The behavior during dissolution of edge and basal surfaces of the mica phlogopite were examined using in situ atomic force microscopy (AFM), x-ray photoelectron spectroscopy (XPS) and low-energy electron diffraction (LEED) in an attempt to characterize the reactive surface area during dissolution. Mica minerals are the ideal material for this study because they offer a high degree of structural anisotropy. Therefore surfaces with different structures are easily identified. Dissolution is shown to proceed preferentially by removal of material from {hk0} edges. Dissolution rates were calculated by measuring the volume of material removed from etch pits, and normalizing to either the "reactive" surface area of {hk0} edges exposed at pit walls, or to a total "BET-equivalent" surface area. Rates normalized to total surface area are in the range of dissolution rates reported in the literature. Edge surface normalized rates are about 100 times faster. Long-term in situ AFM observations of phlogopite dissolution reveal that exposed (001) surfaces also display a distinct reactivity, though it operates on a different time scale. The top layer is shown to expand between 39 and 63 hours in contact with pH 2 HCl solution. Subsequent LEED analysis shows that the (001) surface becomes amorphous upon reacting with pH 2 HCl. Compositional characterization of the phlogopite after reaction shows that for pitted phlogopite surfaces, dissolution is characterized by leaching of octahedral cations and polymerization of the silica-enriched residual layer. No chemical changes or polymerization are observed for freshly cleaved unpitted phlogopite after reaction with pH 2 HCl for 24 hours. This suggests a gallery access mechanism is facilitated by edge attack, and is only significant on exposed (001) surfaces after a certain amount of dissolution by edge attack. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/31837 |
| Date | 11 May 2001 |
| Creators | Rufe, Eric |
| Contributors | Geological Sciences, Hochella, Michael F. Jr., Rimstidt, J. Donald, Bodnar, Robert J. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | RUFEpdf.pdf |
Page generated in 0.0022 seconds