Orientadores: Ana Maria M. Nazar, Ricardo E. Medrano / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-22T10:50:05Z (GMT). No. of bitstreams: 1
Sagradi_Marcello_M.pdf: 11321510 bytes, checksum: 9e4a5b3b4d657979e73fcaff4ac13ac4 (MD5)
Previous issue date: 1997 / Resumo: Materiais superplásticos podem sofrer altos níveis de deformação de maneira homogênea quando submetidos a condições de processamento específicas (alta temperatura e baixa taxa de deformação). Os aços inoxidáveis duplex podem ser superplásticos, contudo isto só é possível para materiais com estrutura refinada, ou seja, é necessário que o tamanho de grão seja inferior a 10 µm. O objetivo deste trabalho é desenvolver e estudar, em função da microestrutura de partida, o comportamento superplástico do aço inoxidável duplex 2205 (21,13% Cr; 4,73% Ni; 2,75% Mo; 0.18N). Para atingir este propósito, um material não superplástico foi submetido a diversos tratamentos termomecânicos, incluindo laminação a quente (80% de redução de área) no campo bifásico, laminação a frio (vários graus de redução) após um tratamento de solubilização no campo monofásico (ferrítico) e um tratamento de solubilização após cada processo de deformação. Desta forma, fabricaram-se duas categorias de materiais: os materiais brutos de laminação e os materiais solubilizados. Para avaliar a superplasticidade, todos os materiais listados acima foram submetidos ao ensaio de tração à temperatura de 980°C com mudança de taxa de deformação. Tal procedimento permitiu a determinação do expoente de sensibilidade à taxa de deformação (m) em função da taxa de deformação. Para verificar a correlação existente entre os resultados obtidos pelos ensaios e a microestrutura de partida, em alguns casos, realizaram-se ensaios de tração até a fratura com uma taxa de 3 x I0-4 s-1 na mesma temperatura. Foi feita ainda uma análise metalográfica em cada corpo-de-prova após cada ensaio de tração. O trabalho permitiu concluir que, como o processo de deformação a frio produz microestruturas mais refinadas, este é mais indicado para tornar o aço estudado superplástico. O tratamento mais efetivo foi a laminação do material a frio com uma redução de 80% após uma solubilização a 1380°C, o que resultou em tamanhos de grão da ordem de 5 µm. Neste caso, o valor máximo encontrado para o alongamento foi de 1500%, para uma taxa de 3 x I0-4 s-1, onde o valor de m é de 0,64. Taxas de deformação menores não melhoraram a superplasticidade do material, devido à precipitação de fase sigma em ensaios mais lentos. Acredita-se que a fase sigma nucleia cavidades, promovendo a falha prematura do material / Abstract: Superplastic materials can undergo high deformation levels with high uniformity when submitted to specific conditions (high temperature and slow strain rate). Duplex stainless steel may exhibit superplastic behavior. However, this is only possible to fine-grained materials, in other words, a grain size less than 10 µm is required. The purpose of this work is to develop and study as a function of prior microstructure the superplastic behavior of the 2205 duplex stainless steel (21.13% Cr, 4.73% Ni, 2.75% Mo, 0.18N). To reach this goal, a non-superplastic material was submitted to several thermomechanical treatments, including hot rolling (80% of area reduction) in the dual-phase field, cold rolling (several levels of area reduction) after a solution treatment in the single phase field (ferritic) and a solution treatment after each deformation process Therefore, it was made two categories of materials: the as rolled materials and the solution treated ones. To evaluate the superplasticity, all materials listed were tested by means of the tensile strain rate change test at 980°C. This allowed the determination of the strain rate sensitivity exponent (m) as a function of strain rate. To verify the correlation between the results of the tensile strain rate change tests and the prior microstructure, in some cases hot tensile tests were performed at 980°C with a strain rate of 3 x I0-4 s-1. The final microstructure of each hot tensile test sample was also analyzed. The main conclusions are listed as follows as the cold work processes produce more refined microstructures, they are more suitable to impair a superplastic behavior to the steel studied. The most effective treatment was cold rolling the material (80%) after a solution treatment at 1380°C. This treatment produced materials whose grain size was about 5 µm. In this case, for a strain rate of 3 x I0-4 s-1the elongation reached 1500% and m value obtained was 0.64. Lower values of strain rate do not increase the material superplasticity. This is related to sigma phase precipitation in the slower test. It was believed that sigma phase nucleates cavities and then promotes premature failure of the material / Mestrado / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263054 |
| Date | 08 April 1997 |
| Creators | Sagradi, Marcello |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Medrano, Ricardo Enrique, 1937-, Martinez Nazar, Ana Maria, 1948-, Nazar, Ana Maria M., Ferreira, Itamar, Isore, Alain Jose |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 126f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0087 seconds