Experimental and theoretical study of on-chip back-end-of-line (BEOL) stack fracture during flip-chip reflow assembly

With continued feature size reduction in microelectronics and with more than a billion transistors on a single integrated circuit (IC), on-chip interconnection has become a challenge in terms of processing-, electrical-, thermal-, and mechanical perspective. Today’s high-performance ICs have on-chip back-end-of-line (BEOL) layers that consist of copper traces and vias interspersed with low-k dielectric materials. These layers have thicknesses in the range of 100 nm near the transistors and 1000 nm away from the transistors close to the solder bumps. In such BEOL layered stacks, cracking and/or delamination is a common failure mode due to the low mechanical and adhesive strength of the dielectric materials as well as due to high thermally-induced stresses. However, there are no available cohesive zone models and parameters to study such interfacial cracks in sub-micron thick microelectronic layers.
This work focuses on developing framework based on cohesive zone modeling approach to study interfacial delamination in sub-micron thick layers. Such a framework is then successfully applied to predict microelectronic device reliability. As intentionally creating pre-fabricated cracks in such interfaces is difficult, this work examines a combination of four-point bend and double-cantilever beam tests to create initial cracks and to develop cohesive zone parameters over a range of mode-mixity. Similarly, a combination of four-point bend and end-notch flexure tests is used to cover additional range of mode-mixity. In these tests, silicon wafers obtained from wafer foundry are used for experimental characterization. The developed parameters are then used in actual microelectronic device to predict the onset and propagation of crack, and the results from such predictions are successfully validated with experimental data. In addition, nanoindenter-based shear test technique designed specifically for this study is demonstrated. The new test technique can address different mode mixities compared to the other interfacial fracture characterization tests, is sensitive to capture the change in fracture parameter due to changes in local trace pattern variations around the vicinity of bump and the test mimics the forces experienced by the bump during flip-chip assembly reflow process. Through this experimental and theoretical modeling research, guidelines are also developed for the reliable design of BEOL stacks for current and next-generation microelectronic devices.

Identiferoai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/54298
Date07 January 2016
CreatorsRaghavan, Sathyanarayanan
ContributorsSitaraman, Suresh
PublisherGeorgia Institute of Technology
Source SetsGeorgia Tech Electronic Thesis and Dissertation Archive
Languageen_US
Detected LanguageEnglish
TypeDissertation
Formatapplication/pdf

Page generated in 0.002 seconds