In this experimental investigation, the tensile creep behavior of commercial-purity molybdenum sheet at temperatures between 1300°C and 1700°C is critically evaluated, based upon experimental creep testing and microstructural characterizations. The high-temperature properties of molybdenum are of interest because there are many applications in which molybdenum and molybdenum alloys are used at elevated temperatures. Understanding of the creep mechanisms and the constitutive relations between stress and strain at elevated temperatures is needed in order to determine if molybdenum is an appropriate choice for a given high-temperature design application and to accurately predict its creep life. The creep behavior of two commercially-available grades of molybdenum was determined using short-term creep tests (1/2 to 14 hours) at slow to moderate true-strain rates of 10⁻⁶ to 10⁻⁴ s⁻¹ and temperatures between 1300°C and 1700°C. High-temperature, uniaxial tensile testing was used to produce data defining the relationship between tensile creep strain-rate and steady-state flow stress at four temperatures: 1340°C, 1440°C, 1540°C, 1640°C. Microstructural changes that occurred during creep testing were evaluated and compared to changes resulting from elevated temperature exposure alone. Mechanisms for dynamic abnormal grain growth that occurred during creep testing and the causes of the microstructural changes that occurred as a function of temperature are discussed. / text
| Identifer | oai:union.ndltd.org:UTEXAS/oai:repositories.lib.utexas.edu:2152/9678 |
| Date | 21 January 2011 |
| Creators | Ciulik, James R. |
| Source Sets | University of Texas |
| Language | English |
| Detected Language | English |
| Format | electronic |
| Rights | Copyright is held by the author. Presentation of this material on the Libraries' web site by University Libraries, The University of Texas at Austin was made possible under a limited license grant from the author who has retained all copyrights in the works. |
Page generated in 0.002 seconds