Acoplamento oxidativo de metano sobre catalisadores Li-Mn/MgO-SiO2

Orientador: Gustavo Paim Valença / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-24T13:00:51Z (GMT). No. of bitstreams: 1
Legracie_FabianaBoschiero_M.pdf: 2134507 bytes, checksum: 2eec0ada9e053e3653ac897e1b0b3182 (MD5)
Previous issue date: 1999 / Resumo: A conversão de metano a produtos de maior valor ou mais facilmente transportáveis é um objetivo de interesse científico e prático. Dentre as alternativas para a conversão direta de metano grande atenção tem sido voltada para a reação de acoplamento oxidativo de metano. Assim, catalisadores de Li-Mn/MgO-Si¿O Ind. 2¿ foram preparados e testados na reação de acoplamento oxidadtivo de metano. Um planejamento experimental tipo estrela foi utilizado para estudar a influência da razão nominal de átomos de Mg:Si no suporte e os teores de lítio e manganês. Os precursores de óxidos mistos de magnésia e sílica foram preparados por coprecipitação nas razões nominais de Mg:Si iguais a 1:0, 4:1, 1:1, 1:4 e 0:1. a adição da fase ativa, Mn e Li, a esses precursores foi feita pelo método de impregnação incipiente e foi variada na faixa de 0,2 a 19,8% e 1 a 6% em peso de catalisador, respectivamente. Os sólidos preparados foram caracterizados por difração de raios-X e medida da área superficial BET. A reação foi efetuada a 1100, 1150 e 1200 K, à pressão ambiente em um reator de quartzo e com um fluxo de alimentação de 132 'cm POT. 3¿ 'min POT. ¿1¿ com uma razão 'N IND. 2¿: 'CH IND. 4¿: 'O IND. 2¿ em 5:5:1... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: Oxidative coupling of methane is an alternative route for the conversion of methane to hydrocarbons of higher molecular mass and higher boiling points. This reaction has received considerable scientific and industrial attention over the past 20 years. In this work 17 samples of Li-Mn/MgO-Si¿O IND. 2¿ were prepared and tested in the oxidative coupling of methane. The solids were prepared changing three different variables in a '2 POT. 3¿ star factorial design to study the influence of the nominal Mg:Si atom ratio in the supports and of the amount of Li and Mn on the surface of the supports. The mixed oxides of magnesia and silica were prepared by precipitation from aqueous solutions containing MG¿(N¿O IND. 3¿) IND. 2¿ 6¿H IND. 2¿O and amorphous Si¿O IND. 2¿ at nomial ratios of Mg:Si equal to 1:0, 1:4, 1:1, 4:1 and 0:1. The active phases, Mn and Li, were added to the supports by the incipient wetmess method. The percentages of Mn and Li added to the mixed oxides varied from 0.2 to 19.8 w/w% and from 0 to 6 w/w%, respectively. The solids were characterized by X-ray diffraction and by BET surface area. The reaction was studied in a quartz reactor at 1100, 1150 and 1200 K, at atmospheric pressure... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Mestre em Engenharia Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267287
Date05 April 1999
CreatorsLegracie, Fabiana Boschiero
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Valença, Gustavo Paim, 1960-, Bueno, Jose Maria Correa, Moura, José Claudio
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format80p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds