Compósitos de PVC reforçados com fibra de vidro: uso de técnicas de processamento convencionais da indústria brasileira. / Glass fiber reinforced PVC composites: use of conventional processing techniques currently employed in the Brazilian industry.

Este trabalho apresenta o estudo da incorporação de fibra de vidro curta em composto rígido de poli(cloreto de vinila) - PVC - por meio de equipamentos e técnicas de processamento convencionais da indústria brasileira. Foram avaliadas as influências de: a) tamanho de fibra de vidro (tipo E), b) dosagem de fibra de vidro, c) dosagem de dióxido de titânio (TiO2) e d) a temperatura de processamento nas propriedades físicas, térmicas, mecânicas e na adesão entre matriz polimérica e fibra de vidro (analisada por Microscopia Eletrônica de Varredura). O custo-benefício dos compósitos foi calculado por meio de Índices de Mérito para os modos de carregamento mecânico encontrados nos tubos pressurizados para água fria (Cilindro com Pressão Interna) e perfis rígidos utilizados em construção civil (Barra em Flexão), dado o grande uso de PVC nestas aplicações. Entre os resultados obtidos, destaca-se o aumento de 45% no módulo de elasticidade para os compósitos com 20% de fibra de vidro moída que, para algumas aplicações, pode apresentar uma relação custo-benefício bastante favorável. / This work presents the impact of the short glass fiber incorporation in rigid PVC compound through conventional processing techniques currently employed in the Brazilian industry. It were studied the influences of a) glass fiber geometry (E type), b) glass fiber content, c) titanium dioxide content and d) processing temperature in the physical, mechanical and thermal properties. The adhesion conditions between polymeric matrix and glass fiber was analyzed by scanning electron microscopy (SEM). Cost-benefit relation of composites was evaluated using materials index technique for mechanical conditions found in pressurized water pipes (cylinder with internal pressure) and in building construction profiles (beam loaded in bending). The results attained suggested that, in some cases, the mechanical properties enhancement (such as the increase of 45% in the modulus of elasticity for composites containing 20% of glass fiber) and the processing techniques required to produce it can present an interesting cost-benefit relation.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-28032008-171828
Date15 February 2008
CreatorsFeltran, Murilo de Barros
ContributorsValenzuela Díaz, Francisco Rolando
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0021 seconds