Orientadores: Cecilia Amelia de Carvalho Zavaglia, Raul Garcia Carrodeguas / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-15T14:41:52Z (GMT). No. of bitstreams: 1
Motisuke_Mariana_D.pdf: 16445878 bytes, checksum: 24051dcb16ae3df67a3a90e36fb1c391 (MD5)
Previous issue date: 2010 / Resumo: A necessidade de novos biomateriais que permitem considerável melhora na qualidade de vida de pessoas que sofrem de doenças relacionadas à velhice ou que apresentam algum tipo de lesão no tecido ósseo advindas de acidentes ou doenças como a obesidade e o câncer tem despertado o interesse dos pesquisadores. Neste contexto, o desenvolvimento de novos biomateriais para a ortopedia baseados nos fosfatos de cálcio é relevante uma vez que estes apresentam excelente biocompatibilidae e bioatividade devido à sua composição química semelhante à fase mineral de ossos e dentes. A substituição por silicato de alguns grupos fosfatos é, hoje em dia, uma área muito promissora no desenvolvimento de fosfatos de cálcio uma vez que a presença deste elemento pode aumentar a bioatividade e estimular a diferenciação das células aderidas à superfície dos substitutos ósseos. Dentre estes materiais, o que recebe grande destaque é o Si-a-TCP, que se utilizado como cimento ósseo promete resultados interessantes. Além disso, o silício atua como um elemento estabilizante da fase a, tornando possível a sua formação em temperaturas mais baixas que as normalmente empregadas e, por isso, reduzindo os custos de sua síntese. Assim, o principal objetivo deste trabalho é investigar a influência do Si nas propriedades químicas, físicas, mecânicas, de biocompatibilidade e de bioatividade do cimento de a-TCP. No entanto, a síntese do a-TCP puro não é uma tarefa simples, uma vez que muitas condições de processo podem alterar suas propriedades finais ou, ainda, inibir a sua formação. O fator de maior influência é a qualidade dos reagentes de partida, que pode impossibilitar a formação de a-TCP em temperaturas tão altas como 1600°C, comprometendo a reprodutibilidade de seu processamento. Portanto, em conjunto com o desenvolvimento do Si-a-TCP, foram sintetizados reagentes com elevado teor de pureza, ou seja, livres da principal impureza que interfere na síntese do a-TCP, o magnésio. Este elemento é um famoso estabilizante da fase ß e eleva a temperatura de transição de fase ß??a para até 1500ºC. Verificou-se que a padronização das propriedades dos reagentes de partida garantiu a reprodutibilidade do processo de fabricação do a-TCP. Porém, observou-se que o Si reduz em quase quatro vezes a reatividade do a-TCP uma vez que por estabilizar a fase a, torna o material menos solúvel. Além disso, devido a esta baixa reatividade do pó com silício a resistência mecânica do cimento ósseo nos primeiros instantes de cura foi extremamente baixa (0,81 ± 0,25 MPa). Mesmo assim, alcançou valores similares ao cimento sem silício (18 MPa para o a-TCP e 15 MPa para o Si-a-TCP) após 168 horas de cura. Por outro lado, a biocompatibilidade e a formação de uma camada de apatita na superfície dos cimentos após ensaio em Fluido Corpóreo Simulado demonstram que o silício
interfere positivamente nos processos de regeneração óssea. Foi possível desenvolver um novo cimento ósseo baseado no Si-a-TCP obtido a partir de reagentes sintetizados em laboratório que garantiram uma considerável redução de custos de síntese e um elevado teor de pureza. A produção dos precursores CaCO3, CaHPO4 e CaSiO3 em laboratório foi a etapa mais significante para a redução de custos uma vez que a baixa quantidade de impurezas presentes é responsável pela menor temperatura de síntese necessária (1200°C para o Si-a-TCP e 1300°C para o a-TCP) e o consequente aumento na facilidade de processamento (moagem) e na bioatividade em FCS do cimento ósseo. Os resultados obtidos neste trabalho demonstram que foi desenvolvida tecnologia nacional para a produção de um cimento ósseo com potencial de aplicação clínica e que será mais acessível à população brasileira. / Abstract: The need for new biomaterials which could improve life quality of people who suffer from oldness diseases or who have any bone tissue injury due to accidents and diseases like obesity and cancer are resulting in a growing number of researches. In this context, the development of new orthopedics biomaterials based on calcium phosphates compounds is relevant once they present excellent bioactivity and biocompatibility due to its chemical composition similar to the mineral part of bone and teeth. Silicon substitution into some phosphorous sites of calcium phosphate bioceramics is a promising field on the development of new biomaterials for orthopedics applications due to the increased bioactivity and cell differentiation on the material's surface which could be promoted by the presence of this element. In this manner, Si-a-TCP is receiving huge efforts since its employment as bone cement could be of great interest. Moreover, silicon is known to stabilize the a-TCP structure and to promote its formation at lower temperatures leading to a cost reduction of its processing. Thus, the major objective of this study is to investigate the influence of Si on the chemical, physical, mechanical, biocompatible and bioactive properties of the calcium phosphate cement once there is a lack of publication regarding this material. On the other hand, the synthesis of a pure a-tricalcium phosphate is not an easy task since all process conditions can change its final properties, or even inhibit its formation. The most limiting factor is the quality of the starting reagents which may preclude the formation of a-TCP at temperatures as high as 1600° C. Therefore, the reproducibility of a-TCP synthesis becomes very difficult and, in some cases, impossible. In this context, and together with the development of Si-a-TCP, high purity reagents were synthesized to eliminate the most important impurity which is an established stabilizer element of ß-TCP, magnesium. It has been discovered that the standardization of the reagents properties guaranteed the reproducibility of a-TCP manufacturing process. Nevertheless, it was also observed that Si has a strong influence on the setting reaction of the cement by reducing by almost four times the TCP reactivity once this element stabilizes the a-TCP structure and the final material is less soluble. As a result, the mechanical strength of the cement at initial times was extremely low (0,81 ± 0,25 MPa) even though it has achieved similar values to the cement without silicon after 168 hours of setting (18 MPa for a-TCP e 15 MPa for Si-a-TCP). Nonetheless, the biocompatibility after in vivo study and the precipitation of an apatite layer after SBF immersion lead to the conclusion that Si has a positive interference on the bone regeneration process. It was possible to develop a new calcium phosphate cement based on Si-a-TCP obtained from laboratory synthesized reagents which lead to a considerable reduction on the production costs and in a high purity level of the final material. The synthesis of CaCO3, CaHPO4 and CaSiO3 with low contents of impurities was the most significant step to cost reduction due to the lower temperatures needed to synthesize Si-a-TCP (1200°C) and a-TCP (1300°C), the enhanced facility on milling and the improved bone cement bioactivity in Simulated Body Fluid. National technology was developed in order to guarantee the production of a bone cement which has a huge potential to clinical application and, certainly, it will be more accessible to Brazilian people. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263563 |
| Date | 15 August 2018 |
| Creators | Motisuke, Mariana |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Carrodeguas, Raul Garcia, Zavaglia, Cecília Amélia de Carvalho, 1954-, Freire, Celia Marina Alvarenga, Bertran, Celso Aparecido, Bressiani, Jose Carlos, Fortulan, Carlos Alberto |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 160 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds