The superior characteristics of silicon carbide, compared with silicon, have suggested considering this material for the next generation of power semiconductor devices. Among the different power switches, the bipolar junction transistor (BJT) can provide a very low forward voltage drop, a high current capability and a fast switching speed. However, in order to compete on the market, it is crucial to a have high current gain and a breakdown voltage close to ideal. Moreover, the absence of conductivity modulation and long-term stability has to be solved. In this thesis, these topics are investigated comparing simulations and measurements. Initially, an efficient etched JTE has been simulated and fabricated. In agreement with the simulations, the fabricated diodes exhibit the highest BV of around 4.3 kV when a two-zone JTE is implemented. Furthermore, the simulations and measurements demonstrate a good agreement between the electric field distribution inside the device and the optical luminescence measured at breakdown. Additionally, an accurate model to simulate the forward characteristics of 4H-SiC BJTs is presented. In order to validate the model, the simulated current gains are compared with measurements at different temperatures and different base-emitter geometries. Moreover, the simulations and measurements of the on-resistance are compared at different base currents and different temperatures. This comparison, coupled with a detailed analysis of the carrier concentration inside the BJT, indicates that internal forward biasing of the base-collector junction limits the BJT to operate at high current density and low forward voltage drop simultaneously. In agreement with the measurements, a design with a highly-doped extrinsic base is proposed to alleviate this problem. In addition to the static characteristics, the comparison of measured and simulated switching waveforms demonstrates that the SiC BJT can provide fast switching speed when it acts as a unipolar device. This is crucial to have low power losses during transient. Finally, the long-term stability is investigated. It is observed that the electrical stress of the base-emitter diode produces current gain degradation; however, the degradation mechanisms are still unclear. In fact, the analysis of the measured Gummel plot suggests that the reduction of the carrier lifetime in the base-emitter region might be only one of the causes of this degradation. In addition, the current gain degradation due to ionizing radiation is investigated comparing the simulations and measurements. The simulations suggest that the creation of positive charge in the passivation layer can increase the base current; this increase is also observed in the electrical measurements. / QC 20120522
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-95320 |
| Date | January 2012 |
| Creators | Buono, Benedetto |
| Publisher | KTH, Integrerade komponenter och kretsar, Stockholm |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Trita-ICT/MAP AVH, 1653-7610 ; 2012:08 |
Page generated in 0.0024 seconds