Previous issue date: 2016-02-29 / Capes / O presente trabalho trata da obtenção e caracterização de filmes planos de PEBDL/bentonita com e sem a incorporação de um agente compatibilizante (PE-gMA). Os filmes foram obtidos por extrusão plana e suas propriedades mecânicas, de permeabilidade e térmicas foram avaliadas em função do teor (0 a 5% em massa) e do tipo de carga incorporada. Duas argilas foram utilizadas: a) uma bentonita de origem local (Paraibana) e b) uma argila organofílica comercial importada. A argila paraibana foi purificada e organofilizada antes de ser incorporada à matriz polimérica. As argilas utilizadas foram caracterizadas através da sua capacidade de troca catiônica (CTC), por difração de raios-x (DRX), por espectroscopia no infravermelho por transformada de Fourier (FTIR), análise da composição química por energia dispersiva (EDX), análise granulométrica e por análise termogravimétrica (TGA). Os nanocompósitos obtidos na forma de filmes planos foram caracterizados por DRX, microscopia eletrônica de varredura (MEV), permeabilidade ao vapor de água e aos gases O2 e CO2, propriedades mecânicas, análise termogravimétrica (TGA) e análise da calorimetria exploratória diferencial (DSC). Os filmes de nanocompósitos com compatibilizante apresentaram morfologia intercalada/parcialmente esfoliada e os filmes sem a presença do compatibilizante apresentaram morfologia compatível com a de nanocompósitos intercalados/microcompósitos. Os resultados das propriedades mecânicas mostraram que os filmes preparados com o agente compatibilizante apresentaram propriedades superiores à da matriz pura e às dos outros sistemas preparados. A presença do agente compatibilizante reduziu significativamente a permeabilidade ao vapor de água e a permeabilidade ao gás O2 nos filmes, mas os filmes sem a presença do agente compatibilizante apresentaram aumento desta propriedade quando comparados ao filme de PEBDL puro. As analises térmicas mostraram um aumento discreto da estabilidade térmica para os filmes de nanocompósitos preparados com o agente compatibilizante. / The present work deals with the manufactur and characterization of flat films of LLDPE/bentonite with and without the incorporation of a compatibilizing agent (PE-g-MA). The films were obtained by flat die extrusion and its mechanical, permeability and thermal properties were evaluated in function of clay content (0 to 5% by mass) and clay identity. Two clays were used: a) a local bentonite (from Paraiba) and b) an imported commercial organoclay. The local clay was purified and organophilized before being incorporated into the polymer matrix. The clays were characterized by cation exchange capacity (CEC), x-ray diffraction (XRD), spectroscopy Fourier transform infrared (FTIR), analysis, chemical composition by dispersive energy (EDX), particle size analysis and by thermogravimetric analysis (TG). Nanocomposites obtained as flat films were characterized by XRD, scanning electron microscopy (SEM), water vapor, O2 and CO2 gas permeability, mechanical properties, thermogravimetric analysis (TG) and differential scanning calorimetry (DSC). The nanocomposite films with compatibilizer showed an intercalated/partially exfoliated morphology while the morphology of the films without compatibilizer was compatible with that of intercalated nanocomposites/microcomposites. The mechanical properties of the films prepared with the compatibilizer agent were higher than those of the neat matrix and the other systems prepared. Compatibilizing agent addition significantly reduced water vapor and O2 gas permeability in films, but the films without the presence of the compatibilizer showed an increase of this property when compared to pure LLDPE film. The influence of compatibilizer addition on CO2 permeability was small. Thermal analyzes showed a slight increase of thermal stability for the films of nanocomposites prepared with the compatibilizing agent.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1044 |
Date | 26 June 2018 |
Creators | SILVA, Eduardo de Mello. |
Contributors | CARVALHO, Laura Hecker de., LARANJEIRA, Edilane., WELLEN, Renate Maria Ramos., CANEDO, Eduardo Luis., MELO, Tomás Jeferson Alves de. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds