No / An extensive study of the fibre orientation structures developed in a transverse ribbed plate during injection moulding, and the use of these structures to investigate the effect of local fibre orientation state on crack initiation resistance, is reported. The fibre orientation results for the ribbed plate, measured using large area image analysis system developed at Leeds University, showed that after an initial settling down period, the central core region, where the fibres are aligned perpendicular to the flow direction, decreased in size monotonically, with an associated monotonic increase in the outer shell regions, where the fibres are aligned preferentially along the injection direction. Interestingly, the level of orientation in the two regions remained almost constant: only the proportions of the two regions were found to change with flow length. Across the plate, close to the gate, the central core region was found to have a lens-like shape, while at the other end of the plate the core was thinner and also consistent in thickness across the sample width. The transverse rib was found to cause little disturbance to the fibre orientation of the base plate. The different proportions of the shell and core regions at different locations over the ribbed plate provided an ideal case to test the proposition of Friedrich that the crack resistance of a short fibre reinforced material depends on the number of fibres that are perpendicular to the crack tip. The impact test results gathered in this way confirmed this hypothesis of Friedrich.
| Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/2780 |
| Date | January 2004 |
| Creators | Coates, Philip D., Caton-Rose, Philip D., Duckett, R.A., Hine, P.J. |
| Source Sets | Bradford Scholars |
| Language | English |
| Detected Language | English |
| Type | Article, No full-text available in the repository |
| Relation | http://www.ingentaconnect.com/content/maney/prc/2004/00000033/00000001/art00008;jsessionid=13lt0rq4ij4m6.victoria |
Page generated in 0.0029 seconds