Uma série de complexos de tricloreto do grupo 4, coordenados com ligantes tridentados, foram estudados na homopolimerização de etileno e copolimerização etileno/hexeno. Os complexos (Ln)TiCl3, n = 1 – 4 (L1 = 3,5-tBu-2-(OH)C6H2CH-N-8- C9H6N, L2 = 3,5-tBu-2-(OH)C6H2CH-N-C2H4-O-C6H5, L3 = 3,5-tBu-2-(OH)C6H2CHN- CH2-C6H4OMe e L4 = 3,5-tBu-2-(OH)C6H2CH-N-C6H4-O-C6H5), foram sintetizados pela reação do respectivo pré-ligante, com 1 eq de TiCl4 a -94 ºC, formando os complexos Ti1 – Ti4. Os complexos (L1)ZrCl3 (Zr1) e (L1)HfCl3 (Hf1) foram sintetizados pela reação do sal de lítio do ligante Li(L1) a -94 ºC, com ZrCl4(THF)2 e HfCl4(THF)2, respectivamente. Quando ativados com PMAO-IP a 60ºC, os complexos de titânio Ti1 – Ti4 apresentaram atividades altas (200 – 660 kg de PE/mol[M]·h·bar) e geraram polímeros com pesos moleculares viscosimétricos (PMv) entre 184 – 355 kg/mol. Os précatalisadores Zr1 e Hf1 tiveram atividade moderada (40 – 50 kg de PE/mol[M]·h·bar) e PMv entre 700 e 620 kg/mol respectivamente. A distribuição do peso molecular dos polímeros produzidos com Ti1 – Ti4 foi investigada por reologia dinâmica, gerando um índice de polidispersão calculado superior a 25. Ti1 e Ti4 produziram copolímeros etileno/1-hexeno com alto rendimento e alto teor de comonômero incorporado (2,4 %mol, 0,33 M de 1-hexeno, 60ºC). Ti1 foi termicamente estável de 30 - 80ºC, com máximo de atividade em 60 ºC. Variando a quantidade de cocatalisador, a maior atividade catalítica para polimerização de eteno foi obtida na razão [PMAO]/[Ti1] = 2200. Imobilizado em sílica/PMAO o complexo Ti1 apresentou atividade 160 kg de PE/mol[M]·h·bar e PMv = 720 kg/mol. / A series of Group 4 trichlorides complexes bearing tridentate ligands, were studied and employed as catalysts in ethylene polymerization and ethylene/1-hexene copolymerization. Complexes (Ln)TiCl3, n = 1 – 4 (L1 = 3,5-tBu-2-(OH)C6H2CH-N-8- C9H6N, L2 = 3,5-tBu-2-(OH)C6H2CH-N-C2H4-O-C6H5, L3 = 3,5-tBu-2-(OH)C6H2CHN- CH2-C6H4OMe e L4 = 3,5-tBu-2-(OH)C6H2CH-N-C6H4-O-C6H5), were synthesized by reaction of corresponding pre ligand with 1 eq TiCl4 at -94 ºC, producing complexes Ti1 – Ti4. Complexes (L1)ZrCl3 (Zr1) e (L1)HfCl3 (Hf1) were synthesized by treatment of lithium ligand salt Li(L1) at -94 ºC, with ZrCl4(THF)2 and HfCl4(THF)2, respectively. Activated by PMAO at 60 ºC, titanium complexes Ti1 – Ti4 reached high polymerization activity (200 – 660 kg of PE/mol[M]·h·bar) and produced polymers with viscosimetric molecular weight (Mv) between 184 – 355 kg/mol. Pre catalysts Zr1 and Hf1 showed moderate activity (40 – 50 kg de PE/mol[M]·h·bar) and Mv from 700 to 620 kg/mol respectively. Polymer molecular weight distribution obtained with Ti1 – Ti4 was investigated by dynamic reology, producing polidispersivity index calculated higher than 25. Ti1 and Ti4 generated copolymer ethylene/1-hexene with high yield and high comonomero content (2,4 %mol, 0,33 M of 1-hexene, 60ºC). Ti1 was thermally stable from 30 to 80ºC, with maximum activity at 60 ºC. Varing the amount of cocatalyst, the highest activity for ethylene polymerization was achieved using ratio [PMAO]/[Ti1] = 2200. Immobilized over silica/PMAO, complex Ti1 achieved activity of 160 kg de PE/mol[M]·h·bar and Mv = 720 kg/mol.
| Identifer | oai:union.ndltd.org:IBICT/oai:lume.ufrgs.br:10183/102026 |
| Date | January 2012 |
| Creators | Gomes, Fernando da Silva |
| Contributors | Casagrande Júnior, Osvaldo de Lázaro |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFRGS, instname:Universidade Federal do Rio Grande do Sul, instacron:UFRGS |
| Rights | info:eu-repo/semantics/openAccess |