Previous issue date: 2015-02-12 / Capes / O efeito da incorporação, purificação e organofilização de uma carga mineral
nanoparticulada (argila bentonítica), nas propriedades mecânicas, térmicas e
morfológicas de sistemas PHB poli(3-hidroxibutirato)/bentonita com
concentrações de argila variando de 1 a 3% em massa foi avaliado. As argilas
bentoníticas nas suas formas natural, purificada por ultrassom e organofílica
com sal Cetremide, foram caracterizadas por FTIR e DRX antes de serem
incorporadas ao PHB. As composições obtidas foram caracterizadas por
difração de raios X (DRX), calorimetria exploratória diferencial (DSC), análise
dinâmico-mecânica (DMA), microscopia eletrônica de varredura (MEV) e
propriedades mecânicas. Os resultados mostraram que a purificação e
organofilização da argila foram eficientes. A incorporação da argila organofílica
ao PHB provocou um aumento no módulo de elasticidade e armazenamento.
As resistências à tração e ao impacto diminuíram com a adição das
nanocargas. As propriedades mecânicas dos compósitos foram
significativamente afetadas pela exposição prolongada a temperaturas
elevadas. Os resultados obtidos sugerem que a incorporação da argila
organofílica ao PHB acelera o processo de degradação térmica da matriz. / The influence of addition, purification and organophilization of a nanoparticulate
mineral filler (bentonite clay) on the mechanical, thermal and morphological
properties of PHB (polyhydroxybutyrate)/bentonite with concentrations ranging
from 1 to 3% w/w was investigated. Pristine, purificed (sonication) and
organophilic (Cetremide) bentonite clays, were characterized by FTIR and XRD
before being incorporated into the PHB. The compositions were characterized
with X-ray diffraction (XRD), differential scanning calorimetry (DSC), dynamic
mechanical analysis (DMA), scanning electron microscopy (SEM) and
mechanical properties. Results showed that the purification and
organophilization clay were effective. The incorporation of the organoclay to
PHB caused an increase in tensile and storage modulus, while tensile and
impact strength decreased with clay addition. Mechanical properties were
significantly affected by prolonged exposure to elevated temperatures. Results
suggest that the incorporation of the organoclay to PHB accelerates the thermal
degradation of the polymer.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/990 |
Date | 14 June 2018 |
Creators | ALMEIDA, Tatiara Gomes de. |
Contributors | CARVALHO, Laura Hecker de., CANEDO, Eduardo Luis., ARAÚJO, Edcleide Maria., ALVES, Tatianny Soares. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.1153 seconds