Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2015 / Made available in DSpace on 2016-02-09T03:13:30Z (GMT). No. of bitstreams: 1
337468.pdf: 2551108 bytes, checksum: f1ebd900c498ad4fd0b693641b47a291 (MD5)
Previous issue date: 2015 / Um dos mais eficientes métodos de dispersão de materiais é o uso de um agente dispersante (em geral, um aditivo superplastificante de base policarboxilato) em conjunto com um equipamento que gera ondas ultrassônicas. Essa dispersão ocorre pela formação de bolhas de cavitação, que colapsam e desaglomeram as partículas. Porém, a literatura sugere que tal método danifica os materiais sonicados e compromete o desempenho de trabalhabilidade e fluidez de pastas cimentícias elaboradas com esse aditivo de base policarboxilato (SP). Neste trabalho, investigaram-se os efeitos das ondas ultrassônicas (sonicação) no aditivo SP utilizado na elaboração de pastas cimentícias. Para isso, primeiramente verificou-se, através da termogravimetria e calorimetria diferencial de varredura, que não há variação de massa nem transição de fase em função da temperatura e fluxo de calor entre 0 e 110º C. Após isso, diversas soluções diluídas e concentradas de aditivo SP foram analisadas por meio de espectrofotometria na região do infravermelho, a fim de definir a sensibilidade da técnica e do equipamento utilizado na detecção de alterações na estrutura polimérica do aditivo sob investigação. Após essa avaliação, o aditivo foi sonicado em diversas amplitudes de sonicação por três tempos de duração distintos, e pastas cimentícias foram elaboradas com cada solução de aditivo sonicado. Através do ensaio de espectroscopia na região do infravermelho, pode-se observar que houve alterações na molécula de policarboxilato, apesar de que seus principais grupos puderam ser distinguidos. Os comportamentos reológicos de pastas no estado fresco foram avaliados por meio de reometria aos 5, 30 e 60 minutos, após o primeiro contato do cimento com a água. Foi possível verificar que certas pastas elaboradas com aditivo pré-tratado por sonicação apresentaram comportamento reológico distinto ao da pasta sem aditivo pré-tratado. Ainda, em certos casos, para uma mesma pasta, o comportamento foi atípico entre seus próprios parâmetros reológicos, dificultando a formulação de hipóteses conclusivas que relacionem a sonicação de aditivo SP e alterações no seu desempenho. Mesmo assim, é possível verificar que a sonicação comprometeu o desempenho reológico das pastas.<br> / Abstract : One of the most efficient methods to disperse material is using a dispersing agent (typically a polycarboxylate based superplasticizer) together with an equipment that produces ultrasonic waves. Such dispersion occurs by creating cavitation bubbles, which collapse and deagglomerate the particles. However, the literature suggests that such method damages sonicated materials and compromises the performance of workability and flow of cement pastes prepared with this polycarboxylate base admixture (SP). This study investigated the effects of ultrasound waves (sonication) in SP admixture used to prepare cement pastes. For this, first it was found by thermogravimetry and differential scanning calorimetry, there is no weight change or phase transition as a function of temperature and heat flux between 0 and 110o C. After that, several dilute and concentrated solutions of SP admixture were analyzed by spectrophotometry in the infrared region in order to set the sensitivity of the technique and equipment used in detecting changes in the polymer structure of the admixture under investigation. After this evaluation, the admixture was sonicated in various amplitudes of sonication for three different duration times, and cement pastes were prepared with each sonicated admixture solution. Through the spectroscopy in the infrared region test, it can be seen that are changes in polycarboxylate molecule, even though its major groups could be distinguished. The rheological behavior of fresh pastes were evaluated by rheometry at 5, 30 and 60 minutes after the first contact of the cement with water. It was observed that certain pastes prepared with pre-treated by sonication admixture showed distinct rheological behavior of without pre-treated admixture pastes. Furthermore, in certain cases, for a same cement paste, the behavior was atypical of its own rheologic parameters, making it difficult to formulate conclusive hypotheses relate to sonication SP admixture and changes in its performance. Even then, it s still possible to verify that sonication has compromised the rheological performance of cementitious pastes.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/158872 |
Date | January 2015 |
Creators | Carlesso, Débora Martinello |
Contributors | Universidade Federal de Santa Catarina, Repette, Wellington Longuini |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 139 p.| il., grafs., tabs. |
Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds