Previous issue date: 2015-03-30 / Sem bolsa / Este estudo avaliou, a radiopacidade, o pH, a citotoxicidade e o efeito antimicrobiano de um material experimental à base de MTA para obturação de dentes decíduos. Também foram avaliados: Vitapex, Óxido de zinco e eugenol (OZE), e Calen espessado com óxido de zinco. A radiopacidade dos materiais foi comparada a uma escala de alumínio com variação de 0,5 a 5 mm, utilizando sensor digital, com distância focal e tempo de exposição padronizados. A mensuração do pH foi realizada em água deionizada, em períodos entre 1 hora e 30 dias. A viabilidade celular foi avaliada em fibroblastos gengivais humanos, expostos aos materiais por 1, 3 e 7 dias, através do teste de MTT. A atividade antimicrobiana dos materiais foi testada sobre uma cepa de Enterococcus faecalis, através do teste de contato direto. Foi realizada ainda, a avaliação do efeito antimicrobiano sobre biofilme de uma pasta de hidróxido de cálcio; iodofórmio; Vitapex; OZE, e Calen espessado com óxido de zinco. Amostras de biofilme misto foram suspensas em BHI e incubadas, em condições anaeróbicas, usando discos de hidroxiapatita como substrato por 21 dias. Os espécimes foram colocados em contato com os materiais em períodos experimentais de 7 e 30 dias. A porcentagem de bactérias mortas no biofilme foi determinada em microscopia confocal de varredura a laser. Os resultados de radiopacidade mostraram que o material experimental apresentou 3,28 mmAl, valor estatisticamente inferior ao apresentado pelos demais materiais (p<0,05). O material experimental e o Calen espessado com óxido de zinco apresentaram valores de pH >12 enquanto que o cimento de OZE e o Vitapex mostraram valores menores (p>0,05). As células expostas a extratos de Vitapex apresentaram maior viabilidade em todas as concentrações, enquanto que as células expostas aos extratos de OZE apresentaram menor viabilidade (p<0,001). O material à base de MTA e a pasta Calen foram estatisticamente semelhantes (p= 0,115). O teste de contato direto revelou que o material experimental a base de MTA eliminou E. faecalis após 4 horas de contato.O Vitapex foi o material de maior eficácia sobre o biofilme misto. Após 30 dias, apenas 49.49% do volume do biofilme estava viável. Houve diferença significativa entre os materiais em relação ao efeito sobre o biofilme (F = 73,073, p= 0,00). Conclui-se que o MTA experimental apresenta propriedades satisfatórias para emprego como material obturador de dentes decíduos. / The aim of this study was to evaluate radiopacity, pH, cytotoxicity and antimicrobial effect of an experimental MTA-based material comparing to zinc oxide eugenol (ZOE) cement, Calen paste thickened with zinc oxide, and Vitapex. The radiopacity of materials was compared to graduated aluminum stepwedge ranging from 0.5 to 5 mm using a digital sensor with standardized focal distance and exposure time. The measurement of pH was performed in deionized water in periods between 1 hour and 30 days. Cell viability was evaluated in human gingival fibroblasts exposed to materials for 1, 3 and 7 days through the MTT assay. Mixed-species biofilm samples were suspended in BHI and incubated in anaerobic conditions using sterile hydroxyapatite disks as substrate for 21 days. The specimens were placed in contact with the tested materials for experimental periods of 7 and 30 days. The percentage of killed bacteria within biofilm was determined by confocal laser scanning microscopy. The antimicrobial activity of the materials was tested on a strain of Enterococcus faecalis, through direct contact test. The results of radiopacity showed that the experimental MTA presented 3.28 mmAl but statistically lower than that presented by the other materials (p<0.05). Experimental MTA based material and Calen thickened with zinc oxide had pH> 12 while ZOE and Vitapex had lower values (p>0.05). Cells exposed to extracts from Vitapex showed the highest viability rate at all concentrations, whereas cells exposed to ZOE extracts displayed the lowest viabilityrate (p<0.001). MTA- based material and Calen paste were statistically equivalent (p = 0.115). Experimental MTA killed E. faecalis effectively after 4 hours of exposure. Vitapex was the most effective material against biofilm. After 30 days of incubation with Vitapex, 49.59% biofilm volume was viable. There were significant differences in the killing ratio between different materials (F = 73.073, p= 0.00). In conclusion, experimental MTA- based material has satisfactory properties for use as endodontic filling material.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3523 |
| Date | 30 March 2015 |
| Creators | Pilownic, Katerine Jahnecke |
| Contributors | 93545037053, http://lattes.cnpq.br/1519551419752177, Romano, Ana Regina, Pappen, Fernanda Geraldo |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0115 seconds