Orientador: Teresa Dib Zambon Atvars / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-24T04:00:22Z (GMT). No. of bitstreams: 1
Quites_FernandoJunior_D.pdf: 4476724 bytes, checksum: ad6fd1bd74a45cdc5e9333e1f66da8c0 (MD5)
Previous issue date: 2013 / Resumo: Nesta Tese as propriedades foto e eletroluminescentes de diferentes polímeros conjugados foram abordadas: poli[(9,9-dioctilfluoreno-2,7-diil)-alt-co-(9,9-di-{5 f-pentanil}-fluoreno-2,7-diil)] (PFP) emissor na região do azul, poli[(9,9-dihexilfluoreno-2,7-diil)-alt-co-(bitiofeno)] (F6T2) emissor na região do verde e poli[2-metóxi-5(3 f,7 f-dimetiloctilóxi)1-,4-fenilenovinileno] (MDMO-PPV) emissor na região do vermelho. Primeiramente foram preparados materiais híbridos orgânico-inorgânico baseados em PFP e siliconas (polímeros de silício). Devido à presença de grupos vinílicos laterais na cadeia do PFP, estes foram ligados quimicamente às siliconas através da reação de hidrossililação produzindo dois tipos de siliconas: uma com menor grau (PDHS-PDVS-l-PFP-X) e outra com maior (PDHSS-PDVS-h-PFP-X) grau de reticulação. As propriedades fotofísicas destes materiais híbridos foram comparadas com o polímero PFP na forma de filme e em soluçõoes de THF e de diferentes polissiloxanos usados na reação de hidrossililação. Através de medidas de fotoluminescência no estado estacionário e medidas dinâmicas verificou-se que as cadeias de PFP estão desordenadas em solução e no filme fino e nas siliconas com menor grau de reticulação (PDHS-PDVS-l-PFP-X) independente da quantidade de PFP usada. Entretanto, nas siliconas híbridas com maior grau de reticulação (PDHSS-PDVS-h-PFP-X) uma fase cristalina, conhecida como fase a, foi formada. Além disso, nestes híbridos foram observados agregados emitindo em regiões de mais baixa energia quando a quantidade de PFP foi aumentada (PDHSS-PDVS-h-PFP-X, com X = 2 e 3). Portanto, a força dirigente para a formação da fase cristalina a pode ser pensada como uma combinação de interações p -p entre a cadeia principal planar do polímero e interações hidrofóbicas dos grupos laterais no ambiente mais confinado causado pelas cadeias das siliconas com maior grau de reticulação (PDHSS-PDVS-h-PFP-X). Após o estudo detalhado das propriedades fotofísicas do PFP tanto em solução como no estado sólido, blendas poliméricas baseadas neste polímero e no copolímero F6T2 foram preparadas. As investigações fotofísicas mostraram que há uma eficiente transferência de energia do doador PFP para o receptor F6T2 nestas blendas (PFP/F6T2). A transferência de energia se dá pelos processos não radiativo (mecanismo do tipo Förster) e radiativo. Foram também preparados diodos eletroluminescentes usando as blendas poliméricas de PFP/F6T2 como camada ativa (configuração do diodo ITO/PEDOT:PSS/blenda polimérica/Ca/Al) com a intenção de produzir dispositivos poliméricos emissores de luz branca (WPLEDs). Nestes dispositivos foi observada uma transferência de energia do PFP para o F6T2 e uma eficiente recombinação de cargas sendo favorecida nos domínios do copolímero F6T2, impossibilitando a preparação de WPLEDs empregando este dois componentes na mesma camada ativa. Como a preparação de WPLEDs foi comprometida usando blendas de PFP e F6T2, devido a eficiente recombinação de cargas nos domínios do F6T2, foi proposta uma metodologia empregando dois materiais poliméricos com propriedades de emissão de luz diferentes: um composto eletroluminescente, neste caso foi usado o PFP e outro composto fotoluminescentes (para isto foi escolhido o MDMO-PPV). Nesta metodologia foi construido um diodo EL baseado no polímero PFP (ITO/PEDOT/PSS:PFP/Ca/Al) que emitiu luz azul-esverdeada. Na face oposta deste dispositivo (onde há a saída de luz, substrato de quartzo/ITO) foi colocado um filme fino (depositado sobre um substrato de quartzo) do polímero MDMO-PPV. Este filme absorve na região da eletroemissão esverdeada do PFP, ou seja, a luz emitida pelo PFP e capaz de excitar as moléculas de MDMO-PPV, e ambos os componente emitem fazendo surgir uma emissão de luz branca. A cor branca foi confirmada pela coordenada de cromaticidade CIE (x = 0.35 e y = 0.31). / Abstract: In this work the photo and electroluminescent properties of the different conjugated polymers were investigated: poly[(9,9-dioctylfluorene-2,7-diyl)-alt-(9,9-di(pent-4-en-1-yl)fluorene-2,7-diyl)]) (PFP) blue emitter, poly [(9,9-dihexilfluoreno-2 ,7-diyl)-alt-co-(bithiophene)] (F6T2) green emitter and poly[2-methoxy-5-(3',7'-dimethyloctyloxy)-1,4-phenylenevinylene] ( MDMO -PPV ) red emitter. Firstly, we prepared organic-inorganic hybrid materials based on silicones and PFP polymer. The presence of vinyl moieties in the side chain of PFP react with Si-H groups of the silicone by the hydrosilylation producing two types of silicones: with lower (PDHS-PDVS-l-PFP-X) and higher (PDHSS-PDVS-PFP-h-X) crosslinking degree. The photophysical properties of these hybrid materials were compared with PFP polymer in film form and in the solutions of THF and of the different polysiloxanes used in the hydrosilylation reaction. Based on the steady-state and dynamic photoluminescence data, PFP chains are disordered in solutions, in the film and in the silicones with a lower degree of crosslinking (PDHS-PDVS-l-PFP-X) independent of the amount of PFP used. Nevertheless, in the hybrids with a higher degree of crosslinking (PDHSS-PDVS-PFP-h-X) the crystalline a-phase of the polyfluorene was formed. Aggregates emitting in longer wavelengths are only formed when other crystalline phases are present in PDHSS-PDVS-h-PFP-X (X = 2 and 3) silicones. The driving force for this formation is probably a combination of p - p interaction between the planar backbone and the hydrophobic interactions of the lateral groups in the poor solvent in a more confined environment such as brittle PDHSS-PDVS-h-PFP. After detailed study of the photophysical properties of PFP both in solution and in the solid state, polymer blends based on this polymer and in the F6T2 copolymer were prepared. The photophysical investigations showed that there is an efficient energy transfer from the donor (PFP) to the acceptor (F6T2) in these blends (PFP/F6T2). The energy transfer occurs by non-radiative process (Förster-type mechanism) and radiative. Electroluminescent diodes were also studied using polymer blends of PFP/F6T2 as active layer (device configuration: ITO/PEDOT:PSS/polymer blend/Ca/Al) with the intention of produce white polymer light-emitting diodes (WPLEDs). In these diodes was also observed an efficient energy transfer from the PFP to F6T2, and the charge recombination was favored in the dominions of the F6T2 copolymer. The higher transfer energy from donor to acceptor in these diodes compromised the blue light and the withe light using this polymer in the same active layer do not produced. Thus, white-emitting electroluminescent diode was obtained with a single layer of an electro-active greenish component (PFP) and an external photoluminescent (PL) red-emitting material (MDMO-PPV), in a diode configuration of ITO/PEDOT-PPS/PFP/Ca/Al//MDMO-PPV. A thin film of this PL component was deposited onto a glass plate and mounted on the opposite face of a glass/ITO substrate. The MDMO-PPV polymer electronic absorption matches the greenish electroemission of the PFP. The white color, based on the CIE color coordinates (x = 0.35 e y = 0.31), was obtained by the red emission of the external MDMO-PPV film and the blue-greenish EL emission from the formed PFP diode. White emission was produced by adjusting the absorbance of the layer thickness and the blue-greenish component until it reached the CIE white coordinates. / Doutorado / Quimica Inorganica / Doutor em Quimica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/249478 |
| Date | 22 November 2013 |
| Creators | Quites, Fernando Júnior, 1983- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Atvars, Teresa Dib Zambon, 1952-, Rodrigues, Paula Cristina, Guimarães, Francisco Eduardo Gontijo, Nogueira, Ana Flávia, Silva, René Alfonso Nome |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 129 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds