Previous issue date: 2006-10-16 / The isolation of adjacent zones encountered during oilwell drilling is carried out by Portland-based cement slurries. The slurries are pumped into the annular positions between the well and the casing. Their rheological behavior is a very important component for the cementing process. Nowadays, several alternative materials are used in oilwell cementing, with goal the modification and the improvement of their properties, mainly the increase of the fluidity. And this can be reached by using plasticizers additives able to account for different oilwell conditions, yielding compatible cement slurries and allowing enough time for the complete cementing operation. If the rheological properties of the slurry are properly characterized, the load loss and flow regime can be correctly predicted. However, this experimental characterization is difficult. Rheological models capable of describing the cement slurry behavior must be capable of predicting the slurry cement deformation within reasonable accuracy. The aim of this study was to characterize rheologically the slurries prepared with a especial class of Portland cement, water and plasticizers based on lignosulfonate, melamine and polycarboxylate at temperatures varying from 27?C to 72?C. The tests were carried out according to the practical recommendations of the API RP 10B guidelines. The results revealed a great efficiency and the dispersive power of the polycarboxylate, for all temperatures tested. This additive promoted high fluidity of the slurries, with no sedimentation. High lignosulfonate and melamine concentrations did not reduce the rheological parameters (plastic viscosity and yield stress) of the slurries. It was verified that these additives were not compatible with the type of cement used. The evaluated rheological models were capable of describing the behavior of the slurries only within concentration and temperature ranges specific for each type of additive / Pastas de cimento do tipo Portland s?o usadas para isolamento de po?os de petr?leo. Esse procedimento ? realizado por meio do bombeio da pasta no espa?o anular entre o po?o e a coluna de revestimento, de modo a se obter fixa??o e veda??o eficiente e permanente. Para isso o comportamento reol?gico da pasta de cimento ? um componente de extrema import?ncia para o processo de cimenta??o. Atualmente, diversos materiais alternativos s?o utilizados em pastas para cimenta??o, objetivando a modifica??o e a melhoria de suas propriedades, principalmente no que diz respeito ao aumento de fluidez. Isso pode ser alcan?ado por meio da utiliza??o de novos aditivos do tipo plastificantes, capazes de suportar as diversas condi??es de po?os, promovendo ?s pastas propriedades compat?veis ?s condi??es encontradas, permitindo, ainda, um tempo suficiente de trabalhabilidade para a completa execu??o do servi?o de cimenta??o. Assim, se as propriedades reol?gicas da pasta s?o bem caracterizadas, a perda de carga e o regime de fluxo podem ser prognosticados corretamente. Contudo, essa caracteriza??o ? dif?cil do ponto de vista experimental. Modelos reol?gicas capazes de descrever o que ocorre, dever?o ser capazes de predizer a deforma??o da pasta de cimento com razo?vel exatid?o. Portanto, a finalidade deste trabalho foi o estudo e a caracteriza??o reol?gica de pastas constitu?das de cimento Portland classe especial, ?gua e aditivos do tipo plastificante, a base de lignossulfonato, melamina e policarboxilato, em temperaturas na faixa de 27?C a 72?C. Os testes foram realizados de acordo com as recomenda??es pr?ticas da norma API RP 10B. Os resultados dos ensaios demonstraram a grande efici?ncia e o poder dispersivo do policarboxilato, para todas as temperaturas estudadas. O aditivo promoveu uma alta fluidez, sem efeitos de sedimenta??o. O aumento das concentra??es de lignossulfonato e melamina n?o reduziu os par?metros reol?gicos (viscosidade pl?stica e limite de escoamento). Tamb?m foi verificado que esses aditivos n?o foram compat?veis com o tipo de cimento utilizado. Por fim, os modelos reol?gicos avaliados foram capazes de descrever o comportamento das pastas apenas para faixas de temperatura e concentra??o de cada tipo de aditivo
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12838 |
| Date | 16 October 2006 |
| Creators | Lima, Flank Melo de |
| Contributors | CPF:15724520800, http://lattes.cnpq.br/0022988322449627, Melo, Dulce Maria de Ara?jo, CPF:06117988320, http://lattes.cnpq.br/3318871716111536, Melo, Marcus Ant?nio de Freitas, CPF:04514998320, http://lattes.cnpq.br/5840621182000517, Vitor Sobrinho, Eledir, CPF:64656969915, http://lattes.cnpq.br/8488499388852606, Martinelli, Ant?nio Eduardo |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds