Previous issue date: 2008-02-26 / Atualmente na área de biomateriais destinados à regeneração óssea, existe um interesse no desenvolvimento de materiais capazes de estimular a resposta biológica necessária para restabelecer as funções do tecido ósseo em caso de perda, falta ou mau funcionamento. A hidroxiapatita (HA, Caio(P04)6(OH)2) que apresenta semelhança com a fase mineral dos ossos e dos dentes, é biocompatível e osteocondutiva, e tem excelente afinidade química e biológica com os tecidos ósseos. Este trabalho teve como objetivo
desenvolver biocerâmicas porosas para regeneração óssea utilizando a técnica réplica da esponja polimérica. Foram utilizadas esponjas de poliuretano com densidades variadas para a obtenção dos suportes porosos. Os resultados de espectroscopia no infravermelho e difração de raios X revelaram a formação da HA monofásica e confirmaram a eficiência da reação de neutralização utilizada na obtenção da pasta cerâmica. As análises por microscopia eletrônica de varredura revelaram suportes com poros interconectados com tamanhos variados na ordem de macro (>100um) e microporosidade (1-20um) em menor
ou maior grau dependendo da densidade da esponja utilizada na produção das amostras. Estes resultados foram comprovados pela análise de porosimetria de mercúrio. Os suportes porosos HAPU-28 destacaram-se por apresentar maior porosidade total em comparação com os suportes produzidos com esponja de menor densidade (HAPU-20 e HAPU-25). Os resultados apontam os suportes porosos de HA desenvolvidos nesse estudo como materiais em potencial para aplicação como substitutos ósseos por apresentarem alta porosidade (>70%), composição química, interconectividade e tamanhos dos poros adequados à regeneração óssea. / Currently in the area of biomateriais destined for bone regeneration, exists an interest in the development of materiais capable to stimulate the biological reply necessary to reestablish the functions of the bone tissue in loss, lack or bad functioning case. The hydroxyapatite (HA, Caio(P04)6(OH)2) that shows similarity with the mineral phase of bone and teeth, it is biocompatible and osteoconductive, and has excellent chemical and biological affinity with the bone tissue. This study aimed to develop porous bioceramics for bone regeneration using the replica of the polymeric sponge technique. Polyurethane
sponges were used with varying densities to obtain the scaffolds. Results of infrared spectroscopy and X-ray diffraction analysis revealed the formation of the HA monophasic and confirmed the efficiency of the neutralization reaction used in obtaining the slurry ceramics. Analyses by scanning electron microscopy revealed scaffolds with interconnected pores with different sizes on the order of macro and microporosity to a lesser or greater degree depending on the density of foam used in the production of samples. These results were proven by the analysis of the mercury porosimetry. The porous scaffold HAPU28 detached by showing higher total porosity compared to scaffold produced with sponge of lower density (HAPU-20 and HAPU-25). The results indicate the
porous HA scaffolds developed in this study as potential materiais for application as bone substitutes to have high porosity (> 70%), chemical composition, interconnectivity and pore sizes appropriate to the bone regeneration.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/2017 |
Date | 18 October 2018 |
Creators | FOOK, Ana Carolina Brasil Marcelino., MARCELINO, Ana Carolina Brasil. |
Contributors | FOOK, Marcus Vinícius Lia., SANTANA, Lisiane Navarro de Lima., SOUSA, Lucina Rocha. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0132 seconds