Efficient and robust blue InGaN multiple quantum well (MQW) light emitters have become ubiquitous; however, they still have unattained theoretical potential. It is widely accepted that “localization” of carriers due to indium fluctuations theoretically enhance their efficiency by moderating defect-associated nonradiative recombination. To help develop a complete understanding of localization effects on carrier dynamics, this thesis explores degree of localization in InGaN MQWs and its dependence on well thickness and number of wells, through temperature and power dependent photoluminescence measurements. Additionally, silicon-compatible, nontoxic, colloidally synthesizable 2-5 nm Ge1-xSnx alloy quantum-dots (QDs) are explored for potential visible to near-IR optoelectronic applications. While bulk Ge is an indirect gap material, QD confinement allows enhanced direct transitions, and alloying with Sn improves transition oscillator strengths. Temperature dependent steady-state and time-resolved photoluminescence reveal relaxation pathways involving bright/dark excitons and surface states in Ge1-xSnx QDs, showing their great potential for future use.
Identifer | oai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-6276 |
Date | 01 January 2017 |
Creators | Nakagawara, Tanner A |
Publisher | VCU Scholars Compass |
Source Sets | Virginia Commonwealth University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Rights | © The Author |
Page generated in 0.0016 seconds