Zirconium-doped tantalum oxide high-k gate dielectric films

A new high-k dielectric material, i.e., zirconium-doped tantalum oxide (Zr-doped TaOx), in the form of a sputter-deposited thin film with a thickness range of 5-100 nm, has been studied. Important applications of this new dielectric material include the gate dielectric layer for the next generation metal-oxide-semiconductor field effect transistor (MOSFET). Due to the aggressive device scaling in ultra-large-scale integrated circuitry (ULSI), the ultra-thin conventional gate oxide (SiO2) is unacceptable for many practical reasons. By replacing the SiO2 layer with a high dielectric constant material (high-k), many of the problems can be solved. In this study, a novel high-k dielectric thin film, i.e., TaOx doped with Zr, was deposited and studied. The filmÂ’s electrical, chemical, and structural properties were investigated experimentally. The Zr dopant concentration and the thermal treatment condition were studied with respect to gas composition, pressure, temperature, and annealing time. Interface layer formation and properties were studied with or without an inserted thin tantalum nitride (TaNx) layer. The gate electrode material influence on the dielectric properties was also investigated. Four types of gate materials, i.e., aluminum (Al), molybdenum (Mo), molybdenum nitride (MoN), and tungsten nitride (WN), were used in this study. The films were analyzed with ESCA, XRD, SIMS, and TEM. Films were made into MOS capacitors and characterized using I-V and C-V curves. Many promising results were obtained using this kind of high-k film. It is potentially applicable to future MOS devices.

Identiferoai:union.ndltd.org:TEXASAandM/oai:repository.tamu.edu:1969.1/1346
Date17 February 2005
CreatorsTewg, Jun-Yen
ContributorsKuo, Yue, Hall, Kenneth R., Weichold, Mark H., Eubank, Philip T.
PublisherTexas A&M University
Source SetsTexas A and M University
Languageen_US
Detected LanguageEnglish
TypeElectronic Dissertation, text
Format4352230 bytes, electronic, application/pdf, born digital

Page generated in 0.0026 seconds