dental Co) and after laser welded. In the cemented cylinders' group, only the central cylinder was fixed with acrylic resin and laser welded and the others were cemented with anaerobe resin (panavia F@ - Kuraray Co.). The interfaces' evaluation and measurements were performed using a measurer microscope (Olympus-Japan) with O.OOO5mm of precision. The results were submitted to ANOV A and test F (p<O.O5), showing that, for the central cylinder, the passive fit Was better for the cemented group (mean ill-fit = 25.60:t12.54f.1m) with regard to welded cylinders' group (99.06:t50.47J.1ffi), p<O.O5. In this way, for the distal cylinder, the ill-fit average Was lower for the cemented group (29.17:t16.16f.1m) than welded group (70.21:t56.70J.1ffi), p<O.O5. The cemented cylinders' technique presented the best results of passive fit / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Jose Ricardo de Albergaria-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T05:45:35Z (GMT). No. of bitstreams: 1 Cortez_AndreLuisVieira_M.pdf: 11134343 bytes, checksum: 8b0190a31a9eb9c7df9866709b0d8481 (MD5) Previous issue date: 2002 / Mestrado

Orientador : Francisco Humberto Nociti Junior / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T08:19:23Z (GMT). No. of bitstreams: 1 Duarte_PolianaMendes_M.pdf: 3070725 bytes, checksum: 184f3c24f30630c6e7026d2feed39536 (MD5) Previous issue date: 2003 / Resumo: o objetivo desse estudo foi avaliar a influência do estrógeno (E) e da calcitonina (CT) sobre o reparo e densidade óssea ao redor de implantes inseridos em ratas ovariectomizadas (OVX). Cinqüenta e oito animais foram divididos aleatoriamente em quatro grupos experimentais: Grupo 1 (n=15): ovariectomia simulada; Grupo 2 (n=15): ovariectomia; Grupo 3 (n=14): OVX e administração subcutânea de CT, 4 dias por semana (16 IU/Kg), um dia após OVX durante todo período experimental; Grupo 4 (n=14): OVX e administração diária de 1713 estradiol (20Jl9/Kg) um dia após OVX durante todo período experimental. Vinte e um dias após a ovariectomia bilateral, cada animal recebeu um implante de titânio rosqueável por tíbia. Após sessenta dias da colocação dos implantes os animais foram sacrificados e obtidas secçóes não-descalcificadas. Os parâmetros histométricos analisados foram: densidade óssea (DO) numa região de 500 Jlm lateral ao implante, contato direto osso-implante (CD) e área óssea dentro das roscas (AO). Os resultados foram obtidos e avaliados separadamente na região cortical (zona A) e medular (zona B). Na zona A, a análise intergrupo não demonstrou diferenças estatisticamente significantes para o CD e DO (P>0.05). Em contraste, o grupo 4 demonstrou maior área óssea que os grupos 2 e 3 (P<0.05). Resultados obtidos da zona B revelaram que o estrógeno anulou o efeito negativo da ovariectomia na DO, CD e AO (P<O.05), enquanto a calcitonina não apresentou o mesmo efeito (P>0.05). Dentro dos limites desse estudo, conclui-se que a administração diária de estrógeno pode prevenir a influência negativa da deficiência do estrógeno endógeno no reparo e densidade óssea ao redor de implantes de titânio / Abstract: This study evaluated whether estrogen (E) and calcitonin (CT) administration could influence bone healing and bone density around implants placed in ovariectomized rats (OVX). Twenty-one days betore implant placement, bilateral ovariectomies were performed trom a dorsal approach. One screw-shaped titanium implant was placed bilaterally. The animais were assigned to one of the tollowing groups: Group 1 (n=15): sham surgeries; Group 2 (n=15): OVX rats; Group 3 (n=14): OVX rats subcutaneously administered with calcitonin (CT) 4 days/week (16 IU/Kg); Group 4 (n=14): OVX rats subcutaneously administered with 1713 estradiol daily (20Jlg/Kg). After sixty days, the animais were sacrificed and undecalcified sections obtained. Bone density (8D) (the proportion of mineralized bone in a 500 Jlm-wide zone lateral to the implant), bone-to-implant contact (B/C) and bone area (BA) around the implants were obtained and arranged separately for the cortical (Zone A) and cancellous(Zone B). In Zone A, intergroup analysis revealed no significant difference regarding BIC and BD (P>0.05). In contrast, the group 4 presented a greater bone area than groups 2 and 3 (P<0.05). Data trem Zone B revealed that estrogen nullified the negative effect of the ovariectomy on BD, BIC and BA (P<0.05), while CT presented no effect (P>O.05). Therefore, E-therapy may prevent the influence that endogenous estrogen deficiency exerts on bone healing and bane density around titanium implants / Mestrado / Periodontia / Mestre em Clínica Odontológica

Orientador : Altair Antoninha Del Bel Cury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T15:10:15Z (GMT). No. of bitstreams: 1 Meirelles_LuizAugustoDuarte_M.pdf: 2064072 bytes, checksum: 38b14046d2439ff6fc794b7affc652c2 (MD5) Previous issue date: 2003 / Resumo: Este estudo analisou a distribuição de tensões pela simulação de esforços mastigatórios em tomo a implantes dentários cilíndricos rosqueados com hexágono externo e interno. Foram recortados blocos de policarbonato PSM-l (Photolastic mc. Realeigh, USA) com dimensões de 35 x 25 x 6,1 mm, nos quais foram instalados os implantes dentários. Foram utilizados dois implantes de 3,75 de diâmetro e 10,0 mm de comprimento com hexágono externo e interno (Master Screw e Master Conect AR, Conexão Sistemas de Prótese, São Paulo, Brasil). O carregamento de 10 kgF foi aplicado por um dispositivo mecânico acoplado a uma célula de carga com 15° de inclinação em relação ao implante. Cada implante foi levado individualmente ao polariscópio circular para a visualização e interpretação das franjas fotoelásticas, obtendo-se valores numéricos que correspondem à ordem de franja para cada ponto traçado em tomo do implante sobre a imagem obtida. Foi possível observar padrões de distribuição de tensões distintos quanto à região entre os implantes. O implante com hexágono externo apresentou valores maiores na primeira rosca e na região cervical, enquanto o implante com hexágono interno apresentou valores maiores na região apical do implante. Nas demais regiões os valores encontrados foram similares / Abstract: This study analyzed the stress distribution around cylindrical screwed implants with external and internal hexagon simulating occlusion load. Blocks of PSM-1 (Photolastic mc., Realeigh, USA) were milled with dimensions of 35 x 25 x 6,1 mm where the implants were installed. Implants with diameter of 3.75 mm and high of 10.0 mm with external and internal hexagon (Master Screw and Master Conect AR, Conexão Sistemas de Prótese, São Paulo, Brasil). Load was applied with a mechanical device with a load cell with 15 degrees. Each implants were taken separately to a circular polariscope for the observation and interpretation of the photoelastic fringes. Numerical values of the fringe order were obtained for each point marked around the implants images. It was possible to verify different patterns of stress distribution regarding the area and intensity between the implants under 10 kgF load. Highest values was observed in the implant with external hexagon at the cervical area and at the first screw and in the implant with internal hexagon at the apex of the implant. The remaining areas presented similar values / Mestrado / Protese Dental / Mestre em Clínica Odontológica